CN103525318B - 一种尼龙布与铝合金的粘接方法 - Google Patents

一种尼龙布与铝合金的粘接方法 Download PDF

Info

Publication number
CN103525318B
CN103525318B CN201310485352.6A CN201310485352A CN103525318B CN 103525318 B CN103525318 B CN 103525318B CN 201310485352 A CN201310485352 A CN 201310485352A CN 103525318 B CN103525318 B CN 103525318B
Authority
CN
China
Prior art keywords
nylon cloth
aluminium alloy
stainless steel
caking agent
bonding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310485352.6A
Other languages
English (en)
Other versions
CN103525318A (zh
Inventor
王会增
暂焕文
唐慧林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Xinghang Electromechanical Equipment Co Ltd
Original Assignee
Beijing Xinghang Electromechanical Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Xinghang Electromechanical Equipment Co Ltd filed Critical Beijing Xinghang Electromechanical Equipment Co Ltd
Priority to CN201310485352.6A priority Critical patent/CN103525318B/zh
Publication of CN103525318A publication Critical patent/CN103525318A/zh
Application granted granted Critical
Publication of CN103525318B publication Critical patent/CN103525318B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于粘接技术领域，具体涉及一种尼龙布与铝合金间的粘接工艺方法，采取补强粘接结构，按照相关粘接流程，实现了尼龙布与铝合金的柔性粘接。通过工艺试验，优选出符合粘接指标要求(温度150℃，承载力7Kg，恒温时间30min)的粘接剂类型。本粘接方法满足了某型背景产品的柔性联接耐压及耐温设计指标要求，为下一步的工程应用提供的技术支撑。

