CN103709889A - 一种铜雕塑用增韧氨基树脂漆 - Google Patents
一种铜雕塑用增韧氨基树脂漆 Download PDFInfo
- Publication number
- CN103709889A CN103709889A CN201310676635.9A CN201310676635A CN103709889A CN 103709889 A CN103709889 A CN 103709889A CN 201310676635 A CN201310676635 A CN 201310676635A CN 103709889 A CN103709889 A CN 103709889A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- amino resin
- hour
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种油漆,具体涉及一种铜雕塑用增韧氨基树脂漆,本发明油漆由以下重量份的原料制成:乙二醇单丁醚10-12、2-羟基丁二酸2-3、炭黑4-6、甲基丙烯酸酯13-16、乙烯基醚型氨基甲酸酯20-24、丙烯酸甲酯12-14、丙烯酸乙酯5-7、新戊二醇4-5、硅灰石粉20-24、聚乙二醇3-4、三乙醇胺1-2、过氧化二异丙苯1-2、氨基树脂30-32、促进剂M3-4、甲基三乙氧基硅烷2-3、双十四碳醇酯5-8、助剂5-6、二甲苯10-12、乙酸丁酯10-12;本发明油漆柔韧耐磨,附着力强,光泽饱满,色泽持久耐黄变,耐候老化,使用寿命长,能广泛用于防护各类铜雕工艺品。
Description
技术领域
本发明涉及一种油漆,具体涉及一种铜雕塑用增韧氨基树脂漆及其制备工艺。
背景技术
铜雕塑是日常生活中常见的一类工艺品,具有较高的艺术价值和欣赏价值,然而,铜雕塑艺术品由于其本身材质性质及摆放环境的特点,容易出现氧化腐蚀等问题,影响美观和使用寿命,为了保护铜器,往往需要在雕塑外面涂上油漆,并且对铜雕塑用漆有一定的要求,比如附着力、耐候老化、耐日光暴晒、耐温等等,因此,需要改进油漆配方,配制出适合不同使用场合的油漆,增加其艺术价值。
发明内容
本发明的目的在于,提供一种铜雕塑用增韧氨基树脂漆,以保护雕塑品,为了实现上述目的,本发明采用的技术方案如下:
一种铜雕塑用增韧氨基树脂漆,其特征在于,本发明材料由以下重量份的原料制成:乙二醇单丁醚10-12、2-羟基丁二酸2-3、炭黑4-6、甲基丙烯酸酯13-16、乙烯基醚型氨基甲酸酯20-24、丙烯酸甲酯12-14、丙烯酸乙酯5-7、新戊二醇4-5、硅灰石粉20-24、聚乙二醇3-4、三乙醇胺1-2、过氧化二异丙苯1-2、氨基树脂30-32、促进剂M3-4、甲基三乙氧基硅烷2-3、双十四碳醇酯5-8、助剂5-6、二甲苯10-12、乙酸丁酯10-12。
所述的助剂由以下重量份的原料制成:粘土10-14、纳米铁矿渣粉1-2、促进剂M3-4、苯基三乙氧基硅烷2-3、钼酸钠1-2、磁石2-3、苯甲酸钠1-2、柠檬酸三丁酯35-40、没食子酸丙酯2-3、薏仁油3-4、二硼化钒1-2、表儿茶素2-3;制备方法是将粘土、磁石送入煅烧炉中在720-740℃下煅烧2-3小时,然后取出,送入10-15%的盐酸溶液中浸泡2-3小时,过滤,得滤渣,用清水洗净,烘干、研磨成400-600目粉体;所得粉体与其它剩余成分混合,加热至60-70℃,搅拌反应40-50分钟,冷却,研磨成浆料,即得。
所述的一种铜雕塑用增韧氨基树脂漆,其制备工艺为:
(1)将2-羟基丁二酸、炭黑、甲基丙烯酸酯、新戊二醇、助剂混合,加入到二甲苯、乙酸丁酯溶剂中,加热至120-130℃,反应3-4小时;
