CN103525219A - Environment-friendly antirust primer - Google Patents
Environment-friendly antirust primer Download PDFInfo
- Publication number
- CN103525219A CN103525219A CN201310466683.5A CN201310466683A CN103525219A CN 103525219 A CN103525219 A CN 103525219A CN 201310466683 A CN201310466683 A CN 201310466683A CN 103525219 A CN103525219 A CN 103525219A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- friendly type
- proofing primer
- type rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the paint field, and particularly relates to an environment-friendly antirust primer. The antirust primer comprises following components by weight: 30-45 parts of a hydroxyl acrylic resin, 10-25 parts of an amino resin, 3-6 parts of an epoxy resin, 3-8 parts of a film-forming auxiliary agent, 3-25 parts of an inorganic filling material, 5-25 parts of a diluent, 0.2-0.8 part of a leveling agent, 0.5-3.5 parts of polyacrylamide and 0.3-2.8 parts of a silane coupling agent. Beneficial effects of the technical scheme of the antirust primer are that: the antirust primer is free from lead, chromium or other harmful substances; the antirust primer has good adhesiveness, water resistance, and corrosion resistance; a coating having good adhesiveness and water resistance to a metal material can be obtained by using the primer to perform a coating process, so that the metal material has a strong antirust property and strong corrosion resistance; and the antirust primer has advantages of low toxicity, no pollution, and environment protection.
Description
Technical field
The present invention relates to paint field, especially a kind of environment-friendly type rust-proofing primer.
Background technology
For having obtained better ornamental and erosion resistance, various household electrical appliance, motorcycle accessories have adopted the mode of multiple pass coat, as priming paint, middle japanning, Lacquer finish light cavalry etc.
Rust-inhibiting primer coating is the measure that a kind of protecting materials of widespread use is avoided corrosion.In broad terms, its object of protection comprises that all are suitable for the material of protection.When protection metal, avoid natural medium when corrosion, be called rust proof paint, i.e. metal rust-proofing primer, it must stop and in metal, forms corrosion cell and stop it to continue to develop.Anticorrosive coating often priming paint to the corollary system of finish paint.Rust-proofing primer is the important component part of anticorrosive coating, it directly contacts with metal base, it is the basis of corrosion-proof coating system, should meet the Essential Performance Requirements of priming paint, to there is good wetting property, tack, alkali resistance with metal, with the matching capacity of finish paint, viscosity is low simultaneously, internal stress is little.
Traditional rust-proofing primer, contains the heavy metals such as a large amount of lead, sexavalent chrome, and this rust-proofing primer, because contain a large amount of objectionable impuritiess, can not meet the demand of the new environmental regulation of people, uses and is more and more restricted.
Summary of the invention
The object of the invention is: overcome rust-proofing primer in prior art and contain the objectionable impuritiess such as lead, chromium, the environment-friendly type rust-proofing primer of the objectionable impuritiess such as a kind of unleaded, chromium is provided.
In order to achieve the above object, the technical solution used in the present invention is as follows:
A rust-proofing primer, its mass fraction is composed as follows: Hydroxylated acrylic resin 30-45 part, aminoresin 10-25 part, epoxy resin 3-6 part, film coalescence aid 3-8 part, mineral filler 3-25 part, thinner 5-25 part, flow agent 0.2-0.8 part, polyacrylamide 0.5-3.5 part, silane coupling agent 0.3-2.8 part.
Further, described aminoresin is selected from least one in urea-formaldehyde resin, terpolycyantoamino-formaldehyde resin, Polyamide-Polyamsne-Epichlorohydrin.
Further, film coalescence aid of living in is selected from: at least one in alcohol ester 12, cellaburate.
Further, described mineral filler is selected from: at least one in talcum powder, zinc sulfate, barium sulfate, composite iron-titanium powder.
Further, described thinner is selected from: at least one in N-BUTYL ACETATE, propyl carbinol, isopropylcarbinol, Virahol, hexone, pimelinketone.
Further, described flow agent is polyether modified siloxane.
Further, a rust-proofing primer, its mass fraction is composed as follows: 37 parts of Hydroxylated acrylic resins, 18 parts, aminoresin, 4.5 parts of epoxy resin, 5.5 parts of film coalescence aid, 14 parts of mineral fillers, 15 parts of thinners, 0.5 part of flow agent, 2 parts of polyacrylamides, 1.5 parts of silane coupling agents.
