CN103665738A - Ageing resistant ABS material and preparation method thereof - Google Patents
Ageing resistant ABS material and preparation method thereof Download PDFInfo
- Publication number
- CN103665738A CN103665738A CN201310636271.1A CN201310636271A CN103665738A CN 103665738 A CN103665738 A CN 103665738A CN 201310636271 A CN201310636271 A CN 201310636271A CN 103665738 A CN103665738 A CN 103665738A
- Authority
- CN
- China
- Prior art keywords
- parts
- abs material
- antioxidant
- aging
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses an ageing resistant ABS material and a preparation method thereof. The ageing resistant ABS material comprises, by weight, 80-100 parts of an ABS resin, 0.1-0.3 parts of an antioxidant 1010, 0.2-0.6 parts of an antioxidant 2216, 0.2-0.6 parts of an ultraviolet absorber UV531, 0.2-0.5 parts of an auxiliary assistant LDPE, 0.5-1 part of barium stearate, 5-10 parts of dibutyl phthalate, 0.2-1 part of an organic tin stabilizer, and 1-5 parts of dioctyl sebacate. The preparation method comprises the following steps: mixing the above components in a mixing stirrer, and extruding through a double screw extruder at 178-210DEG C under a screw rotating speed of 20-60rpm. The ageing resistant ABS material has a tensile strength retention rate after an ageing test of above 90.4%, an impact strength retention rate of above 78.26%, and a very good ageing resistance.
Description
Technical field
The invention belongs to chemical material field, particularly a kind of anti-aging ABS material and preparation method thereof.
Background technology
ABS resin is that current production rate is maximum, most widely used polymkeric substance, it is PS, SAN, the various performances of BS are organically united, have concurrently tough, hard, just balanced good mechanical property mutually.ABS resin has kept cinnamic excellent electrical properties and easy processing forming, elasticity, intensity, heat-resisting and erosion resistance have been increased again, and surface hardness is high, chemical resistant properties is good, simultaneously by changing the ratio of above-mentioned three kinds of components, can change the various performances of ABS, therefore ABS engineering plastics have extensive use, be mainly used in the industry such as machinery, electric, weaving, automobile and shipbuilding.But in long-term use procedure, ABS material is easily aging, its performance also declines thereupon, and therefore need to develop a kind of aging-resistant ABS material makes up above deficiency.
Summary of the invention
The object of the invention is to provides a kind of anti-aging ABS material and preparation method thereof in order to overcome above the deficiencies in the prior art.
The present invention realizes by following technique means:
A kind of anti-aging ABS material, in components by weight percent, comprise: ABS resin 80-100 part, antioxidant 1010 0.1-0.3 part, oxidation inhibitor 22160.2-0.6 part, uv-absorbing agent UV5310.2-0.6 part, auxiliary antioxidant LDPE0.2-0.5 part, barium stearate 0.5-1 part, dibutyl phthalate 5-10 part, organotin stabilizer 0.2-1 part, dioctyl sebacate 1-5 part.
Described anti-aging ABS material, preferably can be for comprising in components by weight percent: ABS resin 90-95 part, antioxidant 1010 0.1-0.2 part, oxidation inhibitor 22160.2-0.4 part, uv-absorbing agent UV5310.3-0.5 part, auxiliary antioxidant LDPE0.3-0.5 part, barium stearate 0.5-1 part, dibutyl phthalate 6-8 part, organotin stabilizer 0.4-0.6 part, dioctyl sebacate 2-4 part.
The preparation method of the anti-aging ABS material described in more than one, carries out according to following steps:
(1) according to weight part, take each component;
(2) each component is mixed in mixing and blending machine, mixing temperature is 60-80 ℃, and stir speed (S.S.) is 80-100 rev/min;
(3) mixed compound is extruded in twin screw extruder, wherein extrusion temperature is 178-210 ℃, and screw speed is 20-60 rev/min.
Anti-aging ABS material provided by the invention is more than tensile strength has reached 121MPa after measured, and more than modulus in flexure has reached 19.2MPa, more than flexural strength has reached 28MPa, shock strength has reached 18KJ/m
2above, through weathering test back draft strength retention, reached more than 90.4%, shock strength conservation rate has reached more than 78.26%, shows that anti-aging ABS material provided by the invention has good anti-aging characteristic.
Embodiment:
Embodiment 1
A kind of anti-aging ABS material, in components by weight percent, comprise: 80 parts of ABS resin, 0.1 part of antioxidant 1010,22160.2 parts, oxidation inhibitor, uv-absorbing agent UV5310.2 part, auxiliary antioxidant LDPE0.2 part, 0.5 part of barium stearate, 5 parts of dibutyl phthalates, 0.2 part of organotin stabilizer, 1 part of dioctyl sebacate.
Above-described anti-aging ABS material is prepared according to following steps:
(1) according to weight part, take each component;
(2) each component is mixed in mixing and blending machine, mixing temperature is 60 ℃, and stir speed (S.S.) is 80 revs/min;
(3) mixed compound is extruded in twin screw extruder, wherein extrusion temperature is 178 ℃, and screw speed is 20 revs/min.
Embodiment 2
A kind of anti-aging ABS material, in components by weight percent, comprise: 90 parts of ABS resin, 0.1 part of antioxidant 1010,22160.2 parts, oxidation inhibitor, uv-absorbing agent UV5310.3 part, auxiliary antioxidant LDPE0.3 part, 0.5 part of barium stearate, 6 parts of dibutyl phthalates, 0.4 part of organotin stabilizer, 2 parts of dioctyl sebacates.
