CN103556253A - Bamboo charcoal and turf composite viscose - Google Patents
Bamboo charcoal and turf composite viscose Download PDFInfo
- Publication number
- CN103556253A CN103556253A CN201310527339.2A CN201310527339A CN103556253A CN 103556253 A CN103556253 A CN 103556253A CN 201310527339 A CN201310527339 A CN 201310527339A CN 103556253 A CN103556253 A CN 103556253A
- Authority
- CN
- China
- Prior art keywords
- bamboo charcoal
- rotten mosses
- peat composed
- slurry
- viscose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to bamboo charcoal and turf composite viscose, belonging to the technical field of viscose production. The composite viscose is prepared by the steps of using cellulose fiber pulp as a raw materials to prepare viscose, then adopting injection before spinning to inject bamboo charcoal pulp and turf pulp into the viscose, mixing the pulp with a static mixer and then carrying out wet spinning and aftertreatment, thus obtaining the finished product. The invention provides the new carbon composite viscose product which can reduce the production cost and meet the special requirements of the product; the problem in the prior art that different kinds of carbon pulp can not be mixed uniformly is solved through selection of the index parameters of various carbon pulp in the raw materials and the carbon pulp can be mixed uniformly with the static mixer, thus improving the spinnability in the spinning process, avoiding affecting aftertreatment and ensuring the dyeing uniformity and color fastness during dyeing.
Description
Technical field
The present invention relates to a kind of activated carbon composite viscose, more particularly, the present invention relates to a kind of bamboo charcoal, peat composed of rotten mosses composite viscose fiber, belong to viscose production technical field.
Background technology
Bamboo charcoal is that to take 3 years above high mountain mao bamboons of life be raw material, a kind of charcoal forming through nearly thousand degree high-temperature firings.Bamboo charcoal has loose structure, the fine and closely woven porous of its molecule, and quality is hard.There is very strong adsorption capacity, can purify air, eliminate peculiar smell, moisture absorption mildew-resistant, antibacterial expelling parasite.Contact the absorbing sweat that can dry with human body, promote blood circulation of human body and metabolism, fatigue-relieving.After science is refined processing, be widely used in daily life.
In agricultural, bamboo charcoal can be used as the carrier of a kind of edaphon and organic nutrition composition, contains the required a part of mineral matter of biological growth, can keep good nutrient balance.
In material industry, bamboo charcoal can be made into a part of advanced composite material (ACM), as Ultramicro-powder bamboo carbon cloth, bamboo charcoal ceramic porous article, powder compacting composite, the filler that can also make degradation plastic, feed addictive, wood-based plate etc.
In architectural decoration, bamboo charcoal is placed under building bottom or floor, there is protection against the tide, mildew-resistant, insect protected, improve the effect of environment.Because bamboo charcoal has automatic humidifying function, and effect is sustained, therefore it is much better than China, generally under building, places at present the method for quick lime.Bamboo charcoal powder is for building coating processing, and prospect is boundless.Along with the improvement of resident living quality, the special-purpose bamboo charcoal in floor liking of the laid people of being subject to and advocating of environmental protection circle together with wood floors that nowadays bamboo charcoal particle is packed.
In environmental protection; bamboo charcoal is good purifying water treating agent; bamboo charcoal is placed in to water; residual harmful chemical and the foul smell in water in can adsorbed water, the improvement of administering river course, sewage, particularly municipal sewage with bamboo charcoal particle; not only can purify water; can also remove stink, beautify the environment, particular significant effect.
In medical and health, in bamboo charcoal, contain the compositions such as acetic acid, ether, alcohol, the allergy of skin, asthma, beriberi are had to effect.Long-term bamboo charcoal toothpaste, perfumed soap, mildy wash, cosmetic cream and the bamboo charcoal of using bathed, and can promote skin keratin softening, makes skin brightening salubrious, smooth soft and moist, plays the effect of nursing skin.
Aspect purifying air, the bamboo charcoal that utilizes each position of mao bamboon to fire, is made into damping charcoal, workmanship, as bamboo root charcoal, thick bamboo tube charcoal, charcoal wineglass, the charcoal gaily decorated basket etc.
In daily life, can make daily necessities, bedding according to the characteristic of bamboo charcoal, and refrigerator taste removal is fresh-keeping, the special-purpose charcoal bag of wardrobe mildew-resistant dehumidifying.
In processed food industry, developed in recent years the edible product such as bamboo charcoal peanut, bamboo charcoal dessert, on these food, wrap up one deck bamboo charcoal, edible together in company with food, can play the effect of clean stomach.
