CN103568680A - Preparation method for cold decal paper without high-temperature sintering - Google Patents
Preparation method for cold decal paper without high-temperature sintering Download PDFInfo
- Publication number
- CN103568680A CN103568680A CN201210258070.8A CN201210258070A CN103568680A CN 103568680 A CN103568680 A CN 103568680A CN 201210258070 A CN201210258070 A CN 201210258070A CN 103568680 A CN103568680 A CN 103568680A
- Authority
- CN
- China
- Prior art keywords
- gold stamping
- cold
- marble paper
- preparation
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method for cold decal paper without high-temperature sintering. The method comprises the steps of a) coating a layer of gold stamping base oil on gold stamping paper; b) covering a gold foil having a thickness of 1 [mu]m on the treated gold stamping paper by using a gold stamping machine, with the temperature during a gold stamping process being controlled at 65 DEG C and a travelling speed of the gold stamping machine being controlled to be 240 m/h, so as to obtain a crude product of gold stamping decal paper; and c) printing a protective film having one transparent side on the crude product prepared in the step b) of the gold stamping decal paper with a baking temperature of the cold decal paper being 180-220 DEG C. The cold decal paper has no pollution and saves energy during a decoration firing process compared to high-temperature decal paper at present.
Description
Technical field
The present invention relates to a kind of preparation method of marble paper, particularly a kind of preparation method without the cold marble paper of high-temperature firing.
Background technology
Marble paper on porcelain blank surface label, makes porcelain form various colourful patterns by barbecue, is a kind of general using method of porcelain incrustation, is widely used in the production of household china and furnishings decorative ceramics.
Gold ink and platinum ink that the high temperature embossment carved gilded decoration marble paper of existing ceramic use or high temperature embossment carving platinum marble paper use all contain 12% proof gold.Gold ink and platinum ink printing be to after on paper, and the solvent composition in dry run in ink is dispersed in environment and contaminated environment.The marble paper decoration firing of its making needs 1～5 hour on pottery or glass surface in addition, and roasting temperature is from 550 ℃ to 1250 ℃, and this decoration firing process also can discharge pernicious gas in environment, and it is huge to consume energy.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of preparation method without the cold marble paper of high-temperature firing for the existing problem of prior art.The method has low energy consumption and free of contamination advantage.
Technical problem to be solved by this invention can be achieved through the following technical solutions:
A preparation method for the cold marble paper of high-temperature firing, is characterized in that, its preparation process is as follows:
A) on orange cold foil, apply oil of the gold stamping end of last layer;
B) using gilding press is that 1 μ m gold platinum covers on the orange cold foil after step a) is processed by thickness, and in gold stamping process, temperature is controlled at 65 ℃, and the speed of travel of orange cold foil is within 240m/ hour, to obtain gold stamping marble paper crude product;
C) the transparent diaphragm of a side in the gold stamping marble paper crude product printing of preparing in step b);
The baking temperature of this cold marble paper is 180～220 ℃.
In a preferred version of the present invention, in described step, a) can replace by following steps: on orange cold foil, apply oil of the gold stamping end of last layer, and then use pigment ink to apply last layer patterned layer.
In a preferred version of the present invention, in described step, a) can replace by following steps: on orange cold foil, use pigment ink to be coated with and be covered with two-layer patterned layer.
In a preferred version of the present invention, in described step, a) can replace by following steps: on orange cold foil, apply oil of the gold stamping end of last layer, and then use pigment ink painting to be covered with two-layer patterned layer.Described pigment ink is the mixture of polyacrylic resin and inorganic pigment.
Owing to having adopted technical scheme as above, the present invention compares with existing high temperature marble paper, in pollution-free and decoration firing process, saves the energy.
The specific embodiment
Below in conjunction with embodiment, specifically describe the present invention.
Embodiment 1
A preparation method for the cold marble paper of high-temperature firing, its preparation process is as follows:
A) on orange cold foil, apply oil of the gold stamping end of last layer;
B) using gilding press is that 1 μ m gold platinum covers on the orange cold foil after step a) is processed by thickness, and in gold stamping process, temperature is controlled at 65 ℃, and the speed of travel of orange cold foil is within 240m/ hour, to obtain gold stamping marble paper crude product;
C) the transparent diaphragm of a side in the gold stamping marble paper crude product printing of preparing in step b).
