CN103642390A - Fire-proof paint for intelligent house - Google Patents
Fire-proof paint for intelligent house Download PDFInfo
- Publication number
- CN103642390A CN103642390A CN201310623458.8A CN201310623458A CN103642390A CN 103642390 A CN103642390 A CN 103642390A CN 201310623458 A CN201310623458 A CN 201310623458A CN 103642390 A CN103642390 A CN 103642390A
- Authority
- CN
- China
- Prior art keywords
- paint
- pigment
- temperature
- intelligent house
- rotating speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fire-proof paint for an intelligent house. The fire-proof paint is characterized in that the fire-proof paint comprises the following components in percentage by weight: 10%-25% of oil material, 6%-13% of resin, 6%-11% of pigments, 5%-8% of solvent and 2.5-4.5% of auxiliary materials, and the balance of water, wherein the oil material comprises drying oil and semi-drying oil and is one of main film-forming substances; the resin comprises epoxy resin, acrylic resin and polyurethane at the mass ratio of the epoxy resin to the acrylic resin to the polyurethane of (3-5): (7-9): (3-8); the pigments comprise a coloring pigment, an extender pigment and an anti-rust pigment and are used for the film-forming substances; the auxiliary materials comprise a drier, a wetting agent and a dispersant in the mass ratio of 3: 2: 3.
Description
Technical field
The present invention relates to a kind of paint, relate in particular to a kind of intelligent house retardant paint.
Background technology
Paint is the call in ancient times; Coating, is modern civilization address, comprises more scientific and technological composition, in modern science and technology and industrial circle, is widely used.But paint has some habitual addresses of blurting out still to remain, as emulsion paint, priming paint, finish paint etc.Generally speaking, coating is exactly the material that can be coated in coated article part surface and can form the continuous film of firm attachment.It can be both inorganic, as electro-coppering, and electronickelling, electro-galvanizing etc.Also can be that organically, as most organic polymer material, organic polymer material has formed current Coating Market major portion.Paint is in the market varied, for consumers, always wish to have bought the paint of health environment-friendly, but the paint on market there is greatly the chemical substance of containing, and has affected to a certain extent human consumer's health, and, paint of the prior art does not mostly have fp effect, when there is fire, can not keep out fire, therefore, a kind of new paint scheme of exigence solves above-mentioned technical problem.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of intelligent house retardant paint, environmental protection, health, and work-ing life is longer, cost, and production technique is simple.
An intelligent house retardant paint, is characterized in that: the component of described retardant paint is as follows, and according to mass percent, oil plant 10%-25%, comprises siccative oil and semi-drying oil, is one of main film forming substance;
Resin 6%-13%, comprises epoxy resin, acrylic resin and urethane, and the mass ratio of described epoxy resin, acrylic resin and urethane is 3-5:7-9:3-8; Pigment 6%-11%, comprises tinting pigment, pigment extender and rust-stabilising pigment, for filmogen; Solvent 5%-8%; Subsidiary material 2.5%-4.5%, comprise siccative, wetting agent, dispersion agent, and described siccative, wetting agent, dispersion agent mass ratio are 3:2:3; All the other are water.
As a modification of the present invention, described solvent is benzene, ethyl acetate, acetone, and the mass percent of described benzene, ethyl acetate, acetone is 7:8:7.
As a modification of the present invention: described paint also comprises 5%-20% mica powder.
As a modification of the present invention, described paint also comprises 3%-18% mineral turpentine.
As a modification of the present invention, described paint also comprises 3%-18% zinc oxide.
An intelligent house retardant paint, is characterized in that: said method comprising the steps of,
1) oil plant described in claim 1, resin are mixed according to described ratio, the speed that the rotating speed of take in high speed dispersor is 2000-2500 revs/min is carried out stirring 10-15 minute at a high speed, then heating, in 5 minutes, temperature reaches 30-45 °, and during heating, rotating speed reduces, in 5 minutes of heating, rotating speed reduces by 300-500 revs/min, keep this rotating speed, keep this temperature, continue 2-3 hours;
2) according to described ratio, add a certain amount of mica powder, mineral turpentine, zinc oxide, temperature continues heating, and in 10 minutes, temperature is upgraded to 60-75 °, and this temperature continues 20 minutes;
3) according to aforementioned proportion, add pigment, add temperature after pigment to reduce by 40-50 °;
4) according to aforementioned proportion, add subsidiary material, add after subsidiary material and continue to stir, rotating speed is reduced to 100-150 revs/min, temperature slowly reduces by 20-25 °, keeps this rotating speed and this temperature 50 minutes, can make described paint.
