CN103724917A - Flame-retardant sealing strip for automobile - Google Patents
Flame-retardant sealing strip for automobile Download PDFInfo
- Publication number
- CN103724917A CN103724917A CN201310649571.3A CN201310649571A CN103724917A CN 103724917 A CN103724917 A CN 103724917A CN 201310649571 A CN201310649571 A CN 201310649571A CN 103724917 A CN103724917 A CN 103724917A
- Authority
- CN
- China
- Prior art keywords
- water
- polyurethane dispersion
- flame retardant
- sealed strip
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retardant sealing strip for an automobile. The sealing strip is prepared from block styrol copolymer, fatty group waterborne polyurethane dispersoid, polyamide wax thick liquid, water-base resin containing activated functional groups, polypropylene, calcium carbonate, an antioxygen, an anti-ultraviolet agent, antimonous oxide, an antiscorching agent CTP, phosphoric acid ester and a-tocopherol. The sealing strip is good in flexibility and high in plasticity, flame-retardant, and very suitable for the sealing strip of doors and windows of the automobile, and can be recycled and used circularly.
Description
?
Technical field
The invention belongs to automotive field, be specifically related to a kind of flame retardant automotive sealed strip.
Background technology
The sealed strip material that existing automobile adopts is mainly polyvinylchloride material, thermoset terpolymer EP rubber, silicon rubber and thermoplastic elastomer etc., and what wherein account for large absolutely number is polyvinyl chloride and thermoset terpolymer EP rubber material.There is the defects such as aging resistance is poor, thermo-labile, not environmental protection in PVC sealing strip, is assembled on automobile door and window and uses after certain time limit, will be aging under solar radiation, be full of cracks, do not have good sealing function.Thermoset EPT rubber packing bar is in preparation process, need to be through Banbury mixer banburying and very long baking oven sulfuration, gap produces, complex process, production process is long, consume energy high, facility investment is large, and environment is had to certain pollution, scrap rubber bar or the adhesive tape changing can not reclaim direct recycling, the same with damaged tire go out of use be deposited in outside, form " black pollution ", the material of this product does not have the plastic processing characteristics of heat of thermoplastic resin and can not make colored article etc. simultaneously.In addition, the sealed strip normal temperature good springiness of the thermoplastic elastomer material take SBS, SEBS as base material, but during high temperature, heat-resisting and weathering resistance is slightly poor,, there is easily aging problem in also deviation of elasticity simultaneously, and should not be used for the sealing of automobile door and window.
The ageing resistance of natural rubber is not good, easily aging and cracking, and the prepared sealed strip life-span is shorter.The sealed strip that these materials are made does not belong to environmentfriendly products, causes certain wasting of resources, environmental pollution, and under low temperature condition, snappiness is not good.
Summary of the invention
The object of the invention is to provide a kind of flame retardant automotive sealed strip, can recycle, place the wasting of resources, with protection of the environment.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is:
A kind of flame retardant automotive sealed strip, is characterized in that, sealing bar is comprised of the component of following weight part:
Blocked styrol copolymer 50-55
Water-based aliphaic polyurethane dispersion 15-20
Polyamide wax pulp 10-14
Containing the water-base resin 26-34 of active function groups
Polipropene 25-38
Calcium carbonate 65-80
Oxidation inhibitor 1.5-2.0
Anti UV agent 0.8-1.3
Antimonous oxide 15-17
Anti-scorching agent CTP 0.03-0.05
Phosphoric acid ester 5-10
A-tocopherol 0.15-0. 2.
Further, described water-based aliphaic polyurethane dispersion is formed according to 1: 0.05: 0.2 mixture of mass ratio by ionic water-based aliphaic polyurethane dispersion, non-ionic type water-based aliphaic polyurethane dispersion and polyhutadiene water-based aliphaic polyurethane dispersion.
Further, the described water-base resin containing active function groups is aqueous polyurethane emulsion or the methyl-etherified aminoresin of water based acrylic resin emulsion, hydroxyl.
Further, described oxidation inhibitor is that antioxidant 1010, antioxidant 264 and antioxidant 1076 are according to 1: 0.85: 1.03 mixture of mass ratio.
Further, described uvioresistant is that anti UV agent 326, uvioresistant 327 and anti UV agent 531 are according to 1: 0.94: 0.86 mixture of mass ratio.
Compared with prior art, the present invention is take water-based aliphaic polyurethane dispersion as main film forming binding material, water-based aliphaic polyurethane dispersion is flexible resin, coordinate polyamide wax pulp, water-base resin and antimonous oxide containing active function groups, make sealed strip of the present invention have snappiness good, plasticity-is high, fire-retardant, be highly suitable for automobile door and window sealing strip, and can recycle and reuse.
The present invention simultaneously also adds a-tocopherol can prevent the generation of nitrosamine in formula, and thus obtained weather strip for automobile can reduce the content of inner space of vehicle objectionable impurities.
Embodiment
Below in conjunction with embodiment, the invention will be further described, and described embodiment is only the present invention's part embodiment, is not whole embodiment.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiment used that obtain under creative work prerequisite, belongs to protection scope of the present invention.
Flame retardant automotive sealed strip of the present invention, is comprised of the component of following weight part:
Blocked styrol copolymer 50-55
Water-based aliphaic polyurethane dispersion 15-20
Polyamide wax pulp 10-14
Containing the water-base resin 26-34 of active function groups
Polipropene 25-38
Calcium carbonate 65-80
Oxidation inhibitor 1.5-2.0
Anti UV agent 0.8-1.3
Antimonous oxide 15-17
Anti-scorching agent CTP 0.03-0.05
Phosphoric acid ester 5-10
A-tocopherol 0.15-0. 2.
