CN103571417B - High-impact hot melt adhesive - Google Patents
High-impact hot melt adhesive Download PDFInfo
- Publication number
- CN103571417B CN103571417B CN201310505464.3A CN201310505464A CN103571417B CN 103571417 B CN103571417 B CN 103571417B CN 201310505464 A CN201310505464 A CN 201310505464A CN 103571417 B CN103571417 B CN 103571417B
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- hot melt
- melt adhesive
- mix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a high-impact hot melt adhesive, which is prepared from the following raw materials in parts by weight: 1.2-2.4 parts of 3-aminopropyltrimethoxysilane, 5-7 parts of linear low-density polyethylene (LLDPE), 2-4 parts of paraffin wax, 2-4 parts of polyethersulfone resin, 19-28 parts of epoxy resin E20, 18-25 parts of C5 petroleum resin, 3-5 parts of cross-linking agent TAC, 7-10 parts of composite filler, 1.5-2.5 parts of dioctyl maleate, and 0.8-1.5 parts of acetyl triethyl citrate.
Description
Technical field
The invention belongs to binding agent field, particularly relate to a kind of hot melt adhesive of high impact-resistant.
Background technology
In recent years, the application of the novel material such as matrix material and plastics on automobile made automobile stick with glue agent and the also sustainable growth of seal gum consumption, and wherein automotive upholstery is the field that tackiness agent consumption increases rapidly.The demand of Automotive upholstery hot melt adhesive gets more and more.
Summary of the invention
The object of this invention is to provide a kind of hot melt adhesive of high impact-resistant.
The present invention adopts following technical scheme to achieve these goals:
A hot melt adhesive for high impact-resistant, is characterized in that, it is obtained by the raw material of following weight parts:
3-aminopropyl trimethoxysilane 1.2-2.4, LLDPE 5-7, paraffin 2-4, polyethersulfone resin 2-4, epoxy resin E20 19-28, C5 petroleum resin 18-25, linking agent TAC3-5, compounded mix 7-10, dioctyl maleate 1.5-2.5, acetyl triethyl citrate 0.8-1.5;
Compounded mix is obtained by the raw material of following weight parts: wilkinite 12-18, celestite powder 4-6, jade powder 3-6, polysiloxane 1.5-1.7, paraffin oil 1-2, aluminium nitride powder 1-2, rosin 1-2, Silane coupling agent KH550 0.3-0.5, Radix Angelicae Sinensis oil 0.2-0.4, silicon carbide 0.2-0.4, Secondary ammonium phosphate 0.1-0.2, dinoctyl phthalate 0.1-0.2, nano-carbon powder 1-2, Graphite Powder 99 1-2, alkylphenol polyoxyethylene 0.4-0.6;
The preparation method of described compounded mix is: preparation method is by after wilkinite, celestite powder, jade powder mixing, 4-5 hour is calcined at 500-550 DEG C, then, take out, be soak 4-6 hour in the sodium hydroxide solution of 8-10% in concentration, take out, deionized water wash, dry, add in suitable quantity of water in the lump with nano-carbon powder and grind, adding 10-15% sodium hydroxide solution adjusts PH to be 8.8-9.5, after ground slurry to 400-500 order, then add hydrochloric acid soln and be adjusted to neutrality, dry, mix with surplus stock, ground and mixed evenly and get final product again.
The hot melt adhesive of described a kind of high impact-resistant, is characterized in that:
Preparation process is:
(1) paraffin, epoxy resin E20 are put into blender and mix for subsequent use;
(2) again compounded mix, polyethersulfone resin are put into blender and mixed for subsequent use;
(3), after all the other raw materials being put into blender mixing, granulation, cooling and pelletizing, to obtain final product.
Beneficial effect of the present invention: epoxy resin of the present invention, compounded mix and all the other materials compatibility are good, after mixing, the fusion time is short, has superior shock resistance, and its development time is short simultaneously, and cohesive strength is high.
