CN103556479B - Durability lavender flavor type long-staple cotton/fine denier nylon knitted fabric goods - Google Patents
Durability lavender flavor type long-staple cotton/fine denier nylon knitted fabric goods Download PDFInfo
- Publication number
- CN103556479B CN103556479B CN201310497039.4A CN201310497039A CN103556479B CN 103556479 B CN103556479 B CN 103556479B CN 201310497039 A CN201310497039 A CN 201310497039A CN 103556479 B CN103556479 B CN 103556479B
- Authority
- CN
- China
- Prior art keywords
- fine denier
- denier nylon
- essential oil
- staple cotton
- knitted fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of textile product, particularly relate to and a kind of there are good gas permeability, machine-washable durability lavender flavor type long-staple cotton/fine denier nylon knitted fabric goods.It adopts long-staple cotton and fine denier nylon to be that material knitting forms, and adopts the Final finishing liquid process comprising nanometer Lavender essential oil microcapsule to form; The domain size distribution of nanometer Lavender essential oil microcapsule is 3-15 nanometer, and adopting volume ratio to be the natural lavender essential oil of 6:1-10:1 and camomile essential oil is that raw material is made by fine emulsion polymerization; The preparation method of nanometer Lavender essential oil microcapsule comprises step successively: prepared by base polyurethane prepolymer for use as; Prepared by polyaminoester emulsion; One-step solidification forms preliminary microcapsules; Regelate forms stable microcapsules.The present invention adopts long-staple cotton to be combined the advantage that can give full play to two kinds of fibers with fine denier nylon; Essential oil microcapsules can penetrate in knitted fabric goods, and breaks could discharge fragrance slowly when being subject to the extruding of external force or moving, and extends fragrance remaining time.
Description
Technical field
The present invention relates to a kind of textile product, particularly relate to and a kind of there are good gas permeability, machine-washable durability lavender flavor type long-staple cotton/fine denier nylon knitted fabric goods.
Background technology
Take synthetic fiber at present and generally have terylene (polyester), polyamide fibre (polyamide), polypropylene fibre (polypropylene), spandex (polyurethane), acrylic fibers (polyacrylonitrile) etc.These fibers have different qualities, thus also have different purposes.But general wearing fabric at present, because its fiber is comparatively thick, feel is coarse, flexibility is poor, poor air permeability, water imbibition are poor, be easy to pilling.Along with the raising of people's living standard, the dress for textiles requires also more and more higher.
CN101736433B (2012-9-12) discloses a kind of production method with the fine denier nylon FDY filament of aromatic function, but long filament goods prepared by the method are still to be improved.
Summary of the invention
The object of this invention is to provide and a kind of there are good gas permeability, machine-washable durability lavender flavor type long-staple cotton/fine denier nylon knitted fabric goods.
Above-mentioned technical purpose of the present invention is achieved by the following technical programs:
Durability lavender flavor type long-staple cotton/fine denier nylon knitted fabric goods, adopt long-staple cotton and fine denier nylon to be that material knitting forms, its goods adopt the Final finishing liquid process comprising nanometer Lavender essential oil microcapsule to form; The domain size distribution of described nanometer Lavender essential oil microcapsule is 3-15 nanometer, and adopting volume ratio to be the natural lavender essential oil of 6:1-10:1 and camomile essential oil is that raw material is made by fine emulsion polymerization;
The preparation method of described nanometer Lavender essential oil microcapsule comprises step successively:
(1) base polyurethane prepolymer for use as preparation: first acid adding stirring and adjusting pH value after first polyalcohol 20-85 part and the mixing of second polyalcohol 10-90 part, to 5.0-6.0, is then added 8-30 part MDI isocyanates, 5-10 part additive reacts 10-20min and obtain base polyurethane prepolymer for use as at temperature is 40-50 DEG C; Described first polyalcohol is the polymer of ethylene glycol and propylene glycol, and degree of functionality is 3, hydroxyl value 45-99mgKOH/g; Described second polyalcohol is the polyol of trimethylolpropane and epoxy butane, and epoxy butane content is greater than 60%, hydroxyl value 3-22mgKOH/g; Described additive is one or more in the sodium bicarbonate solution of pentamethylene, normal butane or 5-15%;
(2) polyaminoester emulsion preparation: add after stirring pre-emulsification 5-10min in the aqueous solution of 3-6 part organosiloxane copolymer, 6-10 part emulsifying agent and 30-60 part deionized water composition, adopts homogenous disperse machine dispersion 1-3min to form miniemulsion;
(3) one-step solidification forms preliminary microcapsules: in miniemulsion, add 4-9 part N methyldiethanol amine, natural lavender essential oil that 10-15 part volume ratio is 6:1-10:1 and camomile essential oil be 600-900 rev/min in stir speed (S.S.) and stir 1-3min and obtain preliminary microcapsule solution;
(4) regelate forms stable microcapsules: reduce rotating speed to 500-800 rev/min, add regelate agent and react 10-15min at 45-65 DEG C, then slowly cool to room temperature discharging, obtain nanometer Lavender essential oil microcapsule.