Adopt the beneficial effect of technical scheme of the present invention to be: the objectionable impuritiess such as environment-friendly type rust-proofing primer of the present invention is not leaded, chromium, adhesivity is good, water tolerance and excellent corrosion resistance, use priming paint of the present invention to carry out coating process, can obtain the filming of the adhesivity of metallic substance and water tolerance excellence, thereby make the rust resistance and corrosion resistance of metallic substance strong, and, rust-proofing primer low toxicity of the present invention is nuisanceless, has advantages of environmentally friendly.
Embodiment
According to specific embodiment, the present invention will be further described below.
Embodiment 1
A rust-proofing primer, its mass fraction is composed as follows: 30 parts of Hydroxylated acrylic resins, 10 parts of urea-formaldehyde resins, 3 parts of epoxy resin, 12 parts of alcohol esters, 3 parts of talcum powder, 0.2 part of N-BUTYL ACETATE, propyl carbinol, isopropylcarbinol, 0.5 part of polyacrylamide, 0.3 part of silane coupling agent.
Embodiment 2
A kind of environment-friendly type rust-proofing primer, its mass fraction is composed as follows: 37 parts of Hydroxylated acrylic resins, 18 parts of urea-formaldehyde resin, terpolycyantoamino-formaldehyde resins, 4.5 parts of epoxy resin, 5.5 parts of alcohol ester 12, cellaburates, 14 parts of barium sulfate, composite iron-titanium powders, 15 parts of N-BUTYL ACETATEs, isopropylcarbinol, Virahol, hexone, pimelinketone, 0.5 part of polyether modified siloxane, 2 parts of polyacrylamides, 1.5 parts of silane coupling agents.
The present embodiment is preferred forms.
Embodiment 3
A kind of environment-friendly type rust-proofing primer, its mass fraction is composed as follows: 45 parts of Hydroxylated acrylic resins, 25 parts of urea-formaldehyde resins, terpolycyantoamino-formaldehyde resin, Polyamide-Polyamsne-Epichlorohydrin, 6 parts of epoxy resin, 8 parts of alcohol ester 12, cellaburates, 25 parts of talcum powder, zinc sulfate, barium sulfate, composite iron-titanium powder, 25 parts of N-BUTYL ACETATEs, propyl carbinol, isopropylcarbinol, Virahol, hexone, pimelinketone, polyether modified siloxane 0.2-0.8 part, 3.5 parts of polyacrylamides, 2.8 parts of silane coupling agents.
Although above-described embodiment describes in detail technical scheme of the present invention, but technical scheme of the present invention is not limited to above embodiment, in the situation that not departing from thought of the present invention and aim, any change that technical scheme of the present invention is done all will fall into claims limited range of the present invention.
Claims (7)
1. an environment-friendly type rust-proofing primer, it is characterized in that, its mass fraction is composed as follows: Hydroxylated acrylic resin 30-45 part, aminoresin 10-25 part, epoxy resin 3-6 part, film coalescence aid 3-8 part, mineral filler 3-25 part, thinner 5-25 part, flow agent 0.2-0.8 part, polyacrylamide 0.5-3.5 part, silane coupling agent 0.3-2.8 part.
2. a kind of environment-friendly type rust-proofing primer according to claim 1, is characterized in that, described aminoresin is selected from least one in urea-formaldehyde resin, terpolycyantoamino-formaldehyde resin, Polyamide-Polyamsne-Epichlorohydrin.
3. a kind of environment-friendly type rust-proofing primer according to claim 1, is characterized in that, membrane-forming agent of living in is selected from: at least one in alcohol ester 12, cellaburate.
4. a kind of environment-friendly type rust-proofing primer according to claim 1, is characterized in that, described mineral filler is selected from: at least one in talcum powder, zinc sulfate, barium sulfate, composite iron-titanium powder.
5. a kind of environment-friendly type rust-proofing primer according to claim 1, is characterized in that, described thinner is selected from: at least one in N-BUTYL ACETATE, propyl carbinol, isopropylcarbinol, Virahol, hexone, pimelinketone.
6. a kind of environment-friendly type rust-proofing primer according to claim 1, is characterized in that, described flow agent is polyether modified siloxane.
7. a kind of environment-friendly type rust-proofing primer according to claim 1, it is characterized in that, its mass fraction is composed as follows: 37 parts of Hydroxylated acrylic resins, 18 parts, aminoresin, 4.5 parts of epoxy resin, 5.5 parts of film coalescence aid, 14 parts of mineral fillers, 15 parts of thinners, 0.5 part of flow agent, 2 parts of polyacrylamides, 1.5 parts of silane coupling agents.