CN103601466B - Elevator counterweight block prepared by a kind of kaolin - Google Patents
Elevator counterweight block prepared by a kind of kaolin Download PDFInfo
- Publication number
- CN103601466B CN103601466B CN201310561462.6A CN201310561462A CN103601466B CN 103601466 B CN103601466 B CN 103601466B CN 201310561462 A CN201310561462 A CN 201310561462A CN 103601466 B CN103601466 B CN 103601466B
- Authority
- CN
- China
- Prior art keywords
- kaolin
- water
- counterweight block
- kilograms
- elevator counterweight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides elevator counterweight block prepared by a kind of kaolin, it is, using kaolin as primary raw material, and to the addition of barite, and other auxiliary materials are made.The method of the elevator counterweight block prepared the invention also discloses this kaolin, including coarse crushing, in it is broken, in small, broken bits, mixing, shaping, maintenance, welding etc. step, the cheap water-washed kaoline of the product utilization of the present invention and barite make primary raw material instead of traditional cast iron, reduce cost and save resource, and technique is simple, can industrialized production, with good economic results in society.
Description
Technical field
The present invention relates to a kind of to pouring weight, especially a kind of elevator counterweight block prepared by kaolin.
Background technology
The pure kaolin of matter has that whiteness is high, matter is soft, it is easily scattered suspend in water, good plasticity and high bonding
Property, excellent electrical insulation capability；With physics and chemistry such as good antiacid dissolubility, very low cation exchange capacity (CEC), preferable fire resistances
Property.
All the time, typically cylinder iron material is to pouring weight for elevator industry, and cast iron materials are expensive, and product utilization of the invention is high
Ridge soil replaces cast iron to prepare to pouring weight, and compact conformation intensity is good, environmental, and technique is simple, can industrialized production, have
Good economic results in society.
The content of the invention
The simple and easy to apply, kaolinite that compact conformation intensity is good, environmental is made it is an object of the present invention to provide one kind
Elevator counterweight block prepared by soil.
The method of the elevator counterweight block prepared it is a further object to provide above-mentioned kaolin.
To reach above-mentioned purpose, the present invention takes following technical scheme：
Elevator counterweight block prepared by a kind of kaolin, it is characterised in that containing following raw material, prepared by following weight number：
1000~1200 kilograms of water-washed kaoline, 200~300 kilograms of barite, 1~3 kilogram of calgon, water 100
~130 kilograms.
The method of elevator counterweight block prepared by the kaolin, it is characterised in that its specific steps and technique are：
First step coarse crushing：Barite is put into mineral breaker by raw material proportioning, 125~400 millimeters are crushed to；
It is broken in second step：By above-mentioned material separating twice, 50~100 millimeters are crushed to；
3rd step is in small, broken bits：By above-mentioned three crushing of material, 5~25 millimeters are crushed to；
4th step is mixed：By above-mentioned material and water-washed kaoline, calgon, water by proportioning input mixer stirring 30
It is~40 minutes, well mixed that compound is made；
5th one-step forming：Above-mentioned compound is pressed into required module with 1000 tons of forcing press；
6th step is maintained：Above-mentioned module was sprayed water once every 24 hours, maintained 3~4 days, until module is fully hardened；
7th step is welded：By iron plate cover in the module lid of hardening and it is welded, finished product.
The invention has the advantages that：
1) the cheap water-washed kaoline of product utilization of the invention and barite make primary raw material and replace traditional
Cast iron, greatly reduces cost and saves resource.
2) production of the invention is simple and easy to apply, compact conformation intensity is good and environmental.
Embodiment
The embodiment to the present invention elaborates below：
Embodiment 1
Elevator counterweight block prepared by kaolin, using following raw material, by following weight than being prepared：
1200 kilograms of water-washed kaoline, 300 kilograms of barite, 3 kilograms of calgon, 130 kilograms of water.
Specific preparation method：
First step coarse crushing：Barite is put into mineral breaker by raw material proportioning, 125~400 millimeters are crushed to.
It is broken in second step：By above-mentioned material separating twice, 50~100 millimeters are crushed to.
3rd step is in small, broken bits：By above-mentioned three crushing of material, 5~25 millimeters are crushed to.
4th step is mixed：By above-mentioned material and water-washed kaoline, calgon, water by proportioning input mixer stirring 40
Minute, it is well mixed that compound is made.