Advantage of the present invention is:
1. adopt long-staple cotton to be combined the advantage that can give full play to two kinds of fibers with fine denier nylon, have general cotton fiber knit product concurrently and there is good hygroscopicity, gas permeability, the advantage such as soft, and the characteristic such as soft comfortable, good hygroscopicity, Machine Washable, quick-drying that nylon knitting goods have; There is the resilience of significant wrinkling resistance and brilliance simultaneously; And overcome cotton knitwear and there is the problems such as yielding, washing shrinkage is large;
2. nanometer Lavender essential oil microcapsule of the present invention can penetrate in knitted fabric goods by dressing liquid subsequently, fragrant microcapsule can be fixed wherein, and break could discharge fragrance slowly when being subject to the extruding of external force or moving, thus improve the slow release of fragrance, extend fragrance remaining time;
3. the present invention adopts interfacial polymerization to form polyurethane cyst wall in preparation nanometer Lavender essential oil microcapsule process, makes natural lavender essential oil and camomile essential oil be dispersed in the coated system of polyurethane uniformly;
4. the camomile adopting natural lavender essential oil and have a diastole nervous function is raw material, arranges long-staple cotton/fine denier nylon knitted fabric, gives long-staple cotton/fine denier nylon knitted fabric and have diastole human body and alleviate life stress function, make people relaxed and joyful.Adopt microcapsules technology, make new product lavender flavor type function lasting.This finishing technique new product has the features such as odor type is lasting, balanced and washable, fragrance has diastole human body and alleviates life stress function, make people relaxed and joyful, rich taste, for making high-grade T-shirt, cotta, long sleeves, Lingerie, underpants etc. and real silk nightwear.
As preferably, the emulsifying agent in described step (2) is be the lauryl sodium sulfate that mixes of 2-5:1 and neopelex according to mass ratio.
As preferably, in described step (2), be added with 2.2-3.8 part magnesium monohydrogen phosphate.
Magnesium monohydrogen phosphate as pH buffer, can regulate the pH value of emulsion, makes emulsion polymerisation evenly stable.
As preferably, the described regelate agent in described step (4) is liquid amido organosilicon.
As preferably, the volume ratio of the regelate agent in described step (4) and described preliminary microcapsule solution is 1:40-60.
As preferably, the volume ratio of described natural lavender essential oil and camomile essential oil is 8:1.
As preferably, the warp thread of described knitted fabric goods comprises long-staple cotton and fine denier nylon silk, and every 1 long-staple cotton and every 3 fine denier nylon silks form one through organization unit; Weft yarn is fine denier nylon silk, and every 3 fine denier nylon silks form a latitude organization unit; The adjacent spacing through organization unit is 0.3-0.5mm, and the spacing of adjacent weft organization unit is 0.25-0.4mm; Warp-wise and/or the broadwise of described knitted fabric goods are provided with nanometer Lavender essential oil microcapsule.
As preferably, described knitted fabric goods per square inch in warp thread and weft yarn summation be 300-350 root.
As preferably, described warp thread is that 16 long-staple cotton and 150D fine denier nylon silk combine.
As preferably, the spacing of each described long-staple cotton in organization unit and fine denier nylon silk is 0.1-0.2mm, and the spacing of each described adjacent fine denier nylon silk in organization unit is 0.15-0.25mm.
