CN103555266B - Gold one kind of binder and its preparation method - Google Patents

Gold one kind of binder and its preparation method Download PDF

Info

Publication number
CN103555266B
CN103555266B CN201310527850.2A CN201310527850A CN103555266B CN 103555266 B CN103555266 B CN 103555266B CN 201310527850 A CN201310527850 A CN 201310527850A CN 103555266 B CN103555266 B CN 103555266B
Authority
CN
China
Prior art keywords
gold
binder
soybean oil
alumina powder
dicumyl peroxide
Prior art date
Application number
CN201310527850.2A
Other languages
Chinese (zh)
Other versions
CN103555266A (en
Inventor
林世旺
彭建平
蔡庆林
Original Assignee
林世旺
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 林世旺 filed Critical 林世旺
Priority to CN201310527850.2A priority Critical patent/CN103555266B/en
Publication of CN103555266A publication Critical patent/CN103555266A/en
Application granted granted Critical
Publication of CN103555266B publication Critical patent/CN103555266B/en

Abstract

一种金卡粘结剂及其制备方法,所述金卡粘结剂包括以下质量百分配比的组分:大豆油65-85%,三聚磷酸钠3-10%,有机硅乳拒水剂1-10%,过氧化二异丙苯0.1-0.5%,氧化铝粉10-25%。 Gold preparation and one kind of binder, said binder comprising Gold mass percentage ratio of the components: 65-85% soybean oil, 3-10% sodium tripolyphosphate, water repellent silicone breast agent 1-10%, dicumyl peroxide 0.1-0.5%, 10-25% alumina powder. 本发明还包括所述金卡粘结剂的制备方法。 The present invention further comprises a method of preparing the adhesive Gold. 使用本发明之金卡粘结剂,不易老化,不易开裂。 Gold present invention using an adhesive, not aging, resistance to cracking.

Description

一种金卡粘结剂及其制备方法 Gold one kind of binder and its preparation method

技术领域 FIELD

[0001] 本发明涉及一种粘结剂及其制备方法,尤其是涉及一种金卡粘结剂及其制备方法。 [0001] The present invention relates to a method for preparing the binder and, particularly, to a method for its preparation Gold binder.

背景技术 Background technique

[0002] 金卡又称金属贵宾卡、电泳金卡。 [0002] Also known metal VIP Gold, Gold electrophoresis. 此种金卡系选用高级进口铜材,采用领先新工艺技术,经过设计、线割制模、冲压、腐蚀、印刷、抛光、电镀、填色、包装等流水作业程序精工制成。 Gold-based selection of such import advanced copper, lead using new technology, by design, molding line cutting, stamping, etching, printing, polishing, plating, coloring, packaging Seiko streamlined procedures made. 在金卡制作过程中,所涉及到的粘接剂必须安全、实用。 Gold in the production process, the adhesive involved must be safe and practical.

[0003] 然而,现有的金卡粘结剂普遍存在易老化,易开裂的问题,亟待解决。 [0003] However, the existing Gold binder prevalence easy to aging, easy to crack the problem, to be solved.

发明内容 SUMMARY

[0004] 本发明所要解决的技术问题是,提供一种不易老化,不易开裂的金卡粘结剂及其制备方法。 [0004] The present invention solves the technical problem is to provide an easy to aging, the binder and its preparation method Gold unlikely to be broken.

[0005] 本发明解决其技术问题所采用的技术方案是: [0005] aspect of the present invention to solve the technical problem are:

[0006] 本发明之金卡粘结剂,包括以下质量百分配比的组分:大豆油65-85%,三聚磷酸钠3-10%,有机硅乳拒水剂1-10%,过氧化二异丙苯0.1-0.5%,氧化铝粉10-25%。 [0006] Gold binder of the present invention, comprising the components mass percentage ratio: 65-85% soybean oil, 3-10% sodium tripolyphosphate, silicone water repellents milk 1-10%, over dicumyl peroxide 0.1-0.5%, 10-25% alumina powder.

[0007] 进一步,包括以下质量百分配比的组分:大豆油70-80%,三聚磷酸钠5-8%,有机硅乳拒水剂3-6%,过氧化二异丙苯0.1-0.5%,氧化铝粉15-20%。 [0007] further comprising the mass percentage ratio of the components: 70-80% soybean oil, 5-8% sodium tripolyphosphate, silicone water repellents 3-6% milk, dicumyl peroxide 0.1 0.5%, 15-20% alumina powder.