In addition, in viscose industry, by cellulosic material, extract pure methylcellulose, be called pulp.With caustic soda, carbon disulfide, process, obtain orange-yellow sodium cellulose xanthate, then be dissolved in diluted sodium hydroxide solution, become the spinning solution of thickness, be called viscose glue.Utilize the thick bamboo charcoal slurry that bamboo charcoal makes to mix with viscose glue, then by mixed viscose after filtration, after maturation, deaeration, carry out wet spinning.Sodium cellulose xanthate in viscose glue and the effect of sulfuric acid in coagulating bath and decompose, cellulose regenerated and separate out, gained cellulose fibre becomes bamboo-carbon viscose fibre through washing, desulfurization, bleaching, after dry.The bamboo-carbon fibre that said method makes and make clothing and have that smell is pure and fresh, the effect of antibacterial and bacteriostatic and Adsorption peculiar smell.
It is CN1607271 that State Intellectual Property Office discloses a publication number in 2005.4.20, and name is called the patent of invention of " a kind of bamboo-carbon viscose fibre and manufacture method thereof ", and this patent discloses a kind of bamboo-carbon viscose fibre and manufacture method thereof.This bamboo-carbon viscose fibre, is characterized in that a kind of viscose that contains bamboo charcoal.The manufacture method of this bamboo-carbon viscose fibre, include glue operation and spinning process, it is characterized in that: bamboo charcoal is carried out after selected, coarse crushing, dedusting, removal of impurities, be crushed to again the bamboo charcoal micropowder preparation section of fineness≤0.5 micron, bamboo charcoal micropowder and dispersant S are put into water and make bamboo charcoal water and milk slurry operation, in glue operation, increased with two layers of poplin cloth filter cloth and carried out the step of filtering for the 4th time, above-mentioned bamboo charcoal has been carried out respectively to spinning on long filament frame and short silk spinning machine and can obtain the viscose filament yarn and the short silk that contain bamboo charcoal.The present invention is owing to having added bamboo charcoal micropowder in viscose glue, thereby has place to go peculiar smell with existing viscose ratio, distributes the remarkable result of simple and elegant delicate fragrance, antibacterial and bacteriostatic health-care function.
It is CN1807711 that State Intellectual Property Office discloses a publication number in 2006.7.26, and name is called the patent of invention of " bamboo-carbon viscose fibre and manufacture method thereof ", and this patent discloses bamboo-carbon viscose fibre and manufacture method thereof.This bamboo-carbon viscose fibre, contains bamboo charcoal micropowder and bamboo vinegar.The manufacture method of this bamboo-carbon viscose fibre, comprises glue operation and spinning process, in its glue operation, carry out the preparation of viscose solution and carry out the preparation of bamboo charcoal micropowder emulsion.The preparation of bamboo charcoal micropowder emulsion is in deionized water, to add after dispersant and bamboo charcoal micropowder, stir until obtain finely dispersed bamboo charcoal micropowder emulsion, in spinning process, viscose solution is mixed with described bamboo charcoal micropowder emulsion, then deliver to spinning machine and make fiber.Therefore the present invention compared with prior art, turns, kind is convenient, and the bamboo-carbon viscose fibre quality making is better, and performance is more stable.
It is CN101709512A that State Intellectual Property Office discloses a publication number in 2010.5.19, name is called the patent of invention of " a kind of high-whiteness bamboo-charcoal viscose fiber and manufacture method thereof ", the manufacture method of a kind of high-whiteness bamboo-charcoal viscose fiber that this patent provides, comprise: to take bamboo chemical fibres pulp, be that main raw material floods, squeezing, pulverize, experienced, yellow, dissolve, deaeration, filter, spinning, post processing and baking operation, in process, add Nai Nabai magma material, the percentage by weight that described Nai Nabai magma material accounts for alpha cellulose is 0.5% ~ 10%.The present invention adds Nai Nabai magma material in the manufacture process of bamboo-carbon viscose fibre, produce high-whiteness bamboo-charcoal viscose fiber, no longer as existing bamboo-carbon viscose fibre, only have black or grey, but there is higher whiteness, whiteness >=60%, can adopt multiple dyestuff to dye, and there is bacteria resistance, far-infrared transmitting function, negative oxygen ion function, there is wider Application Areas.
In above-mentioned three prior aries, all mentioned bamboo-carbon viscose fibre and preparation method thereof, the preparation method of bamboo charcoal slurry, has also mentioned the advantage that bamboo-carbon viscose fibre brings.Except bamboo charcoal, also have other natural carbons, as the peat composed of rotten mosses etc.
The peat composed of rotten mosses has another name called peat, is also called mud coal, is the product in formation process of bog, be formed at the Quaternary Period, by the residual body of limnocryptophyte, under the anaerobic condition of many water, can not decompose accumulation completely and form, contain large quantity of moisture and the plant residue thoroughly not decomposed, humus and a part of mineral matter.The content of organic matter is more than 30%, and quality is soft to be easy to fragmentaryly, and proportion 0.7-1.05, is brown or black more, has flammable and air-breathing property, and pH value is generally 5.5-6.5, is subacidity and reacts, and is layered arrangement, is called peat horizon.
