CN103556394A

CN103556394A - Far infrared glue-free cotton and preparing method thereof

Info

Publication number: CN103556394A
Application number: CN201310551522.6A
Authority: CN
Inventors: 陈夕方; 陈静; 潘如如; 苟捷; 李忠健
Original assignee: DANYANG CHAOCHAO GARMENT Co Ltd
Current assignee: DANYANG CHAOCHAO GARMENT Co Ltd
Priority date: 2013-11-08
Filing date: 2013-11-08
Publication date: 2014-02-05
Anticipated expiration: 2033-11-08
Also published as: CN105483933A; CN105483934A; CN105274731A; CN105483937A; CN103556394B; CN105274727A

Abstract

The invention relates to a far infrared glue-free cotton. The far infrared glue-free cotton comprises a far infrared fiber layer, an ES short fiber layer and a polyester fiber layer, which are sequentially laminated up and down; the mass percent of all compositions is 10-20% of far infrared fibers, 20-25% of ES short fibers and 55-70% of polyester fibers. By adding the far infrared function fibers, the far infrared glue-free cotton has the function of emitting far infrared rays with the wavelength of 4-15 microns, and the far infrared rays with the wavelength of 4-15 microns are matched with the radiating wavelength of the far infrared rays of a human body and are easily absorbed by the human body, so the blood circulation and metabolism of the human body are promoted, the oxygen supply state is improved, and the far infrared glue-free cotton has the health-care functions of removing fatigue, restoring strength, relieving a pain symptom and the like; in addition, the far infrared glue-free cotton also has the antibiosis and deodorizing functions and the like; through the antibiosis performance test on the glue-free cotton, the antibacterial rate achieves 37%, and is larger than the stand value of 26% according to the standard issued by the National Ministry of Health, and the test shows that the glue-free cotton has good antibiosis performance.

Description

A kind of far infrared is without collodion and preparation method thereof

Technical field

The present invention relates to Nonwovens In Technology field, what be specifically related to is that a kind of far infrared with antimicrobial health care function is without collodion and preparation method thereof.

Background technology

Very soft without collodion, without glue spraying, free from extraneous odour, non-stimulated to human body, materials are better than gum sprayed cotton, are gum sprayed cotton substitute products.There is the features such as intensity is good, wash resistant, good springiness, good hand touch, softness, smooth, warmth retention property good, environmental protection.Its fluffy softness, smooth well-pressed, be the desirable packing material of all kinds of winter dresses, bedding, household supplies.Yet existing majority without collodion as winter dress filler, through using for a long time, because human body moisture is not in time discharged and do not caused the easy breed bacteria of cotton body, when especially the infant a little less than some resistivities or pregnant woman are used, easily cause allergic phenomenon.

Summary of the invention

Technical problem to be solved by this invention is to provide a kind of far infrared with antimicrobial health care function without collodion and preparation method thereof, this without collodion have promote blood circulation of human body and metabolism, improve for oxygen condition, eliminate tired, regain one's strength and the health care such as alleviating pain symptom.

For solving the problems of the technologies described above, the invention provides a kind of far infrared without collodion, comprise: the far IR fibre layer being cascading up and down, ES short fiber layer and polyester fiber layer, the mass percent of described each component is far IR fibre 10%-20%, ES short fiber 20-25%, polyster fibre 55%-70%.

Above-mentioned far infrared is without the preparation method of collodion, and its step comprises:

(1) ceramic powders with far infrared radiation function is pulverized and mixed after sintering, adopts master batch method to carry out spinning, spinning machine temperature is 280-290 ℃, makes far IR fibre;

(2) get by mass percentage 10%-20% far IR fibre, 20-25%ES short fiber, 55%-70% polyster fibre stacks gradually lay from top to bottom, through opener shredding, and successively by combing, lapping, HEAT SETTING, baking oven drying, the operations such as roll-in, rolling, wherein the mode of heating of baking oven is double-layer electric heating, temperature is controlled as 160-170 ℃, time 20-25 second, makes described far infrared without collodion.

Described component and the mass percent with the ceramic powders of far infrared radiation function is: silica 50-55%, zirconium dioxide 20-25%, di-iron trioxide 20-25%, cupric oxide 5-10%.

