CN103724879B - A kind of electric power protecting pipe and preparation method thereof - Google Patents
A kind of electric power protecting pipe and preparation method thereof Download PDFInfo
- Publication number
- CN103724879B CN103724879B CN201310754814.XA CN201310754814A CN103724879B CN 103724879 B CN103724879 B CN 103724879B CN 201310754814 A CN201310754814 A CN 201310754814A CN 103724879 B CN103724879 B CN 103724879B
- Authority
- CN
- China
- Prior art keywords
- powder
- electric power
- protecting pipe
- power protecting
- borax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to electric power Material Field, disclose a kind of electric power protecting pipe, it is prepared from by the raw material of following weight parts, barium titanate powder 2, aluminum nitride powder 2, carbonization chromium powder 2, borax 2, talcum powder 2, Paris white 2, silica gel 2, TDE 5, stearic acid 8, starch ethers 10, chitin 15, polycarbonate 20, Natvosol 30, polyvinyl alcohol 36, polyvinyl chloride 45.The invention also discloses a kind of preparation method of electric power protecting pipe.Electric power protecting pipe prepared by the present invention possesses good tensile strength, flexural strength, bus hardness, imports the heat-resisting cold tolerance of coefficient, oxygen index and salt tolerant, can be applied to various extreme environment, possess good application prospect.
Description
Technical field
The invention belongs to electric power Material Field, specifically disclose a kind of electric power protecting pipe and preparation method thereof.
Background technology
Electric power protecting pipe is insulation protection heat-shrinkable T bush conventional on a kind of cable; the main material of this series products is PE; through cross-linking radiation and add these two techniques of thermal enlargement; there is thermal contraction function; contraction ratio is about 3: 1; bore from 50-350mm not etc., can be used as pyrocondensation inner sheath, the oversheath in cable accessory, and outer layer insulation water-proof jacket pipe.The main application of electric power protecting pipe is used as cable sheath, and protection cable does not damage by extraneous, and guarantee Electrical Safety, electric power protecting pipe is divided into buried and ground type.The protecting pipe that eighties of last century generally adopts metallic substance to prepare is to protect cable; Along with the development of Material Field, plastic pipe instead of original metal pipe material.
Electric power protecting pipe generally needs to be applied in various severe environment, comprises seabed, snowfield and saline-alkali environment etc.Because environment for use is severe, needs to carry out enhancing modified to plastic material, make it that there is higher ring stiffness, in order to resist extraneous load; Need stronger cold-resistant temperature capacity, and it is not yielding to be not easily corroded, the features such as long service life.Electric power protecting pipe of the prior art often exists various performance can not be had both, and range of application is extensive not, and technician selects the type of electric power protecting pipe often very difficult for varying environment.Chinese patent CN201210250643 discloses a kind of cable sheath tube, and this protecting pipe possesses good rigidity, but it to run under severe cold environment easily ruptural deformation, be not suitable for the Northeast, and flame retardant properties is poor; Chinese patent CN200910197527 discloses a kind of steel wire reinforced polytetrafluoroethylspiral spiral tube component, and this assembly preparation method is complicated, and its suppleness and corrosion resistance nature have much room for improvement.Prior art urgently needs a kind of chance extreme temperature difficult deformation, acid and alkali-resistance microbiological corrosion, the electric power protecting pipe that stretching-resisting bending-resisting intensity is good and flame retardant properties is strong.
Summary of the invention
The chance extreme temperature existed in order to the electric power protecting pipe overcoming prior art is easily out of shape fracture, easily by soda acid microbiological corrosion, and stretching-resisting bending-resisting intensity difference, and the defect such as inflammable; The invention discloses a kind of novel electric power protecting pipe, this electric power protecting pipe possesses good performance, can be widely used in suitability for industrialized production.
For achieving the above object, the technical solution adopted in the present invention is as follows:
A kind of electric power protecting pipe, it is prepared from by the raw material of following weight parts:
Barium titanate powder 1-2, aluminum nitride powder 1-2, carbonization chromium powder 1-2, borax 1-2, talcum powder 1-2, Paris white 1-2, silica gel 1-2, TDE 3-5, stearic acid 6-8, starch ethers 8-10, chitin 12-15, polycarbonate 18-20, Natvosol 25-30, polyvinyl alcohol 32-36, polyvinyl chloride 40-45.
