CN103601468A - 能产生负离子及远红外线的保健瓷砖 - Google Patents
能产生负离子及远红外线的保健瓷砖 Download PDFInfo
- Publication number
- CN103601468A CN103601468A CN201310579945.9A CN201310579945A CN103601468A CN 103601468 A CN103601468 A CN 103601468A CN 201310579945 A CN201310579945 A CN 201310579945A CN 103601468 A CN103601468 A CN 103601468A
- Authority
- CN
- China
- Prior art keywords
- parts
- far infrared
- infrared rays
- negative ion
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种能产生负离子及远红外线的保健瓷砖,包括底层和表层,按重量计,底层组份为:陶瓷料:45~60份,粘土:10~15份,石英砂:5~8份,砂石:20~30份,长石:20~25份;表层组份为:陶瓷料:30~40份,粘土:20~30份,石英砂:2~4份,砂石:10~20份,长石:20~25份,负离子粉:5~10份,锗粉:5~10份,磁粉2~4份。本发明在瓷砖的表层内混合负离子粉、锗粉、磁粉,能释放负氧离子、远红外线及磁场,使安装有该瓷砖的室内具有丰富的负氧离子,能够杀死空气中带正电荷的多种细菌,净化空气,改善心肺功能,提高人体免疫力,而远红外线能够穿过脚底,可改善人体血液循环,提高人体免疫力。
Description
技术领域
本发明涉及一种瓷砖的改进技术。
背景技术
目前,家庭以及商务办公场所的装修中所用的地板一般为木地板或大理石地板或瓷砖等。这些地板的效果仅仅是为了环境整洁,而并无保健功能。
随着亚健康人群的增加,如果能在家庭中或者办公场中所使用的瓷砖具有保健功能、使人们的亚健康状态在生活、工作中缓解,将具有巨大的社会效益和经济利益,提高人们的身体素质。
发明内容
有鉴于此,本发明提供一种可应用于家庭以及商务办公装修中使用、具有保健功能的能产生负离子及远红外线的保健瓷砖。
本发明采取的设计方案为:
一种能产生负离子及远红外线的保健瓷砖,该保健瓷砖包括底层和表层,其中,
按照重量计,该底层组份为:陶瓷料:45~60份,粘土:10~15份,石英砂:5~8份,砂石:20~30份,长石:20~25份;
按照重量计,该表层组份为:陶瓷料:30~40份,粘土:20~30份,石英砂:2~4份,砂石:10~20份,长石:20~25份,负离子粉:5~10份,锗粉:5~10份,磁粉:2~4份;
该保健瓷砖制作方法为:
首先,将陶瓷料、粘土、石英砂、长石以及砂石按照上述比例进行混合,在球磨机中进行粉碎,粉碎后各成分粒径均小于350纳米,形成底层混合料;将陶瓷料、粘土、石英砂、砂石、长石、负离子粉、锗粉以及磁粉按照上述比例进行混合,在球磨机中粉碎,粉碎后的各成分粒径小于200纳米,形成表层混合料;
其次,将底层混合料放入瓷砖模具型腔中,并在底层混合料上铺上表层混合料;
然后,在3000~5000KN压力下压制成坯料;
然后,将坯料在温度为150摄氏度~200摄氏度的环境中干燥,干燥时间为60分钟~70分钟之间;
最后,在温度为1250摄氏度~1350摄氏度下对坯料进行烧制,烧制时间在40分钟~60分钟之间,形成成品。烧制成成品后表层厚度为2mm~5mm之间。