[0008] 本发明之金卡粘结剂的制备方法,包括以下步骤: [0008] The production method of the present invention Gold binder, comprising the steps of:

[0009] (1)按以下质量百分配比称取各组分:大豆油65-85%,三聚磷酸钠3_10%,有机硅乳拒水剂1-10%,过氧化二异丙苯0.1-0.5%,氧化铝粉10-25% ; [0009] (1) according to the following weight percentage of each component weighed ratio: 65-85% soybean oil, 3_10% sodium tripolyphosphate, silicone water repellents milk 1-10%, dicumyl peroxide 0.1 -0.5%, 10-25% alumina powder;

[0010] (2)在搅拌速度15-30rpm下,将所称取的大豆油与氧化铝粉搅拌20_40min,然后加入所称取的三聚磷酸钠和有机娃拒水剂,在搅拌速度31-50rpm下搅拌20_40min,最后加入所称取的过氧化二异丙苯,在搅拌速度51-80rpm下搅拌15-30 min,即成。 [0010] (2) at a stirring speed 15-30rpm, the soybean oil and the weighed alumina powder was stirred 20_40min, then add the weighed baby sodium tripolyphosphate and organic water repellent agent, the stirring speed 31- stirring 50rpm 20_40min, finally adding the weighed dicumyl peroxide, stirred at a stirring speed 51-80rpm 15-30 min, Serve.

[0011] 研究实验表明,使用本发明之金卡粘结剂,不易老化,不易开裂, [0011] Experimental studies show that the adhesive of the present invention using Gold, not aging, resistance to cracking,

具体实施方式 Detailed ways

[0012] 以下结合实施例对本发明作进一步说明。 [0012] The following embodiments in conjunction with the present invention will be further described.

[0013] 实施例1 [0013] Example 1

[0014] 本实施例之金卡粘结剂,包括以下质量百分配比的组分:大豆油75%,三聚磷酸钠5%,有机硅乳拒水剂4.7%,过氧化二异丙苯0.3%,氧化铝粉15%。 [0014] Example of the present embodiment Gold binder, comprising a mass percentage ratio of the components: 75% soybean oil, 5% sodium tripolyphosphate, silicone water repellents 4.7% milk, dicumyl peroxide 0.3%, 15% alumina powder.

[0015] 制备方法,包括以下步骤: [0015] A method, comprising the steps of:

[0016] (1)按以下质量百分配比称取各组分:大豆油75%,三聚磷酸钠5%,有机硅乳拒水剂4.7%,过氧化二异丙苯0.3%,氧化铝粉15% ; [0016] (1) according to the following weight percentage of each component weighed ratio: 75% soybean oil, 5% sodium tripolyphosphate, silicone water repellents 4.7% milk, 0.3% dicumyl peroxide, alumina powder, 15%;

[0017] (2)在搅拌速度15rpm下,将所称取的大豆油与氧化铝粉搅拌35min,然后加入所称取的三聚磷酸钠和有机娃拒水剂,在搅拌速度35rpm下搅拌30min,最后加入所称取的过氧化二异丙苯,在搅拌速度55rpm下搅拌20 min,即成。 [0017] (2) at a stirring speed of 15 rpm, the soybean oil and the weighed alumina powder was stirred for 35min, then the weighed addition of sodium tripolyphosphate and organic baby repellent agent, and stirred at a stirring speed of 35rpm 30min Finally, the weighed addition of dicumyl peroxide, stirred at a stirring speed of 55rpm 20 min, Serve.

[0018] 实验表明,使用本实施例所述金卡粘结剂,不易老化,不易开裂。 [0018] The experiments show that, with the present embodiment, the adhesive Gold, not aging, resistance to cracking.

[0019] 实施例2 [0019] Example 2

[0020] 本实施例之金卡粘结剂,包括以下质量百分配比的组分:大豆油70%,三聚磷酸钠6%,有机硅乳拒水剂3.8%,过氧化二异丙苯0.2%,氧化铝粉20%。 [0020] Example of the present embodiment Gold binder, comprising a mass percentage ratio of the components: 70% soybean oil, 6% of sodium tripolyphosphate, silicone water repellents 3.8% milk, dicumyl peroxide 0.2%, 20% alumina powder.

[0021 ] 制备方法,包括以下步骤: [0021] A method, comprising the steps of:

[0022] (1)按以下质量百分配比称取各组分:大豆油70%,三聚磷酸钠6%,有机硅乳拒水剂3.8%,过氧化二异丙苯0.2%,氧化铝粉20% ; [0022] (1) according to the following weight percentage of each component weighed ratio: 70% soybean oil, 6% of sodium tripolyphosphate, silicone water repellents 3.8% milk, 0.2% dicumyl peroxide, alumina powder, 20%;

[0023] (2)在搅拌速度30rpm下,将所称取的大豆油与氧化铝粉搅拌25min,然后加入所称取的三聚磷酸钠和有机娃拒水剂,在搅拌速度40rpm下搅拌25min,最后加入所称取的过氧化二异丙苯,在搅拌速度65rpm下搅拌18 min,即成。 [0023] (2) at a stirring speed of 30 rpm, the soybean oil and the weighed alumina powder was stirred for 25min, then the weighed addition of sodium tripolyphosphate and organic baby repellent agent, and stirred at a stirring speed of 40rpm 25min Finally, the weighed addition of dicumyl peroxide, stirred at a stirring speed of 65rpm 18 min, Serve.

