CN103556799B - The preparation method of honeycomb aluminum wall floor decoration module - Google Patents
The preparation method of honeycomb aluminum wall floor decoration module Download PDFInfo
- Publication number
- CN103556799B CN103556799B CN201310547982.1A CN201310547982A CN103556799B CN 103556799 B CN103556799 B CN 103556799B CN 201310547982 A CN201310547982 A CN 201310547982A CN 103556799 B CN103556799 B CN 103556799B
- Authority
- CN
- China
- Prior art keywords
- honeycomb aluminum
- plate
- mould
- layer
- decorative surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Honeycomb aluminum wall floor decoration module disclosed by the invention, including metal base plate and the decorative surface layer being compounded on described metal base plate surface, a honeycomb aluminum sandwich layer it is provided with between described decorative surface layer and described metal base plate, being provided with one layer of fibrous mesh cloth on a described honeycomb aluminum sandwich layer at least surface, described decorative surface layer, honeycomb aluminum sandwich layer, fibrous mesh cloth and metal base plate are combined with each other by adhesive glue pressure viscosity；Its preparation method is carried out according to the following step order: a, mould installation steps；B, the laying step of decorative surface layer；C, brushing adhesive glue step；D, fibrous mesh cloth lay step；E, bonding honeycomb aluminum sandwich layer step；F, bonding metal base plate step；And g, curing schedule.The beneficial effects of the present invention is: add honeycomb aluminum sandwich layer and make module material more stable, weight is lighter, and fibrous mesh cloth enhances the bending strength of module；The present invention quickly can be prepared in factory, substantially increases work efficiency.
Description
Technical field
The present invention relates to decorative module field, particularly relate to a kind of honeycomb aluminum wall floor decoration module and system thereof
Preparation Method.
Background technology
In building decoration engineering is constructed, the material such as Wall or floor tile, stone material, mosaic is to embody building decoration
Style and use the essential material of functional requirement, Wall or floor tile paving be in decoration construction one important
Subdivisional work.
But, there is " construction continuity cycle length, material in the paving of traditional Wall or floor tile (stone material, mosaic)
Stockpile puts that occupation of land is big, wall ground layer perpendicularity (flatness) require high, artificial environment's impact is many.On-the-spot
In work progress " select brick sequence, cut that edging, water conservation be moistening, mortar preparation, batch ash are pasted, maintenance
Reason seam, filleting cleaning " etc. a series of wet trade operations, will inevitably impact on making of final Wall or floor tile
By safety and sight, and easily produce hollowing, flake, come off, there is odd in brickwork joint width, row's brick,
The quality problems such as oblique angle.Especially this kind of compact space, construction surface between toilet, Tea Room, kitchen
It is limited by various plumbing, the equipment end such as electrically, is less useful for situ wet job execution, its comprehensive labor
Dynamic rate consume generally more than 2.4～3 works/.Therefore, the paving of Wall or floor tile wet trade be become restriction construct into
Degree, labor cost remain high, and affect the main subdivisional work of monolithic architecture decorative effect.
Therefore, research Wall or floor tile scene dry construction technologies is extremely urgent.
Summary of the invention
The technical problem to be solved: for the deficiencies in the prior art, it is provided that one can be in work
Prefabricated honeycomb aluminum wall floor decoration module completing dry method installation at the scene and preparation method thereof, this wall in factory
Ground decoration mould have lightweight, stable material quality good and reverse bending strength advantages of higher.
Technical problem solved by the invention can realize by the following technical solutions:
Honeycomb aluminum wall floor decoration module, including metal base plate and being compounded on described metal base plate surface
Decorative surface layer, is provided with a honeycomb aluminum sandwich layer, described honeybee between described decorative surface layer and described metal base plate
Be provided with one layer of fibrous mesh cloth on a nest aluminum sandwich layer at least surface, described decorative surface layer, honeycomb aluminum sandwich layer,
Fibrous mesh cloth and metal base plate are combined with each other by adhesive glue pressure viscosity.
In a preferred embodiment of the invention, set between described honeycomb aluminum sandwich layer and described decorative surface layer
It is equipped with one layer of described fibrous mesh cloth.
In a preferred embodiment of the invention, set between described honeycomb aluminum sandwich layer and described decorative surface layer
It is equipped with one layer of described fibrous mesh cloth, between described honeycomb aluminum sandwich layer and described metal base plate, is additionally provided with one
The described fibrous mesh cloth of layer.
