Summary of the invention
The invention provides a kind of GCr15 Heat Treatment Of Steel method, utilize the method can improve the comprehensive mechanical property of GCr15 steel.
The invention provides a kind of GCr15 Heat Treatment Of Steel method, step is as follows:
1), first GCr15 steel is heated to 960-980 DEG C, heating 30-50min; Then in stove, be cooled to 800-820 DEG C to be incubated 3-4 hour; Afterwards GCr15 steel is warming up to again 900-920 DEG C of insulation 20-30min; Then in stove, be cooled to less than 620 DEG C air coolings of coming out of the stove;
2), 900-920 DEG C is heated to, quenching;
3) low-temperaturetempering process is carried out when, being cooled to 160-180 DEG C.
Preferably, GCr15 steel is first heated to 970 DEG C in (1) by step, heating 40min; Then in stove, be cooled to 810 DEG C to be incubated 3 hours; Afterwards GCr15 steel is warming up to again 910 DEG C of insulation 25min; Then in stove, be cooled to less than 620 DEG C air coolings of coming out of the stove.
Preferably, described in step (2), the medium of quenching is quenching oil, and the temperature of described quenching is 40-50 DEG C.
Preferably, described in step (2), the temperature of quenching is 45 DEG C.
Preferably, in step (3), the time of tempering is 1-2 hour.
Preferably, in step (3), the time of tempering is 1.5 hours.
Apply heat treating method of the present invention, GCr15 steel obtains the mechanical properties such as good intensity, hardness, effectively improves the over-all properties of GCr15 steel.
Embodiment
Following embodiment is convenient to understand the present invention better, but does not limit the present invention.
embodiment 1
A kind of GCr15 Heat Treatment Of Steel method of the present invention, step is as follows:
1), first GCr15 steel is heated to 970 DEG C, heating 40min; Then in stove, be cooled to 810 DEG C to be incubated 3 hours; Afterwards GCr15 steel is warming up to again 910 DEG C of insulation 25min; Then in stove, be cooled to less than 620 DEG C air coolings of coming out of the stove;
2), be heated to 910 DEG C, quench with quenching oil, quenching temperature is 45 DEG C;
3), carry out low-temperaturetempering process when being cooled to 170 DEG C, tempering time is 1.5 hours.
embodiment 2
A kind of GCr15 Heat Treatment Of Steel method of the present invention, step is as follows:
1), first GCr15 steel is heated to 980 DEG C, heating 30min; Then in stove, be cooled to 800 DEG C to be incubated 3.5 hours; Afterwards GCr15 steel is warming up to again 900 DEG C of insulation 20min; Then in stove, be cooled to less than 620 DEG C air coolings of coming out of the stove;
2), be heated to 900 DEG C, quench with quenching oil, quenching temperature is 40 DEG C;
3), carry out low-temperaturetempering process when being cooled to 160 DEG C, tempering time is 2 hours.
embodiment 3
A kind of GCr15 Heat Treatment Of Steel method of the present invention, step is as follows:
1), first GCr15 steel is heated to 960 DEG C, heating 50min; Then in stove, be cooled to 820 DEG C to be incubated 4 hours; Afterwards GCr15 steel is warming up to again 920 DEG C of insulation 30min; Then in stove, be cooled to less than 620 DEG C air coolings of coming out of the stove;
2), be heated to 920 DEG C, quench with quenching oil, quenching temperature is 50 DEG C;
3), carry out low-temperaturetempering process when being cooled to 180 DEG C, tempering time is 1 hour.
embodiment 4
A kind of GCr15 Heat Treatment Of Steel method of the present invention, step is as follows:
1), first GCr15 steel is heated to 960 DEG C, heating 50min; Then in stove, be cooled to 820 DEG C to be incubated 4 hours; Afterwards GCr15 steel is warming up to again 900 DEG C of insulation 30min; Then in stove, be cooled to less than 620 DEG C air coolings of coming out of the stove;
2), be heated to 920 DEG C, quench with quenching oil, quenching temperature is 40 DEG C;
3), carry out low-temperaturetempering process when being cooled to 160 DEG C, tempering time is 1 hour.
embodiment 5
A kind of GCr15 Heat Treatment Of Steel method of the present invention, step is as follows:
1), first GCr15 steel is heated to 960 DEG C, heating 50min; Then in stove, be cooled to 800 DEG C to be incubated 4 hours; Afterwards GCr15 steel is warming up to again 900 DEG C of insulation 30min; Then in stove, be cooled to less than 620 DEG C air coolings of coming out of the stove;
2), be heated to 910 DEG C, quench with quenching oil, quenching temperature is 50 DEG C;
3), carry out low-temperaturetempering process when being cooled to 160 DEG C, tempering time is 1.5 hours.
embodiment 6
A kind of GCr15 Heat Treatment Of Steel method of the present invention, step is as follows:
(1), first GCr15 steel is heated to 970 DEG C, heating 50min; Then in stove, be cooled to 820 DEG C to be incubated 4 hours; Afterwards GCr15 steel is warming up to again 900 DEG C of insulation 30min; Then in stove, be cooled to less than 620 DEG C air coolings of coming out of the stove;
(2), be heated to 910 DEG C, quench with quenching oil, quenching temperature is 45 DEG C;
(3), carry out low-temperaturetempering process when being cooled to 170 DEG C, tempering time is 2 hours.
embodiment 7
A kind of GCr15 Heat Treatment Of Steel method of the present invention, step is as follows:
(1), first GCr15 steel is heated to 965 DEG C, heating 50min; Then in stove, be cooled to 805 DEG C to be incubated 4 hours; Afterwards GCr15 steel is warming up to again 900 DEG C of insulation 30min; Then in stove, be cooled to less than 620 DEG C air coolings of coming out of the stove;
(2), be heated to 910 DEG C, quench with quenching oil, quenching temperature is 45 DEG C;
(3), carry out low-temperaturetempering process when being cooled to 165 DEG C, tempering time is 2 hours.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.