CN103643371A - Manufacturing technology of milk meryl fabric - Google Patents
Manufacturing technology of milk meryl fabric Download PDFInfo
- Publication number
- CN103643371A CN103643371A CN201310583506.5A CN201310583506A CN103643371A CN 103643371 A CN103643371 A CN 103643371A CN 201310583506 A CN201310583506 A CN 201310583506A CN 103643371 A CN103643371 A CN 103643371A
- Authority
- CN
- China
- Prior art keywords
- milk
- meryl
- fabric
- mentioned
- ice silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing technology of milk meryl fabric. The manufacturing technology of the milk meryl fabric comprises the following technological steps of (1) using linters and wood as raw materials to extract pure pulp, (2) placing the pulp into a sodium hydroxide aqueous solution to obtain viscous dope, (3) carrying out dehydration and degreasing treatment on liquid milk to obtain milk protein, (4) adding softeners to the milk protein to obtain milk slurry, (5) carrying out spinning on the milk slurry to obtain milk protein fibers through a wet spinning technology, (6) combining the dope in the step (2) and the milk protein fibers in the step (5), carrying out filtration, ripening and deaeration, carrying out wet spinning, and (7) carrying out weaving on yarn obtained through the wet spinning to obtain the milk meryl fabric. According to the mode, the manufacturing technology of the milk meryl fabric is easy to operate, the operating process is easy to control, the fiber output rate of milk meryl is quite high, the manufactured milk meryl fabric has the nature of cotton and the quality of silk, comprises really ecological fibers, is derived from natural materials, and is superior to the natural materials.
Description
Technical field
The present invention relates to functional fabric field, particularly relate to a kind of manufacture craft of milk ice silk cloth.
Background technology
Since entering 21 century, people focus on comfortableness, health, the superior and fashion-orientation of dress ornament more.Milk ice silk cloth is as a kind of novel cloth, and moisture percentage meets the physiological requirements of human body skin most, has cotton essence, the quality of silk, genuine ecological fiber, is better than naturally yet come from sky, has the smooth feature such as nice and cool, ventilative, antistatic, lucuriant in design.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of simple to operate, the manufacture craft of the milk ice silk cloth that operating process is easy to control, the fiber output ratio of milk ice silk is high.
For solving the problems of the technologies described above, the invention provides a kind of manufacture craft of milk ice silk cloth, comprise following processing step:
(1) cotton linter and timber are extracted to pure pulp as raw material,
(2) above-mentioned pulp is put into sodium hydrate aqueous solution, obtains the spinning solution of thickness,
(3) aqueous milk is carried out to dewatering and defatting processing, obtains milk protein,
(4) above-mentioned milk protein is added to softener makes milk slurries,
(5) above-mentioned milk slurries are passed through to wet spinning process, are spun into milk protein fiber,
(6) milk protein fiber in the spinning solution in above-mentioned (2) and above-mentioned (5) is combined after filtration, maturation, deaeration, carries out wet spinning,
(7) saying that above-mentioned wet spinning weaves forms milk ice silk cloth.
In a preferred embodiment of the present invention, it is 15%-20% that described pulp is put into sodium hydrate aqueous solution concentration.
In a preferred embodiment of the present invention, described dewatering and defatting process in fat content lower than 0.3%, the percentage that described content is weight.
In a preferred embodiment of the present invention, the volume ratio that described spinning solution and milk protein fiber combine is 1:2.
In a preferred embodiment of the present invention, described maturation refers under the environment of 18-25 degree places 20-30 hour, to reduce the esterification number of cellulose xanthate ester.
The invention has the beneficial effects as follows: the manufacture craft fiber output ratio simple to operate, that operating process is easy to control, milk ice silk of milk ice silk cloth of the present invention is high, the milk ice silk cloth being made has cotton essence, the quality of silk, genuine ecological fiber, yet come from from being better than nature, contain 7 seed amino acids and multiple natural antibiotics, its antibiotic rate is higher than 85%, therefore milk ice silk face fabric is with health role, and the while hygroscopicity of milk ice silk face fabric is strong, good permeability, antistatic, lucuriant in design.
The specific embodiment
Below the technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is only a part of embodiment of the present invention, rather than whole embodiment.Embodiment based in the present invention, those of ordinary skills, not making all other embodiment that obtain under creative work prerequisite, belong to the scope of protection of the invention.
The embodiment of the present invention comprises:
A manufacture craft for milk ice silk cloth, comprises following technique:
(1) cotton linter and timber are extracted to pure pulp as raw material,
(2) above-mentioned pulp is put into sodium hydrate aqueous solution, obtains the spinning solution of thickness,
(3) aqueous milk is carried out to dewatering and defatting processing, obtains milk protein,
(4) above-mentioned milk protein is added to softener makes milk slurries,
(5) above-mentioned milk slurries are passed through to wet spinning process, are spun into milk protein fiber,
(6) milk protein fiber in the spinning solution in above-mentioned (2) and above-mentioned (5) is combined after filtration, maturation, deaeration, carries out wet spinning,
(7) saying that above-mentioned wet spinning weaves forms milk ice silk cloth.
In addition, to put into sodium hydrate aqueous solution concentration be 15%-20% to described pulp.
In addition, described dewatering and defatting process in fat content lower than 0.3%, the percentage that described content is weight.
In addition, the volume ratio that described spinning solution and milk protein fiber combine is 1:2.
In addition, described maturation refers under the environment of 18-25 degree places 20-30 hour, to reduce the esterification number of cellulose xanthate ester.
The manufacture craft fiber output ratio simple to operate, that operating process is easy to control, milk ice silk of milk ice silk cloth of the present invention is high, the milk ice silk cloth being made has cotton essence, the quality of silk, genuine ecological fiber, yet come from from being better than nature, contain 7 seed amino acids and multiple natural antibiotics, its antibiotic rate is higher than 85%, therefore milk ice silk face fabric is with health role, and the while hygroscopicity of milk ice silk face fabric is strong, good permeability, antistatic, lucuriant in design.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or conversion of equivalent flow process that utilizes description of the present invention to do; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. a manufacture craft for milk ice silk cloth, is characterized in that, comprises following processing step:
(1) cotton linter and timber are extracted to pure pulp as raw material,
(2) above-mentioned pulp is put into sodium hydrate aqueous solution, obtains the spinning solution of thickness,
(3) aqueous milk is carried out to dewatering and defatting processing, obtains milk protein,
(4) above-mentioned milk protein is added to softener makes milk slurries,
(5) above-mentioned milk slurries are passed through to wet spinning process, are spun into milk protein fiber,
(6) milk protein fiber in the spinning solution in above-mentioned (2) and above-mentioned (5) is combined after filtration, maturation, deaeration, carries out wet spinning,
(7) above-mentioned wet spinning is woven and form milk ice silk cloth.
2. the manufacture craft of milk ice silk cloth according to claim 1, is characterized in that, it is 15%-20% that described pulp is put into sodium hydrate aqueous solution concentration.
3. the manufacture craft of milk ice silk cloth according to claim 1, is characterized in that, described dewatering and defatting process in fat content lower than 0.3%, the percentage that described content is weight.
4. the manufacture craft of milk ice silk cloth according to claim 1, is characterized in that, the health check-up ratio that described spinning solution and milk protein fiber combine is 1:2.
5. the manufacture craft of milk ice silk cloth according to claim 1, is characterized in that, described maturation refers under the environment of 18-25 degree places 20-30 hour, to reduce the esterification number of cellulose xanthate ester.