(2)将步骤(1)的物料冷却至70-85℃,加入丙烯酸甲酯、丙烯酸乙酯、聚乙二醇、过氧化二异丙苯,搅拌反应3-4小时;
(3)将步骤(2)的物料降温至50-65℃,加入其它剩余物料,搅拌反应40-60分钟后,冷却至室温,研磨成20-60μm浆料,即得。
与现有技术相比,本发明提供的铜雕塑用油漆具备以下优点:利用炭黑、硅灰石粉等原料,增进了氨基树脂漆的韧性,使其坚固耐磨,再结合其他原料,制备的油漆漆膜与铜器附着力强,光泽饱满,色泽持久耐黄变,耐候老化,使用寿命长,生产工艺相对简单,可以广泛用于防护各类铜雕工艺品。
具体实施方式
实施例
本实施例油漆由以下重量份原料制成:乙二醇单丁醚12、2-羟基丁二酸3、炭黑6、甲基丙烯酸酯16、乙烯基醚型氨基甲酸酯24、丙烯酸甲酯14、丙烯酸乙酯7、新戊二醇5、硅灰石粉24、聚乙二醇4、三乙醇胺2、过氧化二异丙苯2、氨基树脂32、促进剂M4、甲基三乙氧基硅烷3、双十四碳醇酯6、助剂6、二甲苯12、乙酸丁酯12。
所述的助剂由以下重量份的原料制成:粘土14、纳米铁矿渣粉2、促进剂M4、苯基三乙氧基硅烷3、钼酸钠2、磁石3、苯甲酸钠2、柠檬酸三丁酯40、没食子酸丙酯3、薏仁油4、二硼化钒2、表儿茶素3;制备方法是将粘土、磁石送入煅烧炉中在720-740℃下煅烧3小时,然后取出,送入15%的盐酸溶液中浸泡3小时,过滤,得滤渣,用清水洗净,烘干、研磨成600目粉体;所得粉体与其它剩余成分混合,加热至60-70℃,搅拌反应50分钟,冷却,研磨成浆料,即得。
所述的一种铜雕塑用增韧氨基树脂漆,其制备工艺为:
(1)将2-羟基丁二酸、炭黑、甲基丙烯酸酯、新戊二醇、助剂混合,加入到二甲苯、乙酸丁酯溶剂中,加热至120-130℃,反应4小时;
(2)将步骤(1)的物料冷却至70-85℃,加入丙烯酸甲酯、丙烯酸乙酯、聚乙二醇、过氧化二异丙苯,搅拌反应4小时;
(3)将步骤(2)的物料降温至50-65℃,加入其它剩余物料,搅拌反应60分钟后,冷却至室温,研磨成60μm浆料,即得。
本发明油漆的性能测试结果为:
上述测试均遵循相关标准进行。
Claims (2)
1.一种铜雕塑用增韧氨基树脂漆,其特征在于,该油漆由以下重量份的原料制成:乙二醇单丁醚10-12、2-羟基丁二酸2-3、炭黑4-6、甲基丙烯酸酯13-16、乙烯基醚型氨基甲酸酯20-24、丙烯酸甲酯12-14、丙烯酸乙酯5-7、新戊二醇4-5、硅灰石粉20-24、聚乙二醇3-4、三乙醇胺1-2、过氧化二异丙苯1-2、氨基树脂30-32、促进剂M 3-4、甲基三乙氧基硅烷2-3、双十四碳醇酯5-8、助剂5-6、二甲苯10-12、乙酸丁酯10-12;
所述的助剂由以下重量份的原料制成:粘土10-14、纳米铁矿渣粉1-2、促进剂M 3-4、苯基三乙氧基硅烷2-3、钼酸钠1-2、磁石2-3、苯甲酸钠1-2、柠檬酸三丁酯35-40、没食子酸丙酯2-3、薏仁油3-4、二硼化钒1-2、表儿茶素2-3;制备方法是将粘土、磁石送入煅烧炉中在720-740℃下煅烧2-3小时,然后取出,送入10-15%的盐酸溶液中浸泡2-3小时,过滤,得滤渣,用清水洗净,烘干、研磨成400-600目粉体;所得粉体与其它剩余成分混合,加热至60-70℃,搅拌反应40-50分钟,冷却,研磨成浆料,即得。
2.如权利要求1所述的一种铜雕塑用增韧氨基树脂漆,其制作工艺为:
(1)将2-羟基丁二酸、炭黑、甲基丙烯酸酯、新戊二醇、助剂混合,加入到二甲苯、乙酸丁酯溶剂中,加热至120-130℃,反应3-4小时;
(2)将步骤(1)的物料冷却至70-85℃,加入丙烯酸甲酯、丙烯酸乙酯、聚乙二醇、过氧化二异丙苯,搅拌反应3-4小时;
(3)将步骤(2)的物料降温至50-65℃,加入其它剩余物料,搅拌反应40-60分钟后,冷却至室温,研磨成20-60μm浆料,即得。