CN103666129A - High-build coating for copper - Google Patents

High-build coating for copper Download PDF

Info

Publication number
CN103666129A
CN103666129A CN201310618648.0A CN201310618648A CN103666129A CN 103666129 A CN103666129 A CN 103666129A CN 201310618648 A CN201310618648 A CN 201310618648A CN 103666129 A CN103666129 A CN 103666129A
Authority
CN
China
Prior art keywords
parts
coating
thick
zinc
type copper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201310618648.0A
Other languages
Chinese (zh)
Inventor
王惠
张松岩
钱忆张
陈新燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU PAQINI COPPER INDUSTRY Co Ltd
Original Assignee
JIANGSU PAQINI COPPER INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU PAQINI COPPER INDUSTRY Co Ltd filed Critical JIANGSU PAQINI COPPER INDUSTRY Co Ltd
Priority to CN201310618648.0A priority Critical patent/CN103666129A/en
Publication of CN103666129A publication Critical patent/CN103666129A/en
Withdrawn legal-status Critical Current

Abstract

A high-build coating for copper comprises components in parts by mass as follows: 100 parts of vinyl chloride acetate copolymer, 20-30 parts of liquid asphalt, 30-40 parts of phenolic resin, 2-8 parts of talcum powder, 10-20 parts of cyclohexanone, 10-15 parts of xylene, 15-20 parts of methylbenzene, 1-5 parts of glycol ether, 10-15 parts of tricresyl phosphate, 1-5 parts of a rheological agent, 5-10 parts of epoxydized soya bean oil, 10-20 parts of zinc oxide and 15-25 parts of zinc yellow. The coating has rust conversion and corrosion protection functions, the dry film thickness is 50-150 micrometers, and sagging and dripping are prevented; and the product construction is convenient, the process is simple, the cost is low, and the coating can be produced widely and replaces conventional materials continuously.

Description

A kind of thick-slurry type copper coating
 
Technical field
The application belongs to paint field, relates in particular to a kind of thick-slurry type copper coating.
 
Background technology
Bituminous epoxy high build paint is epoxide resin type macromolecular antiseptic waterproof series, and be permanent anticorrosion water-proof material work-ing life.Bituminous epoxy high build paint is to be major ingredient by chloroprene rubber in high-quality petroleum pitch and introducing import epoxy resin modification latex acceding state, be aided with solar oil, oleic acid, coal tar pitch, coal tar, ripe stone flour, asbestos powder, talcum powder, mica powder, breeze, silica powder various additives in addition again, the anticorrosion water-proof material of polymer asphalt cement that weighting agent is formulated, long service life, easy construction.
That high build paint has is applied widely, the life-span is long, weathering resistance, resistance to deformation, tensile strength is high, unit elongation is large, base-layer contraction and craze and transfiguration strong adaptability, resistance to acid, alkali-resistivity, superior, any complex region of corrosion-resistanting waterproofing performance are all easily constructed, solved traditional anticorrosion water-proof material, as coating facade glides, coiled material hollowing, and complicated part operates a difficult difficult problem.Be replaced in traditional anticorrosion water-proof material completely.Have than better anticorrosion, waterproof, insulating property, along with the development of social city, technicalization, hommization, design and a kind ofly there is rust and transform and corrosion-resisting function, the thick-slurry type copper of sagging, with coating to meet the need of market, is not very important.
 
Summary of the invention
the technical problem solving:
The application for existing copper by anticorrosion with coat erosion ability a little less than, easily the technical problem such as sagging, provides a kind of thick-slurry type copper coating.
technical scheme:
A thick-slurry type copper coating, is comprised of following raw materials according, take mass fraction representation as 100 parts of vinyl chloride-vinyl acetate resins; Asphaltic liquid 20-30 part; Resol 30-40 part; Talcum powder 2-8 part; Pimelinketone 10-20 part; Dimethylbenzene 10-15 part; Toluene 15-20 part; Ethylene glycol ethyl ether is 1-5 part; Tritolyl phosphate is 10-15 part; Rheological agent 1-5 part; Epoxidized soybean oil 5-10 part; Zinc oxide 10-20 part; Zinc yellow 15-25 part.
As a preferred technical solution of the present invention: described composition be take mass fraction representation as 100 parts of vinyl chloride-vinyl acetate resins; 25 parts of asphaltic liquids; 35 parts, resol; 5 parts of talcum powder; 15 parts of pimelinketone; 12.5 parts of dimethylbenzene; 17.5 parts of toluene; Ethylene glycol ethyl ether is 3 parts; Tritolyl phosphate is 12.5 parts; 3 parts of rheological agents; 7.5 parts of epoxidized soybean oils; 18 parts, zinc oxide; 20 parts of zinc yellows.
As a preferred technical solution of the present invention: described rheological agent is organobentonite.
 
