CN103666243A - Polyester-polyamide coating for copper - Google Patents
Polyester-polyamide coating for copper Download PDFInfo
- Publication number
- CN103666243A CN103666243A CN201310619016.6A CN201310619016A CN103666243A CN 103666243 A CN103666243 A CN 103666243A CN 201310619016 A CN201310619016 A CN 201310619016A CN 103666243 A CN103666243 A CN 103666243A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- polyester
- resistant
- polyamide coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A polyester-polyamide coating for copper comprises the components in parts by mass as follows: 100 parts of dimethyl terephthalate, 5-7 parts of chlorinated paraffin, 10-15 parts of 12-aminododecanoic acid, 10-15 parts of precipitated barium sulfate, 15-25 parts of cyclohexanone, 10-15 parts of talc powder, 25-35 parts of a cellosolve acetate, 30-35 parts of micaceous iron oxide, 5-15 parts of toluene, 1-5 parts of an anti-setting agent, 35-45 parts of melamine-formaldehyde, 50-60 parts of ethylene glycol and neopentyl glycol. The coating can be cured to form a paint layer 20 micrometers in thickness within 2 h; and the coating is anti- corrosion, high-temperature-resistant, moisture-resistant, wear-resistant, sun-proof, high in adhesive force and capable of being widely produced and continuously replacing existing materials.
Description
Technical field
The application belongs to metallic paint field, relates in particular to a kind of copper polyester-polyamide coating.
Background technology
Epoxy polyester type powder coating is a kind of of thermosetting powder coating(s).Adopting epoxy resin and vibrin is that main raw material(s) is prepared from, possess both special performances separately simultaneously, filming of making to produce have extremely good levelling property, ornamental, mechanical property and stronger erosion resistance, and wide model is applied to the application of various indoor metal goods.
Polyester-polyamide coating is mainly used in the external coating of the industries such as automobile, household electrical appliance, art metal furniture, instrument, indoor body-building sports equipment, scatterer, development along with social city, technicalization, hommization, design copper that a kind of chemicals-resistant, resistance to soiling are good with polyester-polyamide coating to meet the need of market, be very important.
Summary of the invention
the technical problem solving:
The application, for the technical problems such as coating is not corrosion-resistant, resistance to soiling is poor for existing copper, provides a kind of copper polyester-polyamide coating.
technical scheme:
A copper polyester-polyamide coating, is comprised of following raw materials according, take mass fraction representation as 100 parts of dimethyl terephthalate (DMT); Clorafin 5-7 part; The amino dodecylic acid 10-15 of 1,2-part; Process white 10-15 part; Pimelinketone 15-25 part; Talcum powder 10-15 part; Cellosolve acetate 25-35 part; Iron mica is 30-35 part; Toluene is 5-15 part; Anti-settling agent 1-5 part; Terpolycyantoamino-formaldehyde resin 35-45 part; Ethylene glycol 50-60 part; Neopentyl glycol 60-70 part.
As a preferred technical solution of the present invention: described composition be take mass fraction representation as 100 parts of dimethyl terephthalate (DMT); 6 parts of clorafins; 13 parts of the amino dodecylic acids of 1,2-; 12 parts of process whites; 20 parts of pimelinketone; 12 parts of talcum powder; 30 parts of cellosolve acetates; Iron mica is 32.5 parts; Toluene is 10 parts; 3 parts of anti-settling agents; 40 parts of terpolycyantoamino-formaldehyde resins; 55 parts of ethylene glycol; 65 parts of neopentyl glycol.
As a preferred technical solution of the present invention: described anti-settling agent is organobentonite.
beneficial effect:
A kind of copper of the present invention adopts above technical scheme compared with prior art with polyester-polyamide coating, has following technique effect: 1, product 2h can solidify to form the enamelled coating of 20 micron thickness; 2, corrosion-resistant, high temperature resistant, strong adhesion; 3, product humidity, wear-resisting, sun-proof, can the not division of history into periods of widespread production replace current material.
