CN103590567B - A kind of bamboo mat strengthening composite floor and production technology thereof - Google Patents
A kind of bamboo mat strengthening composite floor and production technology thereof Download PDFInfo
- Publication number
- CN103590567B CN103590567B CN201210303017.5A CN201210303017A CN103590567B CN 103590567 B CN103590567 B CN 103590567B CN 201210303017 A CN201210303017 A CN 201210303017A CN 103590567 B CN103590567 B CN 103590567B
- Authority
- CN
- China
- Prior art keywords
- bamboo
- basic unit
- hot
- temperature
- duration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of bamboo mat strengthening composite floor and production technology thereof, basic unit adopts bamboo to slight crisscross knitting and spells rear lamination, and intermediate layer is high density fiberboard, and surface layer is impregnated paper.Basic unit and intermediate layer hot-press gluing.This floor good stability, multilayer is crisscross knits and spells bamboo and slight seat and effectively overcome floor base material moisture-sensitive and expand, dry shrink arch camber shortcoming and the bad and easily dry and cracked shortcoming of heat conductivility.
Description
Technical field
The present invention relates to a kind of bamboo mat strengthening composite floor and production technology thereof.
Background technology
Wood floor base material moisture-sensitive of the prior art expands, and dry contraction arch camber, the shortcomings such as heat conductivility is bad and easily dry and cracked, water-fast, moisture-resistance is poor, the invention provides a kind of bamboo mat strengthening composite floor effectively to improve above-mentioned shortcoming for above-mentioned shortcoming.
Summary of the invention
Technical scheme of the present invention is: a kind of bamboo mat strengthening composite floor, and basic unit adopts bamboo to slight crisscross knitting and spells rear lamination, and intermediate layer is high density fiberboard, and surface layer is impregnated paper.Basic unit and intermediate layer hot-press gluing.Basic unit is embedded in intermediate layer.
The production technology on floor is, adopts bamboo to slight the method for seat and high density fiberboard hot-press gluing, then forms sheet material painted japanning of slotting.Specific practice is, is slightd by bamboo crisscrossly to knit spelling, and recycle water-soluble modified environment-friendlyadhesive adhesive dipping, take high temperature lamination to form basic unit, parameter is, unit pressure 28 kilograms/cm
2, temperature 135 DEG C-145 DEG C, duration 12-13 minute, hot press operating pressure is 0.5 MPa (mpa), and bamboo slights groundwork thickness; 5-15mm, recycles this basic unit and high density fiberboard (1.8mm-6.8mm), impregnated paper carry out hot-press gluing, unit pressure 20 kilograms/Cm
2temperature 150 DEG C-190 DEG C, duration 60 second, compressor operation pressure is 0.22 MPa (mpa), and after completing hot pressing time, then hot press temperature is cooled to 30 DEG C ± 5 DEG C from height point cools sheet material, duration 10 minutes, after sheet material exits press, put into balance room naturally qualitative more than 15 days, then carry out stock processing and forming.Packaging after processing mode adopts UV resin emulsion paint to be coated with after adopting directly the slot shaping rear packaging of mortise or fluting mortise again.
The present invention has the following advantages:
A, good stability, multilayer is crisscross knits and spells bamboo and slight seat and effectively overcome floor base material moisture-sensitive and expand, dry shortcoming of shrinking arch camber.
B, floor face utilize hardness and the strength characteristics of impregnated-paper laminated wood floor, add wear-resisting, scratch-resistant and the impact strength on floor.
C, efficiently solve floor under north heating condition, the shortcoming that heat conductivility is bad and easily dry and cracked, heat conduction is than raising more than 20% compared with conventional floor.Meanwhile, the ground pavement of southern humid climate is conducive to again.
D, water resistance have had remarkable improvement compared with other floors, are easy to arrange.
Accompanying drawing explanation
Fig. 1 is bamboo mat strengthening composite floor rear view one.
Fig. 2 is bamboo mat strengthening composite floor rear view two.
Fig. 3 is bamboo mat strengthening composite floor lateral plan.
Detailed description of the invention
Be described with reference to the accompanying drawings the structure of bamboo mat strengthening composite floor, basic unit (1) adopts bamboo to slight crisscross knitting and spells rear lamination, and intermediate layer (2) are high density fiberboard, and surface layer (3) is impregnated paper.The combination that basic unit and intermediate layer adopt hot-press gluing or inlay in conjunction with hot-press gluing.Impregnated paper can be melmac wood grain impregnated paper, hot pressing wearing layer on it; Also can be alundum (Al2O3) wear-resistant immersion paper.
The production technology on floor is, adopts bamboo to slight the method for seat and high density fiberboard hot-press gluing, then forms sheet material painted japanning of slotting.Specific practice is, is slightd by bamboo crisscrossly to knit spelling, and recycle water-soluble modified environment-friendlyadhesive adhesive dipping, take high temperature lamination to form basic unit, parameter is, unit pressure 28 kilograms/cm
2, temperature 135 DEG C-145 DEG C, duration 12-13 minute, hot press operating pressure is 0.5 MPa (mpa), and bamboo slights groundwork thickness; 5-15mm, recycles this basic unit and high density fiberboard, and thickness 1.8mm-6.8mm, impregnated paper carry out hot-press gluing, unit pressure 20 kilograms/Cm
2temperature 150 DEG C-190 DEG C, duration 1 minute, compressor operation pressure is 0.22 MPa (mpa), and after completing hot pressing time, then hot press temperature is cooled to 30 DEG C ± 5 DEG C from height point cools sheet material, duration 10 minutes, after sheet material exits press, put into balance room naturally qualitative more than 15 days, then carry out stock processing and forming.
Claims (1)
1. the production technology of a bamboo mat strengthening composite floor, it is characterized in that, bamboo is slightd and crisscrossly knits spelling, recycle water-soluble modified environment-friendlyadhesive adhesive dipping, high temperature lamination is taked to form basic unit, parameter is, unit pressure 28 kilograms/cm2, temperature 135 DEG C-145 DEG C, duration 12-13 minute, hot press operating pressure is 0.5 MPa, it is 5-15mm that bamboo slights groundwork thickness, recycle this basic unit and high density fiberboard, impregnated paper carries out hot-press gluing, fiberboard thickness is 1.8mm-6.8mm, unit pressure 20 kilograms/Cm2, temperature 150 DEG C-190 DEG C, duration 60 second, compressor operation pressure is 0.22 MPa, and after completing hot pressing time, again hot press temperature is cooled to 30 DEG C ± 5 DEG C from height point to cool sheet material, duration 10 minutes, after sheet material exits press, put into balance room naturally qualitative more than 15 days, carry out the shaping of stock processing and forming again.