CN103553457B - 一种耐盐腐蚀混凝土 - Google Patents

一种耐盐腐蚀混凝土 Download PDF

Info

Publication number
CN103553457B
CN103553457B CN201310481675.8A CN201310481675A CN103553457B CN 103553457 B CN103553457 B CN 103553457B CN 201310481675 A CN201310481675 A CN 201310481675A CN 103553457 B CN103553457 B CN 103553457B
Authority
CN
China
Prior art keywords
parts
concrete
corrosion resistant
salt corrosion
admixture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310481675.8A
Other languages
English (en)
Other versions
CN103553457A (zh
Inventor
胡涛
胡琳
王赛显
刘伟民
王作峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO LEIXIN CONCRETE CO Ltd
Original Assignee
QINGDAO LEIXIN CONCRETE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO LEIXIN CONCRETE CO Ltd filed Critical QINGDAO LEIXIN CONCRETE CO Ltd
Priority to CN201310481675.8A priority Critical patent/CN103553457B/zh
Publication of CN103553457A publication Critical patent/CN103553457A/zh
Application granted granted Critical
Publication of CN103553457B publication Critical patent/CN103553457B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种耐盐腐蚀混凝土，由以下组分按照重量分数组成：水泥为400-450份，粉煤灰50-100份，矿粉50-100份，砂600-700份，陶粒1000-1200份，水120份，外加剂40-50份；所述外加剂由以下组分按重量份数组成：氧化钙-硫铝酸钙复合膨胀剂20-30份，多环芳香族盐类减水剂2-4份，烷基苯磺酸盐类引气剂0.05-0.2份，聚酯纤维1-2份，矿渣粉40-50份，新戊二醇1-2份。本发明的优势是：配方合理，在不改变原有混凝土特性的前提下，提高了混凝土的耐盐腐蚀性。

Description

一种耐盐腐蚀混凝土
技术领域
本发明涉及混凝土，特别涉及一种耐盐腐蚀的混凝土。
背景技术
在道路施工过程中，混凝土是必须的建筑材料，但是，在有些特殊的地区，存在大面积的盐渍土，盐渍土中含有的硫酸盐、氯盐会对道路、桥涵中的混凝土产生腐蚀作用，因此，普通的混凝土满足不了实际需求。
现有的耐盐腐蚀混凝土的配方在实际使用中难以实施，而且原材料复杂多样性增加了存储、品质控制，称量和搅拌的困难。
发明内容
针对现有技术中存在的缺陷，本发明的目的在于提供一种耐盐腐蚀混凝土。
本发明的技术方案如下：
一种耐盐腐蚀混凝土，由以下组分按照重量分数组成：
水泥400-450份，粉煤灰50-100份，矿粉50-100份，砂600-700份，陶粒1000-1200份，水120份，外加剂40-50份；
所述外加剂由以下组分按重量份数组成：
氧化钙-硫铝酸钙复合膨胀剂   20-30份
多环芳香族盐类减水剂        2-4   份
烷基苯磺酸盐类引气剂     0.05-0.2份
聚酯纤维                    1-2   份
矿渣粉                     40-50  份
新戊二醇                    1-2   份。
在上述方案的基础上，一种耐盐腐蚀混凝土，由以下组分按照重量分数组成：
水泥400份，粉煤灰80份，矿粉80份，砂650份，陶粒1100份，水120份，外加剂45份；
所述外加剂由以下组分按重量份数组成：
氧化钙-硫铝酸钙复合膨胀剂  25份
多环芳香族盐类减水剂        3份
烷基苯磺酸盐类引气剂      0.1份
聚酯纤维                  1.5份
矿渣粉                    45  份
新戊二醇                   1.5份。
一种制备上述耐盐腐蚀混凝土的备方法，具体步骤如下：
1）按量称取上述组分，将除外加剂和水以外的其他组分充分混合；
2）将外加剂加入水中搅匀；
3）将步骤2）的产物缓慢加入到步骤1）制得的混合物中。
本发明的优势是：配方合理，在不改变原有混凝土特性的前提下，提高了混凝土的耐盐腐蚀性。
具体实施方式
实施例1
一种耐盐腐蚀混凝土，由以下组分按照重量分数组成（每份100g）：
水泥400份，粉煤灰80份，矿粉80份，砂650份，陶粒1100份，水120份，外加剂45份；
所述外加剂由以下组分按重量份数组成：
氧化钙-硫铝酸钙复合膨胀剂  25份
多环芳香族盐类减水剂        3份
烷基苯磺酸盐类引气剂      0.1份
聚酯纤维                  1.5份
矿渣粉                    45  份
新戊二醇                   1.5份；
具体步骤如下：
1）按量称取上述组分，将除外加剂和水以外的其他组分充分混合；
2）将外加剂加入水中搅匀；
3）将步骤2）的产物缓慢加入到步骤1）制得的混合物中。
上述方法制备的混凝土的28d通电量小于900C，28天抗压强度与不加外加剂相比，提高25%
实施例2
一种耐盐腐蚀混凝土，由以下组分按照重量分数组成（每份100g）：
水泥400份，粉煤灰80份，矿粉80份，砂650份，陶粒1100份，水120份，外加剂45份；
所述外加剂由以下组分按重量份数组成：
氧化钙-硫铝酸钙复合膨胀剂  25份
多环芳香族盐类减水剂        3份
烷基苯磺酸盐类引气剂      0.1份
聚酯纤维                  1.5份
矿渣粉                    45  份
新戊二醇                   1.5份。
一种制备上述耐盐腐蚀混凝土的备方法，具体步骤如下：
1）按量称取上述组分，将除外加剂和水以外的其他组分充分混合；
2）将外加剂加入水中搅匀；
3）将步骤2）的产物缓慢加入到步骤1）制得的混合物中。
上述方法制备的混凝土的28d通电量小于900C，28天抗压强度与不加外加剂相比，提高28%。
实施例3
一种耐盐腐蚀混凝土，由以下组分按照重量分数组成（每份100g）：
水泥450份，粉煤灰100份，矿粉100份，砂700份，陶粒1200份，水120份，外加剂50份；
所述外加剂由以下组分按重量份数组成：
氧化钙-硫铝酸钙复合膨胀剂  30份
多环芳香族盐类减水剂       4   份
烷基苯磺酸盐类引气剂    0.2份
聚酯纤维                  2   份
矿渣粉                   50  份
新戊二醇                    2   份。
上述方法制备的混凝土的28d通电量小于900C，28天抗压强度与不加外加剂相比，提高24%。

Claims (1)

1.一种耐盐腐蚀混凝土，其特征在于由以下组分按照重量份数组成：
水泥400份，粉煤灰80份，矿粉80份，砂650份，陶粒1100份，水120份，外加剂45份；
所述外加剂由以下组分按重量份数组成：
所述的耐盐腐蚀混凝土的制备方法，具体步骤如下：
1)按量称取上述组分，将除外加剂和水以外的其他组分充分混合；
2)将外加剂加入水中搅匀；
3)将步骤2)的产物缓慢加入到步骤1)制得的混合物中。
CN201310481675.8A 2013-10-16 2013-10-16 一种耐盐腐蚀混凝土 Active CN103553457B (zh)