CN103660757A - Shell carving black pottery and manufacture method thereof - Google Patents
Shell carving black pottery and manufacture method thereof Download PDFInfo
- Publication number
- CN103660757A CN103660757A CN201210336190.5A CN201210336190A CN103660757A CN 103660757 A CN103660757 A CN 103660757A CN 201210336190 A CN201210336190 A CN 201210336190A CN 103660757 A CN103660757 A CN 103660757A
- Authority
- CN
- China
- Prior art keywords
- black pottery
- shell
- bottle
- black
- carving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses shell carving black pottery. The shell carving black pottery is formed by splicing shells on the outer surface of a black pottery bottle in a shell carving picture manner, and is a coastal city featured product with extremely high ornamental value, artistic value and collection value. A specific manufacture method of the shell carving black pottery comprises the steps of 1, wiping the surface of the black pottery bottle after firing; 2, selecting shells according to a designed shell carving picture, and sculpturing and polishing the shells for later use, wherein the fitting gap between each shell for later use and the part to be spliced of the black pottery bottle is less than or equal to 1 millimeter; 3, splicing the shells on the surface of the black pottery bottle by woodworking glue; and 4, drying the glue, and cleaning the surface of the black pottery bottle. The shell carving black pottery provided by the invention is convenient to display, present and carry, the simple and elegant property of the black pottery and the exquisite and crystal property of the shell carving are combined and can complement each other, the unique regional culture color of the black pottery is shown, and the superhigh artistic creation level and the high craft level are shown.
Description
Technical field
The present invention relates to a kind of black pottery product, more particularly, relate to a kind of black pottery product of combination shell carving art.
Background technology
Black pottery is a kind of melanin tire ceramic vessel.There are folder carbon black pottery and carburizing black pottery.Typical products is thin as eggshell, and surface-brightening is lubricated, and the section of tire is inside and outside pitch-dark.Also have a kind of casting skin pottery or black clothing pottery, its tire gray or the red only surface of tire are black." black as paint, bright as mirror, thin as a piece of paper, sound is as single sonorous stone, hard as porcelain " is the high level overviews of people to Longshan culture eggshell black pottery.The essence of its technique of Longshan culture eggshell black pottery, U.S., in Chinese art history, occupy critical role, be described as " the exquisitest making of earth civilization before 4,000 years ".U.S. of Longshan culture black pottery, beautiful at its look.Black is the most thought-provoking look, is also the most mysterious look, represents deep, serious, elegant, has inherent strength.Black pottery entire body is distributed soft indigo naturalis gloss, and it is implicit plain, looks solemn and dignified, pure simple and unsophisticated; U.S. of Longshan culture black pottery, beautiful its shape.Than ancient painted pottery, black pottery is plain generous, enriching changeable moulding, hollow out wins the value self existing.So from above-mentioned meaning, black pottery is material and culture legacy, is also non-material cultural heritage.She is the rarity of human culture, the rarity of world culture.
Shell carving (scrimshaw, shell work), the kind of shell is a lot, is the Nature superb craftsmanship's work, and color and texture are also very beautiful, the still very wonderful refractive body having.Shell carving is selected these coloured shells exactly, skilfully uses its natural colored and texture, shape, through clip, car mill, polishing, pile up, the operation such as stickup is chiseled and carved into smooth, mezzo relievo meticulously, inlay, the handicraft of the various ways such as three-dimensional and specification.Shell carving combines people and sea cleverly, and shell carving is the beautiful and traditional culture crystallization of wisdom in sea, and skill and technique U.S. of the conchiferous natural beauty of tool, sculpture and the style of traditional Chinese Painting are beautiful.Record people and extra large story from ancient times, passing on people to yearning for fine tomorrow and expecting.
The shell picture product of prior art, is adhered to and in plane, makes the view picture picture art work mainly with shell.Problem is, shell is adhered in plane, comparatively easy, but how shell is adhered to the bottle surface with radian, and guarantees that bonding is firmly to need the problem that solves.