As preferably, the spacing of the fine denier nylon silk in each described latitude organization unit is 0.08-0.12mm.
Accompanying drawing explanation
Fig. 1 is the schematic diagram of durability lavender flavor type long-staple cotton of the present invention/fine denier nylon knitted fabric goods;
In figure, 1-is through organization unit; 2-latitude organization unit; 3-long-staple cotton; 4-fine denier nylon; 5-Lavender essential oil microcapsule.
Detailed description of the invention
Below in conjunction with accompanying drawing, the present invention is described in further detail.
Embodiment one
As shown in Figure 1, durability lavender flavor type long-staple cotton/fine denier nylon knitted fabric goods, its warp thread comprises long-staple cotton 3 and fine denier nylon silk 4, and every 1 long-staple cotton 3 forms one through organization unit 1 with every 3 fine denier nylon silks 4; Weft yarn is fine denier nylon silk 4, and every 3 fine denier nylon silks 4 form a latitude organization unit 2; The adjacent spacing through organization unit 1 is 0.3mm, and the spacing of adjacent weft organization unit 2 is 0.25mm; The warp-wise of knitted fabric goods and/or broadwise are provided with Lavender essential oil microcapsule 5.Knitted fabric goods per square inch interior warp thread and weft yarn summation are 300.Warp thread is that 16 long-staple cotton 3 combine with 150D fine denier nylon silk 4.Each long-staple cotton 3 in organization unit 1 is 0.1mm with the spacing of fine denier nylon silk 4, and the spacing of each adjacent fine denier nylon silk 4 in organization unit 1 is 0.15mm.The spacing of the fine denier nylon silk 4 in each latitude organization unit 2 is 0.08mm.
These goods adopt the Final finishing liquid process comprising nanometer Lavender essential oil microcapsule to form; The domain size distribution of described nanometer Lavender essential oil microcapsule is 3-15 nanometer, and adopting volume ratio to be the natural lavender essential oil of 6:1 and camomile essential oil is that raw material is made by fine emulsion polymerization;
The preparation method of described nanometer Lavender essential oil microcapsule comprises step successively:
Prepared by base polyurethane prepolymer for use as: first acid adding stirring and adjusting pH value after the first polyalcohol 20 parts and the second polyalcohol 10 parts mixing, to 5.0-6.0, is then added 8 parts of MDI isocyanates, 5 parts of additives react 10-20min and obtain base polyurethane prepolymer for use as at temperature is 40 DEG C; Described first polyalcohol is the polymer of ethylene glycol and propylene glycol, and degree of functionality is 3, hydroxyl value 45mgKOH/g; Described second polyalcohol is the polyol of trimethylolpropane and epoxy butane, and epoxy butane content is greater than 60%, hydroxyl value 3mgKOH/g; Described additive is pentamethylene;
Prepared by polyaminoester emulsion: add after stirring pre-emulsification 5min in the aqueous solution of 3 parts of organosiloxane copolymers, 6 parts of emulsifying agents, 2.2 parts of magnesium monohydrogen phosphates and 30 parts of deionized water compositions, adopts homogenous disperse machine dispersion 1min to form miniemulsion; Emulsifying agent is be the lauryl sodium sulfate that mixes of 2:1 and neopelex according to mass ratio;
One-step solidification forms preliminary microcapsules: in miniemulsion, add 4 parts of N methyldiethanol amines, natural lavender essential oil that 105 parts of volume ratios are 6:1 and camomile essential oil be 6000 revs/min in stir speed (S.S.) and stir 1min and obtain preliminary microcapsule solution;
Regelate forms stable microcapsules: reduce rotating speed to 500 rev/min, add liquid amido organosilicon and react 10min at 45 DEG C, the volume ratio of liquid amido organosilicon and described preliminary microcapsule solution is 1:40, then slowly cools to room temperature discharging, obtains nanometer Lavender essential oil microcapsule.
