CN103709503B - 一种磁性按摩球及其制造方法 - Google Patents
一种磁性按摩球及其制造方法 Download PDFInfo
- Publication number
- CN103709503B CN103709503B CN201310657936.7A CN201310657936A CN103709503B CN 103709503 B CN103709503 B CN 103709503B CN 201310657936 A CN201310657936 A CN 201310657936A CN 103709503 B CN103709503 B CN 103709503B
- Authority
- CN
- China
- Prior art keywords
- massage ball
- raw
- massage
- magnetic
- manufacture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种磁性按摩球及其制造方法，本发明按摩球由10‑20份的天然橡胶、15‑30份的聚丙烯、15‑30份的乙酸乙烯酯、10‑20份的氯丁二烯组成，取得一个最佳的平衡，既保证了按摩球较高的透明度，又保证按摩球具有较高的弹性、抗拉伸强度和耐热性，大大延长了按摩球的使用寿命；通过对原料进行二次加热、打磨、异味、去除、封装和贴片步骤制得，能够进一步保证按摩球的抗拉伸强度和延展性，按摩球具有良好环保性、理疗效果和耐热性。
Description
技术领域
[0001]本发明涉及到健身器材技术领域，尤其涉及一种磁性按摩球及其制造方法。
背景技术
[0002]健身运动中常见的是杠铃。采用杠铃健身时，在杠铃器械的轻重、动作的做法，安排的组数、次数，运动的速度等方面都有特殊的要求和安排。除了这些特殊要求，健身过程中很重要的两点便是:持续性和渐进性。持续性和渐进性是制订训练计划的两个重要原则。不坚持训练，肌肉就得不到持续的、有规律的刺激，以致生长缓慢;训练强度不增加，肌肉对所给予的刺激产生适应性，生长也会迟缓。一个有效的计划除了保证训练的持续性外，还要保证循序渐进地增加训练强度。而频度又是健身过程中另一个非常重要的点。频度是指一星期练几次。频度的设定取决于训练后的恢复能力，恢复能力又取决于本身的身体素质、睡眠质量和营养三个因素。无论是杠铃，还是其他健身器材，要想获得一个良好的健身效果，都必须保证健身的数量和强度。数量就是训练量，练多少组、每组多少次以及组间休息时间的长短等。强度是指训练中你所承受的负荷水平。负荷水平的高低取决于三个因素:重量、训练间歇、力竭程度。了解强度的概念和要点对如何增加重量是很重要的。因为增加重量就要影响训练次数和力竭程度。以上所述的健身可简单归为动态健身，即通过运动来健身。反之，静态健身也是一种不错的选择，所谓静态健身，犹如气功中的观想，佛家的静坐，道家的静心，心理学中的心灵释放，辟谷养生，中医的养心法，也就是在静止不运动的状态平衡心灵，调整情绪，疏通经络，调和气血，达到健身的目的，静态健身方法，适用于体弱多病，行动不便者。近年来，一些健身爱好者喜欢随身携带一些建议的健身器外出，不仅能够天天坚持锻炼，而且携带自由方便。简易的健身器材主要有哑铃、按摩球等。近年来按摩球相当流行，按摩球的外表是一种像玩具一样的球体，其材质为橡胶，这种橡胶质地的按摩球最高可承受400公斤的压力。按摩球是一项新兴、有趣、特殊的体育健身运动;按摩球可以训练胸、腹、背、臀、腿等处的肌肉群，而这些肌肉群在保持身体平衡、改善身体姿势以及预防运动损伤等方面发挥着重要作用。随着按摩球的普及，按摩球操也应运而生。
[0003]按摩球操适合各个年龄层的锻炼者，在场的学员中涵盖了老中青三代人。在做按摩球操时，每一个动作都要在球上完成，躺在球上做仰卧起坐或将球压在腿下双手撑地做俯卧撑等，锻炼效果较好。
[0004]按摩球操有助于训练人体的平衡能力；以往的健身运动都是在地面或稳定性很强的器材上进行，运动者不用太多地考虑身体的平衡问题，而按摩球则不同，运动者借助按摩球脱离地面，例如:坐在球上是一种平衡练习，抬高一腿，平衡难度就增加一点。将抬高的腿稍作移动便会难上加难。而在做腿搭在球上双手撑地做俯卧撑时，运动者要完成曲伸双臂的动作，首先要保持身体的平衡，不让球滚动，就得靠腿部、腰部、腹部的力量来控制，这使身体的协调性以及对肌肉的控制能力得到了有效的训练。公开号为CN 102357293A，公开日为2012年02月22日的中国专利文献公开了一种环保健身球，其特征是，其每100份包含各组份的重量百分比为:醋酸乙烯45-55%;低密度聚乙烯45-55%。本发明公开的环保健身球中的低密度聚乙烯异味严重，长时间使用后对身体健康有影响，不能起到真正的环保目的，此夕卜，按摩效果也很差。