Description

一种尼龙布与铝合金的粘接方法
技术领域
本发明属于粘接技术领域，具体涉及一种尼龙布与铝合金间的粘接工艺方法。
背景技术
尼龙布与金属材料铝合金间的粘接方式，是某型产品柔性对接的重点需求。该型产品要求在10kg压力载荷及200℃温度条件下实现尼龙布质材料与2A12铝质材料的柔性联连，以确保其结构功能。目前，在国内、外公开的文献资料上还未见相关技术报道，无现成经验可借鉴。
发明内容
本发明涉及一种尼龙布与铝合金板的粘接工艺方法。采取不锈钢薄板环圈压粘的补强粘接结构，按照规定的粘接流程，实现了尼龙布与铝合金板的柔性粘接。通过试验，优选出了满足粘接性能要求(温度150℃，承载力7Kg，恒温时间30min)的粘接剂类型。
具体技术方案如下：
(1)粘接结构
尼龙布与铝合金板材采取搭接的方法，搭接量约为10mm。尼龙布通过粘接剂与铝合金板实现柔性粘接。在此基础上，采用不锈钢薄板(厚约0.2mm)通过相同粘接剂环圈压粘尼龙布的补强措施。强化柔性粘接性能。不锈钢的搭接量与尼龙布的搭接量一致，不锈钢薄板环圈的两端头采取对接方式(粘接结构见附图1)。
(2)粘接流程
尼龙布与铝合金板材柔性粘接的工艺过程是：
表面处理：用毛刷清理尼龙布表面的灰尘等杂物。用丙酮清洗铝板材粘接面的油污等异物并风干粘接面。
配胶：按相应粘接剂的组份调合比例要求进行。
涂敷：用玻璃棒将胶液均匀涂抹于被粘接物品上。
补强：将不锈钢薄板(厚约0.2mm)环圈压粘于尼龙布上，不锈钢板两端头采取对接方式。
固化：按粘接剂完全固化时间进行静态固化处理。
修整：粘接剂固化后，对压粘过程中溢出的胶液进行清理。
(3)粘接试验
对粘接固化后的整体柔性粘联物进行性能验证试验。试验过程是选用不同搭接宽度及不同类型的粘接剂，针对尼龙与铝板的柔性粘联物(附图1)，利用承载工装(附图2)，在加热炉内(设定恒温150℃)利用热承载工装(附图3)进行尼龙布与铝板的热载荷(7Kg，30min)试验。通过试验，验证粘接结构的有效性并优选出粘接剂品种。同时，排除不适宜的粘接剂类型。
本粘接方法的有益效果是：依据设计的补强粘接结构，按相应的粘接流程，在试验验证的基础上，实现了尼龙布与铝板材(2A12)的柔性粘接。满足了某型背景产品的柔性联接耐压及耐温设计指标要求，为相关柔性粘接的工程应用提供了技术支撑。同时，排除了部分不适宜的粘接剂类型。
附图说明
图1尼龙布与铝板粘接示意图
图2承载工装示意图
图3热承载工装示意图
具体实施方式
实施例1
(1)柔性粘接试验工作准备
选取不同搭接宽度(如：宽10mm、15mm、20mm等)的尼龙布及不同类型(如：XY401胶、强力蜜月胶、铁锚101胶等)的粘接剂。采用厚约0.2mm的不锈钢薄板作为粘接补强板。设计简易的柔性粘接结构模拟件(附图1)、承载工装(附图2)及热承载工装(附图3)。作好尼龙布与铝合金板的柔性粘接前的准备工作。
(2)模拟件准备
用毛刷清理尼龙布表面的灰尘等杂物。用丙酮清洗铝板材粘接面的油污等异物并风干粘接面。按相应粘接剂组份的调合比例要求进行粘接剂(三种：XY401胶、强力蜜月胶、铁锚101胶)的调制。用玻璃棒将胶液均匀涂抹于尼龙布及铝合金板的粘接面上。将尼龙布绷直与铝合金板实施粘接。之后，通过同样的清理及粘接过程，实现不锈钢薄板(约0.2厚)对尼龙布的环圈覆盖压粘。粘接完成后，在室温条件下按粘接剂的规定固化时间(一般为24小时)进行室温静态固化。固化后，对压粘过程中溢出的胶液进行去除和清理。
按以上过程完成不同类型粘接剂及不同规格尼龙布与铝合金板柔性粘接的多个系列的模拟件准备工作。
(3)工装准备
按附图2及附图3结构关系，完成承载工装及热承载工装的工装生产准备。
(4)柔性粘接试验实施
针对尼龙布与铝合金板的柔性粘联物(附图1)，利用承载工装(附图2)，在加热炉内(设定恒温150℃，时间30min)利用热承载工装(附图3)对尼龙布与铝合金板的柔性粘接物进行热载荷(7Kg)试验。
通过试验，优选出铁锚101粘接剂，按图1的补强结构进行尼龙布与铝合金板的柔性粘接，满足额定条件下(即温度150℃，承载力7Kg，恒温时间30min)无拉脱及开胶的设计性能要求。同时，XY401胶及强力蜜月胶等胶接剂不能满足性能要求，此类胶接剂被排除。
该试验结果为后续进一步的柔性粘接工程应用打下了坚实技术基础。

Claims (1)

1.一种尼龙布与铝合金的粘接方法，其特征在于：采取粘接件表面清理，配胶，涂敷，补强，固化，修整的顺序，先用丙酮清洗铝合金板外表面并风干，然后将裁制的多种规格的尼龙布以搭接方式通过铁锚101粘接剂粘于铝合金板上，满足在温度150℃，承载力7Kg，恒温时间30min条件下不拉脱、不开胶的性能要求；最后再用薄不锈钢板通过相同的粘接剂于尼龙布上环圈覆盖压粘，粘接固化24小时即可，其中不锈钢板的搭接量与尼龙布的搭接量一致，不锈钢板两端头采取对接方式。
CN201310485352.6A 2013-10-15 2013-10-15 一种尼龙布与铝合金的粘接方法 Active CN103525318B (zh)