Above-described anti-aging ABS material is prepared according to following steps:
(1) according to weight part, take each component;
(2) each component is mixed in mixing and blending machine, mixing temperature is 70 ℃, and stir speed (S.S.) is 88 revs/min;
(3) mixed compound is extruded in twin screw extruder, wherein extrusion temperature is 190 ℃, and screw speed is 50 revs/min.
Embodiment 3
A kind of anti-aging ABS material, in components by weight percent, comprise: 93 parts of ABS resin, 0.1 part of antioxidant 1010,22160.3 parts, oxidation inhibitor, uv-absorbing agent UV5310.4 part, auxiliary antioxidant LDPE0.4 part, 0.8 part of barium stearate, 7 parts of dibutyl phthalates, 0.5 part of organotin stabilizer, 3 parts of dioctyl sebacates.
Above-described anti-aging ABS material is prepared according to following steps:
(1) according to weight part, take each component;
(2) each component is mixed in mixing and blending machine, mixing temperature is 65 ℃, and stir speed (S.S.) is 85 revs/min;
(3) mixed compound is extruded in twin screw extruder, wherein extrusion temperature is 185 ℃, and screw speed is 40 revs/min.
Embodiment 4
A kind of anti-aging ABS material, in components by weight percent, comprise: 95 parts of ABS resin, 0.2 part of antioxidant 1010,22160.4 parts, oxidation inhibitor, uv-absorbing agent UV5310.5 part, auxiliary antioxidant LDPE0.5 part, 1 part of barium stearate, 8 parts of dibutyl phthalates, 0.6 part of organotin stabilizer, 4 parts of dioctyl sebacates.
Above-described anti-aging ABS material is prepared according to following steps:
(1) according to weight part, take each component;
(2) each component is mixed in mixing and blending machine, mixing temperature is 80 ℃, and stir speed (S.S.) is 90 revs/min;
(3) mixed compound is extruded in twin screw extruder, wherein extrusion temperature is 200 ℃, and screw speed is 50 revs/min.
Embodiment 5
A kind of anti-aging ABS material, in components by weight percent, comprise: 100 parts of ABS resin, 0.3 part of antioxidant 1010,22160.6 parts, oxidation inhibitor, uv-absorbing agent UV5310.6 part, auxiliary antioxidant LDPE0.5 part, 1 part of barium stearate, 10 parts of dibutyl phthalates, 1 part of organotin stabilizer, 5 parts of dioctyl sebacates.
Above-described anti-aging ABS material is prepared according to following steps:
(1) according to weight part, take each component;
(2) each component is mixed in mixing and blending machine, mixing temperature is 78 ℃, and stir speed (S.S.) is 100 revs/min;
(3) mixed compound is extruded in twin screw extruder, wherein extrusion temperature is 210 ℃, and screw speed is 60 revs/min.
The anti-aging ABS material that above embodiment is prepared carries out performance test, the results are shown in following table:
Project | Bioassay standard | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
Elongation (%) | D638 | 1.5 | 1.6 | 1.6 | 1.7 | 1.6 |
Tensile strength (MPa) | D638 | 121 | 125 | 123 | 122 | 123 |
Modulus in flexure (MPa) | D790 | 19.2 | 19.8 | 20.5 | 20.3 | 20.1 |
Flexural strength (MPa) | D790 | 28 | 32 | 35 | 34 | 33 |
Shock strength (KJ/m 2) | D256 | 18 | 20 | 23 | 21 | 19 |
The anti-aging ABS material that above embodiment is prepared carries out accelerated aging test, and condition is 90 ℃, and 500 hours, after weathering test, carry out performance measurement, the results are shown in following table:
Project | Bioassay standard | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
Elongation (%) | D638 | 1.3 | 1.4 | 1.4 | 1.5 | 1.3 |
Tensile strength (MPa) | D638 | 110 | 113 | 113 | 114 | 112 |
Stretching strength retentivity % | ? | 90.91 | 90.4 | 91.87 | 93.44 | 91.06 |
Shock strength (KJ/m 2) | D256 | 16 | 18 | 18 | 17 | 15 |
Shock strength conservation rate % | ? | 88.89 | 90 | 78.26 | 80.95 | 78.95 |
As can be seen from the above results, weathering test back draft strength retention has reached more than 90.4%, and shock strength conservation rate has reached more than 78.26%, shows that anti-aging ABS material provided by the invention has good anti-aging characteristic.
Claims (3)
1. an anti-aging ABS material, it is characterized in that, in components by weight percent, comprise: ABS resin 80-100 part, antioxidant 1010 0.1-0.3 part, oxidation inhibitor 2216 0.2-0.6 parts, uv-absorbing agent UV531 0.2-0.6 part, auxiliary antioxidant LDPE 0.2-0.5 part, barium stearate 0.5-1 part, dibutyl phthalate 5-10 part, organotin stabilizer 0.2-1 part, dioctyl sebacate 1-5 part.
2. anti-aging ABS material according to claim 1, it is characterized in that, in components by weight percent, comprise: ABS resin 90-95 part, antioxidant 1010 0.1-0.2 part, oxidation inhibitor 2216 0.2-0.4 parts, uv-absorbing agent UV531 0.3-0.5 part, auxiliary antioxidant LDPE 0.3-0.5 part, barium stearate 0.5-1 part, dibutyl phthalate 6-8 part, organotin stabilizer 0.4-0.6 part, dioctyl sebacate 2-4 part.
3. a preparation method for anti-aging ABS material claimed in claim 1, is characterized in that, according to following steps, carries out:
(1) according to weight part, take each component;
(2) each component is mixed in mixing and blending machine, mixing temperature is 60-80 ℃, and stir speed (S.S.) is 80-100 rev/min;
(3) mixed compound is extruded in twin screw extruder, wherein extrusion temperature is 178-210 ℃, and screw speed is 20-60 rev/min.