发明内容
[0005]本发明为了克服上述现有技术的缺陷，提供一种磁性按摩球及其制造方法，本发明通过对原料进行二次加热、打磨、异味去除、封装、贴片步骤制得的按摩球，环保性和按摩效果大大提尚。
[0006]本发明通过下述技术方案实现:
[0007] —种磁性按摩球，其特征在于，由以下重量份数的组分组成:
[0008]天然橡胶 10-20份
[0009] 聚丙烯 15-30份
[0010] 乙酸乙烯酯 15-30份
[0011]氯丁二烯 10-20 份。
[0012] —种磁性按摩球的制造方法，其特征在于，依次由以下工艺步骤组成:
[0013] A、选取配方量的天然橡胶、聚丙烯、乙酸乙烯酯、氯丁二烯作为原料，将其混合搅拌均匀；
[0014] B、将A步骤混合均匀后的原料加入成型机中进行首次加热；
[0015] C、将B步骤加热后的原料自然冷却，然后再进行再次加热；
[0016] D、将C步骤经过再次加热后的原料通过成型机的挤压机头挤出，再通过圆型模具成型；
[0017] E、将D步骤成型后得到的按摩球取出并通风冷却；
[0018] F、将E步骤通风冷却后的按摩球用抛光机进行表面打磨处理；
[0019] G、将F步骤打磨后的按摩球放水盛装有木炭和水的除味池里除去异味，最后通风晾干；
[0020 ] H、将G步骤除味后的按摩球粘接封装按摩凸起壳体；
[0021 ] 1、将H步骤封装后的按摩球用粘胶贴合磁片，即得成品。
[0022 ]所述B步骤中对混合均匀后的原料进行首次加热的温度为100-120摄氏度。
[0023]所述C步骤中对自然冷却后的原料进行再次加热的温度为20-30摄氏度。
[0024]本发明的有益效果主要表现在以下几个方面:
[0025] 一、本发明的按摩球由天然橡胶、聚丙烯、乙酸乙烯酯、氯丁二烯10-20份组成，天然橡胶具有较高的弹性和机械强度;聚丙烯，加工容易抗弯曲疲劳性强；乙酸乙烯酯具有良好的透明性和弹性;采用10-20份的天然橡胶、15-30份的聚丙烯、15-30份的乙酸乙烯酯和10-20份的氯丁二烯特定配比，取得一个最佳的平衡，既保证了按摩球较高的透明度，又保证按摩球具有较高的弹性和耐热性，大大延长了按摩球的使用寿命。
[0026] 二、本发明将配方量的天然橡胶、聚丙烯、乙酸乙烯酯和氯丁二烯作为原料混合搅拌均匀后放入成型机中进行两次加热，中间间隔一次冷却，能够进一步提高按摩球的抗拉伸强度、延展性更好。
[0027] 三、本发明对成型后的按摩球进行通风冷却，并打磨处理，提高了按摩球的光滑度，能够有效保证使用效果。
[0028]四、本发明将按摩球放水盛装有木炭和水的除味池里除去异味，最后通风晾干，能够有效除去按摩球的异味，提高按摩球的环保性，长期使用更安全。
[0029]五、本发明除味后的按摩球粘接封装按摩凸起壳体，使用时，凸起起到了较好的按摩效果，使整个按摩球的按摩效果大大提高。
[0030]六、本发明封装后的按摩球用粘胶贴合磁片，磁片产生的磁场具有较好的理疗效果O
[0031]七、本发明将首次加热原料的温度控制在100-120摄氏度，再次加热的温度控制在20-30摄氏度，能够进一步保证按摩球的抗拉伸强度和延展性。
具体实施方式
[0032] 实施例1
[0033] —种磁性按摩球，由以下重量份数的组分组成:
[0034]天然橡胶 10份
[0035] 聚丙烯 15份
[0036]乙酸乙烯酯 15份
[0037]氯丁二烯 10 份。
[0038] 实施例2
[0039] —种磁性按摩球，由以下重量份数的组分组成:
[0040]天然橡胶 15份[0041 ] 聚丙烯 20份
[0042]乙酸乙烯酯 25份
[0043]氯丁二烯 15 份。
[0044] 实施例3
[0045] —种磁性按摩球，由以下重量份数的组分组成:
[0046]天然橡胶 20份
[0047] 聚丙烯 30份
[0048] 乙酸乙烯酯 30份
[0049]氯丁二烯 20 份。
[0050] 实施例4
[0051 ] 一种磁性按摩球的制造方法，依次由以下工艺步骤组成:
[0052] A、选取配方量的天然橡胶、聚丙烯、乙酸乙烯酯、氯丁二烯作为原料，将其混合搅拌均匀；
[0053] B、将A步骤混合均匀后的原料加入成型机中进行首次加热；
[0054] C、将B步骤加热后的原料自然冷却，然后再进行再次加热；
[0055] D、将C步骤经过再次加热后的原料通过成型机的挤压机头挤出，再通过圆型模具成型；