Embodiment two
As shown in Figure 1, durability odor type long-staple cotton/fine denier nylon knitted fabric goods, its warp thread comprises long-staple cotton 3 and fine denier nylon silk 4, and every 1 long-staple cotton 3 forms one through organization unit 1 with every 3 fine denier nylon silks 4; Weft yarn is fine denier nylon silk 4, and every 3 fine denier nylon silks 4 form a latitude organization unit 2; The adjacent spacing through organization unit 1 is 0.5mm, and the spacing of adjacent weft organization unit 2 is 0.4mm; The warp-wise of knitted fabric goods and/or broadwise are provided with Lavender essential oil microcapsule 5.Knitted fabric goods per square inch interior warp thread and weft yarn summation are 350.Warp thread is that 16 long-staple cotton 3 combine with 150D fine denier nylon silk 4.Each long-staple cotton 3 in organization unit 1 is 0.2mm with the spacing of fine denier nylon silk 4, and the spacing of each adjacent fine denier nylon silk 4 in organization unit 1 is 0.25mm.The spacing of the fine denier nylon silk 4 in each latitude organization unit 2 is 0.12mm.
These goods adopt the Final finishing liquid process comprising nanometer Lavender essential oil microcapsule to form; The domain size distribution of described nanometer Lavender essential oil microcapsule is 3-15 nanometer, and adopting volume ratio to be the natural lavender essential oil of 10:1 and camomile essential oil is that raw material is made by fine emulsion polymerization;
The preparation method of described nanometer Lavender essential oil microcapsule comprises step successively:
Prepared by base polyurethane prepolymer for use as: first acid adding stirring and adjusting pH value after the first polyalcohol 85 parts and the mixing of second polyalcohol 10-90 part, to 5.0-6.0, is then added 30 parts of MDI isocyanates, 10 parts of additives react 20min and obtain base polyurethane prepolymer for use as at temperature is 50 DEG C; Described first polyalcohol is the polymer of ethylene glycol and propylene glycol, and degree of functionality is 3, hydroxyl value 99mgKOH/g; Described second polyalcohol is the polyol of trimethylolpropane and epoxy butane, and epoxy butane content is greater than 60%, hydroxyl value 22mgKOH/g; Described additive is the sodium bicarbonate solution of 5-15%;
Prepared by polyaminoester emulsion: add after stirring pre-emulsification 10min in the aqueous solution of 6 parts of organosiloxane copolymers, 10 parts of emulsifying agents, 3.8 parts of magnesium monohydrogen phosphates and 60 parts of deionized water compositions, adopts homogenous disperse machine dispersion 3min to form miniemulsion; Emulsifying agent is be the lauryl sodium sulfate that mixes of 5:1 and neopelex according to mass ratio;
One-step solidification forms preliminary microcapsules: in miniemulsion, add 9 parts of N methyldiethanol amines, natural lavender essential oil that 15 parts of volume ratios are 10:1 and camomile essential oil be 900 revs/min in stir speed (S.S.) and stir 3min and obtain preliminary microcapsule solution;
Regelate forms stable microcapsules: reduce rotating speed to 800 rev/min, add liquid amido organosilicon and react 15min at 65 DEG C, the volume ratio of liquid amido organosilicon and described preliminary microcapsule solution is 1:60, then slowly cools to room temperature discharging, obtains nanometer Lavender essential oil microcapsule.
Embodiment three
As shown in Figure 1, durability odor type long-staple cotton/fine denier nylon knitted fabric goods, its warp thread comprises long-staple cotton 3 and fine denier nylon silk 4, and every 1 long-staple cotton 3 forms one through organization unit 1 with every 3 fine denier nylon silks 4; Weft yarn is fine denier nylon silk 4, and every 3 fine denier nylon silks 4 form a latitude organization unit 2; The adjacent spacing through organization unit 1 is 0.4mm, and the spacing of adjacent weft organization unit 2 is 0.3mm; The warp-wise of knitted fabric goods and/or broadwise are provided with Lavender essential oil microcapsule 5.Knitted fabric goods per square inch interior warp thread and weft yarn summation are 320.Warp thread is that 16 long-staple cotton 3 combine with 150D fine denier nylon silk 4.Each long-staple cotton 3 in organization unit 1 is 0.15mm with the spacing of fine denier nylon silk 4, and the spacing of each adjacent fine denier nylon silk 4 in organization unit 1 is 0.2mm.The spacing of the fine denier nylon silk 4 in each latitude organization unit 2 is 0.01mm.
