CN103664200A - 一种刚玉莫来石轻质砖及其制备方法 - Google Patents

一种刚玉莫来石轻质砖及其制备方法 Download PDF

Info

Publication number
CN103664200A
CN103664200A CN201210353397.3A CN201210353397A CN103664200A CN 103664200 A CN103664200 A CN 103664200A CN 201210353397 A CN201210353397 A CN 201210353397A CN 103664200 A CN103664200 A CN 103664200A
Authority
CN
China
Prior art keywords
corundum
parts
mullite
weight brick
light
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210353397.3A
Other languages
English (en)
Inventor
张利新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210353397.3A priority Critical patent/CN103664200A/zh
Publication of CN103664200A publication Critical patent/CN103664200A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种刚玉莫来石轻质砖，它是由以下重量份数的原料制成：高铝矾土60-80、α-Al2O3微粉20-30、聚苯乙烯球3-5、三聚磷酸钠0.5-0.9、磷酸二氢铝5-9。本产品的主晶相莫来石含量在90％以上，另含有少量刚玉相，体积密度为0.4，气孔率打85％，结构均匀，含有大量闭合的小孔结构，热导率为0.25W/m·k，远小于普通的轻质砖，且使用温度远高于普通轻质砖，可达1600℃。本发明低温烧成，高温使用，能耗低。

Description

一种刚玉莫来石轻质砖及其制备方法
技术领域
本发明涉及一种刚玉莫来石轻质砖及其制备方法。
背景技术
在工业窑炉等热工设备以及金属冶炼中使用轻质保温耐火材料作为一种能够显著节能降耗的简便而有效的方法，但是，普通的轻质保温耐火材料都是通过机压法或挤泥法生产的，需要的生产设备工艺复杂而且生产过程能耗比较高。
发明内容
本发明要解决的技术问题是轻质保温耐火材料通过机压法或挤泥法生产的生产设备工艺复杂，提供一种刚玉莫来石轻质砖。
本发明的技术方案是：一种刚玉莫来石轻质砖，它是由以下重量份数的原料制成：
高铝矾土60-80、α-Al2O3微粉20-30、聚苯乙烯球3-5、三聚磷酸钠0.5-0.9、磷酸二氢铝5-9。
所述的刚玉莫来石轻质砖的制备方法：将原料搅拌后，浇注到模具里，干燥后脱模，放入窑炉内经1000-1600℃烧制。
本发明的有益效果是：本产品的主晶相莫来石含量在90％以上，另含有少量刚玉相，体积密度为0.4，气孔率打85％，结构均匀，含有大量闭合的小孔结构，热导率为0.25W/m·k，远小于普通的轻质砖，且使用温度远高于普通轻质砖，可达1600℃。本发明低温烧成，高温使用，能耗低。
具体实施方式
实施例1
一种刚玉莫来石轻质砖，它是由以下原料制成：高铝矾土80kg、α-Al2O3微粉30kg、聚苯乙烯球5kg、三聚磷酸钠0.9kg、磷酸二氢铝5-9kg。
刚玉莫来石轻质砖的制备方法：将原料搅拌后，浇注到模具里，干燥后脱模，放入窑炉内经1000℃烧制。
实施例2
一种刚玉莫来石轻质砖，它是由以下原料制成：高铝矾土60kg、α-Al2O3微粉20kg、聚苯乙烯球3kg、三聚磷酸钠0.5kg、磷酸二氢铝5kg。
刚玉莫来石轻质砖的制备方法：将原料搅拌后，浇注到模具里，干燥后脱模，放入窑炉内经1600℃烧制。
实施例3
一种刚玉莫来石轻质砖，它是由以下原料制成：高铝矾土75kg、α-Al2O3微粉28kg、聚苯乙烯球4.5kg、三聚磷酸钠0.8kg、磷酸二氢铝8kg。
刚玉莫来石轻质砖的制备方法：将原料搅拌后，浇注到模具里，干燥后脱模，放入窑炉内经1200℃烧制。
实施例4
一种刚玉莫来石轻质砖，它是由以下原料制成：高铝矾土65kg、α-Al2O3微粉22kg、聚苯乙烯球3.5kg、三聚磷酸钠0.6kg、磷酸二氢铝6kg。
刚玉莫来石轻质砖的制备方法：将原料搅拌后，浇注到模具里，干燥后脱模，放入窑炉内经1400℃烧制。
实施例5
一种刚玉莫来石轻质砖，它是由以下原料制成：高铝矾土70kg、α-Al2O3微粉25kg、聚苯乙烯球4kg、三聚磷酸钠0.7kg、磷酸二氢铝7kg。
刚玉莫来石轻质砖的制备方法：将原料搅拌后，浇注到模具里，干燥后脱模，放入窑炉内经1600℃烧制12小时。

Claims (2)

1.一种刚玉莫来石轻质砖，其特征在于，它是由以下重量份数的原料制成：高铝矾土60-80、α-Al2O3微粉20-30、聚苯乙烯球3-5、三聚磷酸钠0.5-0.9、磷酸二氢铝5-9。
2.根据权利要求1所述的刚玉莫来石轻质砖的制备方法，其特征在于：将原料搅拌后，浇注到模具里，干燥后脱模，放入窑炉内经1000-1600℃烧制。
CN201210353397.3A 2012-09-13 2012-09-13 一种刚玉莫来石轻质砖及其制备方法 Pending CN103664200A (zh)