CN103694675A - 耐黄抗紫外线的聚氨酯弹性体 - Google Patents
耐黄抗紫外线的聚氨酯弹性体 Download PDFInfo
- Publication number
- CN103694675A CN103694675A CN201310678452.0A CN201310678452A CN103694675A CN 103694675 A CN103694675 A CN 103694675A CN 201310678452 A CN201310678452 A CN 201310678452A CN 103694675 A CN103694675 A CN 103694675A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- parts
- polyurethane elastomer
- resistant
- ultraviolet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐黄抗紫外线的聚氨酯弹性体,由如下组分组成:1-2质量份聚甘油单硬脂酸酯,4质量份双[β(3-叔丁基-5-甲基-4-羟基苯基)丙酸]三甘醇酯,20质量份聚醚多元醇,1质量份三乙烯二胺,3质量份2-(2’-羟基-3’,5’-二[1,1-二甲基苯基])–苯并三唑)-5-氯化苯并三唑,0质量份环氧丙烷型聚醚多元醇,18质量份甲苯二氰酸酯,1质量份羟乙基纤维素,9质量份二乙基甲苯二胺。本发明耐黄抗紫外线的聚氨酯弹性体,其物理机械性能好、耐黄、抗紫外线能力强。
Description
技术领域
本发明涉及耐黄抗紫外线的聚氨酯弹性体。
背景技术
现有聚氨酯弹性体,其物理机械性能一般,不具有耐黄、抗紫外线能力。
发明内容
本发明的目的在于提供一种耐黄抗紫外线的聚氨酯弹性体,其物理机械性能好、耐黄、抗紫外线能力强。
为实现上述目的,本发明的技术方案是设计一种耐黄抗紫外线的聚氨酯弹性体,由如下组分组成:
1-2质量份聚甘油单硬脂酸酯,
4质量份双[β(3-叔丁基-5-甲基-4-羟基苯基)丙酸]三甘醇酯,
20质量份聚醚多元醇,
1质量份三乙烯二胺,
3质量份2-(2’-羟基-3’,5’-二[1,1-二甲基苯基])–苯并三唑)-5-氯化苯并三唑,50质量份环氧丙烷型聚醚多元醇,
18质量份甲苯二氰酸酯,
1质量份羟乙基纤维素,
9质量份二乙基甲苯二胺。
本发明的优点和有益效果在于:提供一种耐黄抗紫外线的聚氨酯弹性体,其物理机械性能好、耐黄、抗紫外线能力强。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种耐黄抗紫外线的聚氨酯弹性体,由如下组分组成:
2质量份聚甘油单硬脂酸酯,
4质量份双[β(3-叔丁基-5-甲基-4-羟基苯基)丙酸]三甘醇酯,
20质量份聚醚多元醇,
1质量份三乙烯二胺,
3质量份2-(2’-羟基-3’,5’-二[1,1-二甲基苯基])–苯并三唑)-5-氯化苯并三唑,50质量份环氧丙烷型聚醚多元醇,
18质量份甲苯二氰酸酯,
1质量份羟乙基纤维素,
9质量份二乙基甲苯二胺。
实施例2
一种耐黄抗紫外线的聚氨酯弹性体,由如下组分组成:
1质量份聚甘油单硬脂酸酯,
4质量份双[β(3-叔丁基-5-甲基-4-羟基苯基)丙酸]三甘醇酯,
20质量份聚醚多元醇,
1质量份三乙烯二胺,
3质量份2-(2’-羟基-3’,5’-二[1,1-二甲基苯基])–苯并三唑)-5-氯化苯并三唑,50质量份环氧丙烷型聚醚多元醇,
18质量份甲苯二氰酸酯,
1质量份羟乙基纤维素,
9质量份二乙基甲苯二胺。
实施例3
一种耐黄抗紫外线的聚氨酯弹性体,由如下组分组成:
1.2质量份聚甘油单硬脂酸酯,
4质量份双[β(3-叔丁基-5-甲基-4-羟基苯基)丙酸]三甘醇酯,
20质量份聚醚多元醇,
1质量份三乙烯二胺,
3质量份2-(2’-羟基-3’,5’-二[1,1-二甲基苯基])–苯并三唑)-5-氯化苯并三唑,50质量份环氧丙烷型聚醚多元醇,
18质量份甲苯二氰酸酯,
1质量份羟乙基纤维素,
9质量份二乙基甲苯二胺。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.耐黄抗紫外线的聚氨酯弹性体,其特征在于,由如下组分组成:
1-2质量份聚甘油单硬脂酸酯,
4质量份双[β(3-叔丁基-5-甲基-4-羟基苯基)丙酸]三甘醇酯,
20质量份聚醚多元醇,
1质量份三乙烯二胺,
3质量份2-(2’-羟基-3’,5’-二[1,1-二甲基苯基])–苯并三唑)-5-氯化苯并三唑,50质量份环氧丙烷型聚醚多元醇,
18质量份甲苯二氰酸酯,
1质量份羟乙基纤维素,
9质量份二乙基甲苯二胺。