CN103630106B - 混凝土楼板施工缝处干燥收缩约束应变的测量方法 - Google Patents
混凝土楼板施工缝处干燥收缩约束应变的测量方法 Download PDFInfo
- Publication number
- CN103630106B CN103630106B CN201310641654.8A CN201310641654A CN103630106B CN 103630106 B CN103630106 B CN 103630106B CN 201310641654 A CN201310641654 A CN 201310641654A CN 103630106 B CN103630106 B CN 103630106B
- Authority
- CN
- China
- Prior art keywords
- strain
- drying shrinkage
- concrete floor
- concrete
- contraction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种混凝土楼板施工缝处干燥收缩约束应变的测量方法，包括步骤：浇筑一混凝土楼板，测定所述混凝土楼板施工缝处的实际干燥收缩应变δ实际干缩；利用与所述混凝土楼板相同的混凝土材料制作混凝土试件，测定所述混凝土试件的自由干燥收缩应变δ自由干缩；计算所述混凝土楼板施工缝处受到下层框架柱或墙约束而产生的干燥收缩约束应变δ约束=δ自由干缩‑δ实际干缩。通过测量出混凝土楼板施工缝处实际发生的干燥收缩应变δ实际干缩与同条件下自由变形试件的干燥收缩应变δ自由干缩，计算出混凝土楼板施工缝处受到下层框架柱或墙约束而产生的干燥收缩约束应变δ约束，进而指导混凝土楼板裂缝控制。
Description
技术领域
本发明涉及一种工程建筑领域，尤其涉及一种混凝土楼板施工缝处干燥收缩约束应变的测量方法。
背景技术
使用跳仓法浇筑的混凝土楼板，使用施工缝代替温度后浇带，相邻混凝土浇筑块7天后即在施工缝处连成整体，施工缝处混凝土在7天后开始承受两边混凝土的干燥收缩。楼板混凝土的收缩并不能完成发生，将受到周围梁与内部钢筋的约束，而产生约束应变，进而产生开裂。由于周围梁与内部钢筋对混凝土的约束程度很难通过理论计算得到，因此楼板混凝土所受的约束变形也难以通过理论计算获得。且施工缝处由于混凝土是二次浇筑，混凝土本身的抗拉强度较低，较易在约束变形的作用下产生开裂。
为此本发明提供一种方法，通过测量出施工缝处混凝土楼板实际发生的干燥收缩变形与同条件下自由变形试件的干燥收缩变形，得到施工缝处混凝土楼板干燥收缩约束变形，从而可反推出周边梁与内部钢筋对楼板干燥收缩的约束程序，及产生约束力的大小，进而指导混凝土楼板裂缝控制。
发明内容
本发明所要解决的技术问题是提供一种利用振弦式应变计和应变巡检仪针对使用跳仓法浇筑的混凝土楼板结构，在浇筑后三个月内，测量施工缝处楼板混凝土由于干燥收缩受到大梁、钢筋等约束作用，而产生的混凝土楼板施工缝处干燥收缩约束应变的测量方法，
为实现上述技术效果，本发明公开了一种混凝土楼板施工缝处干燥收缩约束应变的测量方法，所述方法包括以下步骤：
浇筑一混凝土楼板，测定所述混凝土楼板施工缝处的实际干燥收缩应变δ实 际干缩；
利用与所述混凝土楼板相同的混凝土材料制作混凝土试件，测定所述混凝土试件的自由干燥收缩应变δ自由干缩；
计算所述混凝土楼板施工缝处受到下层框架柱或墙约束而产生的干燥收缩约束应变δ约束=δ自由干缩-δ实际干缩。
本发明进一步的改进在于，通过以下步骤测定所述混凝土楼板施工缝处的实际干燥收缩应变δ实际干缩：
在所述混凝土楼板施工缝处设置第二振弦式应变计，所述第二振弦式应变计跨过所述施工缝，并且两端分别固定在所述施工缝两侧的所述混凝土楼板上；
利用应变巡检仪测定所述第二振弦式应变计的读数，并以该读数作为所述混凝土楼板施工缝处的实际干燥收缩应变δ实际干缩。
本发明进一步的改进在于，其特征在于通过以下步骤测定所述混凝土楼板施工缝处的自由干燥收缩应变δ自由干缩：
利用与所述混凝土楼板相同的混凝土材料制作所述混凝土试件，并且在所述混凝土试件中预埋第一振弦式应变计；
浇筑所述混凝土试件达到终凝后，将所述混凝土试件的四个侧面进行密封，使得所述混凝土试件仅在上下两个表面发生干燥收缩，以模拟所述混凝土楼板的干燥收缩；
利用应变巡检仪测定所述第一振弦式应变计的读数，并以该读数作为所述混凝土试件的自由干燥收缩应变δ自由干缩。
本发明进一步的改进在于，所述第一振弦式应变计为内置式振弦式应变计。
本发明进一步的改进在于，所述第二振弦式应变计为外置式振弦式应变计，两端分别通过结构胶固定在所述施工缝两侧的所述混凝土楼板上。
