CN103721367A - Composite type protective material for comprehensive toxicant prevention - Google Patents
Composite type protective material for comprehensive toxicant prevention Download PDFInfo
- Publication number
- CN103721367A CN103721367A CN201310606243.5A CN201310606243A CN103721367A CN 103721367 A CN103721367 A CN 103721367A CN 201310606243 A CN201310606243 A CN 201310606243A CN 103721367 A CN103721367 A CN 103721367A
- Authority
- CN
- China
- Prior art keywords
- weight
- toxicant
- prevention
- comprehensive
- composite type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a toxicant prevention material, particularly to a composite type protective material for comprehensive toxicant prevention. The material comprises activated carbon serving as a carrier and an impregnant adsorbed by the activated carbon, wherein the impregnant comprises 7%-10% (by weight) of Cu, 1%-2% (by weight) of Mo, 0.6%-3% (by weight) of an active component additive Ag, 0.4%-1% (by weight) of Zn and 5%-10% (by weight) of a multi-amine compound TEDA (triethylene diamine). The material is reasonable in design, and the composite type protective material capable of effectively protecting against various toxicants such as classic toxicants of HCN (hydrogen cyanide) and CNCL (cyanogen chloride), a penetrating toxicant of perfluoroisobutylene and the like, is developed.
Description
Technical field
The present invention relates to gas defence material, be specially a kind of compound protective materials for comprehensive gas defence.
Background technology
Protection Immesion active carbon, along with development of the situation constantly updates, after entering the nineties, has caused people's attention take perfluoroisobutylene (PFIB) as the penetrability toxic agent of representative.
But, less to the Protective Research of penetrability toxic agent both at home and abroad at present, the PPC protection pedigree limitation coming into operation is larger, can only meet the protection to perfluoroisobutylene, with China, the PPC of development when for protective equipment, be by with classical toxic agent protective materials be ASZM-T impregnated carbon layering filling, thereby realize the object of simultaneously classical toxic agent and penetrability toxic agent effectively being protected.Such type of feed is to being designed with higher requirement, give simultaneously and produce, use and bring many inconvenience, and the use neighborhood of product limitation is very large, can only be used for collective protective equipment, and can not use belonging in the individual protection equipment of thin layer filling.
Summary of the invention
The object of the present invention is to provide a kind of compound protective materials for comprehensive gas defence.
The present invention adopts following technical scheme to realize:
A kind of compound protective materials for comprehensive gas defence, comprise that described impregnating agent comprises 7%~10%(weight as the active carbon of carrier and the impregnating agent of charcoal absorption) Cu, 1%~2%(weight) Mo, 0.6%~3%(weight) active component auxiliary agent A g, 0.4%~1%(weight) Zn, 5%~10%(weight) polyamines based compound TEDA.Wherein, the interior weight of bracket refers to the gross weight of compound protective materials.
The preparation method of the above-mentioned compound protective materials for comprehensive gas defence, comprises the steps:
(1), by the impregnating agent of active component, be basic copper carbonate, zinc carbonate, ammonium molybdate, silver nitrate, add (those skilled in the art calculate the consumption of ammoniacal liquor according to the water capacity of absorbent charcoal carrier) in ammoniacal liquor, heating melts and is mixed with maceration extract, maceration extract temperature keeps 60-80 ℃, and to be impregnated dose fully dissolves, adopt equivalent impregnation method (relation that the water capacity that is obtain solution consumption and absorbent charcoal carrier is 1:1), it is mixed with active carbon, and standing 1-2h;
(2), adopt the bed activation method that flows, utilize ebuillition of heated stove to make impregnated carbon under the effect of high temperature hot gas stream, give the process of its catalytic reaction activity, activation temperature is controlled between 160~190 ℃, continuous activation 40~50min;
(3), polyamines based compound TEDA is adsorbed, adsorption temp is controlled between 55~70 ℃.
Wherein Cu derives from basic copper carbonate, in ammonia spirit, generate the complex of cuprammonium, the filtering effect to perfluoroisobutylene (PFIB) can be provided, by heat treatment, transform, part exists with the form of oxide, contributes to provide the filtering effect to toxic agent such as HCN, CNCL.
Zn derives from zinc carbonate, in ammonia spirit, generate the complex of zinc ammonia, the filtering effect to perfluoroisobutylene (PFIB) can be provided, by heat treatment, transform, part exists with the form of oxide, contributes to provide the filtering effect to toxic agent such as HCN, CNCL.
Mo derives from ammonium molybdate, and the filtering effect to HCN, CNCL can be provided.
Ag derives from silver nitrate, as active component auxiliary agent, can improve the decentralization of active component at activated carbon surface, improves reaction or the catalytic activity of active component.
TEDA is solid at normal temperatures, by heating, is volatilized and is adsorbed in the top layer of impregnated carbon, contributes to improve impregnated carbon protective capacities to CNCL and perfluoroisobutylene (PFIB) under high humidity.