Embodiment
embodiment 1:
A copper polyester-polyamide coating, its composition be take mass fraction representation as 100 parts of dimethyl terephthalate (DMT); Clorafin 5-7 part; The amino dodecylic acid 10-15 of 1,2-part; Process white 10-15 part; Pimelinketone 15-25 part; Talcum powder 10-15 part; Cellosolve acetate 25-35 part; Iron mica is 30-35 part; Toluene is 5-15 part; Organobentonite 1-5 part; Terpolycyantoamino-formaldehyde resin 35-45 part; Ethylene glycol 50-60 part; Neopentyl glycol 60-70 part.
Product product 2h can solidify to form the enamelled coating of 20 micron thickness, and humidity, corrosion-resistant is high temperature resistant, strong adhesion and wear-resisting.
embodiment 2:
A copper polyester-polyamide coating, its composition be take mass fraction representation as 100 parts of dimethyl terephthalate (DMT); Clorafin 5-7 part; The amino dodecylic acid 10-15 of 1,2-part; Process white 10-15 part; Pimelinketone 15-25 part; Talcum powder 10-15 part; Cellosolve acetate 25-35 part; Iron mica is 30-35 part; Toluene is 5-15 part; Organobentonite 1-5 part; Terpolycyantoamino-formaldehyde resin 35-45 part; Ethylene glycol 50-60 part; Neopentyl glycol 60-70 part.
Product product 1.5h can solidify to form the enamelled coating of 20 micron thickness, and humidity, corrosion-resistant is high temperature resistant, strong adhesion and wear-resisting.
embodiment 3:
A copper polyester-polyamide coating, is characterized in that: its composition be take mass fraction representation as 100 parts of dimethyl terephthalate (DMT); 6 parts of clorafins; 13 parts of the amino dodecylic acids of 1,2-; 12 parts of process whites; 20 parts of pimelinketone; 12 parts of talcum powder; 30 parts of cellosolve acetates; Iron mica is 32.5 parts; Toluene is 10 parts; 3 parts of organobentonites; 40 parts of terpolycyantoamino-formaldehyde resins; 55 parts of ethylene glycol; 65 parts of neopentyl glycol.
Product product 1h can solidify to form the enamelled coating of 20 micron thickness, and humidity, corrosion-resistant is high temperature resistant, strong adhesion and wear-resisting.
All components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, therefore in the implication suitable with claims of the present invention and any change in scope, all should think to be included in the scope of claims.
Claims (3)
1. a copper polyester-polyamide coating, is characterized in that: its composition be take mass fraction representation as 100 parts of dimethyl terephthalate (DMT); Clorafin 5-7 part; The amino dodecylic acid 10-15 of 1,2-part; Process white 10-15 part; Pimelinketone 15-25 part; Talcum powder 10-15 part; Cellosolve acetate 25-35 part; Iron mica is 30-35 part; Toluene is 5-15 part; Anti-settling agent 1-5 part; Terpolycyantoamino-formaldehyde resin 35-45 part; Ethylene glycol 50-60 part; Neopentyl glycol 60-70 part.
2. a kind of copper polyester-polyamide coating according to claim 1, is characterized in that: its composition be take mass fraction representation as 100 parts of dimethyl terephthalate (DMT); 6 parts of clorafins; 13 parts of the amino dodecylic acids of 1,2-; 12 parts of process whites; 20 parts of pimelinketone; 12 parts of talcum powder; 30 parts of cellosolve acetates; Iron mica is 32.5 parts; Toluene is 10 parts; 3 parts of anti-settling agents; 40 parts of terpolycyantoamino-formaldehyde resins; 55 parts of ethylene glycol; 65 parts of neopentyl glycol.
3. a kind of copper polyester-polyamide coating according to claim 1, is characterized in that: described anti-settling agent is organobentonite.