CN103602923B - 一种斗齿的合金及其生产方法 - Google Patents

一种斗齿的合金及其生产方法 Download PDF

Info

Publication number
CN103602923B
CN103602923B CN201310530038.5A CN201310530038A CN103602923B CN 103602923 B CN103602923 B CN 103602923B CN 201310530038 A CN201310530038 A CN 201310530038A CN 103602923 B CN103602923 B CN 103602923B
Authority
CN
China
Prior art keywords
bucket tooth
alloy
temperature
mass percent
stove
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310530038.5A
Other languages
English (en)
Other versions
CN103602923A (zh
Inventor
徐雪明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGBO YUXIANG MACHINERY CASTING Co Ltd
Original Assignee
NINGBO YUXIANG MACHINERY CASTING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO YUXIANG MACHINERY CASTING Co Ltd filed Critical NINGBO YUXIANG MACHINERY CASTING Co Ltd
Priority to CN201310530038.5A priority Critical patent/CN103602923B/zh
Publication of CN103602923A publication Critical patent/CN103602923A/zh
Application granted granted Critical
Publication of CN103602923B publication Critical patent/CN103602923B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种斗齿的合金,其化学成分质量百分比为:C:0.31‑0.39%,Si:1.77‑1.95%,Mn:1.1‑1.6%,P:≤0.02%,S:≤0.02%,Nb:0.2‑0.6%,Ti:0.15‑0.2%,Ni:0.15‑0.35%,Cu:0.25‑0.5%,Cr:0.35‑0.8%,Zn:0.15‑0.2%,B:0.003‑0.007%,Mo:≤0.1%,V:≤0.03%,Al:0.012‑0.02%,余量为Fe,本发明添加了Cr,Mo,V,Al、Nb、Ni、Ti、Zn元素,使用了全新的生产方法,合理的热处理工艺,提高了斗齿所用合金的屈服强度和耐磨性,本发明加工出的斗齿,可以适应恶劣的工作环境,使用寿命长,减少停机和维修次数,提高了劳动生产率和设备利用率,降低了生产成本。

