CN103556001A - Zinc-base alloy - Google Patents

Zinc-base alloy Download PDF

Info

Publication number
CN103556001A
CN103556001A CN201310485514.6A CN201310485514A CN103556001A CN 103556001 A CN103556001 A CN 103556001A CN 201310485514 A CN201310485514 A CN 201310485514A CN 103556001 A CN103556001 A CN 103556001A
Authority
CN
China
Prior art keywords
zinc
base alloy
alloy
content
copper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310485514.6A
Other languages
Chinese (zh)
Inventor
陈保云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU LIONY METALS Co Ltd
Original Assignee
CHANGSHU LIONY METALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU LIONY METALS Co Ltd filed Critical CHANGSHU LIONY METALS Co Ltd
Priority to CN201310485514.6A priority Critical patent/CN103556001A/en
Publication of CN103556001A publication Critical patent/CN103556001A/en
Pending legal-status Critical Current

Abstract

The invention discloses a zinc-base alloy. The zinc-base alloy is a Zn-Al-Cu-Mg series alloy and comprises the following elements in percentage by mass: 4%-5.5% of aluminum, 0.8%-1.2% of copper, 0.05%-0.08% of magnesium, not more than 0.02% of iron, not more than 0.001% of lead, not more than 0.002% of cadmium, not more than 0.001% of tin, and the balance of zinc and inevitable impurities, wherein the content of the zinc is no less than 94%, and the total content of the impurities is not more than 0.02%. By the manner, the zinc-base alloy is low in the content of detrimental impurities, has high corrosion resistance, high strength and high wear resistance and is suitable for the casting of metal ornaments and accessories which are high in accuracy and complicated in structure; and castings have high surface quality and are difficult to fracture.