Embodiment
A hot melt adhesive for high impact-resistant, it is obtained by the raw material of following weight kg:
3-aminopropyl trimethoxysilane 2.4, LLDPE 7, paraffin 4, polyethersulfone resin 4, epoxy resin E20 28, C5 petroleum resin 25, linking agent TAC5, compounded mix 10, dioctyl maleate 2.5, acetyl triethyl citrate 1.5;
Compounded mix is obtained by the raw material of following weight kg: wilkinite 18, celestite powder 6, jade powder 6, polysiloxane 1.7, paraffin oil 2, aluminium nitride powder 2, rosin 1, Silane coupling agent KH550 0.5, Radix Angelicae Sinensis oil 0.3, silicon carbide 0.4, Secondary ammonium phosphate 0.2, dinoctyl phthalate 0.2, nano-carbon powder 1, Graphite Powder 99 2, alkylphenol polyoxyethylene 0.6;
The preparation method of described compounded mix is: preparation method is by after wilkinite, celestite powder, jade powder mixing, calcines 5 hours, then at 550 DEG C, take out, be soak 6 hours in the sodium hydroxide solution of 10% in concentration, take out, deionized water wash, dry, add in suitable quantity of water in the lump with nano-carbon powder and grind, adding 15% sodium hydroxide solution adjusts PH to be 9.5, after ground slurry to 500 order, then add hydrochloric acid soln and be adjusted to neutrality, dry, mix with surplus stock, ground and mixed evenly and get final product again.
The hot melt adhesive of described a kind of high impact-resistant, preparation process is:
(1) paraffin, epoxy resin E20 are put into blender and mix for subsequent use;
(2) again compounded mix, polyethersulfone resin are put into blender and mixed for subsequent use;
(3), after all the other raw materials being put into blender mixing, granulation, cooling and pelletizing, to obtain final product.
The apparent viscosity of the binding agent of the present embodiment is 5400MPa.s, stripping strength 56N/2.5cm
2, initial bonding strength reaches No. 5 steel balls, open hour 37s, and within 24 hours, thermally-stabilised proterties is stablized.
Claims (2)
1. a hot melt adhesive for high impact-resistant, is characterized in that, it is obtained by the raw material of following weight parts:
3-aminopropyl trimethoxysilane 1.2-2.4, LLDPE 5-7, paraffin 2-4, polyethersulfone resin 2-4, epoxy resin E20 19-28, C5 petroleum resin 18-25, linking agent TAC3-5, compounded mix 7-10, dioctyl maleate 1.5-2.5, acetyl triethyl citrate 0.8-1.5;
Compounded mix is obtained by the raw material of following weight parts: wilkinite 12-18, celestite powder 4-6, jade powder 3-6, polysiloxane 1.5-1.7, paraffin oil 1-2, aluminium nitride powder 1-2, rosin 1-2, Silane coupling agent KH550 0.3-0.5, Radix Angelicae Sinensis oil 0.2-0.4, silicon carbide 0.2-0.4, Secondary ammonium phosphate 0.1-0.2, dinoctyl phthalate 0.1-0.2, nano-carbon powder 1-2, Graphite Powder 99 1-2, alkylphenol polyoxyethylene 0.4-0.6;
The preparation method of described compounded mix is: preparation method is by after wilkinite, celestite powder, jade powder mixing, 4-5 hour is calcined at 500-550 DEG C, then, take out, be soak 4-6 hour in the sodium hydroxide solution of 8-10% in concentration, take out, deionized water wash, dry, add in suitable quantity of water in the lump with nano-carbon powder and grind, adding 10-15% sodium hydroxide solution adjusts PH to be 8.8-9.5, after ground slurry to 400-500 order, then add hydrochloric acid soln and be adjusted to neutrality, dry, mix with surplus stock, ground and mixed evenly and get final product again.
2. the hot melt adhesive of a kind of high impact-resistant according to claim 1, is characterized in that:
Preparation process is:
(1) paraffin, epoxy resin E20 are put into blender and mix for subsequent use;
(2) again compounded mix, polyethersulfone resin are put into blender and mixed for subsequent use;
(3), after all the other raw materials being put into blender mixing, granulation, cooling and pelletizing, to obtain final product.