CN103589244A - 一种无树脂色浆 - Google Patents
一种无树脂色浆 Download PDFInfo
- Publication number
- CN103589244A CN103589244A CN201310559503.8A CN201310559503A CN103589244A CN 103589244 A CN103589244 A CN 103589244A CN 201310559503 A CN201310559503 A CN 201310559503A CN 103589244 A CN103589244 A CN 103589244A
- Authority
- CN
- China
- Prior art keywords
- resin
- mill base
- color paste
- diethylene glycol
- free color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种涂料领域使用的色浆。一种无树脂色浆,按质量百分比计由如下组分组成:丙二醇甲醚醋酸酯20~25%,超级分散剂3~5%,二乙二醇乙醚醋酸酯2~5%,有效成分为8~12%的膨润土浆5~10%,83#黄色粉20%,二甲苯20~40%,乙酸丁酯20~30%。本发明采用超级高分子量的分散剂和助剂一起直接研磨颜料,获得无树脂色浆,解决了有树脂色浆的局限性,由于不含树脂,因此该色浆与所有涂料体系有很好的相容性。
Description
技术领域
本发明涉及一种涂料领域使用的色浆。
背景技术
色浆是由颜料或颜料和填充料分散在漆料内而成的半制品。以纯油为胶粘剂的称油性色浆,以树脂漆料为胶粘剂的称树脂色浆,以水为介质添加表面活性剂分散而成的颜填料浆称为水性色浆。由于漆料种类很多,色浆种类也很多。
木器漆用色浆一般为树脂色浆,作为木器漆中色漆中最主要的组成部分的色浆一直备受业界的关注,由于色浆与涂料体系存在着单一的相容性,色浆与使用体系的相容性是影响色漆的浮色发花、絮凝和有些漆膜表面缺陷的关键,因此涂料体系选择色浆时必须考虑色浆与涂料体系的相容性,因此,树脂色浆的发展多样却单一。
发明内容
本发明所要解决的技术问题是提供一种无树脂的色浆,该色浆由于不含有树脂,因此与所有涂料体系有很好的相容性。
本发明所要解决的技术问题通过以下技术方案予以实现:
一种无树脂色浆,按质量百分比计由如下组分组成:
丙二醇甲醚醋酸酯 20~25%,其作用是增加色浆与油漆体系的相容性;
超级分散剂 3~5%,又名超分散剂,一种特殊的表面活性剂,其作用是分散色粉防止发花缩短研磨时间增强附着力。
二乙二醇乙醚醋酸酯 2~5%,是慢干溶剂,可增加色浆的贮储性;
有效成分为8~12%的膨润土浆 5~10%,其作用是增加色浆的流变性和防沉效果;
黄色粉 20%,是色浆的主要成分;
二甲苯 20~40%,其作用是对色浆的溶解和稀释;
乙酸丁酯 20~30%,其作用是对色浆的溶解和稀释。
优选的,该无树脂色浆按质量百分比计由如下组分组成:
丙二醇甲醚醋酸酯 22%,
超级分散剂三星化工的BES-3600 4%,
二乙二醇乙醚醋酸酯 5%,
有效成分为10%的膨润土浆 5%,
83#黄色粉 20%,
二甲苯 20%,
乙酸丁脂 24%。
本发明具有如下有益效果:
本发明采用超级高分子量的分散剂和助剂一起直接研磨颜料,获得无树脂色浆,解决了有树脂色浆的局限性,由于不含树脂,因此该色浆与所有涂料体系有很好的相容性。
具体实施方式