In prior art, there is no the compounded viscose of polytype charcoal, only contain a kind of viscose function singleness of charcoal.And the charcoal that various charcoals are made slurry cannot mix well, and charcoal slurry skewness in viscose glue, can have influence on the spinnability in spinning technique like this, the oven dry in later stage refining, washing, also can affect the dyeing of later stage fiber.
Summary of the invention
The present invention is intended to solve does not have the compound viscose product making of multiple charcoal in prior art, and the problem that the charcoal that multiple charcoal is made slurry cannot mix, a kind of bamboo charcoal, peat composed of rotten mosses composite viscose fiber are provided, can reduce production costs, meet special product function demand, and various charcoal slurries can mate mutually, mix, with compound bamboo charcoal, the peat composed of rotten mosses composite viscose fiber made of viscose glue.
In order to realize foregoing invention object, its concrete technical scheme is as follows:
A kind of bamboo charcoal, peat composed of rotten mosses composite viscose fiber, it is characterized in that: take cellulose fibre pulp as raw material, be made into viscose glue, then adopt and to spin front injection bamboo charcoal slurry, peat composed of rotten mosses slurry are injected into viscose glue, by static mixer, mix, then carry out wet spinning and post processing and obtain finished product;
Described finished product comprises following according to the raw material of parts by weight meter:
Bamboo charcoal slurry 0.1-10 part
Peat composed of rotten mosses slurry 0.1-5 part
Viscose glue 85-99.8 part;
Described bamboo charcoal slurry is containing alkali 4-9%, and viscosity is 40-50 milli pascal second;
Described peat composed of rotten mosses slurry is containing alkali 3-10%, and viscosity is 35-50 milli pascal second;
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber finished product index are:
Gas permeability >=500mm/s
The adsorptivity of carbon is ammonia absorptivity >=50%
Water-fastness COLOR FASTNESS is 4-5 level
Total carbon content is 0.2-15%.
Bamboo charcoal of the present invention, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, peat composed of rotten mosses composite viscose filament yarn, and dry is 1.6-2.5cN/dtex by force, dry stretching for 16-22%, dry variation≤8% of stretching.
Bamboo charcoal of the present invention, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, the compound viscose staple fibre of the peat composed of rotten mosses, and dry is 2.2-3.5cN/dtex by force, dry stretching for 16-20%, dry strong variation≤18%, fault≤4mg/100g.
The viscosity of viscose glue of the present invention is that 30-50 milli pascal second, methylcellulose content are that 8-9.5%, alkalinity are that 4-15%, degree of ripeness are 7-12 milliliter.
Bamboo charcoal slurry of the present invention comprises following according to the raw material of parts by weight meter:
Bamboo charcoal powder 5-10 part
Dispersant 1-2 part
Thickener 1-5 part
NaOH 4-8 part
Solvent 75-89 part.
The granularity of above-mentioned bamboo charcoal powder is particle diameter≤0.8um.
Above-mentioned bamboo charcoal slurry is made by following methods: in solvent, add after dispersant, bamboo charcoal powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Peat composed of rotten mosses slurry of the present invention comprises following according to the raw material of parts by weight meter:
Peat composed of rotten mosses powder 10-50 part
Dispersant 1-2 part
Thickener 1-5 part
NaOH 4-8 part
Solvent 35-84 part.
The granularity of above-mentioned peat composed of rotten mosses powder is particle diameter≤0.8um.
Above-mentioned peat composed of rotten mosses slurry is made by following methods: in solvent, add after dispersant, peat composed of rotten mosses powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Dispersant of the present invention is still dispersant polyacrylic acid sodium salt.
Thickener of the present invention is cellulose thickener.
Solvent of the present invention is deionized water.
The useful technique effect that the present invention brings:
1, bamboo charcoal of the present invention, peat composed of rotten mosses composite viscose fiber evenly mix spinning afterwards by bamboo charcoal slurry, peat composed of rotten mosses slurry with viscose glue and form, and the adsorptivity of its finished product gas permeability >=500mm/s, carbon is that ammonia absorptivity >=50%, water-fastness COLOR FASTNESS are 4-5 level, always carbon content is 0.2-15%.The activated carbon composite viscose that the present invention makes not only has advantages of bamboo-carbon fibre, also there are other kind charcoals that add, just because of raw material, adopted addition ratio of the present invention, and the alkali content of various charcoal slurries and the selection of viscosity, various charcoals are starched can be compound with viscose glue well, make activated carbon composite viscose, thereby the functional advantage that various charcoal slurries are brought can not affect each other, can, when keeping bamboo-carbon fibre advantage, bring the functional advantage of other charcoal slurries and the functional advantage that other charcoals slurry is combined with bamboo charcoal on the contrary:
Basic functionality advantage:
1) soft and smooth soft warm, there is unit fineness thin, soft; Whiteness is good, color is beautiful; Toughness and ABRASION RESISTANCE are strong, have unique resilience; There is stronger vertical and horizontal intensity, and stable uniform, drapability is good; The soft smooth body of not pricking, also softer than cotton, there is distinctive velvet sense.