Paint provided by the invention, production technique is simple, and material cost reduces, and greatly reduces the production cost of this product; This product is healthy, environmental protection, can not affect the healthy of human consumer, can relievedly use; When there is fire, gauge paint can stop to a certain extent fire continue spread, reduce the loss that fire causes people and property; This product in like product, better quality, result of use obtains human consumer's approval always.
Embodiment
Below in conjunction with embodiment, further illustrate the present invention, should understand following embodiment and only for the present invention is described, is not used in and limits the scope of the invention.
embodiment 1:
An intelligent house retardant paint, the component of described retardant paint is as follows, according to mass percent,
Oil plant 20%, comprises siccative oil and semi-drying oil, is one of main film forming substance;
Resin 6%, comprises epoxy resin, acrylic resin and urethane, and the mass ratio of described epoxy resin, acrylic resin and urethane is 3-5:7-9:3-8; Pigment 6%, comprises tinting pigment, pigment extender and rust-stabilising pigment, for filmogen; Solvent 5%, described solvent is benzene, ethyl acetate, acetone, the mass percent of described benzene, ethyl acetate, acetone is 7:8:7; Subsidiary material 2.5%, comprise siccative, wetting agent, dispersion agent, and described siccative, wetting agent, dispersion agent mass ratio are 3:2:5;
5% mica powder;
3% mineral turpentine;
3% zinc oxide;
All the other are water.
embodiment 2:
An intelligent house retardant paint, the component of described retardant paint is as follows, according to mass percent,
Oil plant 25%, comprises siccative oil and semi-drying oil, is one of main film forming substance;
Resin 13%, comprises epoxy resin, acrylic resin and urethane, and the mass ratio of described epoxy resin, acrylic resin and urethane is 3-5:7-9:3-8; Pigment 11%, comprises tinting pigment, pigment extender and rust-stabilising pigment, for filmogen; Solvent 8%, described solvent is benzene, ethyl acetate, acetone, the mass percent of described benzene, ethyl acetate, acetone is 7:8:7; Subsidiary material 4.5%, comprise siccative, wetting agent, dispersion agent, and described siccative, wetting agent, dispersion agent mass ratio are 3:2:5;
5% mica powder;
6% mineral turpentine;
8% zinc oxide;
All the other are water.
embodiment 3:
An intelligent house retardant paint, the component of described retardant paint is as follows, according to mass percent,
Oil plant 25%, comprises siccative oil and semi-drying oil, is one of main film forming substance;
Resin 8%, comprises epoxy resin, acrylic resin and urethane, and the mass ratio of described epoxy resin, acrylic resin and urethane is 3-5:7-9:3-8; Pigment 8%, comprises tinting pigment, pigment extender and rust-stabilising pigment, for filmogen; Solvent 6%, described solvent is benzene, ethyl acetate, acetone, the mass percent of described benzene, ethyl acetate, acetone is 7:8:7; Subsidiary material 3%, comprise siccative, wetting agent, dispersion agent, and described siccative, wetting agent, dispersion agent mass ratio are 3:2:5;
5% mica powder;
5% mineral turpentine;
8% zinc oxide;
All the other are water.
embodiment 4:
An intelligent house retardant paint, the component of described retardant paint is as follows, according to mass percent,
Oil plant 20%, comprises siccative oil and semi-drying oil, is one of main film forming substance;
Resin 10%, comprises epoxy resin, acrylic resin and urethane, and the mass ratio of described epoxy resin, acrylic resin and urethane is 3-5:7-9:3-8; Pigment 7%, comprises tinting pigment, pigment extender and rust-stabilising pigment, for filmogen; Solvent 5%, described solvent is benzene, ethyl acetate, acetone, the mass percent of described benzene, ethyl acetate, acetone is 7:8:7; Subsidiary material 2.5%, comprise siccative, wetting agent, dispersion agent, and described siccative, wetting agent, dispersion agent mass ratio are 3:2:5;
10% mica powder;
12% mineral turpentine;
12% zinc oxide;
All the other are water.