下面结合实施例对本发明进行详细的说明,实施例仅是本发明的优选实施方式,不是对本发明的限定。
实施例1
一种无树脂色浆,按质量百分比计由如下组分组成:
丙二醇甲醚醋酸酯PMA 22%,
超级分散剂河南新乡三星化工的BES-3600 4%,
二乙二醇乙醚醋酸酯BDGA 5%,
有效成分为10%的膨润土浆 5%,
83#黄色粉(P.Y.83) 20%,
二甲苯 20%,
乙酸丁脂 24%。
该无树脂色浆的制备方法为:
1制浆:按方加入PMA/BES-3600/BDGA/膨润浆分散10分钟,再加入PY83/二甲苯/用乙酸丁酯洗净缸边分散20分钟。
2研磨:按浆和玻璃珠重量比为1:2在快手进行研磨到细度小于15微米。
本实施例制备的无树脂色浆经测试,与各种涂料体系具有良好的相容性。
色浆与涂料的相容性测试方法为:
指研法取白漆100克,加入2-3克待试色浆,充分搅匀后,涂布在被涂物表面,待快要凝结时,用手指研磨涂膜表层部分,待漆膜干透后,观察用手指研擦过和未经研擦过的地方是否有色差,如差别较大,则色浆与所测试涂料的相容性不好,以此色浆调出的涂料易产生浮色现象。如颜色相同,一般不会产生浮色现象。
测试结果如下:
涂料体系 | 测试结果 | 相容性 |
聚氨脂体系 | 较相应的有树脂效果好 | 优 |
不饱和体系 | 较相应的有树脂效果好 | 优 |
丙烯酸体系 | 较相应的有树脂效果好 | 优 |
实施例2
一种无树脂色浆,按质量百分比计由如下组分组成:
丙二醇甲醚醋酸酯PMA 25%,
超级分散剂——河南新乡三星化工的BES-3600 3%,
二乙二醇乙醚醋酸酯BDGA 2%,
有效成分为10%的膨润土浆 10%,
83#黄色粉(P.Y.83) 20%,
二甲苯 20%,
乙酸丁脂 20%。
本实施例制备的无树脂色浆经测试,与各种涂料体系具有良好的相容性。
本实施例无树脂色浆的制备方法和测试方法和实施例1相同。
测试结果如下:
涂料体系 | 测试结果 | 相容性 |
聚氨脂体系 | 较相应的有树脂效果好 | 优 |
不饱和体系 | 较相应的有树脂效果好 | 优 |
丙烯酸体系 | 较相应的有树脂效果好 | 优 |
实施例3
一种无树脂色浆,按质量百分比计由如下组分组成:
丙二醇甲醚醋酸酯PMA 20%,
超级分散剂河南新乡三星化工的BES-3600 5%,
二乙二醇乙醚醋酸酯BDGA 5%,
有效成分为10%的膨润土浆 5%,
83#黄色粉(P.Y.83) 20%,
二甲苯 25%,
乙酸丁脂 20%。
本实施例制备的无树脂色浆经测试,与各种涂料体系具有良好的相容性。
本实施例无树脂色浆的制备方法和测试方法和实施例1相同。
测试结果如下:
涂料体系 | 测试结果 | 相容性 |
不饱和体系 | 较相应的有树脂效果好 | 好 |
聚氨脂体系 | 较相应的有树脂效果好 | 好 |
丙烯酸体系 | 较相应的有树脂效果好 | 好 |
Claims (2)
1.一种无树脂色浆,其特征在于按质量百分比计由如下组分组成:
丙二醇甲醚醋酸酯 20~25%,
超级分散剂 3~5%,
二乙二醇乙醚醋酸酯 2~5%,
有效成分为8~12%的膨润土浆 5~10%,
黄色粉 20%,
二甲苯 20~40%,
乙酸丁酯 20~30%。
2.根据权利要求1所述的无树脂色浆,其特征在于按质量百分比计由如下组分组成:
丙二醇甲醚醋酸酯 22%,
超级分散剂——河南新乡三星化工的BES-3600 4%,
二乙二醇乙醚醋酸酯 5%,
有效成分为10%的膨润土浆 5%,
83#黄色粉 20%,
二甲苯 20%,
乙酸丁脂 24%。