2) moisture absorption is ventilative, and cool in summer and warm in winter, cross section has been covered with big and small oval-shaped hole, can transient absorption and evaporate a large amount of moisture, can get rid of unnecessary hot gas and moisture content in body, and do not get angry, do not send out dry.
3) have significant bacteria resistance function, good with the compatibility of human body skin, warmth retention property is good, and taking is good, has good health properties, environmental protection, uvioresistant.
4) superpower absorption affinity, the harmful substances such as PARA FORMALDEHYDE PRILLS(91,95), benzene, toluene, ammonia and dust can be brought into play absorption, decompose the effect of peculiar smell and smelly eliminating.
5) emitting far-infrared, heat accumulation thermal: far infrared emissivity is up to 0.87, energy heat accumulation thermal, temperature rise speed is faster than common cotton fabric, damping, reach the effect dehumidifying with dry, have high equilibrium moisture regain and water retention rate, anion emission concentration is high, is of value to healthy, content of mineral substances is high, has special health care.
Further, the present invention adopt the peat composed of rotten mosses and bamboo charcoal compound, it has brought following advantage:
1) owing to containing a large amount of humus in the peat composed of rotten mosses, thus the heat-insulating property of fiber improved, and moisture absorption, dash, permeability are excellent.
2) in the peat composed of rotten mosses, contain a large amount of organic matters, be mainly cellulose, hemicellulose, lignin, can be distributed in better in viscose glue, improve spinnability.
3) peat composed of rotten mosses quality is soft, makes charcoal slurry and mixes more evenly, also can mix with bamboo charcoal slurry and viscose glue better.
Further, the present invention is owing to adopting the compound viscose of making of multiple charcoal slurry, so have the following advantages:
1) multiple charcoal of the present invention starches that compound viscose has more flourishing specific area and narrower pore-size distribution makes it have adsorption/desorption speed and larger adsorption capacity faster.The structure of viscose of the present invention has flourishing specific area, and the absorption micropore of abundant and marshalling, therefore its adsorptivity is very strong.
2) activated carbon composite viscose adsorbance of the present invention is large, and adsorption rate is fast, and easily, desorption rate is fast in regeneration, good heat resistance, acidproof, alkaline-resisting, there is good electric conductivity and chemical stability, ash is few, and good moldability is easily processed into the forms such as felt, silk, cloth, paper.
3) viscose of the present invention not only can be used as the raw material of clothing, also can be used as industrial absorption, parting material, contain abundant organo-functional group, there is good redox characteristic, the organic substance in gas phase and liquid phase and inorganic impurity are all had to good suction-operated.And there is good desorption and regeneration performance, reusable.Intensity is high, consumes less, has good filling, the adaptability of winding performance and equipment.Under vibration, can not produce filling becomes flexible and excessive closely knit phenomenon.
4) Application Areas is extensive:
Air cleaning: with this material, make air cleaner, can the airborne O of adsorption filtration
3, SO
2, NO
2and the pernicious gas such as stench, poison gas, flue gas, can be used for room, other contaminated indoor air purification of kitchen tools.
Purification of water quality: can remove organic matter in water and heavy metal ion and fustiness smell, bacterium and for the decolouring of water, in the production equipment for water purification for industry, decoloration process and the pure water such as the industry of drinking water, beverage, beer, medicine sugaring, direct drinking.
Sewage disposal: can be used for administering the sewage that the pollution sources such as chemical industry, plating, metallurgy, printing and dyeing, process hides, medicine life produce, remove organic substance, bacterium and organic dyestuff in water.Especially containing the processing of poisonous, the harmful waste water of high volence metal ion.
Organic solvent reclaims: the organic solvent to types such as benzene, ketone, fat, alcohol all can adsorb recovery.Can be used for glue and spray paint, the retracting device of cinefilm equal solvent, in triphen purification recovery device and administer waste gas, in the environment-friendly engineering of sewage.
The healthy prevention: with active carbon fiber felt, make breathing mask, gas defence anti-dust respirator, protective clothing can have good absorption to hide worn-out effect to poisonous gas.This material is also suitable for use in sealing and the partition in radioactivity place, in the engineerings such as the screen screening of radiation device.
Medical usage: owing to thering is chemical stability, heat endurance and irradiation stability, thereby do not have any variation while using various sterilization methods to carry out disinfection.Viscose of the present invention is all very effective to the absorption of the heterotoxin of human body and endogenous toxin, aspect blood filtration, removing toxic substances for oral administration, wound wrapping and treatment, is having important use.