并且,在表层表面设置有用于按摩脚底的凸点。
与现有技术相比,本分明具有如下优点:
本发明在烧制时将瓷砖进行分层设置,在瓷砖的表层内混合负离子粉、锗粉和磁粉成分,使瓷砖能释放负氧离子、远红外线以及磁场,使安装有该类瓷砖的室内具有丰富的负氧离子,既能够杀死空气中带正电荷的多种细菌,净化空气,还可大大改善居于该环境中人们的心肺功能,提高人体免疫力;同时,该瓷砖释放的远红外线能够穿过脚底,可改善人体血液循环,提高人体免疫力。并且本发明只在瓷砖表层中含有负离子粉、锗粉及磁粉,使价格昂贵的负离子粉和锗粉集中在表层,在具有良好保健效果的前提下,有效的控制了成本。此外,在瓷砖表层的表面可增设按摩脚底的凸点,通过负氧离子、远红外线、磁场以及脚底物理按摩,本发明的保健效果更佳。
具体实施方式
为了让本领域的技术人员更好地理解本发明的技术方案,下面结合实施例对本发明作进一步阐述。
一种能产生负离子及远红外线的保健瓷砖,该保健瓷砖包括底层和表层,其中,
按照重量计,该底层组份为:陶瓷料50份,粘土12份,石英砂6份,砂石25份,长石22份;
按照重量计,该表层组份为:陶瓷35份,粘土25份,石英砂3份,砂石15份,长石22份,负离子粉7份,锗粉7份,磁粉3份;
该保健瓷砖制作方法为:
首先,将陶瓷料、粘土、石英砂、长石以及砂石按照上述比例进行混合,在球磨机中进行粉碎,粉碎后各成分粒径均小于350纳米,形成底层混合料;将陶瓷料、粘土、石英砂、砂石、长石、负离子粉、锗粉及磁粉按照上述比例进行混合,在球磨机中粉碎,粉碎后的各成分粒径小于200纳米,形成表层混合料;
其次,将底层混合料放入瓷砖模具型腔中,并在底层混合料上铺上表层混合料;
然后,在3000~5000KN压力下压制成坯料;
然后,将坯料在温度为150摄氏度~200摄氏度的环境中干燥,干燥时间为60分钟~70分钟之间;
最后,在温度为1250摄氏度~1350摄氏度下对坯料进行烧制,烧制时间在40分钟~60分钟之间,形成成品。烧制成成品后表层厚度为2mm~5mm之间。
采用上述成分以及方法制得的瓷砖由于其表层含有负离子粉,能够释放远红外线和负氧离子。对于瓷砖中的远红外线而言,可以激活生物大分子的活性,使生物体的分子处于较高振动状态,这样便激活了核酸蛋白质等生物大小分子的活性,从而发挥了生物大分子调节机体代谢、免疫等活动的功能,有利于机能的恢复和平衡,达到防病治病的目的;也可以促进和改善血液循环,当远红外作用于皮肤后,大部分能量被皮肤所吸收被吸收的能量转化为热能,引起皮温升高,刺激皮肤内热感受器,通过丘脑反射,使血管平滑肌松弛,血管扩张,血液循环加快,另一方面,由于热作用,引起血管活性物质的释放,血管张力降低,浅小动脉、浅毛细管和浅静脉扩张,血液循环加快,血液循环得以改善(通过中国医学科学院血液病研究所检测,20分钟可使微循环血流量提高114%);并且,远红外线可以增强新陈代谢,如果人体的新陈代谢发生紊乱,引起体内外物质的交换失常,那么,各种疾病将会不约而至,诸如水和电解质代谢的紊乱,将给生命带来危险;糖代谢紊乱,会导致的糖尿病;脂代谢紊乱引起的高脂血症、肥胖症;蛋白质代谢紊乱引起痛风等等。通过远红外热效应,可以增加细胞的活力调整神经液机体,加强新陈代谢,使体内外的物质交换处于平稳状态;并且,本发明设计的瓷砖可以提高人体免疫功能,经临床观察,远红外保健品确有提高机体的巨噬细胞吞噬功能,增强人体的细胞免疫和人体液免疫功能,有利于人体的健康;此外,本发明设计的瓷砖还可以消炎、消肿以及镇痛,由于成分中的远红外的热效应,降低了神经末梢的兴奋性,血液循环的改善,水肿的消退,减轻了神经末梢的化学和机械刺激。