By load various active component on absorbent charcoal carrier and polyamines based compound TEDA, realize the compound of protective capacities, the compound protective materials of preparation can meet classical toxic agent to organic gas benzene, chloroethanes etc. and the complex protection capability of penetrability toxic agent.
Advantage is as follows:
1, large, the pore structure of the specific area rational absorbent charcoal carrier that distributes;
2, the kind of load active component, has mainly comprised Cu, Mo, Zn, Ag and TEDA;
3, on described carrier material, load specified activity component and polyamines based compound are prepared compound protective materials, have the synthetic filter effect to classical toxic agent and penetrability toxic agent.
Compound protective materials the performance test results:
As seen from the above table, compound protective materials provided by the invention not only has good protective capacities to benzene, chloroethanes, HCN, CNCL etc., and also can provide effective protection to penetrability toxic agent PFIB, combine the protective capacities of ASZM-T and PP charcoal, realized technically the compound of two kinds of protective materials.
The present invention is reasonable in design, develop a kind of compound protective materials that can simultaneously meet the effective protection of the multiple toxic agent such as classical toxic agent HCN, CNCL and penetrability toxic agent perfluoroisobutylene, the pattern that thoroughly changes multiple material layering filling or load in mixture, overcome application limitation, no matter be that collective protective equipment or individual protection equipment can be widely used, thus the usage level of lifting protective equipment.
The specific embodiment
Below specific embodiments of the invention are elaborated.
embodiment 1
A kind of compound protective materials for comprehensive gas defence, comprise as the active carbon of carrier and the impregnating agent of charcoal absorption, described impregnating agent comprises 8%(weight) Cu, 2%(weight) Mo, 0.7%(weight) Zn, 3%(weight) active component auxiliary agent A g, 8%(weight) polyamines based compound TEDA.
Preparation method is as follows:
(1), by the impregnating agent of above-mentioned active component, by the content of active component, calculate respectively the required weight of basic copper carbonate, zinc carbonate, ammonium molybdate, silver nitrate, add in ammoniacal liquor, heating melts and is mixed with maceration extract, mixed solution temperature keeps 70 ℃, and to be impregnated dose fully dissolves, adopt equivalent impregnation method, it is mixed with active carbon, and standing 2h;
(2), adopt flow bed activation method, activation temperature is controlled at 180 ℃, continuous activation 50min;
(3), polyamines based compound TEDA is adsorbed, adsorption temp is controlled at 55 ℃.
embodiment 2
A kind of compound protective materials for comprehensive gas defence, comprise as the active carbon of carrier and the impregnating agent of charcoal absorption, described impregnating agent comprises 10%(weight) Cu, 0.5%(weight) Mo, 0.4%(weight) Zn, 3%(weight) active component auxiliary agent A g, 5%(weight) polyamines based compound TEDA.
Preparation method is as follows:
(1), by the impregnating agent of above-mentioned active component, by the content of active component, calculate respectively the required weight of basic copper carbonate, zinc carbonate, ammonium molybdate, silver nitrate, add in ammoniacal liquor, heating melts and is mixed with maceration extract, mixed solution temperature keeps 80 ℃, and to be impregnated dose fully dissolves, adopt equivalent impregnation method, it is mixed with active carbon, and standing 1.5h;
(2), adopt flow bed activation method, activation temperature is controlled at 160 ℃, continuous activation 40min;
(3), polyamines based compound TEDA is adsorbed, adsorption temp is controlled between 70 ℃.
embodiment 3
A kind of compound protective materials for comprehensive gas defence, comprise the impregnating agent of active carbon as carrier (the broken charcoal of coconut husk) and charcoal absorption, described impregnating agent comprises 7%(weight) Cu, 1%(weight) Mo, 1%(weight) Zn, 0.6%(weight) active component auxiliary agent A g, 10%(weight) polyamines based compound TEDA.
Preparation method is as follows:
(1), by the impregnating agent of above-mentioned active component, by the content of active component, calculate respectively the required weight of basic copper carbonate, zinc carbonate, ammonium molybdate, silver nitrate, add in ammoniacal liquor, heating melts and is mixed with maceration extract, mixed solution temperature keeps 60 ℃, and to be impregnated dose fully dissolves, adopt equivalent impregnation method, it is mixed with active carbon, and standing 1h;
(2), adopt flow bed activation method, activation temperature is controlled at 190 ℃, continuous activation 45min;
(3), polyamines based compound TEDA is adsorbed, adsorption temp is controlled at 60 ℃.
Claims (2)
1. the compound protective materials for comprehensive gas defence, it is characterized in that: comprise that described impregnating agent comprises 7%~10%(weight as the active carbon of carrier and the impregnating agent of charcoal absorption) Cu, 1%~2%(weight) Mo, 0.6%~3%(weight) active component auxiliary agent A g, 0.4%~1%(weight) Zn, 5%~10%(weight) polyamines based compound TEDA.
2. the compound protective materials for comprehensive gas defence according to claim 1, is characterized in that: described active carbon is the broken charcoal of coconut husk.