2, the selection of the various charcoal slurry of product of the present invention index parameter has solved in prior art cannot finely starch variety classes charcoal the problem mixing, can evenly mix by static mixer, and make the viscosity of charcoal slurry and viscose glue, alkalinity matches, make it to there is compatibility with viscose glue, do not destroy, affect the stability of viscose glue, can make the charcoal slurry mixing be evenly distributed in viscose glue, can guarantee that the standard profile of charcoal in viscose glue is to be not less than one thousandth in per unit milliliter viscose glue, improved like this spinnability in spinning process, and can not affect the bleaching in post-processed, desulfurization, dry and washing, postprocessing working procedures can be carried out smoothly, when fiber is dyeed, also can guarantee uniformity and the COLOR FASTNESS of dyeing.
3, the present invention is compound by different types of active carbon, makes multiple charcoal composite viscose fiber, can combine according to the demand of the price of raw material and finished product like this, can either reduce production costs, and can meet different functional requirements again.
4, the viscosity of viscose glue of the present invention is that 30-50 milli pascal second, methylcellulose content are that 8-9.5%, alkalinity are that 4-15%, degree of ripeness are 7-12 milliliter.The parameter of above-mentioned viscose glue selects further to make various charcoal slurries to be distributed in viscose glue better.
5, in the raw material of various charcoal slurries of the present invention, increased thickener and the alkali not having in prior art, object is viscosity and the alkalinity that increases charcoal slurry, make it to match with viscosity and the alkalinity of viscose glue, there is compatibility with viscose glue, do not destroy, affect the stability of viscose glue, guaranteed the spinnability of activated carbon composite fiber.
6, the various charcoals of the present invention slurry preparation raw material is selected still dispersant polyacrylic acid sodium salt, contributes to various powdered carbons to be uniformly dispersed in water, and free settling not; Meanwhile, solution liquid, without bubble, does not affect the spinnability of fiber, is the further guarantee of bamboo-carbon fibre spinnability; Equally, it is also in order to guarantee not destroy the spinnability of fiber that thickener is selected cellulose thickener, cellulose thickener is realized the raising of viscosity by the winding of strand, show as in static and low shearing and have high viscosity, it under high shear, is low viscosity, be of value to like this mixing of various charcoal slurries, thereby also just improved the spinnability of later stage fiber.
7, the particle diameter≤0.8 μ m of the powdered carbon in the various charcoal slurries of the present invention, obviously strengthens its adsorption function.
8, production technology of the present invention, front injection is spun in employing, then charcoal slurry is directly sent to the spinning of spinning board after fully mixing by static mixer with viscose glue, after mixing, increase again storage tank and filter plant, dead time in the middle of reducing, avoid mixed liquor to change, and greatly reduced in daily production process, tear filter open, the waste of viscose glue, charcoal slurry while rushing jar and pipeline, reduced expense that environmental wastewater administers and the pollution of environment simultaneously.
The specific embodiment
embodiment 1
, a peat composed of rotten mosses composite viscose fiber, take cellulose fibre pulp as raw material, be made into viscose glue, then adopt and to spin front injection bamboo charcoal slurry, peat composed of rotten mosses slurry are injected into viscose glue, by static mixer, mix, then carry out wet spinning and post processing and obtain finished product;
Described finished product comprises following according to the raw material of parts by weight meter:
0.1 part, bamboo charcoal slurry
0.1 part, peat composed of rotten mosses slurry
85 parts of viscose glues;
Described bamboo charcoal slurry is containing alkali 4%, and viscosity is 50 milli pascal seconds;
Described peat composed of rotten mosses slurry is containing alkali 3%, and viscosity is 50 milli pascal seconds;
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber finished product index are:
Gas permeability >=500mm/s
The adsorptivity of carbon is ammonia absorptivity >=50%
Water-fastness COLOR FASTNESS is 4 grades
Total carbon content is 0.2%.
embodiment 2
, a peat composed of rotten mosses composite viscose fiber, take cellulose fibre pulp as raw material, be made into viscose glue, then adopt and to spin front injection bamboo charcoal slurry, peat composed of rotten mosses slurry are injected into viscose glue, by static mixer, mix, then carry out wet spinning and post processing and obtain finished product;
Described finished product comprises following according to the raw material of parts by weight meter:
10 parts, bamboo charcoal slurry
5 parts, peat composed of rotten mosses slurry
99.8 parts of viscose glues;
Described bamboo charcoal slurry is containing alkali 9%, and viscosity is 40 milli pascal seconds;
Described peat composed of rotten mosses slurry is containing alkali 10%, and viscosity is 35 milli pascal seconds;
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber finished product index are:
Gas permeability >=500mm/s
The adsorptivity of carbon is ammonia absorptivity >=50%
Water-fastness COLOR FASTNESS is 4 grades
Total carbon content is 15%.