Preferably, barium titanate powder, aluminum nitride powder, carbonization chromium powder, borax, the size controlling of talcum powder and Paris white is more than 300 orders;
Preferably, the pore volume of silica gel is 0.6-0.8ml/g, and mean pore size is 5.0-7.0nm, and specific surface is 500650m
2/ g.
The invention also discloses the preparation method of above-mentioned electric power protecting pipe, comprise the steps:
(1) above-mentioned each raw material for standby is taken according to weight part;
(2) by barium titanate powder, aluminum nitride powder, carbonization chromium powder, borax, talcum powder and Paris white are put in stirrer, stir and obtain mixture 1;
(3) put in retort by the mixture 1 that step (2) obtains, the temperature of retort controls at 50 DEG C, and add silica gel edge with back and stir, stirring velocity is 100 revs/min, and churning time is 5 minutes, obtains mixture 2;
(4) by the mixture 2 that step (3) obtains, TDE, stearic acid, starch ethers, chitin, polycarbonate, Natvosol, polyvinyl alcohol and polyvinyl chloride are put in whizzer successively, 2000 turns/min centrifugal mixer 2-3 minute, after mixing, enter twin screw extruder and be squeezed into molten state, after product pulls out by forming machine, by cutting machine fixed length cutting, send into pipe-expanding machine, after enlarging completes, namely obtain above-mentioned electric power protecting pipe.
Electric power protecting pipe prepared by the present invention possesses effect useful as follows:
Electric power protecting pipe prepared by the present invention possesses good tensile strength, flexural strength, bus hardness, thermal conductivity and oxygen index; This electric power protecting pipe possesses the heat-resisting cold tolerance of good salt tolerant, can be used in various extreme environment, have wide range of applications, long service life, plays effective provide protection to underground and earth's surface cable; Preparation method of the present invention is simple, with low cost, possesses good application prospect.
Embodiment
Below employing specific embodiment is further explained the present invention, but should not regards the restriction to initiative spirit of the present invention as.
Embodiment 1
A kind of electric power protecting pipe, it is prepared from by the raw material of following weight parts:
Barium titanate powder 1, aluminum nitride powder 1, carbonization chromium powder 1, borax 1, talcum powder 1, Paris white 1, silica gel 1, TDE 3, stearic acid 6, starch ethers 8, chitin 12, polycarbonate 18, Natvosol 25, polyvinyl alcohol 32, polyvinyl chloride 40.
Above-mentioned barium titanate powder, aluminum nitride powder, carbonization chromium powder, borax, the size controlling of talcum powder and Paris white is at 400 orders;
The pore volume of silica gel is 0.6-0.8ml/g, and mean pore size is 5.0-7.0nm, and specific surface is 500-650m
2/ g.
The preparation method of above-mentioned electric power protecting pipe, comprises the steps:
(1) above-mentioned each raw material for standby is taken according to weight part;
(2) by barium titanate powder, aluminum nitride powder, carbonization chromium powder, borax, talcum powder and Paris white are put in stirrer, stir and obtain mixture 1;
(3) put in retort by the mixture 1 that step (2) obtains, the temperature of retort controls at 50 DEG C, and add silica gel edge with back and stir, stirring velocity is 100 revs/min, and churning time is 5 minutes, obtains mixture 2;
(4) by the mixture 2 that step (3) obtains, TDE, stearic acid, starch ethers, chitin, polycarbonate, Natvosol, polyvinyl alcohol and polyvinyl chloride are put in whizzer successively, 2000 turns/min centrifugal mixer 2 minutes, after mixing, enter twin screw extruder and be squeezed into molten state, after product pulls out by forming machine, by cutting machine fixed length cutting, send into pipe-expanding machine, after enlarging completes, namely obtain above-mentioned electric power protecting pipe.
Embodiment 2
A kind of electric power protecting pipe, it is prepared from by the raw material of following weight parts:
Barium titanate powder 2, aluminum nitride powder 2, carbonization chromium powder 2, borax 2, talcum powder 2, Paris white 2, silica gel 2, TDE 5, stearic acid 8, starch ethers 10, chitin 15, polycarbonate 20, Natvosol 30, polyvinyl alcohol 36, polyvinyl chloride 45.
