CN103571193A - High-performance conductive rubber material - Google Patents
High-performance conductive rubber material Download PDFInfo
- Publication number
- CN103571193A CN103571193A CN201310482559.8A CN201310482559A CN103571193A CN 103571193 A CN103571193 A CN 103571193A CN 201310482559 A CN201310482559 A CN 201310482559A CN 103571193 A CN103571193 A CN 103571193A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- good
- polyether
- conductive rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-performance conductive rubber material, comprising the following components in parts by weight: 20-30 parts of silicon rubber, 10-20 parts of polyether rubber, 1-6 parts of vulcanizing agent, 3-5 parts of diethyl dithiocarbamate, 1-5 parts of clay powder, 10-20 parts of acetylene black, 3-5 parts of scorch retarder, 5-8 parts of hydroxyl silicone oil and 1-5 parts of rosin. Compared with the prior art, the mildew proof rubber disclosed by the invention adopts the silicon rubber and the polyether rubber as main raw materials. The polyether rubber has good tensile strength, good low-temperature flexibility and good electrical insulating property, so that the product disclosed by the invention has excellent electrical conductivity and shielding effect, excellent electrical insulating property, good air permeability, good oxidative resistance and high and low temperature resistance, can be used in a bad environment, and is easy to process and mold.
Description
Technical field
The present invention relates to a kind of high performance conductive rubber material.
Background technology
At present, on market main mainly with carbon black the electro-conductive material as conducting medium, polymer base-material mainly adopts natural rubber, terpolymer EP rubber, isoprene-isobutylene rubber etc., but they exist the low and easy shortcoming such as aging of conductivity.Based on this, invented and take silicon rubber as carrier, the conductive rubber making by adding conductive filler material therein, the performances such as it has excellent electric and physical property, and conductivity is good, ageing-resistant, high-low temperature resistant, can be applied to the Military Electronic Equipment such as Aeronautics and Astronautics, naval vessel, communication terminal, notebook computer, digital audiovisual and signal equipment etc.
Summary of the invention
The deficiency existing for prior art, technical problem to be solved by this invention is to provide a kind of machinery, good physical performance, the high performance conductive rubber material that electroconductibility is high and fungicidal properties is good.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of high performance conductive rubber material, is grouped into by the one-tenth of following weight part:
Silicon rubber 20~30;
Polyether rubber 10~20;
Vulcanizing agent 1~6;
Diethyldithiocar bamic acid 3~5;
Potter's clay powder 1~5;
Shawinigan black 10~20;
Scorch retarder 3~5;
Hydroxy silicon oil 5~8;
Rosin 1~5.
The advantage of the high performance conductive rubber material of the present invention is: compared with prior art, it is main raw material that mildewproof rubber of the present invention adopts silicon rubber and polyether rubber, because polyether rubber has good tensile strength, low temperature is soft, electrical insulating property is good, product of the present invention has good electroconductibility and shield effectiveness, excellent electric insulating quality and good ventilation property, good scale resistance and resistant of high or low temperature can be used in rugged environment; Easily machine-shaping.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further details;
A conductive rubber material, is grouped into by the one-tenth of following weight part:
Silicon rubber 20~30;
Polyether rubber 10~20;
Vulcanizing agent 1~6;
Diethyldithiocar bamic acid 3~5;
Potter's clay powder 1~5;
Shawinigan black 10~20;
Scorch retarder 3~5;
Hydroxy silicon oil 5~8;
Rosin 1~5.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (1)
1. a high-performance conductive rubber, is characterized in that, by the one-tenth of following weight part, is grouped into:
Silicon rubber 20~30;
Polyether rubber 10~20;
Vulcanizing agent 1~6;
Diethyldithiocar bamic acid 3~5;
Potter's clay powder 1~5;
Shawinigan black 10~20;
Scorch retarder 3~5;
Hydroxy silicon oil 5~8;
Rosin 1~5.