CN103725235A - Grey bonder for glass fiber cotton and curing process of bonder - Google Patents
Grey bonder for glass fiber cotton and curing process of bonder Download PDFInfo
- Publication number
- CN103725235A CN103725235A CN201310142606.4A CN201310142606A CN103725235A CN 103725235 A CN103725235 A CN 103725235A CN 201310142606 A CN201310142606 A CN 201310142606A CN 103725235 A CN103725235 A CN 103725235A
- Authority
- CN
- China
- Prior art keywords
- grey
- parts
- binding agent
- bonder
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a grey bonder for glass fiber cotton. A bonder is mixed with pigments, sprayed on glass fibers and cured through a curing furnace to obtain the grey bonder. The bonder comprises the following components in parts by weight: 30-80 parts of resin, 40-90 parts of additives, 50-80 parts of softening water and 2-5 parts of the pigments. According to the grey bonder, the components of the bonder are reasonably proportioned and the corresponding curing process is combined, so that the conventional single color of a conventional glass fiber cotton felt is changed by adding the pigments for enabling the cotton felt to be grey while the excellent performance of the original glass fiber cotton felt is kept, and parameters such as a used part, volume weight and fiber diameter can be distinguished.
Description
Technical field
The present invention relates to a kind of grey binding agent and curing process thereof, particularly relate to grey binding agent and curing process thereof for a kind of glass fibre cotton.
Background technology
Glass fibre is a kind of engineering materials, have do not fire, corrosion-resistant, high temperature resistant, moisture absorption is little, extend the premium propertiess such as little, at aspects such as electric, mechanics, chemistry and optics, also has good characteristic.Traditional glass fibre cotton felt is on glass fibre cotton, evenly to spray binding agent, then through 100～300 ℃ of hot setting moulding, can be used for the insulation such as building, aircraft, steamer, freight container, refrigerator denoising structure, in Application in Building, also need to take into account the aspects such as attractive in appearance, cost, differentiation simultaneously.In the traditional glass cellucotton of domestic application, adopt resol or urea-formaldehyde resin as binder substrate at present, and add various auxiliarys and improve its performance, resol or urea-formaldehyde resin are solidified into yellow under the solidifying agent catalysis such as ammonium sulfate, ammonium chloride.The unicity of yellow glass cellucotton color limits it and uses, and the different size that different sites is used, the cotton felt of different performance are not easy difference, cause engineering unreasonable.The present invention is by the composition of rational proportion binding agent, at binder system, add and make cotton felt present the pigment of grey, coordinate improved production technique, keeping on the basis of original glass fibre cotton premium properties, changed the conventional tone of glass fibre cotton, good looking appearance is generous, increases its application performance.
Summary of the invention
The object of the invention is to overcome the shortcoming of binding agent and curing process thereof for existing glass fibre cotton, grey binding agent and curing process thereof for a kind of glass fibre cotton is provided.
For solving the problems of the technologies described above, the present invention is achieved in that
A kind of glass fibre cotton grey binding agent, it is comprised of resin, additive, soft water and pigment, each components by weight percent is: 30～80 parts of resins, 40～90 parts of additives, 50～80 parts of softening waters, 2～5 parts of pigment, resin is a kind of in terpolycyantoamino-formaldehyde resin or melamine urea-formaldehyde resin or epoxy-phenolic resin., additive is by solidifying agent, coupling agent, hydrophober, stablizer, dust-proofing agent, softening water forms, each components by weight percent is: 4～12 parts, solidifying agent, 1～10 part of coupling agent, 5～55 parts of hydrophober, 1～8 part of stablizer, 6～40 parts of dust-proofing agents, 100～1000 parts of softening waters, pigment is a kind of in the special purple P5620 of the goth black P0070 of floridity or the goth black P0080 of floridity or floridity or the special purple P5030 of floridity, solidifying agent is vulkacit H, a kind of in diammonium phosphate, coupling agent is KH-550 silane coupling agent, hydrophober is a watt gram silicone oil, a kind of or its mixed system in methyl-silicone oil.
Curing process of the present invention comprises the following steps:
(1) grey binding agent is sprayed with fan shape spraying from shower nozzle, be evenly sprayed on glass fibre cotton, and utilize transporting chain plate that the cotton that is sprayed with grey binding agent is transported in curing oven;
(2) curing oven length is 10～30m, and temperature is 220～250 ℃, adopts the dry solidification technique of thermal cycling wind heating to heat;
(3) adjust transfer rate at 10～20m/min, make the glass fibre cotton that is sprayed with grey binding agent in curing oven, stop 1～3min.
