CN103568331A - Preparation method and product of glass fabric reinforced thermoplastic polyurethane composite material - Google Patents
Preparation method and product of glass fabric reinforced thermoplastic polyurethane composite material Download PDFInfo
- Publication number
- CN103568331A CN103568331A CN201210285009.2A CN201210285009A CN103568331A CN 103568331 A CN103568331 A CN 103568331A CN 201210285009 A CN201210285009 A CN 201210285009A CN 103568331 A CN103568331 A CN 103568331A
- Authority
- CN
- China
- Prior art keywords
- thermoplastic polyurethane
- fiber
- glass
- fabric
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method and product of a glass fabric reinforced thermoplastic polyurethane composite material. The preparation method comprises the following steps: (1) preparing a thermoplastic polyurethane solution; (2) pouring the thermoplastic polyurethane solution in a molding vessel, drying, cooling and demolding to obtain thermoplastic polyurethane films; (3) overlapping glass fabric between two layers of thermoplastic polyurethane films, heating, pressing and forming so as to immerse the thermoplastic polyurethane in the glass fiber, thus obtaining a glass fabric pre-immersed sheet; (4) clipping and laying the glass fabric pre-immersed sheet obtained in the step (3), hot-pressing and forming to obtain the glass fabric reinforced thermoplastic polyurethane composite material. Compared with the existing method of melting and wetting the thermoplastic plastic, the melting process of the plastic in the pre-immersed sheet is saved, the equipment investment is reduced, the operation is simple, and the thermoplastic polyurethane can be uniformly distributed in fiber-reinforced layer to improve the performance of the obtained laminated composite material.
Description
Technical field
The invention belongs to material technology field, relate to a kind of glass-fiber-fabric and strengthen preparation method of thermoplastic polyurethane composite and products thereof.
Background technology
Continuous fiber reinforced thermoplastic plastic (Continuous Fiber Reinforced Thermoplastic Plastics is called for short CFRTP) is a kind of polymer matrix composite of early 1970s exploitation.It is mainly comprised of thermoplastic resin matrix and continuous fortifying fibre, and resin is evenly distributed between fiber, forms continuous phase, with the locus of anchoring fiber, and in material internal transmitted load, gives the good mechanical property of material, processing characteristics etc.Continuous fiber can adopt glass fibre, carbon fiber, aramid fiber etc., wherein comparatively conventional with glass fibre again.CFRTP has than continuous fiber reinforced thermosetting plastics advantage that following several respects are outstanding: (1) prepreg can long preservation; (2) high comprehensive performance particularly still can keep good mechanical property under high temperature, high humility; (3) moulding wide adaptability, production efficiency are high; (4) goods can repeat processing, regeneration.In recent years, continuous glass fibre reinforced thermoplastic plastics (CGFRTP) is more and more subject to various countries and payes attention to, and research application is very active.Mainly select at present the short reinforcing materials of impregnation time such as chopped strand, long fibre, continuous felt both at home and abroad, but adopt continuous-filament woven fabric to there is more excellent performance as reinforcing material, therefore develop continuous-filament woven fabric enhancing compound polyurethane material significant.
Generally, the need of production of continuous fiber reinforced thermoplastic plastic composite is through two processes: the preparation of (1) sheet material (prepreg); (2) moulding of product.At present, the method for preparing continuous fiber reinforced thermoplastic plastic composite has the multiple technologies of preparing such as solution dipping method, melt impregnation method, powder infusion process, pulpous state resin precipitated method, shuffling method, pellicular cascade method and reaction infusion process.
What the most frequently used, use scale was the widest at present is melt impregnation method, melt impregnation method is by thermoplastic polyurethane heating and melting, again the thermoplastic polyurethane of fusing is immersed in fiber by pressurization, make prepreg, and then prepreg stack heating, pressurization are made to composite.And pellicular cascade method is fiber-reinforced layer and thermoplastic material film's stack, then heat, pressurizeing immerses in reinforcing material plastics, this method has been saved the melting of thermoplastic polyurethane in melt impregnation method, thereby the input that reduces equipment, operates fairly simple, and is convenient to the preparation of composite, owing to having used film, can guarantee the uniformity that thermoplastic polyurethane distributes, can make thermoplastic be evenly distributed in fiber, make high-quality laminated product.
Summary of the invention
The object of the present invention is to provide a kind of glass-fiber-fabric to strengthen method of thermoplastic polyurethane composite and products thereof.