而且,由于本发明可释放负氧离子,负氧离子可通过人的神经系统及血液循环能对人的机体生理活动产生影响,研究表明,负离子可使人体大脑皮层功能增强,增强脑组织的氧化过程,具有明显扩张血管的作用,可解除动脉血管痉挛,降低血压,改善心脏功能,有利于血氧输送、吸收和利用,可提高人体肺活量,改善和增强肺功能。并且锗粉的功能也可以调节人体电位差,促进血液循环,消除肌肉酸痛等症状。如果在室内安装本发明设计的瓷砖,可以大大增加室内负氧离子含量,脚底也可持续受远红外线刺激,达到保健的效果。经过测量,在靠近本发明瓷砖表面位置,负氧离子浓度可达40000个/立方厘米,而瀑布附近一般才3000个/立方厘米,一般的森林中才2000个/立方厘米,可见本发明安装于室内的效果。
对于底层和表层的含量,除了上述实施例描述之外,也可以为如下含量:
对于底层组份,陶瓷料可为45~60份之间任一值,如45份或48份或55份或60份,粘土可为10~15份之间任一值,如10份或13份或15份,石英砂可为5~8份之间任一值,如5份或8份,砂石可为20~30份之间任一值,如20份或23份或27份或30份,长石可为20~25份之间任一值,如20份或23份或25份;
对于表层组份,陶瓷料可为30~40份之间任一值,如30份或33份或37份或49份,粘土可为20~30份之间任一值,如20份或23份或30份,石英砂可为2~4份之间任一值,如2份或4份,砂石可为10~20份之间任一值,如10份或13份或17份或20份,长石可为20~25份之间任一值,如20份或25份,负离子粉可为5~10份之间任一值,如5份或8份或9份,锗粉可为5~10份之间任一值,如5份或8份或10份,磁粉可为2~4份之间任一值,如2份或4份等;
采用上述各成分取值制得的瓷砖均可达到本发明设计要求,具有相同的技术效果。
上述所描述的保健瓷砖可设计为表层表面为平面,也可以在成型时在表层表面加工出密集分布的凸点,该凸点对脚底具有按摩作用,可按摩穴位,促进脚底血液循环。
以上为本发明较佳的实现方式,需要说明的是,在不背离本发明精神及其实质的情况下,熟悉本领域的技术人员当可根据本发明作出各种相应的改变和变形,这些改变和变形都应属于本发明所附的权利要求的保护范围。
Claims (3)
1.一种能产生负离子及远红外线的保健瓷砖,其特征在于,该保健瓷砖包括底层和表层,其中,
按照重量计,该底层组份为:陶瓷料:45~60份,粘土:10~15份,石英砂:5~8份,砂石:20~30份,长石:20~25份;
按照重量计,该表层组份为:陶瓷料:30~40份,粘土:20~30份,石英砂:2~4份,砂石:10~20份,长石:20~25份,负离子粉:5~10份,锗粉:5~10份,磁粉:2~4份;
该保健瓷砖制作方法为:
首先,将陶瓷料、粘土、石英砂、长石以及砂石按照上述比例进行混合,在球磨机中进行粉碎,粉碎后各成分粒径均小于350纳米,形成底层混合料;将陶瓷料、粘土、石英砂、砂石、长石、负离子粉、锗粉以及磁粉按照上述比例进行混合,在球磨机中粉碎,粉碎后的各成分粒径小于200纳米,形成表层混合料;
其次,将底层混合料放入瓷砖模具型腔中,并在底层混合料上铺上表层混合料;
然后,在3000~5000KN压力下压制成坯料;
然后,将坯料在温度为150摄氏度~200摄氏度的环境中干燥,干燥时间为60分钟~70分钟之间;
最后,在温度为1250摄氏度~1350摄氏度下对坯料进行烧制,烧制时间在40分钟~60分钟之间,形成成品。
2.根据权利要求1所述的能产生负离子及远红外线的保健瓷砖,其特征在于,烧制成成品后表层厚度为2mm~5mm之间。
3.根据权利要求2所述的能产生负离子及远红外线的保健瓷砖,其特征在于,在表层表面设置有用于按摩脚底的凸点。