Description

一种斗齿的合金及其生产方法
技术领域
本发明属于合金钢生产方法,具体涉及一种斗齿的合金及其生产方法。
背景技术
挖掘机前端的挖斗是工作的主要部位,挖斗上的斗齿是挖掘机上的主要易损件,由于挖掘机的工作环境一般比较恶劣,对斗齿的材质提出了比较高的要求,既要强度高、耐磨,又要有韧性,这样斗齿的使用寿命才会长,所以有必要通过合理改变材质来提高斗齿的使用寿命,这样做既不会增加生产成本,又能够进一步研究挖掘机斗齿的耐磨性和生产工艺,为研制出性能完善的斗齿做贡献。
发明内容
为解决上述问题,本发明公开了一种斗齿的合金及其生产方法,这种合金钢耐磨、强度范围大,同时又有较好的韧性,斗齿寿命有很明显提高。
为达到上述目的,本发明的技术方案如下:
一种斗齿的合金,其化学成分质量百分比为:C:0.31-0.39%,Si:1.77-1.95%,Mn:1.1-1.6%,P:≤0.02%,S:≤0.02%,Nb:0.2-0.6%,Ti:0.15-0.2%,Ni:0.15-0.35%,Cu:0.25-0.5%, Cr:0.35-0.8%,Zn:0.15-0.2%,B: 0.003-0.007%,Mo:≤0.1%,V:≤0.03%,Al:0.012-0.02%,余量为Fe。
一种制造上述合金的生产方法,包括以下步骤:
(1)碱性氧气转炉冶炼
按化学成分质量百分比,将成分为C:0.31-0.39%,Si:1.77-1.95%,Mn:1.1-1.6%,P:≤0.02%,S:≤0.02%,Cu:0.25-0.5%,余量为Fe的炼钢原料加入碱性氧气转炉内吹炼,脱硫,钢水温度为1590-1630℃,
(2)炉外精炼炉吹氧脱碳
真空状态下在炉外精炼炉吹氧脱碳,按化学成分质量百分比,将成分为Nb:0.2-0.6%,Ti:0.15-0.2%,Ni:0.15-0.35%,Cr:0.35-0.8%,Zn:0.15-0.2%,B:0.003-0.007%,Mo:≤0.1%,V:≤0.03%,Al:0.012-0.02%的炼钢原料以及合金加入钢包进行脱氧合金化,所述炼钢原料以及合金在出钢前1-2分钟加入钢包内;
(3)浇铸成型
钢水浇铸到斗齿形状的树脂砂模中,采用冒口加冷铁铸造,浇铸温度为1500-1550℃,将铸件自然冷却到室温后脱模;
(4)热处理
a:淬火
淬火炉加热温度为1080±10℃,保温3-5小时,出炉采用内喷外淋式水淬,外淋水量为2000-2500m3/h,内喷水量为700-1000 m3/h,以水为淬火冷却介质,淬火前,冷却水水温≤25℃,冷却完毕水温不应超过40℃;
b:回火
进炉回火,加温到240±10℃,保温3-4小时,出炉自然冷却到室温;
(5)后期处理
进行喷丸处理,提高斗齿的表面强度。
含锰的钢材一般为铸件,不需正火和退火,但是必须进行淬火回火。
本发明运用微合金化理论,在普通钢的基础上添加了Cr、Mo、V、Al、Nb、Ni、Ti、Zn元素,使用了全新的生产方法,提高了斗齿所用钢材的屈服强度和耐磨性,通过加入0.35-0.8%Cr、低于0.1% Mo和低于0.03%的V此类碳化物形成元素,在冶炼过程中产生化学反应,改变了钢材中碳化物的分布形态,使其均匀分布在奥氏体基体上,耐磨性提高50-60%,添加了0.012-0.02%的Al和0.25-0.5%的 Cu,起细化晶粒作用,提高了钢材的韧性,再通过温度为1080±10℃,保温3-5小时,水淬以及温度为240±10℃,保温3-4小时回火,钢体内奥氏体晶粒细小,晶内颗粒状碳化物均匀,力学性能有了明显提高,经检验,化学成分质量百分比为:C:0.31-0.39%,Si:1.77-1.95%,Mn:1.1-1.6%,P:≤0.02%,S:≤0.02%,Nb:0.2-0.6%,Ti:0.15-0.2%,Ni:0.15-0.35%,Cu:0.25-0.5%, Cr:0.35-0.8%,Zn:0.15-0.2%,B: 0.003-0.007%,Mo:≤0.1%,V:≤0.03%,Al:0.012-0.02%,余量为Fe的原料通过本发明所述的生产方法生产出来的斗齿的力学性能为:抗拉强度≥1670MPa,屈服强度≥1180MPa,硬度硬度HRC54-57,伸长率≥11%,冲击韧性≥19J/cm2
本发明的有益效果是:
本发明添加了Cr,Mo,V,Al、Nb、Ni、Ti、Zn元素,使用了全新的生产方法,合理的热处理工艺,提高了斗齿所用合金的屈服强度和耐磨性,使用本发明所述的合金钢加工出的斗齿,可以适应恶劣的工作环境,使用寿命长,减少停机和维修次数,提高了劳动生产率和设备利用率,降低了生产成本。
具体实施方式
下面结合具体实施方式,进一步阐明本发明,应理解下述具体实施方式仅用于说明本发明而不用于限制本发明的范围。
实施例1:
一种斗齿的合金,其化学成分质量百分比为:C:0.36%,Si:1.86%,Mn:1.45%,P:0.014%,S:0.015%,Nb:0.4%,Ti:0.16%,Ni:0.2%,Cu:0.38%, Cr:0.55%,Zn:0.19%,B:0.006%,Mo:0.06%,V:0.025%,Al:0.018%,余量为Fe。
一种制造上述合金的生产方法,包括以下步骤:
(1)碱性氧气转炉冶炼
按化学成分质量百分比,将成分为C:0.36%,Si:1.86%,Mn:1.45%,P:0.014%,S:0.015%,Cu:0.38%,余量为Fe的炼钢原料加入碱性氧气转炉内吹炼,脱硫,钢水温度为1620℃;
(2)炉外精炼炉吹氧脱碳
真空状态下在炉外精炼炉吹氧脱碳,按化学成分质量百分比,将成分为Nb:0.4%,Ti:0.16%,Ni:0.2%,Cr:0.55%,Zn:0.19%,B: 0.006%,Mo:0.06%,V:0.025%,Al:0.018%的炼钢原料以及合金加入钢包进行脱氧合金化,所述炼钢原料以及合金在出钢前1分钟加入钢包内;
(3)浇铸成型
钢水浇铸到斗齿形状的树脂砂模中,采用冒口加冷铁铸造,浇铸温度为1520℃,将铸件自然冷却到室温后脱模;
(4)热处理
a:淬火
淬火炉加热温度为1080℃,保温5小时,出炉采用内喷外淋式水淬,外淋水量为2300m3/h,内喷水量为800 m3/h,以水为淬火冷却介质,淬火前,冷却水水温25℃,冷却完毕水温38℃;
b:回火
进炉回火,加温到240℃,保温4小时,出炉自然冷却到室温;
(5)后期处理
进行喷丸处理,提高斗齿的表面强度。
经检验,本实施例所述的斗齿的力学性能为:抗拉强度1695MPa,屈服强度1270MPa,硬度硬度HRC57,伸长率13%,冲击韧性23J/cm2,使用寿命延长60%。
实施例2
一种斗齿的合金,其化学成分质量百分比为:C:0.31%,Si:1.77%,Mn:1.1%,P:0.018%,S:0.014%,Nb:0.2%,Ti:0.15%,Ni:0.15%,Cu:0.25%, Cr:0.35%,Zn:0.15%,B:0.003%,Mo:0.09%,V:0.02%,Al:0.012%,余量为Fe。
一种制造上述合金的生产方法,包括以下步骤:
(1)碱性氧气转炉冶炼
按化学成分质量百分比,将成分为C:0.31%,Si:1.77%,Mn:1.1%,P:0.018%,S:0.014%,Cu:0.25%,余量为Fe的炼钢原料加入碱性氧气转炉内吹炼,脱硫,钢水温度为1590℃,
(2)炉外精炼炉吹氧脱碳
真空状态下在炉外精炼炉吹氧脱碳,按化学成分质量百分比,将成分为Nb:0.2%,Ti:0.15%,Ni:0.15%,Cr:0.35%,Zn:0.15%,B: 0.003%,Mo:0.09%,V:0.02%,Al:0.012%的炼钢原料以及合金加入钢包进行脱氧合金化,所述炼钢原料以及合金在出钢前2分钟加入钢包内;
(3)浇铸成型
钢水浇铸到斗齿形状的树脂砂模中,采用冒口加冷铁铸造,浇铸温度为1500℃,将铸件自然冷却到室温后脱模;
(4)热处理
a:淬火
淬火炉加热温度为1070℃,保温3小时,出炉采用内喷外淋式水淬,外淋水量为2000m3/h,内喷水量为700 m3/h,以水为淬火冷却介质,淬火前,冷却水水温24℃,冷却完毕水温为39℃;
b:回火
进炉回火,加温到230℃,保温3小时,出炉自然冷却到室温;
(5)后期处理
进行喷丸处理,提高斗齿的表面强度。
经检验,本实施例所述的斗齿的力学性能为:抗拉强度1670MPa,屈服强度1180MPa,硬度硬度HRC54,伸长率11%,冲击韧性19J/cm2
实施例3
一种斗齿的合金,其化学成分质量百分比为:C:0.39%,Si:1.95%,Mn:1.65%,P:0.02%,S:0.018%,Nb:0.6%,Ti:0.2%,Ni:0.35%,Cu:0.5%, Cr:0.8%,Zn:0.2%,B: 0.007%,Mo:0.082%,V:0.022%,Al:0.02%,余量为Fe。
一种制造上述合金的生产方法,包括以下步骤:
(1)碱性氧气转炉冶炼
按化学成分质量百分比,将成分为C:0.39%,Si:1.95%,Mn:1.65%,P:0.02%,S:0.018%,Cu:0.5%余量为Fe的炼钢原料加入碱性氧气转炉内吹炼,脱硫,钢水温度为1630℃,
(2)炉外精炼炉吹氧脱碳
真空状态下在炉外精炼炉吹氧脱碳,按化学成分质量百分比,将成分为Nb:0.6%,Ti:0.2%,Ni:0.35%,Cr:0.8%,Zn:0.2%,B: 0.007%,Mo:0.082%,V:0.022%,Al:0.02%的炼钢原料以及合金加入钢包进行脱氧合金化,所述炼钢原料以及合金在出钢前1分钟加入钢包内;
(3)浇铸成型
钢水浇铸到斗齿形状的树脂砂模中,采用冒口加冷铁铸造,浇铸温度为1550℃,将铸件自然冷却到室温后脱模;
(4)热处理
a:淬火
淬火炉加热温度为1090℃,保温3-5小时,出炉采用内喷外淋式水淬,外淋水量为2500m3/h,内喷水量为1000 m3/h,以水为淬火冷却介质,淬火前,冷却水水温23℃,冷却完毕水温为39℃;
b:回火
进炉回火,加温到250℃,保温4小时,出炉自然冷却到室温;
(5)后期处理
进行喷丸处理,提高斗齿的表面强度。
经检验,本实施例所述的斗齿的力学性能为:抗拉强度1680MPa,屈服强度1190MPa,硬度硬度HRC55,伸长率12%,冲击韧性22J/cm2
本发明所公开的技术手段不仅限于上述实施方式所公开的技术手段,还包括由以上技术特征任意组合所组成的技术方案。