beneficial effect:
A kind of thick-slurry type copper of the present invention adopts above technical scheme compared with prior art with coating, has following technique effect: 1, product has rust conversion and corrosion-resisting function; 2, build 50-150 micron, sagging, does not drop down and drips; 3, product easy construction, technique is simple, with low cost, can the not division of history into periods of widespread production replace current material.
Embodiment
embodiment 1:
A thick-slurry type copper coating, its composition be take mass fraction representation as 100 parts of vinyl chloride-vinyl acetate resins; 20 parts of asphaltic liquids; 30 parts, resol; 2 parts of talcum powder; 10 parts of pimelinketone; 10 parts of dimethylbenzene; 15 parts of toluene; Ethylene glycol ethyl ether is 1 part; Tritolyl phosphate is 10 parts; 1 part of organobentonite; 5 parts of epoxidized soybean oils; 10 parts, zinc oxide; 15 parts of zinc yellows.
50 microns of product builds, sagging, does not drop down and drips, protection against corrosion.
 
embodiment 2:
A thick-slurry type copper coating, its composition be take mass fraction representation as 100 parts of vinyl chloride-vinyl acetate resins; 30 parts of asphaltic liquids; 40 parts, resol; 8 parts of talcum powder; 20 parts of pimelinketone; 15 parts of dimethylbenzene; 20 parts of toluene; Ethylene glycol ethyl ether is 5 parts; Tritolyl phosphate is 15 parts; 5 parts of organobentonites; 10 parts of epoxidized soybean oils; 20 parts, zinc oxide; 25 parts of zinc yellows.
100 microns of product builds, sagging, does not drop down and drips, protection against corrosion.
 
embodiment 3:
A thick-slurry type copper coating, is characterized in that: its composition be take mass fraction representation as 100 parts of vinyl chloride-vinyl acetate resins; 25 parts of asphaltic liquids; 35 parts, resol; 5 parts of talcum powder; 15 parts of pimelinketone; 12.5 parts of dimethylbenzene; 17.5 parts of toluene; Ethylene glycol ethyl ether is 3 parts; Tritolyl phosphate is 12.5 parts; 3 parts of organobentonites; 7.5 parts of epoxidized soybean oils; 18 parts, zinc oxide; 20 parts of zinc yellows.
150 microns of product builds, sagging, does not drop down and drips, protection against corrosion.
All components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, therefore in the implication suitable with claims of the present invention and any change in scope, all should think to be included in the scope of claims.

Claims (3)

1. a thick-slurry type copper coating, is characterized in that: its composition be take mass fraction representation as 100 parts of vinyl chloride-vinyl acetate resins; Asphaltic liquid 20-30 part; Resol 30-40 part; Talcum powder 2-8 part; Pimelinketone 10-20 part; Dimethylbenzene 10-15 part; Toluene 15-20 part; Ethylene glycol ethyl ether is 1-5 part; Tritolyl phosphate is 10-15 part; Rheological agent 1-5 part; Epoxidized soybean oil 5-10 part; Zinc oxide 10-20 part; Zinc yellow 15-25 part.
2. a kind of thick-slurry type copper coating according to claim 1, is characterized in that: its composition be take mass fraction representation as 100 parts of vinyl chloride-vinyl acetate resins; 25 parts of asphaltic liquids; 35 parts, resol; 5 parts of talcum powder; 15 parts of pimelinketone; 12.5 parts of dimethylbenzene; 17.5 parts of toluene; Ethylene glycol ethyl ether is 3 parts; Tritolyl phosphate is 12.5 parts; 3 parts of rheological agents; 7.5 parts of epoxidized soybean oils; 18 parts, zinc oxide; 20 parts of zinc yellows.
3. a kind of thick-slurry type copper coating according to claim 1, is characterized in that: described rheological agent is organobentonite.
CN201310618648.0A 2013-11-29 2013-11-29 High-build coating for copper Withdrawn CN103666129A (en)