CN103497635B - 一种导电粉末涂料 - Google Patents
一种导电粉末涂料 Download PDFInfo
- Publication number
- CN103497635B CN103497635B CN201310396029.1A CN201310396029A CN103497635B CN 103497635 B CN103497635 B CN 103497635B CN 201310396029 A CN201310396029 A CN 201310396029A CN 103497635 B CN103497635 B CN 103497635B
- Authority
- CN
- China
- Prior art keywords
- raw material
- powder paint
- conductive powder
- compounded mix
- calcium silicates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种导电粉末涂料，它是由下述重量份的原料组成的：E-42环氧树脂70-80、炭黑10-15、双氰胺10-20、酚醛树脂6-10、纳米二氧化硅10-15、导电硫酸钡10-15、导电聚苯胺4-6、聚山梨酯80？2.0-3.5、三烯丙基异氰脲酸酯1-2、四甲氧基甲基甘脲2-3、复合填料10-20；本发明涂膜具有很好的耐湿热和耐高低温性，流平性、柔韧性、抗冲击性强，涂料对钢管的附着力好,钢管的防腐性能也得到了提高。
Description
技术领域
本发明主要涉及一种涂料，尤其涉及一种导电粉末涂料。
背景技术
粉末涂料是一种新型的不含溶剂100%固体粉末状涂料。具有无溶剂、无污染、可回收、环保、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点，而通过加入不同的助剂来改善粉末涂料的性能是目前提高粉末涂料性能一个比较好的方式。
发明内容
本发明目的就是为了提供一种导电粉末涂料。
本发明是通过以下技术方案实现的：
一种导电粉末涂料，其特征在于它是由下述重量份的原料组成的：
E-42环氧树脂70-80、炭黑10-15、双氰胺10-20、酚醛树脂6-10、纳米二氧化硅10-15、导电硫酸钡10-15、导电聚苯胺4-6、聚山梨酯802.0-3.5、三烯丙基异氰脲酸酯1-2、四甲氧基甲基甘脲2-3、复合填料10-20；
所述的复合填料是由下述重量份的原料组成的：
粘土40-50、铁矿渣粉40-50、硅酸钙10-20、氟硅酸铜2-3、氮化铝粉1-2、纳米玉石粉5-7、双巯基乙酸异辛酯二正辛基锡0.2-0.3、玫瑰精油0.6-1、水适量；
将上述硅酸钙与氟硅酸铜混合，将氮化铝粉加入到3-5倍水中，搅拌均匀后加入到硅酸钙与氟硅酸铜的混合物中，搅拌后加入纳米玉石粉，80-100℃下搅拌加热30-40分钟，得料a；将粘土与铁矿渣粉混合，600-700℃煅烧2-3小时，与上述料a、玫瑰精油混合，充分研磨，加入剩余各原料，充分搅拌，烘干，即得所述复合填料。
一种导电粉末涂料的制备方法，包括以下步骤：
将上述各原料加到高速混料机，经干混合后加到挤出机，在熔融挤出、混炼、冷却、压片，再经粉碎机粉碎、分级、过筛、包装，即得所述导电粉末涂料。
本发明的优点是：
本发明涂膜具有很好的耐湿热和耐高低温性，流平性、柔韧性、抗冲击性强，涂料对钢管的附着力好,钢管的防腐性能也得到了提高。
具体实施方式
实施例1，
一种导电粉末涂料，它是由下述重量份（公斤）的原料组成的：
E-42环氧树脂80、炭黑15、双氰胺20、酚醛树脂10、纳米二氧化硅10-15、导电硫酸钡15、导电聚苯胺4、聚山梨酯803.5、三烯丙基异氰脲酸酯1-2、四甲氧基甲基甘脲2、复合填料20；
所述的复合填料是由下述重量份的原料组成的：
粘土40、铁矿渣粉50、硅酸钙20、氟硅酸铜3、氮化铝粉2、纳米玉石粉5、双巯基乙酸异辛酯二正辛基锡0.3、玫瑰精油0.6、水适量；
将上述硅酸钙与氟硅酸铜混合，将氮化铝粉加入到5倍水中，搅拌均匀后加入到硅酸钙与氟硅酸铜的混合物中，搅拌后加入纳米玉石粉，100℃下搅拌加热40分钟，得料a；将粘土与铁矿渣粉混合，700℃煅烧2小时，与上述料a、玫瑰精油混合，充分研磨，加入剩余各原料，充分搅拌，烘干，即得所述复合填料。
一种导电粉末涂料的制备方法，包括以下步骤：
将上述各原料加到高速混料机，经干混合后加到挤出机，在熔融挤出、混炼、冷却、压片，再经粉碎机粉碎、分级、过筛、包装，即得所述导电粉末涂料。
性能测试：
附着力1级；
抗冲击强度（J）：≥11；
抗40弯曲：无裂纹；
耐溶剂：240小时，无变化；
盐雾试验（1000h）：无变化。
Claims (2)
1.一种导电粉末涂料，其特征在于它是由下述重量份的原料组成的：
E-42环氧树脂70-80、炭黑10-15、双氰胺10-20、酚醛树脂6-10、纳米二氧化硅10-15、导电硫酸钡10-15、导电聚苯胺4-6、聚山梨酯802.0-3.5、三烯丙基异氰脲酸酯1-2、四甲氧基甲基甘脲2-3、复合填料10-20；
所述的复合填料是由下述重量份的原料组成的：
粘土40-50、铁矿渣粉40-50、硅酸钙10-20、氟硅酸铜2-3、氮化铝粉1-2、纳米玉石粉5-7、双巯基乙酸异辛酯二正辛基锡0.2-0.3、玫瑰精油0.6-1、水适量；
将上述硅酸钙与氟硅酸铜混合，将氮化铝粉加入到3-5倍水中，搅拌均匀后加入到硅酸钙与氟硅酸铜的混合物中，搅拌后加入纳米玉石粉，80-100℃下搅拌加热30-40分钟，得料a；将粘土与铁矿渣粉混合，600-700℃煅烧2-3小时，与上述料a、玫瑰精油混合，充分研磨，加入剩余各原料，充分搅拌，烘干，即得所述复合填料。
2.一种如权利要求1所述的导电粉末涂料的制备方法，其特征在于包括以下步骤：
将上述各原料加到高速混料机，经干混合后加到挤出机，在熔融挤出、混炼、冷却、压片，再经粉碎机粉碎、分级、过筛、包装，即得所述导电粉末涂料。