Claims (4)

1.一种斗齿的合金,其特征在于:其化学成分质量百分比为:C:0.31-0.39%,Si:1.77-1.95%,Mn:1.1-1.6%,P:≤0.02%,S:≤0.02%,Nb:0.2-0.6%,Ti:0.15-0.2%,Ni:0.15-0.35%,Cu:0.25-0.5%, Cr:0.35-0.8%,Zn:0.15-0.2%,B: 0.003-0.007%,Mo:≤0.1%,V:≤0.03%,Al:0.012-0.02%,余量为Fe,其生产方法,包括以下步骤:
(1)碱性氧气转炉冶炼
按化学成分质量百分比,将成分为C:0.31-0.39%,Si:1.77-1.95%,Mn:1.1-1.6%,P:≤0.02%,S:≤0.02%,Cu:0.25-0.5%,余量为Fe的炼钢原料加入碱性氧气转炉内吹炼,脱硫,钢水温度为1590-1630℃;
(2)炉外精炼炉吹氧脱碳
真空状态下在炉外精炼炉吹氧脱碳,按化学成分质量百分比,将成分为Nb:0.2-0.6%,Ti:0.15-0.2%,Ni:0.15-0.35%,Cr:0.35-0.8%,Zn:0.15-0.2%,B:0.003-0.007%,Mo:≤0.1%,V:≤0.03%,Al:0.012-0.02%的炼钢原料以及合金加入钢包进行脱氧合金化;
(3)浇铸成型
钢水浇铸到斗齿形状的树脂砂模中,浇铸温度为1500-1550℃,将铸件自然冷却到室温后脱模;
(4)热处理
a:淬火
淬火炉加热温度为1080±10℃,保温3-5小时,出炉采用内喷外淋式水淬,外淋水量为2000-2500m3/h,内喷水量为700-1000 m3/h,以水为淬火冷却介质,淬火前,冷却水水温≤25℃,冷却完毕水温不应超过40℃;
b:回火
进炉回火,加温到240±10℃,保温3-4小时,出炉自然冷却到室温;
(5)后期处理
进行喷丸处理,提高斗齿的表面强度。
2.根据权利要求1所述的一种斗齿的合金,其特征在于:其化学成分质量百分比为:C:0.36%,Si:1.86%,Mn:1.45%,P:0.014%,S:0.015%,Nb:0.4%,Ti:0.16%,Ni:0.2%,Cu:0.38%,Cr:0.55%,Zn:0.19%,B: 0.006%,Mo:0.06%,V:0.025%,Al:0.018%,余量为Fe。
3.根据权利要求1所述的一种斗齿的合金,其特征在于:所述步骤(2)中炼钢原料以及合金在出钢前1-2分钟加入钢包内。
4.根据权利要求1所述的一种斗齿的合金,其特征在于:所述步骤(3)中采用冒口加冷铁铸造。
CN201310530038.5A 2013-11-01 2013-11-01 一种斗齿的合金及其生产方法 Expired - Fee Related CN103602923B (zh)