In addition, by shell carving and two kinds of art form combinations of black pottery, produce attractive in appearance, shell carving black pottery product firmly, also will open new markets at shell carving and two fields of black pottery, its artistic value will reach a new height.
Summary of the invention
The present invention aims to provide a kind of shell carving black pottery product attractive in appearance, and therefore provides the production method of a set of assurance shell carving and black pottery strong bonded, thereby reaches the perfect adaptation of shell carving art and black pottery art.The present invention has guaranteed shell and black pottery bottle strong bonded with radian especially, guarantee to have demonstrate,proved quality of item, and product of the present invention is attractive in appearance, has higher artistic value and reserve value.
In order to achieve the above object, the invention provides a kind of shell carving black pottery, shell is adhered to the outer surface of black pottery bottle with shell picture form.
Above-mentioned shell carving black pottery preparation method, comprises the steps.
The black pottery bottle surface that Step 1, wiping bake.
The shell picture that Step 2, basis design, selects shell, standby after engraving, polishing; Wherein, the radian of each standby shell is less than or equal to 1 millimeter with the radian laminating gap for the treatment of bonding location place at described black pottery bottle.
Step 3, utilize venamul to be adhered to described black pottery bottle surface in described shell.
Step 4, after glue is dry, clean black pottery bottle surface.
Under optimal way, before firing black pottery bottle, make in the former mud of former mud of black pottery doleiform shape and evenly mix 70-150 object bone meal, the 2-5% that part by weight is former mud.Bone meal can make from the bone of domestic animal, animal.By adding bone meal, can increase the hardness of black pottery bottle, priorly can improve the degree of reinforcing of shell after bonding.
Under optimum way, in bond medium venamul used, also evenly mix 70-150 object bone meal, the 5-15% that part by weight is emulsion, its object is also intended to improve the bonding firmness of shell.
In addition, in bonding process, optimum way, is first preheated to 40-50 ℃ by described shell, then is coated with described venamul at bonding plane, shelves 15-25 and after second, adhere to described black pottery bottle surface under normal temperature.First this process can improve the state of cure of shell and emulsion colloid, simultaneously, because latax is after adhering to Earthen Bottle surface, need to clear up the marginal portion that latax exposes, in order to reduce the bonding degree of latax edge and Earthen Bottle, in case when cleaning cause the damage of bottle, therefore according to latax edge, be easy to dry and hard situation, after coating latax, shelve a period of time, both improved the degree of consolidation at latax center, be easy to again the cleaning of marginal portion, can not injure Earthen Bottle.
Shell carving black pottery of the present invention is convenient to furnishings and present, is carried, and simple and unsophisticated plain and sparkling and crystal-clear the contrasting finely with each other of exquisiteness shell carving of black pottery, brings out the best in each other.The unique local cultural color that shows more black pottery, also demonstrates consummate art creation level and technology difficulty.Shell carving black pottery sight of the present invention is splendid, has artistic value and reserve value, is coastal city distinguishing products.Particularly, shell picture, as a kind of art form, adds the cultural coloring of black pottery bottle uniqueness, and further the artistry of improving product, has high reserve value.
The present invention has selected a kind of conventional bond medium---carpenter's glue, greatly reduces the production cost of goods.Specifically, and venamul of the present invention (trade name: carpenter's glue), the ornamental column board product that can select Beijing Orient petrochemical industry Co., Ltd to produce.This bond medium as 502 glue etc., can guarantee that the shell picture of goods of the present invention is more firmly bonded in black pottery bottle surface compared with the medium of other kinds.Especially the present invention is bonded in the Earthen Bottle surface with arc by the shell of polishing, in order to guarantee bonding firmly to need to guarantee be less than or equal to 1 millimeter in conjunction with gap, has greatly improved the degree of reinforcing of goods.Bone meal adds two stages, has further strengthened the bonding degree of shell picture at black pottery bottle surface; In addition, the bond medium that the present invention selects is dry and hard, is bordering on colourlessly, and under the setting off of black pottery bottle black body, more aobvious shell picture clean, graceful, has guaranteed product quality and aesthetic measure.
