CN103737694A - Processing technology for high-density bamboo floor - Google Patents
Processing technology for high-density bamboo floor Download PDFInfo
- Publication number
- CN103737694A CN103737694A CN201210392657.8A CN201210392657A CN103737694A CN 103737694 A CN103737694 A CN 103737694A CN 201210392657 A CN201210392657 A CN 201210392657A CN 103737694 A CN103737694 A CN 103737694A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- density
- floor
- bamboo floor
- high pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing technology for a high-density bamboo floor, and relates to the technical field of bamboo floor processing. The technological processes comprise the steps of bamboo selecting, punching, rough planing, carbonizing, drying, fine planing, compositing, high-pressure compressing, color matching and product inspecting. The processing technology can effectively solve the problems that when being affected with damp, the bamboo floor warps and goes moldy easily in the use process, and is simple and easy to achieve.
Description
Technical field:
The present invention relates to a kind of baseboard material process technology, be specifically related to a kind of high-density bamboo floor machining process.
Background technology:
China bamboo source is very abundant, occupies first place in the world in output position, is one of main Chan Zhu state in the world.China has bamboo plant kind more than 300, but have the bamboo wood that industrialized utilization is worth, only has kind more than 10.For the bamboo floor of flooring finishing, raw material are mao bamboons, are called again bamboo, bamboo cane, cat head bamboo and Meng Zongzhu, and the main place of production is areas to the south, China the Changjiang river.High-grade bamboo floor adopts the bamboo fresh mao bamboon in 4-6 years ages, through special modified techniques of 30 multiple tracks such as protection against the tide, mildew-resistant, mothproof and degreasings, processes, and color and luster is even, and it is clear that decorative pattern enriches, and aberration is less than timber floor.Because bamboo is plant crude fiber structure, case hardness exceeds more than one times than timber, and not yielding, is only equivalent to the price of middle-grade timber floor.Meanwhile, bamboo just can be become a useful person obviously faster than trees growth period for several years, becomes the resources of production of sustainable development, and has environment-friendly function.
But the humidity resistance of bamboo wood is poor, easily distortion.For solving the humidity resistance of bamboo wood, CN1058822 patent has proposed that a kind of to take cement, pitch be plate substrate material, bamboo wood is surperficial composite plate, because the expand with wet and contract with dry coefficient of bamboo wood is different from cement plate, dry wet variation along with weather, bamboo wood can split away off from cement plate gradually, warpage after can not fundamentally solving bamboo wood and making moist, the problem such as mouldy.
Summary of the invention:
The object of this invention is to provide a kind of high-density bamboo floor machining process, it can effectively solve warpage that bamboo base plate easily causes because of making moist in use, the problem such as mouldy, and processing technology is simple, is easy to realization.
In order to solve the existing problem of background technology, the present invention adopts following technological process: select bamboo, and------carbonization--is dried--adjustable cast iron planes--compound--high pressure compressed--toning--examination and test of products in force plane in punching.
Described selects bamboo General Requirements bamboo wood rod perfectly straight, just round, and diameter is larger.
Described punching is bamboo wood to be washed into the bamboo chip of same equal-specification size.
Described force plane is that acromere in bamboo chip is tied, a part of Outer part and inner part of the bamboo of simultaneously shooting off.
Described carbonization is placed in bamboo chip the environment of high temperature, high humidity, high pressure, makes organic substance in bamboo wood as sugar, starch, and protein decomposes sex change, makes the insects such as fungi lose nutrient source, again the worm's ovum in bamboo wood, fungi is killed simultaneously.Bamboo wood bamboo fibre coking after high temperature, high pressure becomes bronze-colored, or is similar to coffee color, and concrete steps are that bamboo chip is put into gabion, close fire door, open steam valve, and bamboo chip is taken out in exhaust, and the bamboo material surface hardness after carbonization also strengthens one times.
Described oven dry is that bamboo chip is dried to water content between 6%-15%.
Described adjustable cast iron planes is by the surf green of bamboo chip after dry, tabasheer planing totally.
Described compound be by polylith bamboo chip hot-press gluing well-thought-out plan floor.
Described high pressure compressed is that rolling is carried out to through rolling mill in bamboo floor, to improve the density on bamboo floor.
Described toning is to be painted in bamboo floor.
Outward appearance paint quality, inherent quality and the processing precision of products of described examination and test of products main test product.
The present invention can effectively solve warpage that bamboo base plate easily causes because of making moist in use, the problem such as mouldy, and processing technology is simple, is easy to realization.
the specific embodiment:
This specific embodiment adopts following technological process: select bamboo, and------carbonization--is dried--adjustable cast iron planes--compound--high pressure compressed--toning--examination and test of products in force plane in punching.
Described selects bamboo General Requirements bamboo wood rod perfectly straight, just round, and diameter is larger.
Described punching is bamboo wood to be washed into the bamboo chip of same equal-specification size.
Described force plane is that acromere in bamboo chip is tied, a part of Outer part and inner part of the bamboo of simultaneously shooting off.
Described carbonization is placed in bamboo chip the environment of high temperature, high humidity, high pressure, makes organic substance in bamboo wood as sugar, starch, and protein decomposes sex change, makes the insects such as fungi lose nutrient source, again the worm's ovum in bamboo wood, fungi is killed simultaneously.Bamboo wood bamboo fibre coking after high temperature, high pressure becomes bronze-colored, or is similar to coffee color, and concrete steps are that bamboo chip is put into gabion, close fire door, open steam valve, and bamboo chip is taken out in exhaust, and the bamboo material surface hardness after carbonization also strengthens one times.
Described oven dry is that bamboo chip is dried to water content between 6%-15%.
Described adjustable cast iron planes is by the surf green of bamboo chip after dry, tabasheer planing totally.
Described compound be by polylith bamboo chip hot-press gluing well-thought-out plan floor.
Described high pressure compressed is that rolling is carried out to through rolling mill in bamboo floor, to improve the density on bamboo floor.
Described toning is to be painted in bamboo floor.
Outward appearance paint quality, inherent quality and the processing precision of products of described examination and test of products main test product.
This specific embodiment can effectively solve warpage that bamboo base plate easily causes because of making moist in use, the problem such as mouldy, and processing technology is simple, is easy to realization.
Claims (5)
1. a high-density bamboo floor machining process, is characterized in that its technological process is: select bamboo, and------carbonization--is dried--adjustable cast iron planes--compound--high pressure compressed--toning--examination and test of products in force plane in punching.
2. a kind of high-density bamboo floor machining process according to claim 1, it is characterized in that described carbonization is placed in bamboo chip the environment of high temperature, high humidity, high pressure, make organic substance in bamboo wood as sugar, starch, protein decomposes sex change, make the insects such as fungi lose nutrient source, again the worm's ovum in bamboo wood, fungi are killed simultaneously.
3. bamboo wood bamboo fibre coking after high temperature, high pressure becomes bronze-coloredly, or is similar to coffee color, and concrete steps are that bamboo chip is put into gabion, close fire door, open steam valve, and bamboo chip is taken out in exhaust, and the bamboo material surface hardness after carbonization also strengthens one times.
4. a kind of high-density bamboo floor machining process according to claim 1, is characterized in that described oven dry is that bamboo chip is dried to water content between 6%-15%.
5. a kind of high-density bamboo floor machining process according to claim 1, is characterized in that described high pressure compressed is that rolling is carried out to through rolling mill in bamboo floor, to improve the density on bamboo floor.