In a preferred embodiment of the invention, described adhesive glue is composite resin glue.
For preparing the preparation method of above-mentioned honeycomb aluminum wall floor decoration module, the method is according to following step
Rapid order is carried out:
A, mould installation steps, this step is installation mold define honeycomb by mould on the table
The size of aluminum wall floor decoration module；
B, the laying step of decorative surface layer, this step is laying decorative surface layer in the region that mould is defined；
C, brushing adhesive glue step, this step is at the back side brushing adhesive glue of described decorative surface layer；
D, fibrous mesh cloth lay step, and this step is to be laid on adhesive glue by described fibrous mesh cloth；
E, bonding honeycomb aluminum sandwich layer step, this step is that described honeycomb aluminum sandwich layer is laid on described fleece
On Ge Bu；
F, bonding metal base plate step, this step is first at the back side brushing adhesive glue of described honeycomb aluminum sandwich layer,
Again described metal base plate is laid on the back side of described honeycomb aluminum sandwich layer；And
G, curing schedule, this step is the honeycomb aluminum wall ground decoration mould utilizing curing apparatus to not having solidification
Block solidifies, and makes described decorative surface layer, fibrous mesh cloth, honeycomb aluminum sandwich layer and metal base plate mutual
It is adhesively fixed.
In a preferred embodiment of the invention, after described step e, on honeycomb aluminum sandwich layer again
Lay one layer of described fibrous mesh cloth.
In a preferred embodiment of the invention, in described step a, described mould be flat plate mold or
External corner mould or inner corner trim mould.
In a preferred embodiment of the invention, in described step b, defined according to described mould
The size in region and the size of the dalle for described decorative surface layer chosen, calculate for institute
State the quantity of the dalle of decorative surface layer and carry out typesetting design, laying for described according to typesetting design
The dalle of decorative surface layer, carries out staying seam to process by localizer between adjacent described dalle.
In a preferred embodiment of the invention, after completing curing schedule, also include cleaning batch seam
Step, this step is first to take out described localizer, then to the gap between adjacent described dalle
It is cleaned, then gap is carried out batch seam process.
In a preferred embodiment of the invention, the curing apparatus in described step g is hot-press solidifying dress
Put or cold pressing one or more in solidification equipment or light curring unit.
Owing to have employed technical scheme as above, the beneficial effects of the present invention is: add honeycomb aluminum sandwich layer
Making module material more stable, weight is lighter, and fibrous mesh cloth enhances the bending strength of module；This
Bright can quickly prepare in factory, substantially increase work efficiency.
Accompanying drawing explanation
In order to be illustrated more clearly that the embodiment of the present invention or technical scheme of the prior art, below will be to reality
Execute the required accompanying drawing used in example or description of the prior art to be briefly described, it should be apparent that below,
Accompanying drawing in description is only some embodiments of the present invention, for those of ordinary skill in the art,
On the premise of not paying creative work, it is also possible to obtain other accompanying drawing according to these accompanying drawings.
Fig. 1 is the structural representation of the embodiment of the present invention 1.
Fig. 2 is the structural representation of the mould of the embodiment of the present invention 1.
Fig. 3 is the schematic diagram of the decorative surface layer laying step of the embodiment of the present invention 1.
Fig. 4 is the sheet material typesetting schematic diagram of the decorative surface layer of the embodiment of the present invention 1.
Fig. 5 is the schematic diagram of the brushing adhesive glue step of the embodiment of the present invention 1.
Fig. 6 is the schematic diagram of the fibrous mesh cloth laying step of the embodiment of the present invention 1.
Fig. 7 is the schematic diagram of the bonding honeycomb aluminum sandwich layer step of the embodiment of the present invention 1.
Fig. 8 is the structural representation in the curing schedule of the embodiment of the present invention 1.
Fig. 9 is the structural representation of the cleaning batch seam step of the embodiment of the present invention 1.
Figure 10 is the structural representation of the embodiment of the present invention 2.
Figure 11 is the structural representation of the second layer fibrous mesh cloth laying step of the embodiment of the present invention 2.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with being specifically illustrating, the present invention is expanded on further.
