CN103726353A - Processing method of noctilucent coated fabric - Google Patents
Processing method of noctilucent coated fabric Download PDFInfo
- Publication number
- CN103726353A CN103726353A CN201310604718.7A CN201310604718A CN103726353A CN 103726353 A CN103726353 A CN 103726353A CN 201310604718 A CN201310604718 A CN 201310604718A CN 103726353 A CN103726353 A CN 103726353A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- noctilucent
- processing method
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing method of a noctilucent coated fabric. The processing method comprises the following steps: taking inorganic pigment hydrosol with the concentration of 40%-45%, adding a noctilucent powder solution with the concentration of 60%-65% and stirring uniformly, then sequentially adding 30 parts by mass of hydroxypropyl methyl cellulose, 35 parts by mass of cetylpyridinium bromide, 20 parts by mass of lead sulfate tribasic, 30 parts by mass of ethyl hydroxyethyl cellulose and 25 parts by mass of fatty alcohol-polyoxyethylene ether for blending, and stirring for 4-5 hours to prepare noctilucent slurry; and coating the noctilucent slurry uniformly on a plane surface of the fabric in a screen printing mode, and obtaining the noctilucent coated fabric after heating treatment at the temperature of 160-165 DEG C at a stroke speed of 55-60 meter/min. The processing method of the noctilucent coated fabric is simple in technology, convenient to operate, suitable for batch production and small in pollution.
Description
Technical field
The present invention relates to the processing method of Noctilucent coating fabric.
Background technology
Noctilucent coating fabric is manufactured manufacture complexity at present, and the cycle is long and cost is high, is not suitable for promoting the use of, and can produce in addition some poisonous, harmful and radioactive polluters in its manufacture process, harmful.
Summary of the invention
The object of the present invention is to provide a kind of processing method of Noctilucent coating fabric, its technique is simple, easy to operate, is suitable for producing in enormous quantities, pollutes little.
For achieving the above object, technical scheme of the present invention is the processing method of a kind of Noctilucent coating fabric of design, comprises the steps:
Getting concentration is the inorganic pigment hydrosol of 40-45%, adding wherein concentration is that the luminescent powder solution of 60-65% stirs, then add successively 30 parts by mass hydroxypropyl methylcelluloses, 35 parts by mass brocides, 20 parts by mass lead sulfate tribasics, 30 parts by mass ethylhydroxyethylcelluloses and 25 parts by mass fatty alcohol-polyoxyethylene ether to be in harmonious proportion, stir and within 4-5 hour, make noctilucence slip;
Noctilucence slip is evenly coated on to the plane layer of fabric by wire mark mode, then through the heat of 160-165 ℃, scanning frequency 55-60 m/min, dries and process, obtain Noctilucent coating fabric.
Advantage of the present invention and beneficial effect are: a kind of processing method of Noctilucent coating fabric is provided, and its technique is simple, easy to operate, are suitable for producing in enormous quantities, pollute little.
The specific embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A processing method for Noctilucent coating fabric, comprises the steps:
Get concentration and be 45% the inorganic pigment hydrosol, adding wherein concentration is that 65% luminescent powder solution stirs, then add successively 30 parts by mass hydroxypropyl methylcelluloses, 35 parts by mass brocides, 20 parts by mass lead sulfate tribasics, 30 parts by mass ethylhydroxyethylcelluloses and 25 parts by mass fatty alcohol-polyoxyethylene ether to be in harmonious proportion, stir and within 4-5 hour, make noctilucence slip;
Noctilucence slip is evenly coated on to the plane layer of fabric by wire mark mode, then through the heat of 60 ms/min of 165 ℃, scanning frequency, dries and process, obtain Noctilucent coating fabric.
Embodiment 2
A processing method for Noctilucent coating fabric, comprises the steps:
Get concentration and be 40% the inorganic pigment hydrosol, adding wherein concentration is that 60% luminescent powder solution stirs, then add successively 30 parts by mass hydroxypropyl methylcelluloses, 35 parts by mass brocides, 20 parts by mass lead sulfate tribasics, 30 parts by mass ethylhydroxyethylcelluloses and 25 parts by mass fatty alcohol-polyoxyethylene ether to be in harmonious proportion, stir and within 4-5 hour, make noctilucence slip;
Noctilucence slip is evenly coated on to the plane layer of fabric by wire mark mode, then through the heat of 55 ms/min of 160 ℃, scanning frequency, dries and process, obtain Noctilucent coating fabric.
Embodiment 3
A processing method for Noctilucent coating fabric, comprises the steps:
Get concentration and be 43% the inorganic pigment hydrosol, adding wherein concentration is that 64% luminescent powder solution stirs, then add successively 30 parts by mass hydroxypropyl methylcelluloses, 35 parts by mass brocides, 20 parts by mass lead sulfate tribasics, 30 parts by mass ethylhydroxyethylcelluloses and 25 parts by mass fatty alcohol-polyoxyethylene ether to be in harmonious proportion, stir and within 4-5 hour, make noctilucence slip;
Noctilucence slip is evenly coated on to the plane layer of fabric by wire mark mode, then through the heat of 57 ms/min of 162 ℃, scanning frequency, dries and process, obtain Noctilucent coating fabric.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. the processing method of Noctilucent coating fabric, is characterized in that, comprises the steps:
Getting concentration is the inorganic pigment hydrosol of 40-45%, adding wherein concentration is that the luminescent powder solution of 60-65% stirs, then add successively 30 parts by mass hydroxypropyl methylcelluloses, 35 parts by mass brocides, 20 parts by mass lead sulfate tribasics, 30 parts by mass ethylhydroxyethylcelluloses and 25 parts by mass fatty alcohol-polyoxyethylene ether to be in harmonious proportion, stir and within 4-5 hour, make noctilucence slip;
Noctilucence slip is evenly coated on to the plane layer of fabric by wire mark mode, then through the heat of 160-165 ℃, scanning frequency 55-60 m/min, dries and process, obtain Noctilucent coating fabric.