Further, described water-based aliphaic polyurethane dispersion is formed according to 1: 0.05: 0.2 mixture of mass ratio by ionic water-based aliphaic polyurethane dispersion, non-ionic type water-based aliphaic polyurethane dispersion and polyhutadiene water-based aliphaic polyurethane dispersion.
Further, the described water-base resin containing active function groups is aqueous polyurethane emulsion or the methyl-etherified aminoresin of water based acrylic resin emulsion, hydroxyl.
Further, described oxidation inhibitor is that antioxidant 1010, antioxidant 264 and antioxidant 1076 are according to 1: 0.85: 1.03 mixture of mass ratio.
Further, described uvioresistant is that anti UV agent 326, uvioresistant 327 and anti UV agent 531 are according to 1: 0.94: 0.86 mixture of mass ratio.
The preparation method of flame retardant automotive sealed strip of the present invention, can carry out in accordance with the following steps:
1, each composition is by weight ratio prepared starting material;
2, first pour blocked styrol copolymer into agitator;
3, add agitator to stir water-based aliphaic polyurethane dispersion, polyamide wax pulp and the water-base resin containing active function groups again;
4, remaining other raw materials being put into agitator in the lump stirs;
5, the material mixing is put into dual-screw pelletizer extruding pelletization at 245-250 ℃;
6, the particle of step 5 is put on single-screw machine, will after particles melt, at 182-185 ℃, be sent into mould molding, cooling rear taking-up obtains environment-protecting thermoplastic flame retardant automotive door and window sealing strip.
Compared with prior art, the present invention is take water-based aliphaic polyurethane dispersion as main film forming binding material, water-based aliphaic polyurethane dispersion is flexible resin, coordinate polyamide wax pulp, water-base resin and antimonous oxide containing active function groups, make sealed strip of the present invention have snappiness good, plasticity-is high, fire-retardant, be highly suitable for automobile door and window sealing strip, and can recycle and reuse.
The present invention simultaneously also adds a-tocopherol can prevent the generation of nitrosamine in formula, and thus obtained weather strip for automobile can reduce the content of inner space of vehicle objectionable impurities.
Embodiment mono-
50 parts of blocked styrol copolymers, 15 parts of water-based aliphaic polyurethane dispersions, 10 parts of polyamide wax pulps, containing 5 parts of 0.03 part of 15 parts of 0.8 part of 1.5 parts, 65 parts, 26 parts of water-base resins, polipropene 25 part, calcium carbonate, oxidation inhibitor, anti UV agent, antimonous oxides, anti-scorching agent CTP, phosphoric acid ester, 0.15 part of a-tocopherol of active function groups.
Embodiment bis-
55 parts of blocked styrol copolymers, 20 parts of water-based aliphaic polyurethane dispersions, 14 parts of polyamide wax pulps, containing 10 parts of 0.05 part of 17 parts of 1.3 parts of 2 parts, 80 parts, 38 parts of 34 parts of water-base resins, polypropylene, calcium carbonate, oxidation inhibitor, anti UV agents, antimonous oxides, anti-scorching agent CTP, phosphoric acid ester, 0.2 part of a-tocopherol of active function groups.
Embodiment tri-
52 parts of blocked styrol copolymers, 18 parts of water-based aliphaic polyurethane dispersions, 123 parts of polyamide wax pulps, containing 8 parts of 0.04 part of 16 parts of 1.0 parts of 1.8 parts, 70 parts, 30 parts of 27 parts of water-base resins, polypropylene, calcium carbonate, oxidation inhibitor, anti UV agents, antimonous oxides, anti-scorching agent CTP, phosphoric acid ester, 0.18 part of a-tocopherol of active function groups.
Claims (5)
1. a flame retardant automotive sealed strip, is characterized in that, sealing bar is comprised of the component of following weight part:
Blocked styrol copolymer 50-55
Water-based aliphaic polyurethane dispersion 15-20
Polyamide wax pulp 10-14
Containing the water-base resin 26-34 of active function groups
Polipropene 25-38
Calcium carbonate 65-80
Oxidation inhibitor 1.5-2.0
Anti UV agent 0.8-1.3
Antimonous oxide 15-17
Anti-scorching agent CTP 0.03-0.05
Phosphoric acid ester 5-10
A-tocopherol 0.15-0. 2.
2. flame retardant automotive sealed strip according to claim 1, it is characterized in that, described water-based aliphaic polyurethane dispersion is formed according to 1: 0.05: 0.2 mixture of mass ratio by ionic water-based aliphaic polyurethane dispersion, non-ionic type water-based aliphaic polyurethane dispersion and polyhutadiene water-based aliphaic polyurethane dispersion.
3. flame retardant automotive sealed strip according to claim 2, is characterized in that, the described water-base resin containing active function groups is aqueous polyurethane emulsion or the methyl-etherified aminoresin of water based acrylic resin emulsion, hydroxyl.
4. flame retardant automotive sealed strip according to claim 3, is characterized in that, described oxidation inhibitor is that antioxidant 1010, antioxidant 264 and antioxidant 1076 are according to 1: 0.85: 1.03 mixture of mass ratio.
5. according to the arbitrary described flame retardant automotive sealed strip of claim 1-4, it is characterized in that, described uvioresistant is that anti UV agent 326, uvioresistant 327 and anti UV agent 531 are according to 1: 0.94: 0.86 mixture of mass ratio.