CN103555302A - 一种海水配制的钻探护壁泥浆 - Google Patents

一种海水配制的钻探护壁泥浆 Download PDF

Info

Publication number
CN103555302A
CN103555302A CN201310527389.0A CN201310527389A CN103555302A CN 103555302 A CN103555302 A CN 103555302A CN 201310527389 A CN201310527389 A CN 201310527389A CN 103555302 A CN103555302 A CN 103555302A
Authority
CN
China
Prior art keywords
seawater
slurry
fresh water
drilling
cmc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310527389.0A
Other languages
English (en)
Inventor
刘瑞坤
杨鸿根
陈永年
樊杰
刘学为
潘国辉
陈三星
刘文宝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHINA SHIPBUILDING INDUSTRY INSTITUTE OF ENGINEERING INVESTIGATION & DESIGN Co Ltd
Original Assignee
CHINA SHIPBUILDING INDUSTRY INSTITUTE OF ENGINEERING INVESTIGATION & DESIGN Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHINA SHIPBUILDING INDUSTRY INSTITUTE OF ENGINEERING INVESTIGATION & DESIGN Co Ltd filed Critical CHINA SHIPBUILDING INDUSTRY INSTITUTE OF ENGINEERING INVESTIGATION & DESIGN Co Ltd
Priority to CN201310527389.0A priority Critical patent/CN103555302A/zh
Publication of CN103555302A publication Critical patent/CN103555302A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种海水配制的钻探护壁泥浆，其特点是该泥浆按海水：800～1000；淡水：1；NaCO3：5；Na-CMC：13；磷酸盐：3.0～4.0；陶土粉：160～420组分混合而成，所述物质按重量计；所述泥浆按组分混合为先将磷酸盐溶于淡水搅拌成淡水混合液、羧甲基纤维素钠（Na-CMC）和碳酸钠（NaCO3）溶于海水搅拌成海水混合液，然后将两混合液缓缓倒入陶土粉中，搅拌直至泥浆形成。本发明与现有技术相比具有海水取代淡水配制钻探护壁泥浆的特点，较好地解决了泥浆稠度和维持时间，有效防止钻探时砂土的塌孔现象发生，需原材料易得，不污染环境，生产成本低，尤其适合海上钻探的泥浆配制，是一种很有工业使用价值的泥浆配制工艺。

Description

一种海水配制的钻探护壁泥浆
技术领域
本发明涉及岩土工程勘察钻探技术领域，尤其是一种海水配制的钻探护壁泥浆。
背景技术
目前，岩土工程勘察钻探时的泥浆配制主要采用淡水作为水源基础，但海上钻探时淡水获取不易，以致勘察成本过高。如果采用海水按淡水的配置方法直接配置泥浆则稠度和维持时间短，不能达到钻探的实用要求。现有技术无法实现海水作为水源的泥浆配制。
发明内容  
本发明的目的是针对现有技术的不足而提供的一种海水配制的钻探护壁泥浆，采用海水与泥浆处理剂和陶土粉混合成护壁泥浆，达到钻探的实用要求，实现海水作为水源的泥浆配制，较好地解决了泥浆的稠度和维持时间，有效防止钻探时砂土的塌孔现象发生，配制所需原材料易得，不污染环境，生产成本低，尤其适合海上钻探的泥浆配制，是一种很有工业使用价值的泥浆配制工艺。
实现本发明目的的技术方案是：一种海水配制的钻探护壁泥浆，其特点是该泥浆按下述组分混合而成，所述物质按重量计： 
海水：                            800～1000
淡水：                            1
碳酸钠（NaCO3）：                5
羧甲基纤维素钠（Na-CMC）：      13
磷酸盐：                         3.0～4.0
陶土粉：                         160～420
所述泥浆按组分混合为先将磷酸盐溶于淡水均匀搅拌成淡水混合液、羧甲基纤维素钠（Na-CMC）和碳酸钠（NaCO3）溶于海水均匀搅拌成海水混合液，然后将两混合液缓缓倒入陶土粉，不断搅拌直至泥浆形成。
所述磷酸盐为六偏磷酸钠或三聚磷酸钠。 
本发明与现有技术相比具有海水取代淡水配制钻探护壁泥浆的特点，较好地解决了泥浆的稠度和维持时间，有效防止钻探时砂土的塌孔现象发生，所需原材料易得，不污染环境，生产成本低，尤其适合海上钻探的泥浆配制，是一种很有工业使用价值的泥浆配制工艺。
具体实施方式
以下将通过具体的实施例对本发明做进一步的阐述： 
实施例1
取3.3公斤六偏磷酸钠溶于1公斤淡水中，适当加温，使其完全溶解后冷却到低于40℃；取5.0公斤碳酸钠（NaCO3）和13公斤羧甲基纤维素钠（Na-CMC）溶于932公斤海水中均匀搅拌成海水混合液；然后将两混合液缓缓倒入167公斤陶土粉中，不断搅拌直至形成密度为1.10kg/m3的护壁泥浆。
实施例2
取3.3公斤三聚磷酸钠溶于1公斤淡水中，适当加温，使其完全溶解后冷却到低于40℃；取5.0公斤碳酸钠（NaCO3）和13公斤羧甲基纤维素钠（Na-CMC）溶于899公斤海水中均匀搅拌成海水混合液；然后将两混合液缓缓倒入250公斤陶土粉中，不断搅拌直至形成密度为1.15kg/m3的护壁泥浆。
实施例3
取3.2公斤六偏磷酸钠溶于1公斤淡水中，适当加温，使其完全溶解后冷却到低于40℃；取5.0公斤碳酸钠（NaCO3）和13公斤羧甲基纤维素钠（Na-CMC）溶于865公斤海水中均匀搅拌成海水混合液；然后将两混合液缓缓倒入334公斤陶土粉中，不断搅拌直至形成密度为1.20kg/m3的护壁泥浆。
实施例4
取3.2公斤三聚磷酸钠溶于1公斤淡水中，适当加温，使其完全溶解后冷却到低于40℃；取5.0公斤碳酸钠（NaCO3）和13公斤羧甲基纤维素钠（Na-CMC）溶于832公斤海水中均匀搅拌成海水混合液；然后将两混合液缓缓倒入417公斤陶土粉中，不断搅拌直至形成密度为1.25kg/m3的护壁泥浆。
以上各实施例只是对本发明做进一步说明，并非用以限制本发明专利，凡为本发明的等效实施，均应包含于本发明专利的权利要求范围之内。

Claims (3)

1.一种海水配制的钻探护壁泥浆，其特征在于该泥浆按下述组分混合而成，所述物质按重量计： 
海水：                            800～1000
淡水：                            1
碳酸钠（NaCO3）：                5
羧甲基纤维素钠（Na-CMC）：      13
磷酸盐：                         3.0～4.0
陶土粉：                         160～420。
2.根据权利要求1所述海水配制的钻探护壁泥浆，其特征在于所述泥浆按组分混合为先将磷酸盐溶于淡水均匀搅拌成淡水混合液、羧甲基纤维素钠（Na-CMC）和碳酸钠（NaCO3）溶于海水均匀搅拌成海水混合液，然后将两混合液缓缓倒入陶土粉，不断搅拌直至泥浆形成。
3.根据权利要求1或权利要求2所述海水配制的钻探护壁泥浆，其特征在于所述磷酸盐为六偏磷酸钠或三聚磷酸钠。
CN201310527389.0A 2013-10-31 2013-10-31 一种海水配制的钻探护壁泥浆 Pending CN103555302A (zh)