CN103497627A - Thermo-set hammer-tone art powdery paint - Google Patents
Thermo-set hammer-tone art powdery paint Download PDFInfo
- Publication number
- CN103497627A CN103497627A CN201310395110.8A CN201310395110A CN103497627A CN 103497627 A CN103497627 A CN 103497627A CN 201310395110 A CN201310395110 A CN 201310395110A CN 103497627 A CN103497627 A CN 103497627A
- Authority
- CN
- China
- Prior art keywords
- parts
- stria
- powder
- mixed
- malleolar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a thermo-set hammer-tone art powdery paint which is composed of the raw materials of, by weight: 60-70 parts of epoxy resin E12, 1-2 parts of zirconia, 2-3 parts of urotropine, 10-13 parts of wollastonite powder, 1-2 parts of lignin sodium sulfonate, 12-16 parts of polyamide polyamine epichlorohydrin resin, 2-4 parts of aluminum nitride, 1-2 parts of aniline methyl triethoxy silane, 0.1-4 parts of a hammer-tone agent, 0.1-0.3 parts of cobalt ethylhexanoate, 0.1-0.2 parts of tetrachloroisophthalonitrile, and 10-20 parts of a composite filling material. A coat obtained by using the paint provided by the invention has good impact strength and wear resistance, and decorative performance and good appearance. The paint can be widely applied in coating and protection of the metal surfaces of steel office furniture, safes, security doors, windows, and the like.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of thermosetting fine arts powder coating of malleolar stria.
Background technology
The maximum growth field in China's powder coating and their application market is: shipping industry and pipeline industry.The problem existed is that shock-resistance and water absorbability are to be improved and improve, and the researchist concentrates on main energy in the modification with various base-materials.The Anti-Corrosive Epoxy Powder Paint for Pipes of domestic production is coated with and is contained in package stability and applies the application property aspect, with external quality products, compares certain gap is still arranged.Therefore the overall quality that constantly improves powder coating is the important development direction of current coating research.
Summary of the invention
The object of the invention is exactly for a kind of thermosetting fine arts powder coating of malleolar stria is provided.
The present invention is achieved by the following technical solutions:
A kind of thermosetting fine arts powder coating of malleolar stria is characterized in that what it was comprised of the raw material of following weight parts:
Epoxy resin E12 60-70, zirconium white 1-2, urotropine 2-3, wollastonite powder 10-13, sodium lignosulfonate 1-2, Polyamide-Polyamsne-Epichlorohydrin resin 12-16, aluminium nitride 2-4, anilinomethyl triethoxysilane 1-2, mallear stria agent 0.1-4, cobalt iso-octoate 0.1-0.3, termil 0.1-0.2, compounded mix 10-20;
Described compounded mix is comprised of the raw material of following weight parts:
Laterite 30-40, silicon nitride 10-13, aluminium hydroxide 5-7, phthalic ester 2-3, jade powder 2-4, polyvinyl butyral acetal ester 2-3, aminopropyl triethoxysilane 1-3;
Above-mentioned laterite is calcined under 600-700 ℃ to 2-3 hour, mixed with silicon nitride, aluminium hydroxide, aminopropyl triethoxysilane after discharging is cooling, 800-1000 rev/min of dispersed with stirring 3-5 minute, must expect a; Phthalic ester is mixed with the polyvinyl butyral acetal ester, at 50-60 ℃ of lower insulated and stirred 2-4 minute, join in above-mentioned material a, then add the jade powder, fully grind, cross the 60-100 mesh sieve, obtain described compounded mix.
A kind of preparation method of thermosetting fine arts powder coating of malleolar stria comprises the following steps:
After fully being mixed, above-mentioned wollastonite powder, sodium lignosulfonate, aluminium nitride add anilinomethyl triethoxysilane, be heated to 60-65 ℃, 300-500 rev/min of dispersed with stirring 4-6 minute, be cooled to normal temperature, mix with each raw material except the mallear stria agent, be sent to mixing extrusion in high-speed extruder, then after the compressing tablet fragmentation, be dry mixed with the mallear stria agent again, abrasive dust, sieved, obtained described thermosetting fine arts powder coating of malleolar stria.