The baking temperature of this cold marble paper is 180～220 ℃.
Embodiment 2
A preparation method for the cold marble paper of high-temperature firing, its preparation process is as follows:
A) on orange cold foil, apply oil of the gold stamping end of last layer, and then use pigment ink to apply last layer patterned layer;
B) using gilding press is that 1 μ m gold platinum covers on the orange cold foil after step a) is processed by thickness, and in gold stamping process, temperature is controlled at 65 ℃, and the speed of travel of orange cold foil is within 240m/ hour, to obtain gold stamping marble paper crude product;
C) the transparent diaphragm of a side in the gold stamping marble paper crude product printing of preparing in step b).
The baking temperature of this cold marble paper is 180～220 ℃.Described pigment ink is the mixture of polyacrylic resin and inorganic pigment.
Embodiment 3
A preparation method for the cold marble paper of high-temperature firing, its preparation process is as follows:
A) on orange cold foil, apply oil of the gold stamping end of last layer; And then use pigment ink painting to be covered with two-layer patterned layer.
B) using gilding press is that 1 μ m gold platinum covers on the orange cold foil after step a) is processed by thickness, and in gold stamping process, temperature is controlled at 65 ℃, and the speed of travel of orange cold foil is within 240m/ hour, to obtain gold stamping marble paper crude product;
C) the transparent diaphragm of a side in the gold stamping marble paper crude product printing of preparing in step b).
The baking temperature of this cold marble paper is 180～220 ℃.Described pigment ink is the mixture of polyacrylic resin and inorganic pigment.
Embodiment 4
A preparation method for the cold marble paper of high-temperature firing, its preparation process is as follows:
A) on orange cold foil, use pigment ink to be coated with and be covered with two-layer patterned layer;
B) using gilding press is that 1 μ m gold platinum covers on the orange cold foil after step a) is processed by thickness, and in gold stamping process, temperature is controlled at 65 ℃, and the speed of travel of orange cold foil is within 240m/ hour, to obtain gold stamping marble paper crude product;
C) the transparent diaphragm of a side in the gold stamping marble paper crude product printing of preparing in step b).
The baking temperature of this cold marble paper is 180～220 ℃.Described pigment ink is the mixture of polyacrylic resin and inorganic pigment.
Claims (5)
1. without a preparation method for the cold marble paper of high-temperature firing, it is characterized in that, its preparation process is as follows:
A) on orange cold foil, apply oil of the gold stamping end of last layer;
B) using gilding press is that 1 μ m gold platinum covers on the orange cold foil after step a) is processed by thickness, and in gold stamping process, temperature is controlled at 65 ℃, and the speed of travel of orange cold foil is within 240m/ hour, to obtain gold stamping marble paper crude product;
C) the transparent diaphragm of a side in the gold stamping marble paper crude product printing of preparing in step b);
The baking temperature of this cold marble paper is 180～220 ℃.
2. the preparation method of the cold marble paper without high-temperature firing as claimed in claim 1, it is characterized in that, described step a) can replace by following steps: on orange cold foil, apply oil of the gold stamping end of last layer, and then use pigment ink to apply last layer patterned layer.
3. the preparation method of the cold marble paper without high-temperature firing as claimed in claim 1, is characterized in that, described step a) can replace by following steps: on orange cold foil, use pigment ink to be coated with and be covered with two-layer patterned layer.
4. the preparation method of the cold marble paper without high-temperature firing as claimed in claim 1, it is characterized in that, described step a) can replace by following steps: on orange cold foil, apply oil of the gold stamping end of last layer, and then use pigment ink painting to be covered with two-layer patterned layer.
5. the preparation method of the cold marble paper without high-temperature firing as described in claim 1 to 4 any one claim, is characterized in that, described pigment ink is the mixture of polyacrylic resin and inorganic pigment.