CN103694838A - Moisture protection cabinet - Google Patents
Moisture protection cabinet Download PDFInfo
- Publication number
- CN103694838A CN103694838A CN201310698633.XA CN201310698633A CN103694838A CN 103694838 A CN103694838 A CN 103694838A CN 201310698633 A CN201310698633 A CN 201310698633A CN 103694838 A CN103694838 A CN 103694838A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- moisture
- parts
- moisture absorption
- cabinet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a moisture protection cabinet. The inner wall of the cabinet is coated with a moisture-absorbing top coating having a thickness of 0.2mm, wherein the moisture-absorbing top coating is formed by drying water-based moisture-absorbing top coating paint; and the water-based moisture-absorbing top coating paint comprises the following components in parts by mass: 1-2 parts of sodium lauroyl aminoethylsulfate, 55 parts of moisture absorber, 3 parts of polypropylene glycol, 3 parts of polyvinylpyrrolidone, 40 parts of deionized water, 2 parts of polymethacrylic acid, 1 part of amido compound, 5 parts of polyacrylamide, 3 parts of polyacrylic acid and 4 parts of polyethylene glycol. The moisture protection cabinet has favorable moisture absorption performance in the cabinet.
Description
Technical field
The present invention relates to moisture-resistant cabinet.
Background technology
At present during moisture-resistant cabinet life-time service on the market, the inner hygroscopic property of cabinet is not ideal enough.
Summary of the invention
The object of the present invention is to provide a kind of moisture-resistant cabinet, the inner hygroscopic property of its cabinet is good.
For achieving the above object, technical scheme of the present invention is a kind of moisture-resistant cabinet of design, the moisture absorption face coating layer of its cabinet inwall coating thickness 0.2mm;
Described moisture absorption face coating layer is dried and is formed by water-based moisture absorption painting coating, and described water-based moisture absorption painting coating is comprised of following component:
1-2 mass parts lauramide sodium ethyl sulfate, 55 mass parts moisture adsorbents, 3 mass parts polypropylene glycols, 3 mass parts polyvinylpyrrolidones, 40 mass parts deionized waters, 2 mass parts polymethyl acrylic acid, 1 mass parts amido compounds, 5 mass parts polyacrylamides, 3 mass parts polyacrylic acid, 4 mass parts polyoxyethylene glycol.
Advantage of the present invention and beneficial effect are: a kind of moisture-resistant cabinet is provided, and the inner hygroscopic property of its cabinet is good.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A moisture-resistant cabinet, the moisture absorption face coating layer of its cabinet inwall coating thickness 0.2mm;
Described moisture absorption face coating layer is dried and is formed by water-based moisture absorption painting coating, and described water-based moisture absorption painting coating is comprised of following component:
1 mass parts lauramide sodium ethyl sulfate, 55 mass parts moisture adsorbents, 3 mass parts polypropylene glycols, 3 mass parts polyvinylpyrrolidones, 40 mass parts deionized waters, 2 mass parts polymethyl acrylic acid, 1 mass parts amido compounds, 5 mass parts polyacrylamides, 3 mass parts polyacrylic acid, 4 mass parts polyoxyethylene glycol.
Embodiment 2
A moisture-resistant cabinet, the moisture absorption face coating layer of its cabinet inwall coating thickness 0.2mm;
Described moisture absorption face coating layer is dried and is formed by water-based moisture absorption painting coating, and described water-based moisture absorption painting coating is comprised of following component:
1.2 mass parts lauramide sodium ethyl sulfate, 55 mass parts moisture adsorbents, 3 mass parts polypropylene glycols, 3 mass parts polyvinylpyrrolidones, 40 mass parts deionized waters, 2 mass parts polymethyl acrylic acid, 1 mass parts amido compounds, 5 mass parts polyacrylamides, 3 mass parts polyacrylic acid, 4 mass parts polyoxyethylene glycol.
Embodiment 3
A moisture-resistant cabinet, the moisture absorption face coating layer of its cabinet inwall coating thickness 0.2mm;
Described moisture absorption face coating layer is dried and is formed by water-based moisture absorption painting coating, and described water-based moisture absorption painting coating is comprised of following component:
2 mass parts lauramide sodium ethyl sulfate, 55 mass parts moisture adsorbents, 3 mass parts polypropylene glycols, 3 mass parts polyvinylpyrrolidones, 40 mass parts deionized waters, 2 mass parts polymethyl acrylic acid, 1 mass parts amido compounds, 5 mass parts polyacrylamides, 3 mass parts polyacrylic acid, 4 mass parts polyoxyethylene glycol.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. moisture-resistant cabinet, is characterized in that, the moisture absorption face coating layer of its cabinet inwall coating thickness 0.2mm;
Described moisture absorption face coating layer is dried and is formed by water-based moisture absorption painting coating, and described water-based moisture absorption painting coating is comprised of following component:
1-2 mass parts lauramide sodium ethyl sulfate, 55 mass parts moisture adsorbents, 3 mass parts polypropylene glycols, 3 mass parts polyvinylpyrrolidones, 40 mass parts deionized waters, 2 mass parts polymethyl acrylic acid, 1 mass parts amido compounds, 5 mass parts polyacrylamides, 3 mass parts polyacrylic acid, 4 mass parts polyoxyethylene glycol.