For achieving the above object, the present invention is by the following technical solutions:
Glass-fiber-fabric strengthens a preparation method for thermoplastic polyurethane composite, comprises following steps:
(1) prepare thermoplastic polyurethane solution;
(2) above-mentioned thermoplastic polyurethane solution is poured in molding vessel, dry, cooling demoulding, obtains thermoplastic polyurethane film;
(3) glass-fiber-fabric the is added to centre of two layers of thermoplastic polyurethane film, then heating, extrusion forming, be immersed in glass-fiber-fabric thermoplastic polyurethane, makes glass-fiber-fabric preimpregnation sheet material;
(4) according to composite desired thickness, the cutting of glass-fiber-fabric preimpregnation sheet material, laying that step (3) is made, and hot-forming, obtain glass-fiber-fabric and strengthen thermoplastic polyurethane composite.
In described step (1), thermoplastic polyurethane liquid quality fraction is 5～20%, and solvent is one or more of oxolane, dimethyl formamide, dimethylacetylamide, dimethyl sulfoxide (DMSO), gamma-butyrolacton or 1-METHYLPYRROLIDONE.
Being dried of described step (2) is: the thermoplastic polyurethane solution that step (1) is made is poured in flat vessel, dry 10～30min at 100～130 ℃, then at 160～190 ℃, be placed on 10～30min in vacuum drying oven, remove residual solvent.
The masking vessel surface spraying of described step (2) has releasing agent.
Described releasing agent is selected from polytetrafluoroethylene (PTFE) or silicone, with vaporific ejection, maybe can make thermoplastic polyurethane film take off smoothly the whole coverings of masking inner wall of utensil.Releasing agent plays the effect that thermoplastic polyurethane film does not adhere to masking inner wall of utensil, and be convenient to thermoplastic polyurethane film and take off from masking vessel, not a part for polyurethane film.
The thermoplastic polyurethane of described step (1) is U.S. Lu Borun HS85D thermoplastic polyurethane, and normal temperature lower density is 1.215g/cm
3.
The thickness of the thermoplastic polyurethane film making in described step (2) is 0.071～0.165mm.
In described step (3), heating-up temperature is 220～240 ℃, and moulding pressure is 2～4MPa, and molding time is 30～90s.
The surface density of described glass-fiber-fabric is 400g/m
2the RWR400 product that ，Wei megalith group produces, is made by continuous long glass fiber.
The gel content of the glass-fiber-fabric preimpregnation sheet material making in described step (3) is 30～50%, and wherein gel content is:
In described step (4), hot-forming pressure is 4～6MPa, and temperature is 220～240 ℃, and molding time is 5～10min.
In described step (4), the gel content of glass-fiber-fabric enhancing thermoplastic polyurethane composite is 30～50%.
The glass-fiber-fabric that a kind of said method makes strengthens thermoplastic polyurethane composite.
The gel content of described compound polyurethane material is 30～50%.
The present invention has following beneficial effect:
Method of the present invention is compared with existing molten thermoplastic plastics infiltration method, the pellicular cascade legal system that the present invention adopts strengthens thermoplastic polyurethane composite for glass-fiber-fabric, saved the melting of plastics in preimpregnation sheet material, reduced the input of equipment, operate fairly simple, and can make thermoplastic polyurethane be evenly distributed to fiber-reinforced layer, improved the performance of gained laminar composite.The method that the present invention prepares glass-fiber-fabric enhancing thermoplastic polyurethane composite is simpler, feasible, is applicable to medium-sized and small enterprises and scientific research institution and uses.
The specific embodiment
Now by following embodiment, the present invention is further illustrated.
Following glass-fiber-fabric is the RWR400 product that megalith group produces, and by continuous long glass fiber, is made, and surface density is 400g/m
2.
Following thermoplastic polyurethane is U.S. Lu Borun HS85D thermoplastic polyurethane, and normal temperature lower density is 1.215g/cm
3.