Accompanying drawing explanation
Fig. 1 is that the outward appearance of a kind of example of shell carving black pottery of the present invention is faced structural representation.
The specific embodiment
As shown in Figure 1, shell carving black pottery of the present invention, is adhered to shell 2 outer surface of black pottery bottle 1 with shell picture form.
Concrete product process is.
1, drawing embryo---pottery Artist draws embryo to go out shape, smooth surface.
2, burn pottery---air-dry after, with electrical kiln or earth kiln, at the temperature of 700 ~ 900 degrees Celsius of left and right, fire the time of about one week, kiln discharge is exactly ganoid black pottery bottle.
3, clean black pottery bottle---with clean and dry cleaning cloth, by black pottery surface wiped clean, do not want residual soil.
4, polishing---technologist, according to the different drawings that design, chooses required shell, manual with grinder buffing, goes out shape, then with in addition deep processing of dental drill, the shell carving landscape painting that carve is bright and colourful.
5, sticky glutinous---the wood glue really up to the mark by quality scrabbles up figure by the tiny shell carving that polish shape, controlled the radian of bottle, closely shell carving is sticky in to black pottery bottle surface.Attention is smeared evenly, does not use lower than the following wood glue storing of zero degrees celsius, avoids black pottery bottle and shell carving to glue the gap between sticking, and maximum is no more than 1 millimeter.
6, clean---treat that wood glue do, determine its sticky glutinous firm after, again with cleaning cloth by black pottery and the whole wiping meticulously of shell carving, to be effective.
Under optimal way, above-mentioned wood glue is selected venamul.And under optimal way, before firing black pottery bottle, in the former mud of black pottery to be burnt, evenly mixing 70-150 object bone meal, part by weight is the 2-5% of the former mud of black pottery.In order to improve the bonding firmness of shell picture, in wood glue liquid, evenly mix 70-150 object bone meal, the 5-15% that part by weight is wood glue.Optimum way, is first preheated to 40-50 ℃ by shell, then at its bonding plane coating wood glue liquid, shelves 15-25 and after second, adhere to black pottery bottle surface under normal temperature.
Main technological steps of the present invention is implemented at normal temperatures, conventionally at 14-28 degree Celsius.
The above; it is only the preferably specific embodiment of the present invention; but protection scope of the present invention is not limited to this; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; according to technical scheme of the present invention and inventive concept thereof, be equal to replacement or changed, within all should being encompassed in protection scope of the present invention.
Claims (5)
1. a shell carving black pottery, is characterized in that, shell is adhered to the outer surface of black pottery bottle with shell picture form.
2. a shell carving black pottery preparation method, is characterized in that, comprises the steps:
The black pottery bottle surface that S1, wiping bake;
The shell picture that S2, basis design, selects shell, standby after engraving, polishing; Wherein, the radian of each standby shell is less than or equal to 1 millimeter with the radian laminating gap for the treatment of bonding location place at described black pottery bottle;
S3, utilize venamul to be adhered to described black pottery bottle surface in described shell;
S4, after glue is dry, clean black pottery bottle surface.
3. shell carving black pottery preparation method according to claim 2, is characterized in that, before firing black pottery bottle, makes in the former mud of black pottery doleiform shape and evenly mixes 70-150 object bone meal, the 2-5% that part by weight is former mud.
4. shell carving black pottery preparation method according to claim 3, is characterized in that, evenly mixes 70-150 object bone meal, the 5-15% that part by weight is emulsion in described venamul.
5. shell carving black pottery preparation method according to claim 3, is characterized in that, first described shell is preheated to 40-50 ℃, then is coated with described venamul at bonding plane in step S3, shelves 15-25 and after second, adhere to described black pottery bottle surface under normal temperature.