These goods adopt the Final finishing liquid process comprising nanometer Lavender essential oil microcapsule to form; The domain size distribution of described nanometer Lavender essential oil microcapsule is 3-15 nanometer, and adopting volume ratio to be the natural lavender essential oil of 8:1 and camomile essential oil is that raw material is made by fine emulsion polymerization;
The preparation method of described nanometer Lavender essential oil microcapsule comprises step successively:
Prepared by base polyurethane prepolymer for use as: first acid adding stirring and adjusting pH value after the first polyalcohol 45 parts and the second polyalcohol 50 parts mixing, to 5.0-6.0, is then added 20 parts of MDI isocyanates, 8 parts of additives react 15min and obtain base polyurethane prepolymer for use as at temperature is 45 DEG C; Described first polyalcohol is the polymer of ethylene glycol and propylene glycol, and degree of functionality is 3, hydroxyl value 69mgKOH/g; Described second polyalcohol is the polyol of trimethylolpropane and epoxy butane, and epoxy butane content is greater than 60%, hydroxyl value 12mgKOH/g; Described additive is normal butane;
Prepared by polyaminoester emulsion: add after stirring pre-emulsification 8min in the aqueous solution of 5 parts of organosiloxane copolymers, 8 parts of emulsifying agents, 3 parts of magnesium monohydrogen phosphates and 50 parts of deionized water compositions, adopts homogenous disperse machine dispersion 2min to form miniemulsion; Emulsifying agent is be the lauryl sodium sulfate that mixes of 3:1 and neopelex according to mass ratio;
One-step solidification forms preliminary microcapsules: in miniemulsion, add 6 parts of N methyldiethanol amines, natural lavender essential oil that 12 parts of volume ratios are 8:1 and camomile essential oil be 800 revs/min in stir speed (S.S.) and stir 2min and obtain preliminary microcapsule solution;
Regelate forms stable microcapsules: reduce rotating speed to 700 rev/min, add liquid amido organosilicon and react 12min at 55 DEG C, the volume ratio of liquid amido organosilicon and described preliminary microcapsule solution is 1:50, then slowly cools to room temperature discharging, obtains nanometer Lavender essential oil microcapsule.
Below the rate of perviousness of goods and measure wicking height are detected:
(1) tester of poisture-penetrability and method
Fabric moisture-penetrability index is rate of perviousness.Rate of perviousness refers under fabric two sides exists the condition of constant water vapor pressure respectively, by the water vapour weight of fabric per unit area in the stipulated time.
Laboratory apparatus: this test adopts the computermatic fabric moisture transmission instrument of YG601-1 type.Test condition: be 38 DEG C in temperature, relative humidity is 90%, and air velocity is test under the condition of 0.3 ~ 0.5m/s.Experimental technique: five samples all got by often kind of sample, all samples damping 24 hours in incubator before test.Loaded by hygroscopic agent in clean dry cup, hygroscopic agent loading height is apart from sample lower surface 3 ~ 4mm place, and makes it become a plane.
Be placed on upward on cup by the knitted fabric product sample test surfaces of embodiment one-embodiment three, load onto packing ring and pressure ring, screw on nut, composition test group is fit.Be placed on fabric balance by cup rapidly and weigh, recording quality, then builds.Load weighted cup is put into chamber, takes out after 1h, claim its quality, record data.The most often organize the mass change before and after assembly moisture absorption.Utilize formula (3-1):
(1-1)
Wherein U is rate of perviousness, and G is the weight (mg) that after a period of time, hygroscopic agent increases, the disengagement area (cm of t to be sample storage time (min), A be steam
2).
Test result is in table 1:
Test result illustrates: rate of perviousness is large, and show that fabric is strong through the ability of steam, then poisture-penetrability is good, and therefore, the poisture-penetrability of fabric embodies the nice and cool performance of fabric.And the rate of perviousness of conventional common goods is generally less than 19%.Illustrate that knitted fabric goods poisture-penetrability of the present invention is good, dress is ventilative.
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; those skilled in the art can make to the present embodiment the amendment not having creative contribution as required after reading this description, as long as but be all subject to the protection of Patent Law in right of the present invention.