Embodiment 1
(1) take thermoplastic polyurethane, thermoplastic polyurethane is added in tetrahydrofuran solvent, under heating, be stirred to completely and dissolve, the thermoplastic polyurethane solution that preparation mass fraction is 15%;
(2) take thermoplastic polyurethane solution 22.87g prepared by above-mentioned steps (1) and pour the 20 * 20cm that scribbles silicone release agent into
2in flat vessel, dry 20min at 110 ℃, then at 170 ℃, be placed on 10min in vacuum drying oven, cooling demoulding, obtains the thermoplastic polyurethane film that thickness is 0.071mm;
(3) thermoplastic polyurethane film above-mentioned steps (2) being obtained carries out cutting according to the size of glass-fiber-fabric, and cutting size is 15 * 15cm
2by glass-fiber-fabric fiber-reinforced layer and the two-layer thermoplastic polyurethane film stack cutting out, fibre reinforcement is put in centre position, then heats 220 ℃, pressurization 4MPa, molding time 30s, thermoplastic polyurethane is immersed in reinforcing material, the glass-fiber-fabric preimpregnation sheet material that preparation gel content is 30%;
(4) according to the thickness of required composite, glass-fiber-fabric preimpregnation sheet material is carried out to laying, stack, be placed on vulcanizing press laminated into type, pressure is 5MPa, and temperature is 230 ℃, and molding time is 8min, prepare glass-fiber-fabric and strengthen thermoplastic polyurethane composite, its gel content is 30%.
The glass-fiber-fabric making is strengthened to thermoplastic polyurethane composite board and according to GB/T 1449-2005, be prepared into the bend specimen of 15mm * 120mm, carry out performance test, test result is in Table 1.
Embodiment 2
(1) take thermoplastic polyurethane, thermoplastic polyurethane is added in dimethylacetamide solvent, under heating, be stirred to completely and dissolve, the thermoplastic polyurethane solution that preparation mass fraction is 15%;
(2) take thermoplastic polyurethane solution 35.56g prepared by above-mentioned steps (1) and pour the 20 * 20cm that scribbles polytetrafluoroethylene (PTFE) releasing agent into
2in flat vessel, dry 20min at 100 ℃, then at 160 ℃, be placed on 20min in vacuum drying oven,, cooling demoulding, obtains the thermoplastic polyurethane film that thickness is 0.110mm;
(3) thermoplastic polyurethane film above-mentioned steps (2) being obtained carries out cutting according to the size of glass-fiber-fabric, and cutting size is 15 * 15cm
2by glass-fiber-fabric fiber-reinforced layer and the stack of above-mentioned two layers of thermoplastic material film, fibre reinforcement is put in centre position, then heats 230 ℃, pressurization 3MPa, molding time 60s, thermoplastic polyurethane is immersed in reinforcing material, the glass-fiber-fabric preimpregnation sheet material that preparation gel content is 40%;
(4) according to the thickness of required composite, glass-fiber-fabric preimpregnation sheet material is carried out to laying, stack, be placed on vulcanizing press laminated into type, pressure is 4MPa, and temperature is 220 ℃, and molding time is 10min, prepare glass-fiber-fabric and strengthen thermoplastic polyurethane composite, its gel content is 40%.
The glass-fiber-fabric making is strengthened to thermoplastic polyurethane composite board and according to GB/T 1449-2005, be prepared into the bend specimen of 15mm * 120mm, carry out performance test, test result is in Table 1.
Embodiment 3
(1) take thermoplastic polyurethane, thermoplastic polyurethane is added in gamma-butyrolacton or 1-METHYLPYRROLIDONE solvent, under heating, be stirred to completely and dissolve, the thermoplastic polyurethane solution that preparation mass fraction is 15%;
(2) take thermoplastic polyurethane solution 53.33g prepared by above-mentioned steps (1) and pour the 20 * 20cm that scribbles silicone release agent into
2in flat vessel, dry 20min at 110 ℃, then at 170 ℃, be placed on 20min in vacuum drying oven, cooling demoulding, obtains the thermoplastic polyurethane film that thickness is 0.165mm;
(3) thermoplastic polyurethane film above-mentioned steps (2) being obtained carries out cutting according to the size of glass-fiber-fabric, and cutting size is 15 * 15cm
2by glass-fiber-fabric fiber-reinforced layer and the stack of above-mentioned two layers of thermoplastic material film, fibre reinforcement is put in centre position, then heats 240 ℃, pressurization 2MPa, molding time 90s, thermoplastic polyurethane is immersed in reinforcing material, the glass-fiber-fabric preimpregnation sheet material that preparation gel content is 50%;
(4) according to the thickness of required composite, glass-fiber-fabric preimpregnation sheet material is carried out to laying, stack, be placed on vulcanizing press laminated into type, pressure is 6MPa, and temperature is 240 ℃, and molding time is 5min, prepare glass-fiber-fabric and strengthen thermoplastic polyurethane composite, its gel content is 50%.
The glass-fiber-fabric making is strengthened to thermoplastic polyurethane composite board and according to GB/T 1449-2005, be prepared into the bend specimen of 15mm * 120mm, carry out performance test, test result is in Table 1.