Embodiment 1
See Fig. 1, the honeycomb aluminum wall floor decoration module 1000 be given in figure, from internal layer to outer layer, depend on
Secondary include metal base plate 1100, honeycomb aluminum sandwich layer 1300, fibrous mesh cloth 1400 and decorative surface layer 1200.
Decorative surface layer 1200 can use all kinds of Wall or floor tile, ceramic thin plate, lithotome, artificial stone,
PLASTIC LAMINATED, mosaic, art glass etc..
In conjunction with Fig. 2 to Fig. 9, describe the preparation method of honeycomb aluminum wall floor decoration module 1000 in detail, should
Method is carried out according to the following step order:
A, mould installation steps: see Fig. 2, this step is to install in workbench (not shown)
Mould is laid plate 100 and defines tablet cellular aluminum wall floor decoration module by mould laying plate 100
Size, and the size of tablet cellular aluminum wall floor decoration module can arrive working site and measure and calculate
Operating mode, reaches optimum decorative effect.
This mould is laid plate 100 and by one piece of mould flat board 130 and pair of parallel is laid on mould flat board 130
On the long limit location-plate 111 of tablet cellular aluminum wall floor decoration module and pair of parallel be laid on mould
The minor face location-plate 112 of the tablet cellular aluminum wall floor decoration module on flat board 130 is constituted, a block length
The two ends of limit location-plate 111 respectively with one end square crossing of pair of short edges location-plate 112, another block length
The two ends of limit location-plate 111 respectively with the other end square crossing of pair of short edges location-plate 112, such one
Just define to make on mould flat board 130 to long limit location-plate 111 and pair of short edges location-plate 112
The territory, rectangular shaped article preparation area 131 of standby flat wall ground decoration flat sheet mould.Certain long a pair limit location-plate 111
Between distance and pair of short edges location-plate 112 between the flat honeybee that can prepare as required of distance
The size of nest aluminum wall floor decoration module is adjusted.
In order to, during preparing tablet cellular aluminum wall floor decoration module, make long a pair limit location-plate 111
Between size and pair of short edges location-plate 112 between size be relatively fixed, the present embodiment mould put down
Two parallel long limit slide rail 132 minor face slide rails 133 parallel with four it are provided with on plate 130.The longest
The quantity of limit slide rail 132 is also not limited to two, and the quantity of minor face slide rail 133 is also not limited to respectively
Article four, it is also possible to for other number, as long as even number bar.The longest limit slide rail 132 can also be used
Long limit chute replaces, and minor face slide rail 133 can also replace with minor face chute.
Article two, parallel long limit slide rail 132 symmetry sets up separately at two long side edge of mould flat board 130, and one
Each one of limit.Article four, parallel minor face slide rail 133 symmetry sets up the limit of two minor faces at mould flat board 130 separately
At edge, each two；It is spaced a distance between two minor face slide rails 133 on every limit.Long limit is sliding
Rail 132 and minor face slide rail 133 square crossing.
Long a pair limit location-plate 111 is parallel to long limit slide rail 132, pair of short edges location-plate when laying
112 are parallel to minor face slide rail 133 when laying.
After long a pair limit location-plate 111 and pair of short edges location-plate 112 lay, can be on long limit
At least two long limit rotating disc type manual regulating device 210 is installed, at minor face slide rail 133 on slide rail 132
On at least two minor face rotating disc type manual regulating device 220 is installed, the most respectively by two long limit rotating disc types
Manual regulating device 210 moves near long limit location-plate 111 end positions and makes two long limit rotating disc type handss
Conflict at the long side location-plate 111 outer wall near two ends in adjusting rod 211 front end of dynamic adjusting means 210
On, more respectively two minor face rotating disc type manual regulating devices 220 are moved near minor face location-plate 112 liang
End position also makes adjusting rod 221 front end of two minor face rotating disc type manual regulating devices 220 conflict at minor face
Side location-plate 112 is on the outer wall at two ends.Rotate turning on long limit rotating disc type manual regulating device 210
Distance between dish 212 i.e. long a pair limit location-plate 111 of adjustable, rotates minor face rotating disc type and manually regulates
Distance between rotating disk 222 on device 220 i.e. adjustable pair of short edges location-plate 112 is many to adapt to
Plant the size of wall ground decoration flat sheet mould.
