CN103709722B - thermoplastic polyurethane elastomer material - Google Patents
thermoplastic polyurethane elastomer material Download PDFInfo
- Publication number
- CN103709722B CN103709722B CN201310678454.XA CN201310678454A CN103709722B CN 103709722 B CN103709722 B CN 103709722B CN 201310678454 A CN201310678454 A CN 201310678454A CN 103709722 B CN103709722 B CN 103709722B
- Authority
- CN
- China
- Prior art keywords
- mass parts
- polyurethane elastomer
- thermoplastic polyurethane
- elastomer material
- thermoplastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of Thermoplastic polyurethane elastomer material, be made up of following raw material: 1-2 mass parts Trimethyllaurylammonium bromide, 11 mass parts stearic acid, 84 mass parts thermoplastic polyurethanes, 2 mass parts methyl-silicone oils, 6 mass parts titanate coupling agents, 31 mass parts acrylic resins, 1 mass parts phenyl silicone oil, 25 mass parts chlorinatedpolyethylenees, 32 mass parts calcium carbonate, 3 mass parts viscosity are at the hydroxy silicon oil of 400 centipoises.Thermoplastic polyurethane elastomer material of the present invention, its wear resisting property good under there is low temperature and flexible resistance.
Description
Technical field
The present invention relates to Thermoplastic polyurethane elastomer material.
Background technology
Existing polyurethane elastomer material, the wear resisting property under low temperature and flexible resistance not ideal enough.
Summary of the invention
The object of the present invention is to provide a kind of Thermoplastic polyurethane elastomer material, its wear resisting property good under there is low temperature and flexible resistance.
For achieving the above object, technical scheme of the present invention is a kind of Thermoplastic polyurethane elastomer material of design, is made up of following raw material:
1-2 mass parts Trimethyllaurylammonium bromide,
11 mass parts stearic acid,
84 mass parts thermoplastic polyurethanes,
2 mass parts methyl-silicone oils,
6 mass parts titanate coupling agents,
31 mass parts acrylic resins,
1 mass parts phenyl silicone oil,
25 mass parts chlorinatedpolyethylenees,
32 mass parts calcium carbonate,
3 mass parts viscosity are at the hydroxy silicon oil of 400 centipoises.
Advantage of the present invention and beneficial effect are: provide a kind of Thermoplastic polyurethane elastomer material, its wear resisting property good under having low temperature and flexible resistance.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of Thermoplastic polyurethane elastomer material, be made up of following raw material:
1.2 mass parts Trimethyllaurylammonium bromides,
11 mass parts stearic acid,
84 mass parts thermoplastic polyurethanes,
2 mass parts methyl-silicone oils,
6 mass parts titanate coupling agents,
31 mass parts acrylic resins,
1 mass parts phenyl silicone oil,
25 mass parts chlorinatedpolyethylenees,
32 mass parts calcium carbonate,
3 mass parts viscosity are at the hydroxy silicon oil of 400 centipoises.
Embodiment 2
A kind of Thermoplastic polyurethane elastomer material, be made up of following raw material:
2 mass parts Trimethyllaurylammonium bromides,
11 mass parts stearic acid,
84 mass parts thermoplastic polyurethanes,
2 mass parts methyl-silicone oils,
6 mass parts titanate coupling agents,
31 mass parts acrylic resins,
1 mass parts phenyl silicone oil,
25 mass parts chlorinatedpolyethylenees,
32 mass parts calcium carbonate,
3 mass parts viscosity are at the hydroxy silicon oil of 400 centipoises.
Embodiment 3
A kind of Thermoplastic polyurethane elastomer material, be made up of following raw material:
1 mass parts Trimethyllaurylammonium bromide,
11 mass parts stearic acid,
84 mass parts thermoplastic polyurethanes,
2 mass parts methyl-silicone oils,
6 mass parts titanate coupling agents,
31 mass parts acrylic resins,
1 mass parts phenyl silicone oil,
25 mass parts chlorinatedpolyethylenees,
32 mass parts calcium carbonate,
3 mass parts viscosity are at the hydroxy silicon oil of 400 centipoises.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. Thermoplastic polyurethane elastomer material, is characterized in that, is made up of following raw material:
1-2 mass parts Trimethyllaurylammonium bromide,
11 mass parts stearic acid,
84 mass parts thermoplastic polyurethanes,
2 mass parts methyl-silicone oils,
6 mass parts titanate coupling agents,
31 mass parts acrylic resins,
1 mass parts phenyl silicone oil,
25 mass parts chlorinatedpolyethylenees,
32 mass parts calcium carbonate,
3 mass parts viscosity are at the hydroxy silicon oil of 400 centipoises.