Embodiment 4
(1) take thermoplastic polyurethane, thermoplastic polyurethane is added in solvent dimethylformamide, under heating, be stirred to completely and dissolve, the thermoplastic polyurethane solution that preparation mass fraction is 5%;
(2) take thermoplastic polyurethane solution 106.63g prepared by above-mentioned steps (1) and pour the 20 * 20cm that scribbles silicone release agent into
2in flat vessel, dry 10min at 130 ℃, then at 180 ℃, be placed on 30min in vacuum drying oven, and cooling demoulding, obtaining thickness is 0.110mm thermoplastic polyurethane film;
(3) thermoplastic polyurethane film above-mentioned steps (2) being obtained carries out cutting according to the size of glass-fiber-fabric, and cutting size is 15 * 15cm
2by glass-fiber-fabric fiber-reinforced layer and the stack of above-mentioned two layers of thermoplastic material film, fibre reinforcement is put in centre position, then heats 210 ℃, pressurization 3MPa, molding time 60s, thermoplastic polyurethane is immersed in reinforcing material, the glass-fiber-fabric preimpregnation sheet material that preparation gel content is 40%;
(4) according to the thickness of required composite, glass-fiber-fabric preimpregnation sheet material is carried out to laying, stack, be placed on vulcanizing press laminated into type, pressure is 4MPa, and temperature is 220 ℃, and molding time is 10min, prepare glass-fiber-fabric and strengthen thermoplastic polyurethane composite, its gel content is 40%.
The glass-fiber-fabric making is strengthened to thermoplastic polyurethane composite board and according to GB/T 1449-2005, be prepared into the bend specimen of 15mm * 120mm, carry out performance test, test result is in Table 1.
Embodiment 5
(1) take thermoplastic polyurethane, thermoplastic polyurethane is added in dimethyl sulfoxide solvent, under heating, be stirred to completely and dissolve, the thermoplastic polyurethane solution that preparation mass fraction is 20%;
(2) take thermoplastic polyurethane solution 26.66g prepared by above-mentioned steps (1) and pour the 20 * 20cm that scribbles silicone release agent into
2in flat vessel, dry 30min at 120 ℃, then at 190 ℃, be placed on 10min in vacuum drying oven, and cooling demoulding, obtaining thickness is 0.110mm thermoplastic polyurethane film;
(3) thermoplastic polyurethane film above-mentioned steps (2) being obtained carries out cutting according to the size of glass-fiber-fabric, and cutting size is 15 * 15cm
2by glass-fiber-fabric fiber-reinforced layer and the stack of above-mentioned two layers of thermoplastic material film, fibre reinforcement is put in centre position, then heats 210 ℃, pressurization 3MPa, molding time 60s, thermoplastic polyurethane is immersed in reinforcing material, the glass-fiber-fabric preimpregnation sheet material that preparation gel content is 40%;
(4) according to the thickness of required composite, glass-fiber-fabric preimpregnation sheet material is carried out to laying, stack, be placed on vulcanizing press laminated into type, pressure is 4MPa, and temperature is 220 ℃, and molding time is 10min, prepare glass-fiber-fabric and strengthen thermoplastic polyurethane composite, its gel content is 40%.
The glass-fiber-fabric making is strengthened to thermoplastic polyurethane composite board and according to GB/T 1449-2005, be prepared into the bend specimen of 15mm * 120mm, carry out performance test, test result is in Table 1.
Embodiment 6
(1) take thermoplastic polyurethane, thermoplastic polyurethane is added in tetrahydrofuran solvent, under heating, be stirred to completely and dissolve, the thermoplastic polyurethane solution that preparation mass fraction is 8.57%;
(2) take the thermoplastic polyurethane solution 66.69g that above-mentioned steps (1) makes and pour the 20 * 20cm that scribbles silicone release agent into
2in flat vessel, dry 20min at 110 ℃, then at 170 ℃, be placed on 10min in vacuum drying oven, and cooling demoulding, obtaining thickness is 0.118mm thermoplastic polyurethane film;
(3) thermoplastic polyurethane film above-mentioned steps (2) being obtained carries out cutting according to the size of glass-fiber-fabric, and cutting size is 15 * 15cm
2by glass-fiber-fabric fiber-reinforced layer and the two-layer thermoplastic polyurethane film stack cutting out, fibre reinforcement is put in centre position, then heats 220 ℃, pressurization 4MPa, molding time 30s, thermoplastic polyurethane is immersed in reinforcing material, the glass-fiber-fabric preimpregnation sheet material that preparation gel content is 41.67%;
(4) according to the thickness of required composite, glass-fiber-fabric preimpregnation sheet material is carried out to laying, stack, be placed on vulcanizing press laminated into type, pressure is 5MPa, and temperature is 230 ℃, and molding time is 8min, prepare glass-fiber-fabric and strengthen thermoplastic polyurethane composite, its gel content is 41.67%.