embodiment 5:an intelligent house retardant paint, said method comprising the steps of,
1) oil plant described in claim 1, resin are mixed according to described ratio, the speed that the rotating speed of take in high speed dispersor is 2000-2500 revs/min is carried out stirring 10-15 minute at a high speed, then heating, in 5 minutes, temperature reaches 30-45 °, and during heating, rotating speed reduces, in 5 minutes of heating, rotating speed reduces by 300-500 revs/min, keep this rotating speed, keep this temperature, continue 2-3 hours;
2) according to described ratio, add a certain amount of mica powder, mineral turpentine, zinc oxide, temperature continues heating, and in 10 minutes, temperature is upgraded to 60-75 °, and this temperature continues 20 minutes;
3) according to aforementioned proportion, add pigment, add temperature after pigment to reduce by 40-50 °;
4) according to aforementioned proportion, add subsidiary material, add after subsidiary material and continue to stir, rotating speed is reduced to 100-150 revs/min, temperature slowly reduces by 20-25 °, keeps this rotating speed and this temperature 50 minutes, can make described paint.
Be more than better embodiment of the present invention, but protection scope of the present invention is not limited to this.Any those of ordinary skill in the art are within the scope of the disclosed family members of the present invention, and the conversion of expecting without creative work or replacement, within all should being encompassed in protection scope of the present invention.Therefore protection scope of the present invention should be as the criterion with the protection domain that claim was limited.
Claims (6)
1. an intelligent house retardant paint, is characterized in that: the component of described retardant paint is as follows, according to mass percent,
Oil plant 10%-25%, comprises siccative oil and semi-drying oil, is one of main film forming substance;
Resin 6%-13%, comprises epoxy resin, acrylic resin and urethane, and the mass ratio of described epoxy resin, acrylic resin and urethane is 3-5:7-9:3-8; Pigment 6%-11%, comprises tinting pigment, pigment extender and rust-stabilising pigment, for filmogen; Solvent 5%-8%; Subsidiary material 2.5%-4.5%, comprise siccative, wetting agent, dispersion agent, and described siccative, wetting agent, dispersion agent mass ratio are 3:2:3;
All the other are water.
2. a kind of intelligent house retardant paint according to claim 1, is characterized in that: described solvent is benzene, ethyl acetate, acetone, and the mass percent of described benzene, ethyl acetate, acetone is 7:8:7.
3. a kind of intelligent house retardant paint according to claim 1, is characterized in that: described paint also comprises 5%-20% mica powder.
4. according to a kind of intelligent house retardant paint described in claim 1 or 2 or 3, it is characterized in that: described paint also comprises 3%-18% mineral turpentine.
5. according to a kind of intelligent house retardant paint described in claim 1 or 2 or 3, it is characterized in that: described paint also comprises 3%-18% zinc oxide.
6. an intelligent house retardant paint, is characterized in that: said method comprising the steps of,
Oil plant described in claim 1, resin are mixed according to described ratio, the speed that the rotating speed of take in high speed dispersor is 2000-2500 revs/min is carried out stirring 10-15 minute at a high speed, then heating, in 5 minutes, temperature reaches 30-45 °, and during heating, rotating speed reduces, in 5 minutes of heating, rotating speed reduces by 300-500 revs/min, keep this rotating speed, keep this temperature, continue 2-3 hours;
According to described ratio, add a certain amount of mica powder, mineral turpentine, zinc oxide, temperature continues heating, and in 10 minutes, temperature is upgraded to 60-75 °, and this temperature continues 20 minutes;
According to aforementioned proportion, add pigment, add temperature after pigment to reduce by 40-50 °;
According to aforementioned proportion, add subsidiary material, add after subsidiary material and continue to stir, rotating speed is reduced to 100-150 revs/min, temperature slowly reduces by 20-25 °, keeps this rotating speed and this temperature 50 minutes, can make described paint.