CN103667853A - 一种含钛奥氏体不锈钢的两步法冶炼方法 - Google Patents
一种含钛奥氏体不锈钢的两步法冶炼方法 Download PDFInfo
- Publication number
- CN103667853A CN103667853A CN201310646422.1A CN201310646422A CN103667853A CN 103667853 A CN103667853 A CN 103667853A CN 201310646422 A CN201310646422 A CN 201310646422A CN 103667853 A CN103667853 A CN 103667853A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- molten steel
- smelting
- austenitic stainless
- containing austenitic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种含钛奥氏体不锈钢的两步法冶炼方法,涉及不锈钢冶炼技术领域,步骤为:(1)把电弧炉冶炼后的钢水加入到AOD精炼炉中,再加入铝锭、萤石造渣;(2)调渣结束后加入FeNb,加入量是使Nb为钢水量的0.1~0.2%;(3)加入FeTi,加入量是使Nb为钢水量的0.1~0.15%,保证满足(0.5Nb+Ti)≥6C,并搅拌;(4)钢水的化学成分符合标准要求时出炉。本发明提供的含钛奥氏体不锈钢的两步法冶炼方法,它是把电弧炉冶炼后的钢水加入到AOD精炼炉中精炼,本冶炼方法易操作,生产的含钛奥氏体不锈钢的力学性能易符合欧美标准要求。
Description
技术领域:
本发明涉及不锈钢冶炼技术领域,尤其涉及一种含钛奥氏体不锈钢的两步法冶炼方法。
背景技术:
不锈钢不易产生腐蚀、点蚀、锈蚀或磨损。不锈钢还是建筑用金属材料中强度最高的材料之一。由于不锈钢具有良好的耐腐蚀性,所以它能使结构部件永久地保持工程设计的完整性。含铬不锈钢还集机械强度和高延伸性于一身,易于部件的加工制造,可满足建筑师和结构设计人员的需要。
不锈钢常按组织状态分为:马氏体钢、铁素体钢、奥氏体钢、奥氏体-铁素体(双相)不锈钢及沉淀硬化不锈钢等。另外,可按成分分为:铬不锈钢、铬镍不锈钢和铬锰氮不锈钢等。各产品由于用途的不同,其加工工艺和原料的品质要求也不同。
目前,随着不锈钢产品的引用领域越来越广,对不锈钢也提出了更高的要求,现有不锈钢冶炼技术还不能满足市场的需求,尤其是对特种钢需求,现有冶炼技术还存在很大缺陷。含钛奥氏体不锈钢的力学性能不容易达到标准要求。
发明内容:
本发明的目的是提供一种含钛奥氏体不锈钢的两步法冶炼方法。
本发明所要解决的技术问题采用以下技术方案来实现。
一种含钛奥氏体不锈钢的两步法冶炼方法,其特征在于,步骤为:
(1)把电弧炉冶炼后的钢水加入到AOD精炼炉中,再加入铝锭、萤石造渣;
(2)调渣结束后加入FeNb,加入量是使Nb为钢水量的0.1~0.2%;
(3)加入FeTi,加入量是使Nb为钢水量的0.1~0.15%,保证满足(0.5Nb+Ti)≥6C,并搅拌;
(4)钢水的化学成分符合标准要求时出炉。
本发明的有益效果是:
本发明提供的含钛奥氏体不锈钢的两步法冶炼方法,它是把电弧炉冶炼后的钢水加入到AOD精炼炉中精炼,本冶炼方法易操作,生产的含钛奥氏体不锈钢的力学性能易符合欧美标准要求。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
一种含钛奥氏体不锈钢的两步法冶炼方法,步骤为:
(1)把电弧炉冶炼后的钢水加入到AOD精炼炉中,再加入铝锭、萤石造渣;
(2)调渣结束后加入FeNb,加入量是使Nb为钢水量的0.1~0.2%;
(3)加入FeTi,加入量是使Nb为钢水量的0.1~0.15%,保证满足(0.5Nb+Ti)≥6C,并搅拌;
(4)钢水的化学成分符合标准要求时出炉。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (1)
1.一种含钛奥氏体不锈钢的两步法冶炼方法,其特征在于,步骤为:
(1)把电弧炉冶炼后的钢水加入到AOD精炼炉中,再加入铝锭、萤石造渣;
(2)调渣结束后加入FeNb,加入量是使Nb为钢水量的0.1~0.2%;
(3)加入FeTi,加入量是使Nb为钢水量的0.1~0.15%,保证满足(0.5Nb+Ti)≥6C,并搅拌;
(4)钢水的化学成分符合标准要求时出炉。