Claims (6)
1. durability lavender flavor type long-staple cotton/fine denier nylon knitted fabric goods, adopt long-staple cotton and fine denier nylon to be that material knitting forms, it is characterized in that:
The warp thread of described knitted fabric goods comprises long-staple cotton and fine denier nylon silk, and every 1 long-staple cotton and every 3 fine denier nylon silks form one through organization unit; Weft yarn is fine denier nylon silk, and every 3 fine denier nylon silks form a latitude organization unit; The adjacent spacing through organization unit is 0.3-0.5mm, and the spacing of adjacent weft organization unit is 0.25-0.4mm; Warp-wise and/or the broadwise of described knitted fabric goods are provided with nanometer Lavender essential oil microcapsule;
Goods adopt the Final finishing liquid process comprising nanometer Lavender essential oil microcapsule to form; The domain size distribution of described nanometer Lavender essential oil microcapsule is 3-15 nanometer, and adopting volume ratio to be the natural lavender essential oil of 6:1-10:1 and camomile essential oil is that raw material is made by fine emulsion polymerization;
The preparation method of described nanometer Lavender essential oil microcapsule comprises step successively:
(1) base polyurethane prepolymer for use as preparation: first acid adding stirring and adjusting pH value after first polyalcohol 20-85 part and the mixing of second polyalcohol 10-90 part, to 5.0-6.0, is then added 8-30 part MDI isocyanates, 5-10 part additive reacts 10-20min and obtain base polyurethane prepolymer for use as at temperature is 40-50 DEG C; Described first polyalcohol is the polymer of ethylene glycol and propylene glycol, and degree of functionality is 3, hydroxyl value 45-99mgKOH/g; Described second polyalcohol is the polyol of trimethylolpropane and epoxy butane, and epoxy butane content is greater than 60%, hydroxyl value 3-22mgKOH/g; Described additive is one or more in the sodium bicarbonate solution of pentamethylene, normal butane or 5-15%;
(2) polyaminoester emulsion preparation: add after stirring pre-emulsification 5-10min in the aqueous solution of 3-6 part organosiloxane copolymer, 6-10 part emulsifying agent, 2.2-3.8 part magnesium monohydrogen phosphate and 30-60 part deionized water composition, adopts homogenous disperse machine dispersion 1-3min to form miniemulsion;
(3) one-step solidification forms preliminary microcapsules: in miniemulsion, add 4-9 part N methyldiethanol amine, natural lavender essential oil that 10-15 part volume ratio is 6:1-10:1 and camomile essential oil be 600-900 rev/min in stir speed (S.S.) and stir 1-3min and obtain preliminary microcapsule solution;
(4) regelate forms stable microcapsules: reduce rotating speed to 500-800 rev/min, add regelate agent and react 10-15min at 45-65 DEG C, described regelate agent is liquid amido organosilicon; The volume ratio of regelate agent and described preliminary microcapsule solution is 1:40-60; Then slowly cool to room temperature discharging, obtain nanometer Lavender essential oil microcapsule.
2. durability lavender flavor type long-staple cotton according to claim 1/fine denier nylon knitted fabric goods, it is characterized in that: the spacing of each described long-staple cotton in organization unit and fine denier nylon silk is 0.1-0.2mm, and the spacing of each described adjacent fine denier nylon silk in organization unit is 0.15-0.25mm.
3. durability lavender flavor type long-staple cotton according to claim 2/fine denier nylon knitted fabric goods, is characterized in that: the spacing of the fine denier nylon silk in each described latitude organization unit is 0.08-0.12mm.
4. durability lavender flavor type long-staple cotton according to claim 3/fine denier nylon knitted fabric goods, is characterized in that: described knitted fabric goods per square inch interior warp thread and weft yarn summation are 300-350 root.
5. durability lavender flavor type long-staple cotton according to claim 4/fine denier nylon knitted fabric goods, is characterized in that: described warp thread is that 16 long-staple cotton and 150D fine denier nylon silk combine.
6. the durability lavender flavor type long-staple cotton according to any one of claim 1-5/fine denier nylon knitted fabric goods, is characterized in that: the emulsifying agent in described step (2) is be the lauryl sodium sulfate that mixes of 2-5:1 and neopelex according to mass ratio.