CN103555266A - Gold card adhesive and preparation method thereof - Google Patents
Gold card adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN103555266A CN103555266A CN201310527850.2A CN201310527850A CN103555266A CN 103555266 A CN103555266 A CN 103555266A CN 201310527850 A CN201310527850 A CN 201310527850A CN 103555266 A CN103555266 A CN 103555266A
- Authority
- CN
- China
- Prior art keywords
- gold card
- soybean oil
- dicumyl peroxide
- aluminum oxide
- oxide powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a gold card adhesive and a preparation method thereof. The gold card adhesive comprises the following components in percentage by weight: 65%-85% of soybean oil, 3%-10% of sodium tripolyphosphate, 1%-10% of organic silicon emulsion water repellent agents, 0.1%-0.5% of dicumyl peroxide and 10%-25% of alumina powder. The invention also relates to the preparation method of the gold card adhesive. The gold card adhesive disclosed by the invention is difficult to age and difficult to crack.
Description
Technical field
The present invention relates to a kind of binding agent and preparation method thereof, especially relate to a kind of gold card binding agent and preparation method thereof.
Background technology
Gold card claims again metal VIP card, electrophoresis gold card.This kind of gold card system selects senior import copper material, adopts leading novel technique, through design, line cut molding, punching press, burn into printing, polishing, electroplate, color in, the streamline operration program Seiko such as packing makes.In gold card making processes, involved caking agent must be safe, practical.
Yet, easily aging, the easy to crack problem of existing gold card binding agent ubiquity, urgently to be resolved hurrily.
Summary of the invention
Technical problem to be solved by this invention is that a kind of aging, not easy to crack gold card binding agent and preparation method thereof that is difficult for is provided.
The technical solution adopted for the present invention to solve the technical problems is:
The present invention's gold card binding agent, comprises the component of following quality per distribution ratio: soybean oil 65-85%, tripoly phosphate sodium STPP 3-10%, Water Repellent of Silicone Latex 1-10%, dicumyl peroxide 0.1-0.5%, aluminum oxide powder 10-25%.
Further, comprise the component of following quality per distribution ratio: soybean oil 70-80%, tripoly phosphate sodium STPP 5-8%, Water Repellent of Silicone Latex 3-6%, dicumyl peroxide 0.1-0.5%, aluminum oxide powder 15-20%.
The preparation method of the present invention's gold card binding agent, comprises the following steps:
(1) by following quality per distribution ratio, take each component: soybean oil 65-85%, tripoly phosphate sodium STPP 3-10%, Water Repellent of Silicone Latex 1-10%, dicumyl peroxide 0.1-0.5%, aluminum oxide powder 10-25%;
(2) under low whipping speed 15-30rpm, taken soybean oil and aluminum oxide powder are stirred to 20-40min, then add taken tripoly phosphate sodium STPP and organosilicon water repllents, under low whipping speed 31-50rpm, stir 20-40min, finally add taken dicumyl peroxide, under low whipping speed 51-80rpm, stir 15-30 min.
Research experiment shows, uses the present invention's gold card binding agent, be difficult for aging, not easy to crack,
Embodiment
Below in conjunction with embodiment, the invention will be further described.
embodiment 1
The gold card binding agent of the present embodiment, comprises the component of following quality per distribution ratio: soybean oil 75%, tripoly phosphate sodium STPP 5%, Water Repellent of Silicone Latex 4.7%, dicumyl peroxide 0.3%, aluminum oxide powder 15%.
Preparation method, comprises the following steps:
(1) by following quality per distribution ratio, take each component: soybean oil 75%, tripoly phosphate sodium STPP 5%, Water Repellent of Silicone Latex 4.7%, dicumyl peroxide 0.3%, aluminum oxide powder 15%;
(2) under low whipping speed 15rpm, taken soybean oil and aluminum oxide powder are stirred to 35min, then add taken tripoly phosphate sodium STPP and organosilicon water repllents, under low whipping speed 35rpm, stir 30min, finally add taken dicumyl peroxide, under low whipping speed 55rpm, stir 20 min.
Experiment shows, uses gold card binding agent described in the present embodiment, is difficult for aging, not easy to crack.
embodiment 2
The gold card binding agent of the present embodiment, comprises the component of following quality per distribution ratio: soybean oil 70%, tripoly phosphate sodium STPP 6%, Water Repellent of Silicone Latex 3.8%, dicumyl peroxide 0.2%, aluminum oxide powder 20%.
Preparation method, comprises the following steps:
(1) by following quality per distribution ratio, take each component: soybean oil 70%, tripoly phosphate sodium STPP 6%, Water Repellent of Silicone Latex 3.8%, dicumyl peroxide 0.2%, aluminum oxide powder 20%;
(2) under low whipping speed 30rpm, taken soybean oil and aluminum oxide powder are stirred to 25min, then add taken tripoly phosphate sodium STPP and organosilicon water repllents, under low whipping speed 40rpm, stir 25min, finally add taken dicumyl peroxide, under low whipping speed 65rpm, stir 18 min.
Experiment shows, uses gold card binding agent described in the present embodiment, is difficult for aging, not easy to crack.
embodiment 3
The gold card binding agent of the present embodiment, comprises the component of following quality per distribution ratio: soybean oil 72%, tripoly phosphate sodium STPP 7%, Water Repellent of Silicone Latex 5.5%, dicumyl peroxide 0.5%, aluminum oxide powder 15%.
Preparation method, comprises the following steps:
(1) by following quality per distribution ratio, take each component: soybean oil 72%, tripoly phosphate sodium STPP 7%, Water Repellent of Silicone Latex 5.5%, dicumyl peroxide 0.5%, aluminum oxide powder 15%;
(2) under low whipping speed 25rpm, taken soybean oil and aluminum oxide powder are stirred to 30min, then add taken tripoly phosphate sodium STPP and organosilicon water repllents, under low whipping speed 50rpm, stir 22min, finally add taken dicumyl peroxide, under low whipping speed 75rpm, stir 15min.
Experiment shows, uses gold card binding agent described in the present embodiment, is difficult for aging, not easy to crack.
Claims (3)
1. a gold card binding agent, is characterized in that, comprises the component of following quality per distribution ratio: soybean oil 65-85%, tripoly phosphate sodium STPP 3-10%, Water Repellent of Silicone Latex 1-10%, dicumyl peroxide 0.1-0.5%, aluminum oxide powder 10-25%.
2. gold card binding agent according to claim 1, is characterized in that, comprises the component of following quality per distribution ratio: soybean oil 70-80%, tripoly phosphate sodium STPP 5-8%, Water Repellent of Silicone Latex 3-6%, dicumyl peroxide 0.1-0.5%, aluminum oxide powder 15-20%.
3. a preparation method for gold card binding agent as claimed in claim 1, is characterized in that, comprises the following steps:
(1) by following quality per distribution ratio, take each component: soybean oil 65-85%, tripoly phosphate sodium STPP 3-10%, Water Repellent of Silicone Latex 1-10%, dicumyl peroxide 0.1-0.5%, aluminum oxide powder 10-25%;
(2) under low whipping speed 15-30rpm, taken soybean oil and aluminum oxide powder are stirred to 20-40min, then add taken tripoly phosphate sodium STPP and organosilicon water repllents, under low whipping speed 31-50rpm, stir 20-40min, finally add taken dicumyl peroxide, under low whipping speed 51-80rpm, stir 15-30 min.