embodiment 3
, a peat composed of rotten mosses composite viscose fiber, take cellulose fibre pulp as raw material, be made into viscose glue, then adopt and to spin front injection bamboo charcoal slurry, peat composed of rotten mosses slurry are injected into viscose glue, by static mixer, mix, then carry out wet spinning and post processing and obtain finished product;
Described finished product comprises following according to the raw material of parts by weight meter:
5 parts, bamboo charcoal slurry
2.6 parts, peat composed of rotten mosses slurry
92 parts of viscose glues;
Described bamboo charcoal slurry is containing alkali 6.5%, and viscosity is 45 milli pascal seconds;
Described peat composed of rotten mosses slurry is containing alkali 6.5%, and viscosity is 43 milli pascal seconds;
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber finished product index are:
Gas permeability >=500mm/s
The adsorptivity of carbon is ammonia absorptivity >=50%
Water-fastness COLOR FASTNESS is 5 grades
Total carbon content is 8%.
embodiment 4
, a peat composed of rotten mosses composite viscose fiber, take cellulose fibre pulp as raw material, be made into viscose glue, then adopt and to spin front injection bamboo charcoal slurry, peat composed of rotten mosses slurry are injected into viscose glue, by static mixer, mix, then carry out wet spinning and post processing and obtain finished product;
Described finished product comprises following according to the raw material of parts by weight meter:
9 parts, bamboo charcoal slurry
1.5 parts, peat composed of rotten mosses slurry
90 parts of viscose glues;
Described bamboo charcoal slurry is containing alkali 8%, and viscosity is 42 milli pascal seconds;
Described peat composed of rotten mosses slurry is containing alkali 4.5%, and viscosity is 49 milli pascal seconds;
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber finished product index are:
Gas permeability >=500mm/s
The adsorptivity of carbon is ammonia absorptivity >=50%
Water-fastness COLOR FASTNESS is 5 grades
Total carbon content is 5%.
embodiment 5
On the basis of embodiment 1-4, preferred:
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, peat composed of rotten mosses composite viscose filament yarn, and dry is 1.6cN/dtex by force, and dry stretching is 16%, dry variation≤8% of stretching.
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, the compound viscose staple fibre of the peat composed of rotten mosses, and dry is 2.2cN/dtex by force, and dry stretching is 16%, dry strong variation≤18%, fault≤4mg/100g.
The viscosity of described viscose glue is that 30 milli pascal seconds, methylcellulose content are 8%, alkalinity is 15%, degree of ripeness is 7 milliliters.
embodiment 6
On the basis of embodiment 1-4, preferred:
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, peat composed of rotten mosses composite viscose filament yarn, and dry is 2.5cN/dtex by force, and dry stretching is 22%, dry variation≤8% of stretching.
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, the compound viscose staple fibre of the peat composed of rotten mosses, and dry is 3.5cN/dtex by force, and dry stretching is 20%, dry strong variation≤18%, fault≤4mg/100g.
The viscosity of described viscose glue is that 50 milli pascal seconds, methylcellulose content are 9.5%, alkalinity is 15%, degree of ripeness is 12 milliliters.
embodiment 7
On the basis of embodiment 1-4, preferred:
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, peat composed of rotten mosses composite viscose filament yarn, and dry is 2.1cN/dtex by force, and dry stretching is 19%, dry variation≤8% of stretching.
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, the compound viscose staple fibre of the peat composed of rotten mosses, and dry is 2.85cN/dtex by force, and dry stretching is 18%, dry strong variation≤18%, fault≤4mg/100g.
The viscosity of described viscose glue is that 40 milli pascal seconds, methylcellulose content are 8.75%, alkalinity is 9.5%, degree of ripeness is 9.5 milliliters.
embodiment 8
On the basis of embodiment 1-4, preferred:
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, peat composed of rotten mosses composite viscose filament yarn, and dry is 1.9cN/dtex by force, and dry stretching is 21%, dry variation≤8% of stretching.
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, the compound viscose staple fibre of the peat composed of rotten mosses, and dry is 3.2cN/dtex by force, and dry stretching is 17%, dry strong variation≤18%, fault≤4mg/100g.
The viscosity of described viscose glue is that 35 milli pascal seconds, methylcellulose content are 9.2%, alkalinity is 11%, degree of ripeness is 8 milliliters.
embodiment 9
, a peat composed of rotten mosses composite viscose fiber, described bamboo charcoal slurry comprises following according to the raw material of parts by weight meter:
5 parts of bamboo charcoal powder
1 part of dispersant
1 part of thickener
4 parts, NaOH
75 parts of solvents.
Preferably, the granularity of described bamboo charcoal powder is particle diameter≤0.8um.
