CN103638983B - Catalyst carrier that a kind of use double-layer plate makes and preparation method thereof - Google Patents
Catalyst carrier that a kind of use double-layer plate makes and preparation method thereof Download PDFInfo
- Publication number
- CN103638983B CN103638983B CN201310620395.0A CN201310620395A CN103638983B CN 103638983 B CN103638983 B CN 103638983B CN 201310620395 A CN201310620395 A CN 201310620395A CN 103638983 B CN103638983 B CN 103638983B
- Authority
- CN
- China
- Prior art keywords
- thin plate
- sheet metal
- internal layer
- plate
- compartment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides the catalyst carrier that a kind of use double-layer plate makes, including housing and carrier matrix;The carrier matrix includes outer sheet metal and internal layer thin plate, and outer sheet metal is neodymium iron boron plate, and internal layer thin plate is to use pyrolytic oxide preparation, the moulding bodies thin plate with catalysis activity;Adjacent inner layer thin plate constitutes a compartment, and each compartment outer wrap has outer sheet metal;Compartment is regular polygon.Carrier matrix of the invention constitutes regular polygon to constitute by using internal layer with outer sheet metal, outer sheet metal uses the neodymium iron boron with excellent in strength and magnetic, internal layer thin plate is prepared using pyrolytic oxide, the moulding bodies thin plate with catalysis activity, therefore the impact resistance ability of catalyst carrier is not only lifted, improve intensity, and catalytic efficiency when can guarantee that tail gas by its compartment air flue.
Description
Technical field
The present invention relates to exhaust-gas treatment field, the catalyst carrier that more particularly to a kind of use double-layer plate makes.
Background technology
Metallic catalyst carrier is mainly used in placing metallic catalyst, there is through hole, metal catalytic in metallic catalyst carrier
Agent is placed in metallic catalyst carrier through hole, is then allowed waste gas to pass through carrier through hole and is occurred instead with the metallic catalyst on carrier
Should come to process waste gas, the matrix inside current catalyst carrier is generally single layer structure and its stability is relatively low, one
Denier inner base is clashed into, and is easily caused inner base and is deformed upon, and the catalyst on compartment or air flue is impacted,
Reduce its catalytic efficiency.
The content of the invention
For the catalyst carrier that problem above, the present invention make for a kind of use double-layer plate, the catalyst carrier bag
Include housing and carrier matrix;Carrier matrix includes outer sheet metal and internal layer thin plate, and outer sheet metal is neodymium iron boron plate, internal layer thin plate
It is to use pyrolytic oxide preparation, the moulding bodies thin plate with catalysis activity;Adjacent inner layer thin plate constitutes a compartment, each
Compartment outer wrap has outer sheet metal.Outer sheet metal uses neodymium iron boron as material, with outstanding intensity and magnetic so that
Can mutually be adsorbed between outer sheet metal, can mutually be absorbed when being impacted, reduce impulsive force.Internal layer thin plate is with pyrolitic oxidation
Thing is material, and when the tail gas of high temperature passes through, the treated thin plate with catalysis activity accordingly decomposites catalyst and comes right
Tail gas carries out catalytic reaction.
As a further improvement on the present invention, compartment is regular polygon.Be can guarantee that between outer sheet metal from regular polygon
Can be in close contact.
As a further improvement on the present invention, outer sheet metal is 2mm with internal layer lamella thickness.
As a further improvement on the present invention, the specific preparation method of internal layer thin plate is:
A, making sheet:Pyrolytic oxide is fabricated to thin plate according to size requirements, pyrolytic oxide be silica, aluminum oxide,
One or more in titanium oxide and zirconium oxide;
B, pre-activate:The thin plate made is processed by acidic cleaning liquid, and is dried;
C, surface treatment:Alkyl silicate is evenly coated in thin sheet surface;
D, drying:Thin plate is put into temperature for 60-70 DEG C, environmental stress are 1.4x105~1.5x105Carried out in the environment of Pa
Dry;
E, water process:Thin plate is immersed in the water or the slurrying in water;
F, calcining:Calcining heat is 850-950 DEG C, a length of 4-5 hours during calcining.
The catalyst carrier that the present invention makes for a kind of use double-layer plate, carrier matrix is by using internal layer and outer layer
Thin plate constitutes regular polygon to constitute, and outer sheet metal is used using the neodymium iron boron with excellent in strength and magnetic, internal layer thin plate
Prepared by pyrolytic oxide, the moulding bodies thin plate with catalysis activity, therefore the impact resistance ability of catalyst carrier is not only lifted,
Improve intensity, and catalytic efficiency when can guarantee that tail gas by its compartment air flue.