[0024] 实验表明,使用本实施例所述金卡粘结剂,不易老化,不易开裂。 [0024] Experiments show that the use of the present embodiment Gold binder, not aging, resistance to cracking.

[0025] 实施例3 [0025] Example 3

[0026] 本实施例之金卡粘结剂,包括以下质量百分配比的组分:大豆油72%,三聚磷酸钠7%,有机硅乳拒水剂5.5%,过氧化二异丙苯0.5%,氧化铝粉15%。 Gold binder of Example [0026] the present embodiment, comprises a mass percentage ratio of the components: 72% soybean oil, 7% of sodium tripolyphosphate, silicone water repellents 5.5% milk, dicumyl peroxide 0.5%, 15% alumina powder.

[0027] 制备方法,包括以下步骤: [0027] A method, comprising the steps of:

[0028] (1)按以下质量百分配比称取各组分:大豆油72%,三聚磷酸钠7%,有机硅乳拒水剂5.5%,过氧化二异丙苯0.5%,氧化铝粉15% ; [0028] (1) according to the following weight percentage of each component weighed ratio: 72% soybean oil, 7% of sodium tripolyphosphate, silicone water repellents 5.5% milk, 0.5% dicumyl peroxide, alumina powder, 15%;

[0029] (2)在搅拌速度25rpm下,将所称取的大豆油与氧化铝粉搅拌30min,然后加入所称取的三聚磷酸钠和有机娃拒水剂,在搅拌速度50rpm下搅拌22min,最后加入所称取的过氧化二异丙苯,在搅拌速度75rpm下搅拌15min,即成。 [0029] (2) at a stirring speed of 25 rpm, the soybean oil and the weighed alumina powder was stirred for 30min, then the weighed addition of sodium tripolyphosphate and organic baby repellent agent, and stirred at a stirring speed of 50rpm 22min Finally, the weighed addition of dicumyl peroxide, stirred at a stirring speed of 75rpm 15min, Serve.

[0030] 实验表明,使用本实施例所述金卡粘结剂,不易老化,不易开裂。 [0030] The experiments show that, with the present embodiment, the adhesive Gold, not aging, resistance to cracking.

Claims (3)

1.一种金卡粘结剂,其特征在于,包括以下质量百分配比的组分:大豆油65-85%,三聚磷酸钠3-10%,有机硅乳拒水剂1-10%,过氧化二异丙苯0.1-0.5%,氧化铝粉10-25%。 A Gold binder, characterized in that it comprises the ratio of the mass percentage of the components: 65-85% soybean oil, 3-10% sodium tripolyphosphate, water repellent silicone milk 1-10% , dicumyl peroxide 0.1-0.5%, 10-25% alumina powder.
2.根据权利要求1所述的金卡粘结剂,其特征在于,包括以下质量百分配比的组分:大豆油70-75%,三聚磷酸钠5-8%,有机硅乳拒水剂3-6%,过氧化二异丙苯0.1-0.5%,氧化铝粉I5-20%ο Gold binder according to claim 1, characterized in that it comprises the ratio of the mass percentage of the components: 70-75% soybean oil, 5-8% sodium tripolyphosphate, water repellent silicone breast agent 3-6%, 0.1-0.5% dicumyl peroxide, alumina powder I5-20% ο
3.一种如权利要求1所述的金卡粘结剂的制备方法,其特征在于,包括以下步骤: Cl)按以下质量百分配比称取各组分:大豆油65-85%,三聚磷酸钠3-10%,有机硅乳拒水剂1_10%,过氧化二异丙苯0.1-0.5%,氧化铝粉10-25% ; (2)在搅拌速度15-30rpm下,将所称取的大豆油与氧化铝粉搅拌20_40min,然后加入所称取的三聚磷酸钠和有机娃拒水剂,在搅拌速度31-50rpm下搅拌20_40min,最后加入所称取的过氧化二异丙苯,在搅拌速度51-80rpm下搅拌15-30 min,即成。 The method of claim 1 prepared Gold binder as claimed in claim 3, wherein, comprising the steps of: CI) mass percent ratio in the following respective components were weighed: 65-85% soybean oil, tris 3-10% sodium polyphosphate, silicone water repellents 1_10% milk, dicumyl peroxide 0.1-0.5%, alumina powder 10-25%; (2) at a stirring speed 15-30rpm, the alleged taken soybean oil was stirred with alumina powder 20_40min, then add the weighed sodium tripolyphosphate and organic baby water repellents, stirred at a stirring speed 31-50rpm 20_40min, finally adding the weighed dicumyl peroxide the mixture was stirred at a stirring speed 51-80rpm 15-30 min, Serve.
CN201310527850.2A 2013-10-31 2013-10-31 Gold one kind of binder and its preparation method CN103555266B (en)