CN103525350A - High-strength glass reinforced plastic adhesive - Google Patents
High-strength glass reinforced plastic adhesive Download PDFInfo
- Publication number
- CN103525350A CN103525350A CN201310504666.6A CN201310504666A CN103525350A CN 103525350 A CN103525350 A CN 103525350A CN 201310504666 A CN201310504666 A CN 201310504666A CN 103525350 A CN103525350 A CN 103525350A
- Authority
- CN
- China
- Prior art keywords
- parts
- reinforced plastic
- strength glass
- plastic adhesive
- glass reinforced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength glass reinforced plastic adhesive. The high-strength glass reinforced plastic adhesive comprises the following components in parts by weight: 40-60 parts of epoxy resin, 10-20 parts of phenolic resin, 20-40 parts of acetone, 10-20 parts of polyacrylic resin, 10-20 parts of dibutyl phthalate, 10-20 parts of diethylenetriamine, 10-20 parts of light calcium carbonate and 10-20 parts of talcum powder. Compared with the prior art, the high-strength glass reinforced plastic adhesive disclosed by the invention has the beneficial effects of strong adhesive force, good water resistance, simple preparation process and low cost and the like.
Description
Technical field
The invention belongs to adhesive technology field, more specifically relate to a kind of high strength glass fibre reinforced plastic adhesive.
Background technology
Glass reinforced plastic is fiber-reinforced plastic, refers generally to strengthen unsaturated polyester, epoxy resin and phenolic resin as matrix resin with glass fibre.With glass fibre or its goods, make the reinforced plastics of strongthener, appellation is glass filament reinforced plastics, or appellation glass reinforced plastic.Have light weight and hard, non-conductive, physical strength is high, recycles the advantages such as few, corrosion-resistant.Can replace steel manufacturing machine part and automobile, ship housing etc.
Glass reinforced plastic conventionally need to be by adhesive bonds at body surface to reach result of use.
Summary of the invention
The object of the invention is to overcome the deficiency that prior art exists, a kind of high strength glass fibre reinforced plastic adhesive is provided.
For achieving the above object, the present invention has taked following technical scheme:
, in weight part, composed of the following components:
Epoxy resin: 40～60, resol: 10～20, acetone: 20～40,
Polyacrylic resin: 10～20, dibutyl phthalate: 10～20,
Diethylenetriamine: 10～20, light calcium carbonate: 10～20, talcum powder: 10～20.
In technique scheme, the preparation method of described high strength glass fibre reinforced plastic adhesive is:
(1) by proportioning, epoxy resin, resol, polyacrylic resin and acetone are mixed, stir, then add dibutyl phthalate, be uniformly dispersed;
(2) add light calcium carbonate and talcum powder, be uniformly dispersed;
(3) product of step (1) and step (2) is mixed, after being uniformly dispersed, add diethanolamine, after stirring, get final product to obtain finished product.
Compared with prior art, the present invention has the beneficial effects such as cohesive force is strong, good waterproof performance, and preparation technology is simple, with low cost.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
, in weight part, composed of the following components:
Epoxy resin (E-44): 40, resol: 10, acetone: 20,
Polyacrylic resin: 10, dibutyl phthalate: 10,
Diethylenetriamine: 10, light calcium carbonate: 10, talcum powder: 10.
Embodiment 2
, in weight part, composed of the following components:
Epoxy resin (E-44): 60, resol: 20, acetone: 40,
Polyacrylic resin: 20, dibutyl phthalate: 20,
Diethylenetriamine: 20, light calcium carbonate: 20, talcum powder: 20.
Embodiment 3
, in weight part, composed of the following components:
Epoxy resin (E-44): 50, resol: 16, acetone: 30,
Polyacrylic resin: 16, dibutyl phthalate: 15,
Diethylenetriamine: 16, light calcium carbonate: 16, talcum powder: 16.
In above-described embodiment, the preparation method of described high strength glass fibre reinforced plastic adhesive is:
(1) by proportioning, epoxy resin, resol, polyacrylic resin and acetone are mixed, stir, then add dibutyl phthalate, be uniformly dispersed;
(2) add light calcium carbonate and talcum powder, be uniformly dispersed;
(3) product of step (1) and step (2) is mixed, after being uniformly dispersed, add diethanolamine, after stirring, get final product to obtain finished product.
Claims (4)
1. a high strength glass fibre reinforced plastic adhesive, is characterized in that, in weight part, composed of the following components:
Epoxy resin: 40～60, resol: 10～20, acetone: 20～40,
Polyacrylic resin: 10～20, dibutyl phthalate: 10～20,
Diethylenetriamine: 10～20, light calcium carbonate: 10～20, talcum powder: 10～20.
2. a kind of high strength glass fibre reinforced plastic adhesive according to claim 1, is characterized in that, in weight part, composed of the following components:
Epoxy resin: 40, resol: 10, acetone: 20,
Polyacrylic resin: 10, dibutyl phthalate: 10,
Diethylenetriamine: 10, light calcium carbonate: 10, talcum powder: 10.
3. a kind of high strength glass fibre reinforced plastic adhesive according to claim 1, is characterized in that, in weight part, composed of the following components:
Epoxy resin: 60, resol: 20, acetone: 40,
Polyacrylic resin: 20, dibutyl phthalate: 20,
Diethylenetriamine: 20, light calcium carbonate: 20, talcum powder: 20.
4. a kind of high strength glass fibre reinforced plastic adhesive according to claim 1, is characterized in that, in weight part, composed of the following components:
Epoxy resin: 50, resol: 16, acetone: 30,
Polyacrylic resin: 16, dibutyl phthalate: 15,
Diethylenetriamine: 16, light calcium carbonate: 16, talcum powder: 16.