CN103525508B - Un-disassembly cleaning agent for automatic transmission - Google Patents
Un-disassembly cleaning agent for automatic transmission Download PDFInfo
- Publication number
- CN103525508B CN103525508B CN201310442611.7A CN201310442611A CN103525508B CN 103525508 B CN103525508 B CN 103525508B CN 201310442611 A CN201310442611 A CN 201310442611A CN 103525508 B CN103525508 B CN 103525508B
- Authority
- CN
- China
- Prior art keywords
- parts
- cleaning agent
- box
- clean
- automatic gear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to the field of special chemicals for automobile engine maintenance, and particularly relates to a un-disassembly cleaning agent for an automatic transmission. The un-disassembly cleaning agent is characterized in that the chemical formula comprises the following components in parts by weight: 12-88 parts of II-generation base oil N150, 10-49 parts of polyisobutene disuccinimide, 0.1-45.8 parts of barium petroleum sulfonate, 1.9-19.7 parts of phosphate ester, 0.1-12 parts of benzotriazole and 5.0-29.9 parts of dialkyldithiocalcium phosphate. The cleaning agent provided by the invention has the unique features that (1) unique component proportions are adopted; (2) polyisobutene disuccinimide is adopted; (3) dialkyldithiocalcium phosphate is adopted. The cleaning agent has the advantages that (1) the cleaning is quick; (2) the effect is good; (3) abrasion of metal parts is avoided; (4) corrosion to rubber and plastic parts is avoided; (5) precipitation is avoided.
Description
Technical field
The present invention relates to auto repair maintenance and use professional speciality chemical, particularly a kind of automatic gear-box is not disintegrated clean-out system.
Background technology
Automatic gearbox of vehicles greasy filth producing cause: in normal use procedure, automatic gear-box ATF oil is the continuous oxidized acidifying of meeting in the oil drain interval of regulation, and color is blackening gradually.The oily constantly retrogradation of ATF that is oxidized and acidifying, sticks to the surface of the mechanical parts such as valve body, clutch coupling, brake strap/sheet.
The harm of automatic gear-box greasy filth: the continuation normal circulation flowing stopping ATF oil, pollutes the new ATF oil after changing, accelerates the formation of greasy filth and carbon distribution.In addition, deteriorated dirty ATF oil can reduce the ATF oil transmission of power function newly added, and directly affects the use properties of automatic gear-box.
In existing market, the automatic gear-box clean-out system that do not disintegrate only pays close attention to cleansing power, does not pay close attention to the side effect of product to ATF oil and automatic gear-box.Mainly there is several defect below in commercially available prod: (1) commercially available clean-out system can not be completely fused with ATF oil after adding; rubber and plastic components that (2) commercially available clean-out system adds post-etching automatic gear-box can be folded; particularly O shape circle (3) commercially available clean-out system add post-etching metal; particularly (4) commercially available clean-out system can will destroy tempered oil film after adding for non-ferrous metal, accelerates friction and wear.
Summary of the invention
The present invention is directed to above-mentioned the deficiencies in the prior art, provide a kind of automatic gear-box and not disintegrate clean-out system, this clean-out system can when not disintegrating automatic gear-box the dirt such as safety, quick free from corrosion cleaning mud oil.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: a kind of automatic gear-box is not disintegrated clean-out system, and it is characterized in that, chemical formulation component is as follows by weight ratio: II generation base oil N150:12-88 component; Polyisobutylene-bis-succinimide: 10-49 components; Barium mahogany sulfonate: 0.1-45.8 components; Phosphoric acid ester: 1.9-19.7 components; Benzotriazole: 0.1-12 components, dialkyl dithiophosphoric acid calcium salt: 5.0-29.9 components.
The present invention has the unique distinction of several aspect: (1) have employed unique component proportioning and (2) have employed ashless dispersant polyisobutylene-bis-succinimide and (3) have employed phosphoric acid ester bag and (4) have employed the special dialkyl dithiophosphoric acid calcium salt of ATF automatic transmission fluid: 5.0-29.9 components.Achieve following advantage: (1) Rapid Cleaning; in 15-30 minute, complete cleaning (2) effective: can once clean the carbon distribution and greasy filth that are formed in solution 60000 kilometers when (3) cleaning can not to metal parts produce wearing and tearing (4) for rubber and plastic components do not produce corrosion (5) add after and ATF is oily can be completely fused; do not produce after (6) precipitation adds and can compensate destroyed oil film defencive function, avoid producing excessive friction and wearing and tearing.
Clean-out system of the present invention, when not disintegrating automatic gear-box, adds in automatic gear-box ATF.Circulate together with ATF oil in automatic gear-box working process, clean the greasy filth and varnish that have been formed.Greasy filth and varnish are mainly attached to the places such as oil pan, oil pump, application valve body oil circuit, fluid torque-converter.Realize quick, safe and corrosion-free.
Embodiment
Be described principle of the present invention and feature below, example, only for explaining the present invention, is not intended to limit scope of the present invention.
Embodiment 1
Automatic gear-box described in the present embodiment is not disintegrated clean-out system, it is characterized in that chemical composition is as follows by weight ratio:
II generation base oil N150:68 component; Polyisobutylene-bis-succinimide: 11.9 components; Barium mahogany sulfonate: 8.7 components; Phosphoric acid ester: 4.2 components; Benzotriazole: 1.6 components, dialkyl dithiophosphoric acid calcium salt: 5.6 components.
The do not disintegrate collocation method of clean-out system of automatic gear-box described in the present embodiment is:
1) temperature of reaction kettle heating is remained on 45 DEG C
2) add proportioning raw material successively, keep stirring
3) often kind of raw material adds interval 15 minutes
4) raw material keeps stirring 8 hours after adding.
Embodiment 2
Automatic gear-box described in the present embodiment is not disintegrated clean-out system, it is characterized in that chemical composition is as follows by weight ratio:
II generation base oil N150:62 component; Polyisobutylene-bis-succinimide: 14.9 components; Barium mahogany sulfonate: 4.7 components; Phosphoric acid ester: 7.2 components; Benzotriazole: 2.3 components, dialkyl dithiophosphoric acid calcium salt: 8.9 components.
The do not disintegrate collocation method of clean-out system of automatic gear-box described in the present embodiment is:
1) temperature of reaction kettle heating is remained on 45 DEG C
2) add proportioning raw material successively, keep stirring
3) often kind of raw material adds interval 15 minutes
4) raw material keeps stirring 8 little after adding.
Claims (2)
1. automatic gear-box is not disintegrated a clean-out system, it is characterized in that chemical composition is as follows by weight ratio:
II generation base oil 150N:68 part; Polyisobutylene-bis-succinimide: 11.9 parts; Barium mahogany sulfonate: 8.7 parts; Phosphoric acid ester: 4.2 parts; Benzotriazole: 1.6 parts, dialkyl dithiophosphoric acid calcium salt: 5.6 parts.
2. automatic gear-box is not disintegrated a clean-out system, it is characterized in that chemical composition is as follows by weight ratio:
II generation base oil 150N:62 part; Polyisobutylene-bis-succinimide: 14.9 parts; Barium mahogany sulfonate: 4.7 parts; Phosphoric acid ester: 7.2 parts; Benzotriazole: 2.3 parts, dialkyl dithiophosphoric acid calcium salt: 8.9 parts.