[0056] E、将D步骤成型后得到的按摩球取出并通风冷却；
[0057] F、将E步骤通风冷却后的按摩球用抛光机进行表面打磨处理；
[0058] G、将F步骤打磨后的按摩球放水盛装有木炭和水的除味池里除去异味，最后通风晾干；
[0059 ] H、将G步骤除味后的按摩球粘接封装按摩凸起壳体；
[0060] 1、将H步骤封装后的按摩球用粘胶贴合磁片，即得成品。
[0061]所述B步骤中对混合均匀后的原料进行首次加热的温度为100摄氏度。
[0062]所述C步骤中对自然冷却后的原料进行再次加热的温度为20摄氏度。
[0063] 实施例5
[0064] —种磁性按摩球的制造方法，依次由以下工艺步骤组成:
[0065] A、选取配方量的天然橡胶、聚丙烯、乙酸乙烯酯、氯丁二烯作为原料，将其混合搅拌均匀；
[0066] B、将A步骤混合均匀后的原料加入成型机中进行首次加热；
[0067] C、将B步骤加热后的原料自然冷却，然后再进行再次加热；
[0068] D、将C步骤经过再次加热后的原料通过成型机的挤压机头挤出，再通过圆型模具成型；
[0069] E、将D步骤成型后得到的按摩球取出并通风冷却；
[0070] F、将E步骤通风冷却后的按摩球用抛光机进行表面打磨处理；
[0071] G、将F步骤打磨后的按摩球放水盛装有木炭和水的除味池里除去异味，最后通风晾干；
[0072 ] H、将G步骤除味后的按摩球粘接封装按摩凸起壳体；
[0073] 1、将H步骤封装后的按摩球用粘胶贴合磁片，即得成品。
[0074]所述B步骤中对混合均匀后的原料进行首次加热的温度为110摄氏度。
[0075]所述C步骤中对自然冷却后的原料进行再次加热的温度为25摄氏度。
[0076] 实施例6
[0077] —种磁性按摩球的制造方法，依次由以下工艺步骤组成:
[0078] A、选取配方量的天然橡胶、聚丙烯、乙酸乙烯酯、氯丁二烯作为原料，将其混合搅拌均匀；
[0079] B、将A步骤混合均匀后的原料加入成型机中进行首次加热；
[0080] C、将B步骤加热后的原料自然冷却，然后再进行再次加热；
[0081] D、将C步骤经过再次加热后的原料通过成型机的挤压机头挤出，再通过圆型模具成型；
[0082] E、将D步骤成型后得到的按摩球取出并通风冷却；
[0083] F、将E步骤通风冷却后的按摩球用抛光机进行表面打磨处理；
[0084] G、将F步骤打磨后的按摩球放水盛装有木炭和水的除味池里除去异味，最后通风晾干；
[0085 ] H、将G步骤除味后的按摩球粘接封装按摩凸起壳体；
[0086] 1、将H步骤封装后的按摩球用粘胶贴合磁片，即得成品。
[0087]所述B步骤中对混合均匀后的原料进行首次加热的温度为120摄氏度。
[0088]所述C步骤中对自然冷却后的原料进行再次加热的温度为30摄氏度。
[0089]本实施将配方量的天然橡胶、聚丙烯、乙酸乙烯酯、氯丁二烯作为原料混合搅拌均匀后放入成型机中进行两次加热，首次加热原料的温度控制在120摄氏度，再次加热的温度控制在30摄氏度，能够进一步保证按摩球的抗拉伸强度和延展性;将除味后的按摩球粘接封装按摩凸起壳体，使用时，凸起起到了较好的按摩效果，使整个按摩球的按摩效果大大提高;将封装后的按摩球用粘胶贴合磁片，磁片产生的磁场具有较好的理疗效果。
[0090]本发明不限于上述实施例，根据上述实施例的描述，本领域的普通技术人员还可对本发明作出一些显而易见的改变，但这些改变均应落入本发明权利要求的保护范围之内。
Claims (3)
1.一种磁性按摩球的制造方法，其特征在于，依次由以下工艺步骤组成: A、选取10-20份天然橡胶、15-30份聚丙烯、15-30份乙酸乙烯酯和10-20份氯丁二烯作为原料，将其混合搅拌均匀； B、将A步骤混合均匀后的原料加入成型机中进行首次加热； C、将B步骤加热后的原料自然冷却，然后再进行再次加热； D、将C步骤经过再次加热后的原料通过成型机的挤压机头挤出，再通过圆型模具成型； E、将D步骤成型后得到的按摩球取出并通风冷却； F、将E步骤通风冷却后的按摩球用抛光机进行表面打磨处理； G、将F步骤打磨后的按摩球放在盛装有木炭和水的除味池里除去异味，最后通风晾干； H、将G步骤除味后的按摩球粘接封装按摩凸起壳体； 1、将H步骤封装后的按摩球用粘胶贴合磁片，即得成品。
2.根据权利要求1所述一种磁性按摩球的制造方法，其特征在于:所述B步骤中对混合均匀后的原料进行首次加热的温度为100-120摄氏度。
3.根据权利要求2所述一种磁性按摩球的制造方法，其特征在于:所述C步骤中对自然冷却后的原料进行再次加热的温度为20-30摄氏度。