Preferably, described bamboo charcoal slurry is made by following methods: in solvent, add after dispersant, bamboo charcoal powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Preferably, described dispersant is still dispersant polyacrylic acid sodium salt.
Preferably, described thickener is cellulose thickener.
Preferably, described solvent is deionized water.
embodiment 10
, a peat composed of rotten mosses composite viscose fiber, described bamboo charcoal slurry comprises following according to the raw material of parts by weight meter:
10 parts of bamboo charcoal powder
2 parts of dispersants
5 parts of thickeners
8 parts, NaOH
89 parts of solvents.
Preferably, the granularity of described bamboo charcoal powder is particle diameter≤0.8um.
Preferably, described bamboo charcoal slurry is made by following methods: in solvent, add after dispersant, bamboo charcoal powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Preferably, described dispersant is still dispersant polyacrylic acid sodium salt.
Preferably, described thickener is cellulose thickener.
Preferably, described solvent is deionized water.
embodiment 11
, a peat composed of rotten mosses composite viscose fiber, described bamboo charcoal slurry comprises following according to the raw material of parts by weight meter:
7.5 parts of bamboo charcoal powder
1.5 parts of dispersants
3 parts of thickeners
6 parts, NaOH
82 parts of solvents.
Preferably, the granularity of described bamboo charcoal powder is particle diameter≤0.8um.
Preferably, described bamboo charcoal slurry is made by following methods: in solvent, add after dispersant, bamboo charcoal powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Preferably, described dispersant is still dispersant polyacrylic acid sodium salt.
Preferably, described thickener is cellulose thickener.
Preferably, described solvent is deionized water.
embodiment 12
, a peat composed of rotten mosses composite viscose fiber, described bamboo charcoal slurry comprises following according to the raw material of parts by weight meter:
9 parts of bamboo charcoal powder
1.2 parts of dispersants
2 parts of thickeners
7 parts, NaOH
78 parts of solvents.
Preferably, the granularity of described bamboo charcoal powder is particle diameter≤0.8um.
Preferably, described bamboo charcoal slurry is made by following methods: in solvent, add after dispersant, bamboo charcoal powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Preferably, described dispersant is still dispersant polyacrylic acid sodium salt.
Preferably, described thickener is cellulose thickener.
Preferably, described solvent is deionized water.
embodiment 13
, a peat composed of rotten mosses composite viscose fiber, it is characterized in that: described peat composed of rotten mosses slurry comprises following according to the raw material of parts by weight meter:
10 parts, peat composed of rotten mosses powder
1 part of dispersant
1 part of thickener
4 parts, NaOH
35 parts of solvents.
Preferably, the granularity of described peat composed of rotten mosses powder is particle diameter≤0.8um.
Preferably, described peat composed of rotten mosses slurry is made by following methods: in solvent, add after dispersant, peat composed of rotten mosses powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Preferably, described dispersant is still dispersant polyacrylic acid sodium salt.
Preferably, described thickener is cellulose thickener.
Preferably, described solvent is deionized water.
embodiment 14
, a peat composed of rotten mosses composite viscose fiber, it is characterized in that: described peat composed of rotten mosses slurry comprises following according to the raw material of parts by weight meter:
50 parts, peat composed of rotten mosses powder
2 parts of dispersants
5 parts of thickeners
8 parts, NaOH
84 parts of solvents.
Preferably, the granularity of described peat composed of rotten mosses powder is particle diameter≤0.8um.
Preferably, described peat composed of rotten mosses slurry is made by following methods: in solvent, add after dispersant, peat composed of rotten mosses powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Preferably, described dispersant is still dispersant polyacrylic acid sodium salt.
Preferably, described thickener is cellulose thickener.
Preferably, described solvent is deionized water.
embodiment 15
, a peat composed of rotten mosses composite viscose fiber, it is characterized in that: described peat composed of rotten mosses slurry comprises following according to the raw material of parts by weight meter:
30 parts, peat composed of rotten mosses powder
1.5 parts of dispersants
3 parts of thickeners
6 parts, NaOH
59.5 parts of solvents.
Preferably, the granularity of described peat composed of rotten mosses powder is particle diameter≤0.8um.
Preferably, described peat composed of rotten mosses slurry is made by following methods: in solvent, add after dispersant, peat composed of rotten mosses powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Preferably, described dispersant is still dispersant polyacrylic acid sodium salt.
Preferably, described thickener is cellulose thickener.
Preferably, described solvent is deionized water.
embodiment 16
, a peat composed of rotten mosses composite viscose fiber, it is characterized in that: described peat composed of rotten mosses slurry comprises following according to the raw material of parts by weight meter:
12 parts, peat composed of rotten mosses powder
1.6 parts of dispersants
4 parts of thickeners
5 parts, NaOH
80 parts of solvents.
Preferably, the granularity of described peat composed of rotten mosses powder is particle diameter≤0.8um.