If inner corner trim formula honeycomb aluminum wall floor decoration module to be prepared or external corner formula honeycomb aluminum wall ground dress certainly
Decorations module, it is only necessary to mould flat board 130 is replaced with staged Die and mould plate and by long limit location-plate 111
Or one of them long limit location-plate changing l-shaped shape of minor face location-plate 112 or minor face location-plate are allowed to shape
Becoming external corner mould or inner corner trim mould, remaining can prepare external corner formula honeybee according to the method that the present embodiment is identical
Nest aluminum wall floor decoration module or inner corner trim formula honeycomb aluminum wall floor decoration module.Concrete wall ground decoration mould,
Can be prepared according to the concrete shape of honeycomb aluminum wall floor decoration module, about wall ground decoration mould
Preparation method belong to the routine techniques means of those skilled in the art, just prepare external corner formula honeycomb aluminum wall ground
The preparation method of face decorative module or inner corner trim formula honeycomb aluminum wall floor decoration module does not repeats them here.
B, the laying step of decorative surface layer, see Fig. 3, and this step is to lay plate 100 at mould to be defined
Region in lay decorative surface layer 1200, lay, according to mould, the size in region and the choosing that plate is defined
The size of the dalle 311 for decorative surface layer 1200 taken, calculates for decorative surface layer 1200
The quantity of dalle 311 also carries out typesetting design, is used for forming decorative surface layer according to typesetting design laying
The dalle 311 of 1200, is entered by localizer (not shown) between adjacent decoration sheet material 311
Row stays seam to process.Dalle 311 face down is put into during laying mould lay in plate 100.Decoration
The material of sheet material 311 and size can require according to design and select, such as, can select all size
Wall or floor tile, ceramic thin plate, lithotome, artificial stone, PLASTIC LAMINATED, mosaic, art glass etc..
See Fig. 4, between edge's adjacent decoration sheet material that decorative surface layer 1200 contacts with mould 100
Seam uses linear positioner location 310, adopts between the adjacent four packaged decoratice boards in centre of decorative surface layer 1200
Position with cross locator 320, control the gap between adjacent decoration sheet material well.
C, brushing adhesive glue step, see Fig. 5, at the back side brushing composite resin glue of decorative surface layer 1200,
Form one layer of composite resin glue-line；
D, fibrous mesh cloth lay step, see Fig. 6, fibrous mesh cloth 1400 is laid on composite resin
On glue-line；
E, bonding honeycomb aluminum sandwich layer step, see Fig. 7, honeycomb aluminum sandwich layer 1300 be laid on fiber mesh
On the back side of cloth 1400；
F, bonding metal base plate step, first brush one layer of adhesive glue at the back side of honeycomb aluminum sandwich layer 1300,
Base plate 1100 is laid on honeycomb aluminum sandwich layer 1300, is bonded together by binding agent；
G, curing schedule, see Fig. 8, and the honeycomb aluminum wall floor decoration module 1000 made is sent into solidification
Equipment 400 solidifies, curing apparatus 400 can be hot-press solidifying device or cold pressing solidification equipment or
One or several in person's light curring unit, make decorative surface layer 1200 that the stone material that need to be combined constitutes, fine
Dimension grid cloth 1400, honeycomb aluminum sandwich layer 1300 and metal base plate 1100 are adhesively fixed；
H, cleaning batch seam step, see Fig. 9, and this step is first to take out linear positioner location 310 Hes
Cross locator 320, is then cleaned the gap between adjacent decoration sheet material, then carries out gap criticizing
Seam processes, and makes the front of decorative surface layer 1200 have good flatness.
The present invention quickly can be prepared in factory, and the honeycomb aluminum wall floor decoration module prepared
1000 have lightweight, stable material quality bending strength advantages of higher good, reverse, substantially increase work
Efficiency.
Embodiment 2
See Figure 10, the honeycomb aluminum wall floor decoration module 1000 be given in figure, from internal layer to outer layer, depend on
Secondary include metal base plate 1100, ground floor fibrous mesh cloth 1400b, honeycomb aluminum sandwich layer 1300, the second layer
Fibrous mesh cloth 1400a and decorative surface layer 1200.The present embodiment is roughly the same with embodiment 1, its district
Not being, one layer of fibrous mesh cloth is set up at the back side of honeycomb aluminum sandwich layer 1300.Relatively for embodiment 1,
The reverse bending strength of the honeycomb aluminum wall floor decoration module of the present embodiment is higher.