Advantage of the present invention is:
Paint coatings of the present invention has good shock resistance and wear resistance, has ornamental and aesthetic appearance simultaneously, can be widely used in application and the protection of the metallic surfaces such as steel office furniture, strong box, antitheft door, window.
Embodiment
Embodiment 1,
A kind of thermosetting fine arts powder coating of malleolar stria, it is comprised of the raw material of following weight parts (kilogram):
Epoxy resin E12 70, zirconium white 2, urotropine 2, wollastonite powder 13, sodium lignosulfonate 2, Polyamide-Polyamsne-Epichlorohydrin resin 16, aluminium nitride 4, anilinomethyl triethoxysilane 2, mallear stria agent 1, cobalt iso-octoate 0.3, termil 0.2, compounded mix 20;
Described compounded mix is comprised of the raw material of following weight parts:
Laterite 40, silicon nitride 13, aluminium hydroxide 5, phthalic ester 3, jade powder 2, polyvinyl butyral acetal ester 2, aminopropyl triethoxysilane 1;
Above-mentioned laterite is calcined 2 hours under 700 ℃, and discharging mixes with silicon nitride, aluminium hydroxide, aminopropyl triethoxysilane after cooling, and 1000 rev/mins of dispersed with stirring 3 minutes, must expect a; Phthalic ester is mixed with the polyvinyl butyral acetal ester, 60 ℃ of lower insulated and stirred 24 minutes, join in above-mentioned material a, then add the jade powder, fully grind, cross 100 mesh sieves, obtain described compounded mix.
A kind of preparation method of thermosetting fine arts powder coating of malleolar stria comprises the following steps:
After fully being mixed, above-mentioned wollastonite powder, sodium lignosulfonate, aluminium nitride add anilinomethyl triethoxysilane, be heated to 65 ℃, 500 rev/mins of dispersed with stirring 4 minutes, be cooled to normal temperature, mix with each raw material except the mallear stria agent, be sent to mixing extrusion in high-speed extruder, then after the compressing tablet fragmentation, be dry mixed with the mallear stria agent again, abrasive dust, sieved, obtained described thermosetting fine arts powder coating of malleolar stria.
Performance test:
Shock resistance: >=50kg/cm;
Hardness: 2H.
Claims (2)
1. a thermosetting fine arts powder coating of malleolar stria is characterized in that what it was comprised of the raw material of following weight parts:
Epoxy resin E12 60-70, zirconium white 1-2, urotropine 2-3, wollastonite powder 10-13, sodium lignosulfonate 1-2, Polyamide-Polyamsne-Epichlorohydrin resin 12-16, aluminium nitride 2-4, anilinomethyl triethoxysilane 1-2, mallear stria agent 0.1-4, cobalt iso-octoate 0.1-0.3, termil 0.1-0.2, compounded mix 10-20;
Described compounded mix is comprised of the raw material of following weight parts:
Laterite 30-40, silicon nitride 10-13, aluminium hydroxide 5-7, phthalic ester 2-3, jade powder 2-4, polyvinyl butyral acetal ester 2-3, aminopropyl triethoxysilane 1-3;
Above-mentioned laterite is calcined under 600-700 ℃ to 2-3 hour, mixed with silicon nitride, aluminium hydroxide, aminopropyl triethoxysilane after discharging is cooling, 800-1000 rev/min of dispersed with stirring 3-5 minute, must expect a; Phthalic ester is mixed with the polyvinyl butyral acetal ester, at 50-60 ℃ of lower insulated and stirred 2-4 minute, join in above-mentioned material a, then add the jade powder, fully grind, cross the 60-100 mesh sieve, obtain described compounded mix.
2. the preparation method of a thermosetting fine arts powder coating of malleolar stria as claimed in claim 1 is characterized in that comprising the following steps:
After fully being mixed, above-mentioned wollastonite powder, sodium lignosulfonate, aluminium nitride add anilinomethyl triethoxysilane, be heated to 60-65 ℃, 300-500 rev/min of dispersed with stirring 4-6 minute, be cooled to normal temperature, mix with each raw material except the mallear stria agent, be sent to mixing extrusion in high-speed extruder, then after the compressing tablet fragmentation, be dry mixed with the mallear stria agent again, abrasive dust, sieved, obtained described thermosetting fine arts powder coating of malleolar stria.