The glass-fiber-fabric making is strengthened to thermoplastic polyurethane composite board and according to GB/T 1449-2005, be prepared into the bend specimen of 15mm * 120mm, carry out performance test, test result is in Table 1.
The bending property of table 1 composite
From table 1, embodiment 1-3 and 6 can find out, along with the raising of gel content, bending strength and the bending modulus of composite but decrease, and this is because resin content increases, reduce the relativity of reinforcement glass-fiber-fabric in composite, caused bending strength and bending modulus to reduce.From table 1, embodiment 2,4 and 5 can find out, variable concentrations thermoplastic polyurethane solution is prepared gel content while being 40% composite, and bending strength and bending modulus change less, illustrate that composite material and preparation method thereof of the present invention is more stable.
The above-mentioned description to embodiment is can understand and apply the invention for ease of those skilled in the art.Person skilled in the art obviously can easily make various modifications to these embodiment, and General Principle described herein is applied in other embodiment and needn't passes through performing creative labour.Therefore, the invention is not restricted to the embodiment here, those skilled in the art are according to announcement of the present invention, and not departing from the improvement that category of the present invention makes and revise all should be within protection scope of the present invention.
Claims (10)
1. glass-fiber-fabric strengthens a preparation method for thermoplastic polyurethane composite, it is characterized in that: comprise following steps:
(1) prepare thermoplastic polyurethane solution;
(2) above-mentioned thermoplastic polyurethane solution is poured in molding vessel, dry, cooling demoulding, obtains thermoplastic polyurethane film;
(3) glass-fiber-fabric the is added to centre of two layers of thermoplastic polyurethane film, then heating, extrusion forming, be immersed in glass-fiber-fabric thermoplastic polyurethane, makes glass-fiber-fabric preimpregnation sheet material;
(4) cutting of glass-fiber-fabric preimpregnation sheet material, the laying that step (3) are made, and hot-forming, obtain glass-fiber-fabric and strengthen thermoplastic polyurethane composite.
2. preparation method according to claim 1, it is characterized in that: in described step (1), thermoplastic polyurethane liquid quality fraction is 5～20%, and solvent is one or more of oxolane, dimethyl formamide, dimethylacetylamide, dimethyl sulfoxide (DMSO), gamma-butyrolacton or 1-METHYLPYRROLIDONE;
Or being dried of described step (2) is: the thermoplastic polyurethane solution that step (1) is made is poured in flat vessel, dry 10～30min at 100～130 ℃, then at 160～190 ℃, be placed on 10～30min in vacuum drying oven, remove residual solvent.
3. preparation method according to claim 1, is characterized in that: the masking vessel surface spraying of described step (2) has releasing agent.
4. preparation method according to claim 3, is characterized in that: described releasing agent is selected from polytetrafluoroethylene (PTFE) or silicone.
5. preparation method according to claim 1, is characterized in that: the thermoplastic polyurethane normal temperature lower density of described step (1) is 1.215g/cm
3;
Or the thickness of the thermoplastic polyurethane film that makes of described step (2) is 0.071～0.165mm.
6. preparation method according to claim 1, is characterized in that: in described step (3), heating-up temperature is 220～240 ℃, and moulding pressure is 2～4MPa, and molding time is 30～90s.
7. preparation method according to claim 1, is characterized in that: the gel content of the glass-fiber-fabric preimpregnation sheet material making in described step (3) is 30～50%.
8. preparation method according to claim 1, is characterized in that: in described step (4), hot-forming pressure is 4～6MPa, and temperature is 220～240 ℃, and molding time is 5～10min;
Or in described step (4), the gel content of glass-fiber-fabric enhancing thermoplastic polyurethane composite is 30～50%.
9. the glass-fiber-fabric that in a claims 1-8, arbitrary described method makes strengthens thermoplastic polyurethane composite.
10. glass-fiber-fabric according to claim 9 strengthens thermoplastic polyurethane composite, it is characterized in that: the gel content of described compound polyurethane material is 30～50%.