CN103724717A - 一种阻燃耐低温皮碗材料 - Google Patents

一种阻燃耐低温皮碗材料 Download PDF

Info

Publication number
CN103724717A
CN103724717A CN201310677272.0A CN201310677272A CN103724717A CN 103724717 A CN103724717 A CN 103724717A CN 201310677272 A CN201310677272 A CN 201310677272A CN 103724717 A CN103724717 A CN 103724717A
Authority
CN
China
Prior art keywords
parts
low temperature
temperature resistant
rubber
auxiliary agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310677272.0A
Other languages
English (en)
Inventor
朱剑秋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHU JIACHENG ELECTRONIC TECHNOLOGY Co Ltd
Original Assignee
WUHU JIACHENG ELECTRONIC TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHU JIACHENG ELECTRONIC TECHNOLOGY Co Ltd filed Critical WUHU JIACHENG ELECTRONIC TECHNOLOGY Co Ltd
Priority to CN201310677272.0A priority Critical patent/CN103724717A/zh
Publication of CN103724717A publication Critical patent/CN103724717A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃耐低温皮碗材料，由下列重量份的原料制成：丁腈橡胶70-80、硅橡胶35-40、丙烯酸酯12-15、氯化石蜡4-6、邻苯二甲酸二辛酯4-7、硅烷偶联剂KH560 2-3、微晶石蜡1-2、防老剂NBC 0.4-1.2、促进剂DM 0.5-1、烟片胶1-2、硫磺1-2、助剂10-12；本发明所制作的皮碗能应用于要求苛刻的场合，橡胶混炼充分，阻燃无烟，耐低温效果佳。

Description

一种阻燃耐低温皮碗材料
技术领域
本发明涉及橡胶领域，确切地说是一种阻燃耐低温皮碗材料。
背景技术
皮碗，主要用于汽车液压制动系统及离合器操纵系统、加力系统中起传递压力和密封作用。现有皮碗品种和性能单一，无法满足日益增加的多样化需求。
发明内容
本发明的目的在于提高一种阻燃耐低温皮碗材料。
上述目的通过以下方案实现：
一种阻燃耐低温皮碗材料，其特征在于：由下列重量份的原料制成：
丁腈橡胶  70-80、硅橡胶35-40、丙烯酸酯12-15、氯化石蜡4-6、邻苯二甲酸二辛酯4-7、硅烷偶联剂KH560  2-3、微晶石蜡 1-2，防老剂NBC   0.4-1.2，促进剂DM  0.5-1，烟片胶 1-2、硫磺1-2，助剂10-12；
助剂由下列重量份的原料制成：
粘土23-36、轻质碳酸钙5-13、三氧化钨1-2、硅藻土14-25、柠檬酸三丁酯2-3、硅烷偶联剂DL602 1-2，氧化铜1-2、聚丙二醇二缩水甘油醚1-2、磷酸三甲苯酯1-2、氢氧化铝8-10；
所述的助剂的制备方法是将粘土、轻质碳酸钙、硅藻土在500-550℃下煅烧4-5小时，取出，与氢氧化铝一并加入适量水中研磨，加10-15%盐酸溶液调PH为4.5-5.5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末，再与其它剩余成分混合，研磨混合均匀即得。
所述的一种阻燃耐低温皮碗材料，其特征在于：制备方法为：
　　先通过密炼机100-120℃合成橡胶，再将合成橡胶通过开炼机开炼成型后，再经过二次硫化后，即得。
本发明的有益效果为：　
本发明所制作的皮碗能应用于要求苛刻的场合，橡胶混炼充分，阻燃无烟，耐低温效果佳。
具体实施方式
一种阻燃耐低温皮碗材料，由下列重量kg的原料制成：
丁腈橡胶  80、硅橡胶37、丙烯酸酯15、氯化石蜡6、邻苯二甲酸二辛酯4、硅烷偶联剂KH560  2、微晶石蜡2，防老剂NBC   1.2，促进剂DM  0.8，烟片胶2、硫磺1.2，助剂11；
助剂由下列重量kg的原料制成：
粘土36、轻质碳酸钙13、三氧化钨2、硅藻土25、柠檬酸三丁酯3、硅烷偶联剂DL602  2，氧化铜 2、 聚丙二醇二缩水甘油醚2、磷酸三甲苯酯2、氢氧化铝10；
所述的助剂的制备方法是将粘土、轻质碳酸钙、硅藻土在550℃下煅烧4.2小时，取出，与氢氧化铝一并加入适量水中研磨，加15%盐酸溶液调PH为5.2，研磨浆料至500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末，再与其它剩余成分混合，研磨混合均匀即得。
所述的一种阻燃耐低温皮碗材料，制备方法为：
　　先通过密炼机100℃合成橡胶，再将合成橡胶通过开炼机开炼成型后，再经过二次硫化后，即得。
按实施例的原材料配方做成胶料再做成皮碗进行性能试验检测， 检测结果：  
拉伸强度为25Mpa,断裂拉长率为480%,撕裂强度为 38kN/m,经FAM-A油(23℃×48h)泡后其拉伸强度为 19MPa， 耐臭氧性： 500pphm×40℃ ×70h, 拉伸 20%  无裂纹现象 ；-40℃的低温下放置 48h 胶料未出现裂纹现象。

Claims (2)

1.一种阻燃耐低温皮碗材料，其特征在于：由下列重量份的原料制成：
丁腈橡胶  70-80、硅橡胶35-40、丙烯酸酯12-15、氯化石蜡4-6、邻苯二甲酸二辛酯4-7、硅烷偶联剂KH560  2-3、微晶石蜡 1-2，防老剂NBC   0.4-1.2，促进剂DM  0.5-1，烟片胶 1-2、硫磺1-2，助剂10-12；
助剂由下列重量份的原料制成：
粘土23-36、轻质碳酸钙5-13、三氧化钨1-2、硅藻土14-25、柠檬酸三丁酯2-3、硅烷偶联剂DL602 1-2，氧化铜1-2、聚丙二醇二缩水甘油醚1-2、磷酸三甲苯酯1-2、氢氧化铝8-10；
所述的助剂的制备方法是将粘土、轻质碳酸钙、硅藻土在500-550℃下煅烧4-5小时，取出，与氢氧化铝一并加入适量水中研磨，加10-15%盐酸溶液调PH为4.5-5.5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末，再与其它剩余成分混合，研磨混合均匀即得。
2.根据权利要求1所述的一种阻燃耐低温皮碗材料，其特征在于：制备方法为：
　　先通过密炼机100-120℃合成橡胶，再将合成橡胶通过开炼机开炼成型后，再经过二次硫化后，即得。
CN201310677272.0A 2013-12-13 2013-12-13 一种阻燃耐低温皮碗材料 Pending CN103724717A (zh)