Preferably, described peat composed of rotten mosses slurry is made by following methods: in solvent, add after dispersant, peat composed of rotten mosses powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
Preferably, described dispersant is still dispersant polyacrylic acid sodium salt.
Preferably, described thickener is cellulose thickener.
Preferably, described solvent is deionized water.
Claims (13)
1. a bamboo charcoal, peat composed of rotten mosses composite viscose fiber, it is characterized in that: take cellulose fibre pulp as raw material, be made into viscose glue, then adopt and to spin front injection bamboo charcoal slurry, peat composed of rotten mosses slurry are injected into viscose glue, by static mixer, mix, then carry out wet spinning and post processing and obtain finished product;
Described finished product comprises following according to the raw material of parts by weight meter:
Bamboo charcoal slurry 0.1-10 part
Peat composed of rotten mosses slurry 0.1-5 part
Viscose glue 85-99.8 part;
Described bamboo charcoal slurry is containing alkali 4-9%, and viscosity is 40-50 milli pascal second;
Described peat composed of rotten mosses slurry is containing alkali 3-10%, and viscosity is 35-50 milli pascal second;
Described bamboo charcoal, peat composed of rotten mosses composite viscose fiber finished product index are:
Gas permeability >=500mm/s
The adsorptivity of carbon is ammonia absorptivity >=50%
Water-fastness COLOR FASTNESS is 4-5 level
Total carbon content is 0.2-15%.
2. a kind of bamboo charcoal according to claim 1, peat composed of rotten mosses composite viscose fiber, it is characterized in that: described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, peat composed of rotten mosses composite viscose filament yarn, dry is 1.6-2.5cN/dtex by force, dry stretching for 16-22%, dry variation≤8% of stretching.
3. a kind of bamboo charcoal according to claim 1, peat composed of rotten mosses composite viscose fiber, it is characterized in that: described bamboo charcoal, peat composed of rotten mosses composite viscose fiber are bamboo charcoal, the compound viscose staple fibre of the peat composed of rotten mosses, dry is 2.2-3.5cN/dtex by force, dry stretching for 16-20%, dry strong variation≤18%, fault≤4mg/100g.
4. a kind of bamboo charcoal according to claim 1, peat composed of rotten mosses composite viscose fiber, is characterized in that: the viscosity of described viscose glue is that 30-50 milli pascal second, methylcellulose content are that 8-9.5%, alkalinity are that 4-15%, degree of ripeness are 7-12 milliliter.
5. a kind of bamboo charcoal according to claim 1, peat composed of rotten mosses composite viscose fiber, is characterized in that: described bamboo charcoal slurry comprises following according to the raw material of parts by weight meter:
Bamboo charcoal powder 5-10 part
Dispersant 1-2 part
Thickener 1-5 part
NaOH 4-8 part
Solvent 75-89 part.
6. a kind of bamboo charcoal according to claim 5, peat composed of rotten mosses composite viscose fiber, is characterized in that: the granularity of described bamboo charcoal powder is particle diameter≤0.8um.
7. a kind of bamboo charcoal according to claim 5, peat composed of rotten mosses composite viscose fiber, it is characterized in that: described bamboo charcoal slurry is made by following methods: in solvent, add after dispersant, bamboo charcoal powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
8. a kind of bamboo charcoal according to claim 1, peat composed of rotten mosses composite viscose fiber, is characterized in that: described peat composed of rotten mosses slurry comprises following according to the raw material of parts by weight meter:
Peat composed of rotten mosses powder 10-50 part
Dispersant 1-2 part
Thickener 1-5 part
NaOH 4-8 part
Solvent 35-84 part.
9. a kind of bamboo charcoal according to claim 8, peat composed of rotten mosses composite viscose fiber, is characterized in that: the granularity of described peat composed of rotten mosses powder is particle diameter≤0.8um.
10. a kind of bamboo charcoal according to claim 8, peat composed of rotten mosses composite viscose fiber, it is characterized in that: peat composed of rotten mosses slurry is made by following methods: in solvent, add after dispersant, peat composed of rotten mosses powder, thickener and NaOH, through stirring, grinding evenly and get final product, described grinding with zirconium ball containing zirconia amount >=95%, the simultaneous grinding frequency >=8 time.
11. according to a kind of bamboo charcoal described in claim 5 or 8, peat composed of rotten mosses composite viscose fiber, it is characterized in that: described dispersant is still dispersant polyacrylic acid sodium salt.
12. according to a kind of bamboo charcoal described in claim 5 or 8, peat composed of rotten mosses composite viscose fiber, it is characterized in that: described thickener is cellulose thickener.
13. according to a kind of bamboo charcoal described in claim 5 or 8, peat composed of rotten mosses composite viscose fiber, it is characterized in that: described solvent is deionized water.