Description

A kind of zinc base alloy
Technical field
The present invention relates to metal alloy compositions field, particularly relate to a kind of zinc base alloy.
Background technology
The main adding elements of zinc base alloy has aluminium, copper and magnesium etc., can be used for casting household electrical appliances accessory, building decoration, fittings of bathroom, lamp decoration part, toy, clothes metal insert etc., foundry goods need have higher surface quality and good surface treatment properties, and the common defect of Zinc Alloy Die Castings is surface blistering.
As everyone knows, in zinc base alloy, inevitably there is detrimental impurity, these detrimental impurity cause intergranular corrosion as lead, cadmium, tin can be gathered in crystal grain intersection, metallic matrix is because of intergranular corrosion fragmentation, and electroplate, accelerated this disaster, be subject to the position of intergranular corrosion can expand and by coating jack-up, cause cast(ing) surface to bubble.Particularly under wet environment, intergranular corrosion meeting makes casting deformation, cracking, even broken.For intergranular corrosion phenomenon, be mainly the detrimental impurity content of controlling in alloy raw material, particularly plumbous, lead also can damage human bone marrow's hemopoietic system and neural system alloy.Therefore the zinc base alloy a kind of with high corrosion resistance energy has become the trend of zinc alloy development.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of zinc base alloy, detrimental impurity content is low, has high corrosion resistance, has high strength, high-wearing feature simultaneously, is suitable for casting high precision, baroque metal decoration accessory, and surface quality of continuous castings is high, be difficult for breaking.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is:
A kind of zinc base alloy is provided, described zinc base alloy is that Zn-Al-Cu-Mg is associated gold, contained element and mass percent are: aluminium 4 %-5.5%, copper 0.8%-1.2%, magnesium 0.05%-0.08%, all the other are zinc and inevitable impurity, described zinc content is not less than 94%, described total impurities is not higher than 0.02%, and contained element and mass percent are: iron not higher than 0.02%, lead not higher than 0.001%, cadmium not higher than 0.002%, tin is higher than 0.001%.
In a preferred embodiment of the present invention, described impurity is not leaded.
In a preferred embodiment of the present invention, the total amount of described aluminium, copper, magnesium elements is 5.5%-6%.
The invention has the beneficial effects as follows: adopt aluminium, copper, the magnesium elements of reasonable ratio, improved the castability of alloy, increased intensity, hardness and the mobility of alloy, and reduced the response capacity to detrimental impurity; Especially effectively reduced the content of the impurity that cannot avoid in alloy, and in impurity, do not contained or containing the harmful metallic element lead of trace, reduced intergranular corrosion, made alloy there is high corrosion resistance.Zinc base alloy of the present invention is suitable for casting high precision, baroque metal decoration accessory, and surface quality of continuous castings is high, is difficult for breaking.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made to more explicit defining.
The embodiment of the present invention comprises:
A kind of zinc base alloy, described zinc base alloy is that Zn-Al-Cu-Mg is associated gold, contained element and mass percent are: aluminium 4 %-5.5%, copper 0.8%-1.2%, magnesium 0.05%-0.08%, all the other are zinc and inevitable impurity, described zinc content is not less than 94%, described total impurities is not higher than 0.02%, and contained element and mass percent are: iron not higher than 0.02%, lead not higher than 0.001%, cadmium not higher than 0.002%, tin is higher than 0.001%.
Wherein, described impurity is not leaded, makes this alloy material harmless.
And the total amount of described aluminium, copper, magnesium elements is 5.5%-6%, to improve the content of zinc, make alloy there is low melting point, workability energy.
In this zinc base alloy, the effect of each element is as follows:
Aluminium: improve the castability of alloy, increase the mobility of alloy, crystal grain thinning, improves mechanical property.
Aluminium content is controlled at 4 %-5.5%, and the intensity of alloy and mobility are best, and good fluidity is to obtain a condition complete, size is accurate, ganoid foundry goods is essential.
Copper: the hardness and the intensity that increase alloy; Improve the wear resistance of alloy; Reduce intergranular corrosion.Copper content control is at 0.8%-1.2%, and the physical strength of alloy is high, and extendability is low.
Magnesium: reduce intergranular corrosion; Refinement alloy structure, thereby the intensity of increase alloy; Improve the wear resistance of alloy.
Mg content is controlled at 0.05%-0.08%, can improve alloy toughness and mobility best.
Impurity element: iron, lead, cadmium, tin: the intergranular corrosion of zinc alloy is become very responsive, accelerated the intergranular corrosion of itself in temperature, wet environment, reduce mechanical property, and cause that casting dimension changes.
Content of impurities is controlled at below 0.02%, can effectively improve corrosion resistance, the mobility of zinc base alloy, and put forward heavy alloyed intensity, hardness, toughness etc., especially not leaded in impurity, makes alloy material harmless, and safety and environmental protection.
Embodiment mono-:
, described zinc base alloy is that Zn-Al-Cu-Mg is associated gold, contained element and mass percent are: aluminium 5 %, copper 0.8%, magnesium 0.06%, iron 0.015%, cadmium 0.001%, tin 0.001%, all the other are zinc 94.123%.
This zinc base alloy fusing point is 350 ℃, and density is 4.8g/cm 3, thermal conductivity is 150W/m.k, tensile strength is 350MPa.
Embodiment bis-:
, described zinc base alloy is that Zn-Al-Cu-Mg is associated gold, contained element and mass percent are: aluminium 4.8%, copper 1%, magnesium 0.05%, iron 0.017%, cadmium 0.001%, tin 0.001%, all the other are zinc 94.131%.
This zinc base alloy fusing point is 350 ℃, and density is 5g/cm 3, thermal conductivity is 150W/m.k, tensile strength is 350MPa.
The present invention has disclosed a kind of zinc base alloy, adopts aluminium, copper, the magnesium elements of reasonable ratio, has improved the castability of alloy, has increased intensity, hardness and the mobility of alloy, and has reduced the response capacity to detrimental impurity; Especially effectively reduced the content of the impurity that cannot avoid in alloy, and not plumbous containing harmful metallic element in impurity, reduced intergranular corrosion, make alloy there is high corrosion resistance.Zinc base alloy of the present invention is suitable for casting high precision, baroque metal decoration accessory, and surface quality of continuous castings is high, is difficult for breaking.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or conversion of equivalent flow process that utilizes description of the present invention to do; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.

Claims (3)

1. a zinc base alloy, it is characterized in that, described zinc base alloy is that Zn-Al-Cu-Mg is associated gold, contained element and mass percent are: aluminium 4 %-5.5%, copper 0.8%-1.2%, magnesium 0.05%-0.08%, all the other are zinc and inevitable impurity, described zinc content is not less than 94%, and described total impurities is not higher than 0.02%, and contained element and mass percent are: iron not higher than 0.02%, lead not higher than 0.001%, cadmium not higher than 0.002%, tin is higher than 0.001%.
2. zinc base alloy according to claim 1, is characterized in that, described impurity is not leaded.
3. zinc base alloy according to claim 1, is characterized in that, the total amount of described aluminium, copper, magnesium elements is 5.5%-6%.
CN201310485514.6A 2013-10-17 2013-10-17 Zinc-base alloy Pending CN103556001A (en)