5th one-step forming：Above-mentioned compound is pressed into required module with 1000 tons of forcing press.
6th step is maintained：Above-mentioned module was sprayed water once every 24 hours, maintained 4 days, until module is fully hardened.
7th step is welded：By iron plate cover in the module lid of hardening and it is welded, finished product.
Embodiment 2
Elevator counterweight block prepared by kaolin, using following raw material, by following weight than being prepared：
1000 kilograms of water-washed kaoline, 200 kilograms of barite, 1 kilogram of calgon, 100 kilograms of water.
Specific preparation method：
First step coarse crushing：Barite is put into mineral breaker by raw material proportioning, 125~400 millimeters are crushed to.
It is broken in second step：By above-mentioned material separating twice, 50~100 millimeters are crushed to.
3rd step is in small, broken bits：By above-mentioned three crushing of material, 5~25 millimeters are crushed to.
4th step is mixed：By above-mentioned material and water-washed kaoline, calgon, water by proportioning input mixer stirring 30
Minute, it is well mixed that compound is made.
5th one-step forming：Above-mentioned compound is pressed into required module with 1000 tons of forcing press.
6th step is maintained：Above-mentioned module was sprayed water once every 24 hours, maintained 4 days, until module is fully hardened.
7th step is welded：By iron plate cover in the module lid of hardening and it is welded, finished product.
Embodiment 3
Elevator counterweight block prepared by kaolin, using following raw material, by following weight than being prepared：
500 kilograms of water-washed kaoline, barite 120 kg, 0.8 kilogram of calgon, 70 kilograms of water.
Specific preparation method：
First step coarse crushing：Barite is put into mineral breaker by raw material proportioning, 125~400 millimeters are crushed to.
It is broken in second step：By above-mentioned material separating twice, 50~100 millimeters are crushed to.
3rd step is in small, broken bits：By above-mentioned three crushing of material, 5~25 millimeters are crushed to.
4th step is mixed：By above-mentioned material and water-washed kaoline, calgon, water by proportioning input mixer stirring 30
Minute, it is well mixed that compound is made.
5th one-step forming：Above-mentioned compound is pressed into required module with 1000 tons of forcing press.
6th step is maintained：Above-mentioned module was sprayed water once every 24 hours, maintained 3 days, until module is fully hardened.
7th step is welded：By iron plate cover in the module lid of hardening and it is welded, finished product.
Above-described is only embodiments of the present invention.The obvious present invention is implemented not to be limited by aforesaid way
System, if the unsubstantiality for employing inventive concept and technical scheme of the present invention progress is improved, or it is not improved by the present invention
Design and technical scheme directly apply to other occasions, within protection scope of the present invention.
Claims (3)
1. a kind of method that kaolin prepares elevator counterweight block, it is characterised in that elevator counterweight block prepared by described kaolin
Containing following raw material, prepared by following weight number：
1000~1200 kilograms of water-washed kaoline, 200~300 kilograms of barite, 1~3 kilogram of calgon, water 100~130
Kilogram；
The method specific steps and technique that the kaolin prepares elevator counterweight block are：
First step coarse crushing：Barite is put into mineral breaker by raw material proportioning, 125~400 millimeters are crushed to；
It is broken in second step：By above-mentioned material separating twice, 50~100 millimeters are crushed to；
3rd step is in small, broken bits：By above-mentioned three crushing of material, 5~25 millimeters are crushed to；
4th step is mixed：By above-mentioned material and water-washed kaoline, calgon, water by proportioning input mixer stirring 30~40
Minute, it is well mixed that compound is made；
5th one-step forming：Above-mentioned compound is pressed into required module with 1000 tons of forcing press；
6th step is maintained：Above-mentioned module was sprayed water once every 24 hours, maintained 3~4 days, until module is fully hardened；
7th step is welded：By iron plate cover in the module lid of hardening and it is welded, finished product.
2. the method that kaolin as claimed in claim 1 prepares elevator counterweight block, it is characterised in that electricity prepared by the kaolin
Ladder contains following raw material to pouring weight, by following weight than preparing：
1200 kilograms of water-washed kaoline, 300 kilograms of barite, 3 kilograms of calgon, 130 kilograms of water.
3. the method that kaolin as claimed in claim 1 prepares elevator counterweight block, it is characterised in that the weight in the first step
Spar is the barite that proportion is 4.35.