CN103668153A - 一种高效蓝白钝化剂的制备方法 - Google Patents

一种高效蓝白钝化剂的制备方法 Download PDF

Info

Publication number
CN103668153A
CN103668153A CN201210326916.7A CN201210326916A CN103668153A CN 103668153 A CN103668153 A CN 103668153A CN 201210326916 A CN201210326916 A CN 201210326916A CN 103668153 A CN103668153 A CN 103668153A
Authority
CN
China
Prior art keywords
preparation
edta
passivation
efficiency blue
deionized water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210326916.7A
Other languages
English (en)
Inventor
张汝山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN DAGANG GALVANIZED FACTORY
Original Assignee
TIANJIN DAGANG GALVANIZED FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN DAGANG GALVANIZED FACTORY filed Critical TIANJIN DAGANG GALVANIZED FACTORY
Priority to CN201210326916.7A priority Critical patent/CN103668153A/zh
Publication of CN103668153A publication Critical patent/CN103668153A/zh
Pending legal-status Critical Current

Abstract

本发明研制了一种高效蓝白钝化剂的制备方法，配方由三氯化铬、硅酸钠、硝酸、硝酸钠、丙二酸、氟化钠、EDTA和去离子水构成。本发明的优越性：由此研制出来的三价铬钝化膜具有色彩鲜艳、成膜均匀。耐蚀性能优良。钝化液本身性能稳定，陈本价格低，性能好。

Description

一种高效蓝白钝化剂的制备方法
技术领域
本发明涉及一种用于金属锌表面钝化处理的钝化剂的制备方法，尤其涉及一种高效蓝白钝化剂的制备方法。
背景技术
总所周知 ，六价铬有剧毒且污染环境。所以金属锌表面的钝化处理必须寻求无污染的六价铬代替技术，现在已经出现的替代技术有无铬钝化和三价铬钝化。但现有的无铬钝化技术还存在膜层质量较差，工艺复杂、成本较高等缺点。
三价铬化合物是构成钝化膜的重要物质，是膜层的骨架。实验证明通过某些改进手段可以使三价铬钝化工艺达到六价铬钝化的效果。所以三价铬钝化工艺是最有可能的六价铬钝化替代工艺，本发明通过研究得到了一种三价铬钝化剂的钝化工艺。
发明内容
本发明研制了一种高效蓝白钝化剂的制备方法，本发明的技术方案是：高效蓝白钝化剂的配方由三氯化铬、硅酸钠、硝酸、硝酸钠、丙二酸、氟化钠、EDTA和去离子水构成。适宜配方为：三氯化铬为25-30g/L、硅酸钠为8-10g/L、硝酸为1-2ml/L、硝酸钠为10-15g/L、丙二酸为5-10g/L、氟化钠为0.8-1.2g/L，EDTA为0.8-1.2g/L和去离子水配比而成，使用时按照10-15%与水配比稀释，操作温度：室温,PH值控制在：1.8-2.2。
本发明的优越性：由此研制出来的三价铬钝化膜具有蓝白色、成膜均匀。耐蚀性能优良。钝化液本身性能稳定，陈本价格低，性能好。
具体实施方式
下面的实施例可以使本专业技术人员更全面地理解本发明，但不以任何方式限制本发明。
实施例1：
配方为：三氯化铬为25g/L、硅酸钠为8g/L、硝酸为1ml/L、硝酸钠为10g/L、丙二酸为5g/L、氟化钠为0.8g/L，EDTA为0.8g/L和去离子水配比而成，使用时按照10%与水配比稀释，操作温度：室温,PH值控制在：2.0钝化时间为25秒，金属锌层表面颜色为蓝白色且均匀的钝化膜。
实施例2：
配方为：三氯化铬为27.5g/L、硅酸钠为9g/L、硝酸为1.5ml/L、硝酸钠为12.5g/L、丙二酸为5-7.5g/L、氟化钠为1g/L，EDTA为1g/L和去离子水配比而成，使用时按照10%与水配比稀释，操作温度：室温,PH值控制在：2.0。钝化时间为20秒，金属锌层表面颜色为蓝白色且均匀的钝化膜。
实施例3：
配方为：三氯化铬为30g/L、硅酸钠为10g/L、硝酸为2ml/L、硝酸钠为15g/L、丙二酸为10g/L、氟化钠为1.2g/L，EDTA为1.2g/L和去离子水配比而成，使用时按照15%与水配比稀释，操作温度：室温,PH值控制在：1.8-1.8。钝化时间为15秒，金属锌层表面颜色为蓝白色且均匀的钝化膜。
实施例4：
配方为：三氯化铬为25g/L、硅酸钠为8g/L、硝酸为1ml/L、硝酸钠为10g/L、丙二酸为10g/L、氟化钠为1.2g/L，EDTA为1.2g/L和去离子水配比而成，使用时按照15%与水配比稀释，操作温度：室温,PH值控制在：1.8。钝化时间为15秒，金属锌层表面颜色为蓝白色且均匀的钝化膜。

Claims (1)

1.一种高效蓝白钝化剂的制备方法，其特征在于：高效蓝白钝化剂的配方由三氯化铬、硅酸钠、硝酸、硝酸钠、丙二酸、氟化钠、EDTA和去离子水构成，适宜配方为：三氯化铬为25-30g/L、硅酸钠为8-10g/L、硝酸为1-2ml/L、硝酸钠为10-15g/L、丙二酸为5-10g/L、氟化钠为0.8-1.2g/L，EDTA为0.8-1.2g/L和去离子水配比而成，使用时按照10-15%与水配比稀释，操作温度：室温,PH值控制在：1.8-2.2。
CN201210326916.7A 2012-09-06 2012-09-06 一种高效蓝白钝化剂的制备方法 Pending CN103668153A (zh)