Wherein, barium titanate powder, aluminum nitride powder, carbonization chromium powder, borax, the size controlling of talcum powder and Paris white is at 500 orders.
The preparation method of above-mentioned electric power protecting pipe, comprises the steps:
(1) above-mentioned each raw material for standby is taken according to weight part;
(2) by barium titanate powder, aluminum nitride powder, carbonization chromium powder, borax, talcum powder and Paris white are put in stirrer, stir and obtain mixture 1;
(3) put in retort by the mixture 1 that step (2) obtains, the temperature of retort controls at 50 DEG C, and add silica gel edge with back and stir, stirring velocity is 100 revs/min, and churning time is 5 minutes, obtains mixture 2;
(4) by the mixture 2 that step (3) obtains, TDE, stearic acid, starch ethers, chitin, polycarbonate, Natvosol, polyvinyl alcohol and polyvinyl chloride are put in whizzer successively, 2000 turns/min centrifugal mixer 3 minutes, after mixing, enter twin screw extruder and be squeezed into molten state, after product pulls out by forming machine, by cutting machine fixed length cutting, send into pipe-expanding machine, after enlarging completes, namely obtain above-mentioned electric power protecting pipe.
Embodiment 3
The various performance parameters of electric power protecting pipe prepared by the present invention measures: with external diameter 100mm, wall thickness 5mm, length 10m are example.Tensile strength, flexural strength, bus hardness, thermal conductivity and oxygen index are respectively with reference to GB/T1458, GB/T1449, GB/T3854, GB/T5990, GB/T8924.Concrete outcome is in table 1.
Table 1
Salt tolerance: electric power protecting pipe to be soaked in the sodium chloride solution of 10% 30 days, tensile strength only have dropped 1%, and flexural strength have dropped 3%, and bus hardness have dropped 2%.
Resistance to Thermal test: test sample is put into boiling water and boil 1 hour, without distortion and appearance of bubbling, tensile strength, flexural strength and bus hardness retain more than 90%, possess good resistance toheat.
Cold-resistant test: at test sample being placed in-50 DEG C 60 days, leakless occurs, tensile strength, flexural strength and bus hardness retain more than 92%.
Finally, it is also to be noted that what enumerate above is only several specific embodiments of the present invention.Obviously, the invention is not restricted to above embodiment, many distortion can also be had.All distortion that those of ordinary skill in the art can directly derive from content disclosed by the invention or associate, all should think protection scope of the present invention.
Claims (2)
1. an electric power protecting pipe, it is prepared from by the raw material of following weight parts:
Barium titanate powder 1-2, aluminum nitride powder 1-2, carbonization chromium powder 1-2, borax 1-2, talcum powder 1-2, Paris white 1-2, silica gel 1-2, TDE 3-5, stearic acid 6-8, starch ethers 8-10, chitin 12-15, polycarbonate 18-20, Natvosol 25-30, polyvinyl alcohol 32-36, polyvinyl chloride 40-45;
Described barium titanate powder, aluminum nitride powder, carbonization chromium powder, borax, the size controlling of talcum powder and Paris white is more than 300 orders; Its preparation method comprises the steps:
(1) above-mentioned each raw material for standby is taken according to weight part;
(2) by barium titanate powder, aluminum nitride powder, carbonization chromium powder, borax, talcum powder and Paris white are put in stirrer, stir and obtain mixture 1;
(3) put in retort by the mixture 1 that step (2) obtains, the temperature of retort controls at 50 DEG C, and add silica gel edge with back and stir, stirring velocity is 100 revs/min, and churning time is 5 minutes, obtains mixture 2;
(4) by the mixture 2 that step (3) obtains, TDE, stearic acid, starch ethers, chitin, polycarbonate, Natvosol, polyvinyl alcohol and polyvinyl chloride are put in whizzer successively, 2000 turns/min centrifugal mixer 2-3 minute, after mixing, enter twin screw extruder and be squeezed into molten state, after product pulls out by forming machine, by cutting machine fixed length cutting, send into pipe-expanding machine, after enlarging completes and get final product.
2. electric power protecting pipe as claimed in claim 1, it is characterized in that, the pore volume of described silica gel is 0.6-0.8ml/g, and mean pore size is 5.0-7.0nm, and specific surface area is 500-650m
2/ g.