Technique effect of the present invention: far infrared of the present invention passes through to add far infrared functional fibre without collodion, make this without collodion, have and launch the far infrared function that wavelength is 4-15um, and the far-infrared radiation wavelength of the far infrared of this wavelength and human body matches, be easily absorbed by the body, thereby promote blood circulation of human body and metabolism, improve for oxygen condition, there is the fatigue of elimination, regain one's strength and the health care such as alleviating pain symptom, in addition, also there is the effects such as antibacterial deodourizing, by the present invention is tested without collodion anti-microbial property, bacteriostasis rate reaches 37%, according to health ministry, issue standard, the standard value that bacteriostasis rate is greater than 26%, show to there is good anti-microbial property, therefore this far infrared is suitable for a little less than resistivity without collodion infant or pregnant woman use,

In production technology, baking oven equipment adopts the double-layer electric heating baking oven through transformation, than heated more environmental protection and economy with oil, coal in the past, is heated more even without the cotton body of collodion, does not have heating dead angle, and heat utilization rate is high.Compare after tested, the expense cost ratio of this baking oven in the past oil, coal mode of heating is saved more than 50%, and production environment is significantly improved simultaneously, solve useless conduction oil, the impact of boiler on environment, be beneficial to and realize cleaner production, economize on resources, really realize environmental protection, economic low-power consumption industrial production.

The specific embodiment

Embodiment 1

The far infrared of the present embodiment, without collodion, comprising: the far IR fibre layer being cascading up and down, ES short fiber layer and polyester fiber layer, the mass percent of described each component is far IR fibre 20%, ES short fiber 25%, polyster fibre 55%.

(1) ceramic powders with far infrared radiation function is pulverized and mixed after sintering, adopt master batch method to carry out spinning, spinning machine temperature is 290 ℃, make far IR fibre, wherein, component and the mass percent with the ceramic powders of far infrared radiation function are: silica 50%, zirconium dioxide 25%, di-iron trioxide 20%, cupric oxide 5%;

(2) get by mass percentage 20% far IR fibre, 25%ES short fiber, 55% polyster fibre stacks gradually lay from top to bottom, through opener shredding, and successively by combing, lapping, HEAT SETTING, baking oven drying, the operations such as roll-in, rolling, wherein the mode of heating of baking oven is double-layer electric heating, it is 170 ℃ that temperature is controlled, and 20 seconds time, makes described far infrared without collodion.

Adopt double-layer electric heating baking oven, than in the past, with oil, coal heating environmental protection and economy, be heated more even without the cotton body of collodion, do not have heating dead angle, heat utilization rate is high.Compare after tested, the expense cost ratio of this baking oven in the past oil, coal mode of heating is saved more than 50%, and production environment is significantly improved simultaneously, solve useless conduction oil, the impact of boiler on environment, be beneficial to and realize cleaner production, economize on resources, really realize environmental protection, economic low-power consumption industrial production.

Embodiment 2

The far infrared of the present embodiment, without collodion, comprising: the far IR fibre layer being cascading up and down, ES short fiber layer and polyester fiber layer, the mass percent of described each component is far IR fibre 10%, ES short fiber 20%, polyster fibre 70%.

(1) ceramic powders with far infrared radiation function is pulverized and mixed after sintering, adopt master batch method to carry out spinning, spinning machine temperature is 280 ℃, make far IR fibre, wherein, component and the mass percent with the ceramic powders of far infrared radiation function are: silica 52%, zirconium dioxide 20%, di-iron trioxide 20%, cupric oxide 8%;

(2) get by mass percentage 10% far IR fibre, 20%ES short fiber, 70% polyster fibre stacks gradually lay from top to bottom, through opener shredding, and successively by combing, lapping, HEAT SETTING, baking oven drying, the operations such as roll-in, rolling, wherein the mode of heating of baking oven is double-layer electric heating, it is 160 ℃ that temperature is controlled, and 25 seconds time, makes described far infrared without collodion.

Claims

1. a far infrared is without collodion, it is characterized in that comprising: the far IR fibre layer being cascading up and down, ES short fiber layer and polyester fiber layer, the mass percent of described each component is far IR fibre 10%-20%, ES short fiber 20-25%, polyster fibre 55%-70%.

2. far infrared, without a preparation method for collodion, is characterized in that its step comprises:

3. far infrared as claimed in claim 1 is without the preparation method of collodion, it is characterized in that: described in there is the ceramic powders of far infrared radiation function component and mass percent be: silica 50-55%, zirconium dioxide 20-25%, di-iron trioxide 20-25%, cupric oxide 5-10%.