The present invention is by the composition of rational proportioning binding agent, and coordinate corresponding curing process, when keeping original glass fibre cotton felt excellent properties, by adding pigment to make cotton felt present grey, change routine, the single tone of traditional glass cellucotton felt, in order to difference, used the parameters such as position, unit weight, Fibre diameter.Smoked glass cellucotton of the present invention is widely used in insulation or the silene system of building, refrigerator, steamer, train, aircraft, freight container etc.
Embodiment
Below in conjunction with several specific embodiments, further illustrate the present invention, should understand these embodiment is only not used in and limits the scope of the invention for the present invention is described, after having read the present invention, those skilled in the art all fall within the application's claims to the modification of the various equivalent form of values of the present invention and limit.
Embodiment 1
Terpolycyantoamino-formaldehyde resin 40Kg, diammonium phosphate 5Kg, KH-550 silane coupling agent 3Kg, watt gram silicone oil 15Kg, softening water 500Kg, pigment 3Kg.
Curing process in the present embodiment comprises the following steps:
(1) grey binding agent is sprayed with fan shape spraying from shower nozzle, be evenly sprayed on glass fibre cotton, and utilize transporting chain plate that the cotton that is sprayed with grey binding agent is transported in curing oven;
(2) curing oven length is 20m, and temperature is 230 ℃, adopts the dry solidification technique of thermal cycling wind heating to heat;
(3) adjust transfer rate at 15m/min, make the glass fibre cotton that is sprayed with grey binding agent in curing oven, stop 1.5min.
Embodiment 2
Epoxy-phenolic resin 60Kg, vulkacit H 7Kg, KH-550 silane coupling agent 5Kg, watt gram silicone oil 10Kg, dimethyl silicone oil 3Kg, softening water 350Kg, pigment 2Kg.
Curing process in the present embodiment comprises the following steps:
(1) grey binding agent is sprayed with fan shape spraying from shower nozzle, be evenly sprayed on glass fibre cotton, and utilize transporting chain plate that the cotton that is sprayed with grey binding agent is transported in curing oven;
(2) curing oven length is 17m, and temperature is 240 ℃, adopts the dry solidification technique of thermal cycling wind heating to heat;
(3) adjust transfer rate at 16m/min, make the glass fibre cotton that is sprayed with grey binding agent in curing oven, stop 1.3min.Above are only several embodiment of the present invention, but design concept of the present invention is not limited to this, allly utilizes this design to carry out the change of unsubstantiality to the present invention, all should belong to the behavior of invading the scope of protection of the invention.In every case be the content that does not depart from technical solution of the present invention, any type of simple modification, equivalent variations and the remodeling above embodiment done according to technical spirit of the present invention, still belong to the protection domain of technical solution of the present invention.
Claims (8)
1. a glass fibre cotton grey binding agent, is comprised of resin, additive, soft water and pigment, and each components by weight percent is: 30～80 parts of resins, 40～90 parts of additives, 50～80 parts of softening waters, 2～5 parts of pigment.
2. grey binding agent according to claim 1, is characterized in that described resin is a kind of in terpolycyantoamino-formaldehyde resin or melamine urea-formaldehyde resin or epoxy-phenolic resin.
3. grey binding agent according to claim 1, it is characterized in that described additive is comprised of solidifying agent, coupling agent, hydrophober, softening water, each components by weight percent is: 4～12 parts, solidifying agent, 1～10 part of coupling agent, 5～55 parts of hydrophober, 100～1000 parts of softening waters.
4. grey binding agent according to claim 1, is characterized in that described pigment is a kind of in the goth black P0070 of floridity or the goth black P0080 of floridity or the special purple P5620 of floridity or the special purple P5030 of floridity.
5. additive according to claim 3, is characterized in that described solidifying agent is a kind of in vulkacit H, diammonium phosphate.
6. additive according to claim 3, is characterized in that described coupling agent is KH-550 silane coupling agent.
7. additive according to claim 3, is characterized in that described hydrophober is for a kind of or its mixed system in watt gram silicone oil, methyl-silicone oil.
8. a curing process for grey binding agent for glass fibre cotton, is characterized in that comprising the following steps:
(1) grey binding agent is sprayed with fan shape spraying from shower nozzle, be evenly sprayed on glass fibre cotton, and utilize transporting chain plate that the cotton that is sprayed with grey binding agent is transported in curing oven;
(2) curing oven length is 10～30m, and temperature is 220～250 ℃, adopts the dry solidification technique of thermal cycling wind heating to heat;
(3) adjust transfer rate at 10～20m/min, make the glass fibre cotton that is sprayed with grey binding agent in curing oven, stop 1～3min.