Brief description of the drawings
Fig. 1 is schematic diagram of the present invention;
Component in figure is:
1st, housing;2nd, outer layer carrier sheet;3rd, inner side carrier sheet.
Specific embodiment
Invention is described in detail below in conjunction with drawings and Examples:
Used as a kind of embodiment of the invention, the present invention provides a kind of urging for use double-layer plate making as shown in Figure 1
Agent carrier, including housing 1 and carrier matrix;The carrier matrix includes outer sheet metal 2 and internal layer thin plate 3, outer sheet metal 2
It is neodymium iron boron plate, internal layer thin plate 3 is to use pyrolytic oxide preparation, the moulding bodies thin plate with catalysis activity;Adjacent inner layer
Thin plate constitutes a compartment, and each compartment outer wrap has outer sheet metal 2;Compartment is regular hexagon;Outer sheet metal 2 is thin with internal layer
The thickness of plate 3 is 2mm.
The specific preparation method of internal layer thin plate 3 is:
A, making sheet:Pyrolytic oxide is fabricated to thin plate according to size requirements, pyrolytic oxide is silica and oxidation
The mixture of aluminium;
B, pre-activate:The thin plate made is processed by acidic cleaning liquid, and is dried;
C, surface treatment:Alkyl silicate is evenly coated in thin sheet surface;
D, drying:Thin plate is put into temperature for 60 DEG C, environmental stress are 1.4x105It is dried in the environment of Pa;
E, water process:Thin plate is immersed in the water or the slurrying in water;
F, calcining:Calcining heat is 850 DEG C, a length of 4 hours during calcining.
As another embodiment of the invention, there is provided the catalyst that a kind of use double-layer plate as shown in Figure 1 makes
Carrier, including housing 1 and carrier matrix;The carrier matrix includes outer sheet metal 2 and internal layer thin plate 3, and outer sheet metal 2 is neodymium
Iron boron plate, internal layer thin plate 3 is to use pyrolytic oxide preparation, the moulding bodies thin plate with catalysis activity;Adjacent inner layer thin plate
One compartment of composition, each compartment outer wrap has outer sheet metal 2;Compartment is regular hexagon;Outer sheet metal 2 and internal layer thin plate 3
Thickness is 2mm.
The specific preparation method of internal layer thin plate 3 is:
A, making sheet:Pyrolytic oxide is fabricated to thin plate according to size requirements, pyrolytic oxide be silica, aluminum oxide,
One or more in titanium oxide and zirconium oxide;
B, pre-activate:The thin plate made is processed by acidic cleaning liquid, and is dried;
C, surface treatment:Alkyl silicate is evenly coated in thin sheet surface;
D, drying:Thin plate is put into temperature for 70 DEG C, environmental stress are 1.5x105It is dried in the environment of Pa;
E, water process:Thin plate is immersed in the water or the slurrying in water;
F, calcining:Calcining heat is 950 DEG C, a length of 5 hours during calcining.
The above, is only presently preferred embodiments of the present invention, is not the limit for making any other form to the present invention
System, and any modification for being made according to technical spirit of the invention or equivalent variations, still fall within model required for protection of the invention
Enclose.
Claims (3)
1. it is a kind of using double-layer plate manufacture catalyst carrier, it is characterised in that:Including housing(1)With carrier matrix;It is described
Carrier matrix includes outer sheet metal(2)And internal layer thin plate(3), outer sheet metal(2)It is neodymium iron boron plate, internal layer thin plate(3)To make
Prepared with pyrolytic oxide, the moulding bodies thin plate with catalysis activity;Adjacent inner layer thin plate constitutes a compartment, each compartment
Outer wrap has outer sheet metal(2);
Internal layer thin plate(3)Specific preparation method be:
A, making sheet:Pyrolytic oxide is fabricated to thin plate according to size requirements, pyrolytic oxide is silica, aluminum oxide, oxidation
One or more in titanium and zirconium oxide;
B, pre-activate:The thin plate made is processed by acidic cleaning liquid, and is dried;
C, surface treatment:Alkyl silicate is evenly coated in thin sheet surface;
D, drying:Thin plate is put into temperature for 60-70 DEG C, environmental stress are 1.4x105~1.5x105Done in the environment of Pa
It is dry;
E, water process:Thin plate is immersed in the water or the slurrying in water;
F, calcining:Calcining heat is 850-950 DEG C, a length of 4-5 hours during calcining.
2. it is according to claim 1 it is a kind of using double-layer plate manufacture catalyst carrier, it is characterised in that:The compartment
It is regular polygon.
3. it is according to claim 1 it is a kind of using double-layer plate manufacture catalyst carrier, it is characterised in that:The outer layer
Thin plate(2)With internal layer thin plate(3)Thickness is 2mm.