The present embodiment is roughly the same with the preparation process in embodiment 1, and its difference is, honeycomb aluminum sandwich layer
After 1300 lay, lay the step of second layer fibrous mesh cloth 1400a at its back side, such as Figure 11
Shown in.
Honeycomb aluminum wall floor decoration module provided by the present invention can be previously-completed preparation, so in factory
Rear conveyance is to the scene of fitting up, and the prefabricated honeycomb aluminum wall floor decoration module completed is installed to wall to be decorated
On ground, the composite bed simultaneously using grid cloth and honeycomb aluminum sandwich layer to be formed can alleviate honeycomb aluminum wall ground
The weight of decorative module, make honeycomb aluminum wall floor decoration module have lightweight, stable material quality good and
Reversely bending strength advantages of higher, low price.The present invention quickly can be prepared in factory, significantly carries
High work efficiency.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (6)
1. the preparation method of honeycomb aluminum wall floor decoration module, it is characterised in that the method is according to following step
Rapid order is carried out:
A, mould installation steps, this step is that installation mold is laid plate and laid by mould on the table
Plate defines the size of honeycomb aluminum wall floor decoration module；This mould lay plate by one piece of mould flat board and
The long limit location-plate of the pair of parallel tablet cellular aluminum wall floor decoration module being laid on mould flat board and
The minor face location-plate structure of the pair of parallel tablet cellular aluminum wall floor decoration module being laid on mould flat board
Become, the two ends of a block length limit location-plate respectively with one end square crossing of pair of short edges location-plate, another block
The two ends of long limit location-plate respectively with the other end square crossing of pair of short edges location-plate, so long a pair limit
Location-plate and pair of short edges location-plate just define to prepare flat wall ground decoration on mould flat board
The territory, rectangular shaped article preparation area of flat sheet mould；Distance between certain long a pair limit location-plate and pair of short edges location
The size of the tablet cellular aluminum wall floor decoration module that the distance between plate can be prepared as required is carried out
Adjust；
B, the laying step of decorative surface layer, this step is to lay dress in the region that plate is defined laid by mould
Decorations top layer；
C, brushing adhesive glue step, this step is at the back side brushing adhesive glue of described decorative surface layer；
D, fibrous mesh cloth lay step, and this step is to be laid on adhesive glue by described fibrous mesh cloth；
E, bonding honeycomb aluminum sandwich layer step, this step is that described honeycomb aluminum sandwich layer is laid on described fleece
On Ge Bu；
F, bonding metal base plate step, this step is first at the back side brushing adhesive glue of described honeycomb aluminum sandwich layer,
Again described metal base plate is laid on the back side of described honeycomb aluminum sandwich layer；And
G, curing schedule, this step is the honeycomb aluminum wall ground decoration mould utilizing curing apparatus to not having solidification
Block solidifies, and makes described decorative surface layer, fibrous mesh cloth, honeycomb aluminum sandwich layer and metal base plate mutual
It is adhesively fixed.
The preparation method of honeycomb aluminum wall floor decoration module the most as described in the appended claim 1, it is characterised in that
After described step e, honeycomb aluminum sandwich layer re-lays one layer of described fibrous mesh cloth.
3. the preparation method of honeycomb aluminum wall floor decoration module as claimed in claim 1 or 2, its feature exists
In, in described step a, described mould is flat plate mold or external corner mould or inner corner trim mould.
4. the preparation method of honeycomb aluminum wall floor decoration module as claimed in claim 1 or 2, its feature exists
In, in described step b, the size in the region defined according to described mould and choose for institute
State the size of the dalle of decorative surface layer, calculate the quantity of the dalle for described decorative surface layer also
Carry out typesetting design, lay the dalle for described decorative surface layer according to typesetting design, adjacent described
Carry out staying seam to process by localizer between dalle.
5. the preparation method of honeycomb aluminum wall floor decoration module as claimed in claim 4, it is characterised in that
After completing curing schedule, also including cleaning batch seam step, this step is first to take out described localizer,
Then the gap between adjacent described dalle is cleaned, then gap is carried out batch seam process.
6. the preparation method of honeycomb aluminum wall floor decoration module as claimed in claim 1 or 2, its feature exists
In, the curing apparatus in described step g is hot-press solidifying device or cold pressing solidification equipment or photocuring
One or more in device.