本发明由于采用了以上技术方案，使其具有以下有益效果是：通过测量出混凝土楼板施工缝处实际发生的干燥收缩应变δ实际干缩与同条件下自由变形试件的干燥收缩应变δ自由干缩，计算出混凝土楼板施工缝处受到下层框架柱或墙约束而产生的干燥收缩约束应变δ约束，进而指导混凝土楼板裂缝控制。
附图说明
图1是本发明混凝土楼板施工缝处干燥收缩约束应变的测量方法中混凝土试件的自由干燥收缩应变δ自由干缩的测量方法的实施例示意图。
图2是本发明混凝土楼板施工缝处干燥收缩约束应变的测量方法中实际干燥收缩应变δ实际干缩的测量方法的实施例示意图。
具体实施方式
下面结合附图以及具体实施方式对本发明作进一步详细的说明。
参阅图1和图2所示，本发明公开了一种混凝土楼板施工缝处干燥收缩约束应变的测量方法，主要利用了第一振弦式应变仪11、第二振弦式应变仪12、应变巡检仪、超大容量蓄电池等设备，针对使用跳仓法浇筑的混凝土楼板结构，在浇筑后三个月内，测量施工缝13处混凝土楼板14由于干燥收缩受到大梁、钢筋等约束作用，而产生的混凝土楼板14在施工缝13处的干燥收缩约束应变。其主要包括以下步骤：
1、选取内置式的第一振弦式应变仪11和外置式的第二振弦式应变仪12，两种应变计都具有温度修正功能；
2、选取应变巡检仪，能分别按规定时间自动记录第一振弦式应变仪11与第二振弦式应变仪12的读数；
3、利用与混凝土楼板14相同的混凝土材料浇筑三个10cm×10cm×50cm混凝土试件15，如图1所示，并把内置式的第一振弦式应变仪11预埋在混凝土试件15中部，24小时候后拆除混凝土试件15的模具16，使三个混凝土试件15能自由发生干燥收缩变形，拆除模具16后把混凝土试件15的四个侧面用保鲜膜密封，使试件15只在上下两个面发生干燥收缩，这样试件15干燥收缩的大小、速度与混凝土楼板14的相当；
4、在混凝土楼板14浇筑24小时后，把外置式的第二振弦式应变仪12跨过施工缝13，如图2所示，并用结构胶固定在施工缝13两侧的混凝土楼板14上，连接好第二振弦式应变仪12与应变巡检仪，使用高容量直流电池给应变巡检仪供电，使应变巡检仪能持续工作三个月以上时间；
5、安装完毕后用木方垫起应变巡检仪与蓄电池，并用模板覆盖，防止水淋与水浸；
6、24小时后开始用应变巡检仪测量三个自由变形混凝土试件15的读数，并以三个混凝土试件15的读数平均值作为混凝土试件15的自由干燥收缩应变δ自由干缩，由于混凝土试件15终凝后四个侧面用保鲜膜密封，模拟了混凝土楼板14的干燥收缩，因此混凝土试件15的自由干燥收缩应变δ自由干缩也就是混凝土楼板14在不受约束条件下的自由干燥收缩应变δ自由干缩；
7、24小时后开始用应变巡检仪测量外置式的第二振弦式应变计12的读数，并以该读数作为混凝土楼板14施工缝13处实际发生的干燥收缩应变δ实际干缩；
8、最后计算混凝土楼板14施工缝13处受到下层框架柱或墙约束而产生的干燥收缩约束应变δ约束=δ自由干缩-δ实际干缩。
以上结合附图实施例对本发明进行了详细说明，本领域中普通技术人员可根据上述说明对本发明做出种种变化例。因而，实施例中的某些细节不应构成对本发明的限定，本发明将以所附权利要求书界定的范围作为本发明的保护范围。
Claims (4)
1.一种混凝土楼板施工缝处干燥收缩约束应变的测量方法，其特征在于所述方法包括以下步骤：
浇筑一混凝土楼板，测定所述混凝土楼板施工缝处的实际干燥收缩应变δ实际干缩；
利用与所述混凝土楼板相同的混凝土材料制作混凝土试件，测定所述混凝土试件的自由干燥收缩应变δ自由干缩；
计算所述混凝土楼板施工缝处受到下层框架柱或墙约束而产生的干燥收缩约束应变δ约束＝δ自由干缩-δ实际干缩；
通过以下步骤测定所述混凝土试件的自由干燥收缩应变δ自由干缩：
利用与所述混凝土楼板相同的混凝土材料制作所述混凝土试件，并且在所述混凝土试件中预埋第一振弦式应变计；
浇筑所述混凝土试件达到终凝后，将所述混凝土试件的四个侧面进行密封，使得所述混凝土试件仅在上下两个表面发生干燥收缩，以模拟所述混凝土楼板的干燥收缩；
利用应变巡检仪测定所述第一振弦式应变计的读数，并以该读数作为所述混凝土试件的自由干燥收缩应变δ自由干缩。
2.如权利要求1所述的方法，其特征在于通过以下步骤测定所述混凝土楼板施工缝处的实际干燥收缩应变δ实际干缩：
在所述混凝土楼板施工缝处设置第二振弦式应变计，所述第二振弦式应变计跨过所述施工缝，并且两端分别固定在所述施工缝两侧的所述混凝土楼板上；
利用应变巡检仪测定所述第二振弦式应变计的读数，并以该读数作为所述混凝土楼板施工缝处的实际干燥收缩应变δ实际干缩。
3.如权利要求1所述的方法，其特征在于：所述第一振弦式应变计为内置式振弦式应变计。
4.如权利要求2所述的方法，其特征在于：所述第二振弦式应变计为外置式振弦式应变计，两端分别通过结构胶固定在所述施工缝两侧的所述混凝土楼板上。