CN103664226B - 一种发泡硅钙混凝土墙体砌块配料方法 - Google Patents

一种发泡硅钙混凝土墙体砌块配料方法 Download PDF

Info

Publication number
CN103664226B
CN103664226B CN201310671063.5A CN201310671063A CN103664226B CN 103664226 B CN103664226 B CN 103664226B CN 201310671063 A CN201310671063 A CN 201310671063A CN 103664226 B CN103664226 B CN 103664226B
Authority
CN
China
Prior art keywords
concrete wall
calcium
parts
foaming
building block
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310671063.5A
Other languages
English (en)
Other versions
CN103664226A (zh
Inventor
曲春维
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUIZHONG GUANGYUAN NEW MATERIALS Co Ltd
Original Assignee
SUIZHONG GUANGYUAN NEW MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUIZHONG GUANGYUAN NEW MATERIALS Co Ltd filed Critical SUIZHONG GUANGYUAN NEW MATERIALS Co Ltd
Priority to CN201310671063.5A priority Critical patent/CN103664226B/zh
Publication of CN103664226A publication Critical patent/CN103664226A/zh
Application granted granted Critical
Publication of CN103664226B publication Critical patent/CN103664226B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提出的是一种发泡硅钙混凝土墙体砌块配料方法。在以粉煤灰和石灰与水混合组成的主体料浆100份中，按质量比，加入火山凝灰岩粉10份和钢渣粉10份作为增加剂，再加入聚乙烯醇缩甲醛1份和羧甲基纤维素0.5份作为稠化剂，然后加入硬脂酸钙0.1份和油酸三乙醇胺混合物0.1份作为发泡稳定剂，充分搅拌后，在料浆中加入5%浓度的碳酸钠水溶液3份作为助泡剂，最后加入脱脂铝粉50-60克发气剂，将配制后的料浆加入搅拌机内搅拌，搅拌后注模，蒸养后成为发泡硅钙混凝土墙体材料。采用本发明方法制成的发泡硅钙混凝土墙体砌块强度高，气孔分布均匀，节省水泥。适宜作为发泡硅钙混凝土墙体砌块制造方法应用。

Description

一种发泡硅钙混凝土墙体砌块配料方法
技术领域
 本发明提出的是建材领域的墙体材料领域的配料方法，具体地说是一种发泡硅钙混凝土墙体砌块配料方法。
背景技术
目前发泡硅钙混凝土墙体砌块通常采用粉煤灰和石灰作为主体材料，通过在混合料浆中加入铝粉进行发泡，经过蒸养制成发泡硅钙混凝土墙体砌块。为了增加强度，在主体材料中加入水泥，加入水泥后增加了成本。在实际生产中，在搅拌料浆中加入洗衣粉作为泡沫稳定剂，由于洗衣粉为阴离子表面活性剂，虽然能够起到泡沫稳定作用，但影响强度，对铝粉充分发泡没有促进作用，而且对料浆也没有稠化作用，所以在生产过程中容易塌陷，影响发泡率，影响使用性能。
发明内容
为了克服现有发泡硅钙混凝土墙体砌块存在的缺点，本发明提出了一种发泡硅钙混凝土墙体砌块配料方法。该方法通过在硅钙主体材料中加入火山凝灰岩和钢渣，作为增强剂，通过在主体料浆中加入聚乙烯醇缩甲醛和羧甲基纤维素作为稠化剂，通过在料浆中加入硬脂酸钙作为泡沫稳定悬浮剂。解决发泡硅钙混凝土墙体砌块改善性能的技术问题。
本发明解决技术问题所采用的方案是：
在以粉煤灰和石灰与水混合组成的主体料浆100份中，按质量比，加入火山凝灰岩粉10份和钢渣粉10份作为增强剂，再加入聚乙烯醇缩甲醛1份和羧甲基纤维素0.5份作为稠化剂，然后加入硬脂酸钙0.1份和油酸三乙醇胺混合物0.1份作为发泡稳定剂，充分搅拌后，在料浆中加入5%浓度的碳酸钠水溶液3份作为助泡剂，最后加入脱脂铝粉50-60克发气剂，将配制后的料浆加入搅拌机内搅拌，搅拌后注模，蒸养后成为发泡硅钙混凝土墙体材料。
积极效果，由于本发明的发泡硅钙混凝土墙体砌块料浆中加有增强剂，提高了产品的刚性和强度，减少水泥用量；在料浆中加入稠化剂，提高稠化效果，缩短稠化时间；在料浆中加入泡沫稳定悬浮剂，使泡沫均匀，不至于塌陷。适宜作为发泡硅钙混凝土墙体砌块的配料方法应用。
具体实施方式
在以粉煤灰和石灰与水混合组成的主体料浆100份中，按质量比，加入火山凝灰岩粉10份和钢渣粉10份作为增强剂，再加入聚乙烯醇缩甲醛1份和羧甲基纤维素0.5份作为稠化剂，然后加入硬脂酸钙0.1份和油酸三乙醇胺混合物0.1份作为发泡稳定剂，充分搅拌后，在料浆中加入5%浓度的碳酸钠水溶液3份作为助泡剂，最后加入脱脂铝粉50-60克发气剂，将配制后的料浆加入搅拌机内搅拌，搅拌后注模，蒸养后成为发泡硅钙混凝土墙体材料。
本发明配料的技术原理：
配料中所加入的火山凝灰岩和钢渣具有活性，能够增加硅钙混凝土的强度，不需要加入水泥，便能够起到加入水泥的作用，使所制成的发泡硅钙混凝土墙体砌块强度增加，同时，火山凝灰岩和钢渣具有砂质性，在发泡硅钙混凝土中起到骨架作用，因此，能够增加强度。通过试验表明，加入火山凝灰岩和钢渣的发泡混凝土抗压强度与普通加有水泥的发泡混凝土墙体砌块增加耐压值5%以上。
配料中加入的聚乙烯醇缩甲醛和羧甲基纤维素，能够使硅钙混凝土料浆迅速稠化，提早稠化时间，对发泡和稳泡有利。
配料中加入硬脂酸钙和油酸三乙醇胺混合物具有悬浮性和稳泡性，能够使铝粉所产生的气泡稳定，不破裂，而且是料浆中的颗粒物呈悬浮状态，不至于塌陷。
配料中加入的碳酸钠水溶液增加了硅钙混凝土料浆中的碱度，使铝粉充分反应产生氢气气泡，分散在硅钙混凝土料浆中，能够减小容重，增加孔隙率，减少用料，节约成本。

Claims (1)

1.一种发泡硅钙混凝土墙体砌块配料方法，其特征是：
在以粉煤灰和石灰与水混合组成的主体料浆100份中，按质量比，加入火山凝灰岩粉10份和钢渣粉10份作为增强剂，再加入聚乙烯醇缩甲醛1份和羧甲基纤维素0.5份作为稠化剂，然后加入硬脂酸钙0.1份和油酸三乙醇胺混合物0.1份作为发泡稳定剂，充分搅拌后，在料浆中加入5%浓度的碳酸钠水溶液3份作为助泡剂，最后加入脱脂铝粉50-60克发气剂，将配制后的料浆加入搅拌机内搅拌，搅拌后注模，蒸养后成为发泡硅钙混凝土墙体材料。
CN201310671063.5A 2013-12-12 2013-12-12 一种发泡硅钙混凝土墙体砌块配料方法 Active CN103664226B (zh)