CN103483975A - 一种船舶油性沥青防锈漆 - Google Patents
一种船舶油性沥青防锈漆 Download PDFInfo
- Publication number
- CN103483975A CN103483975A CN201310468396.8A CN201310468396A CN103483975A CN 103483975 A CN103483975 A CN 103483975A CN 201310468396 A CN201310468396 A CN 201310468396A CN 103483975 A CN103483975 A CN 103483975A
- Authority
- CN
- China
- Prior art keywords
- rust
- resisting paint
- asphalt
- environment
- hull bottom
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种船舶油性沥青防锈漆,由下列百分比的成分混合组成:环氧树脂10%~30%;硫酸钡10%~12%;有机膨润土5~7%;硅石粉5%~12%;羟基乙酸10%~20%;桐油酸5%~10%;滑石粉5%~8%;去离子水余量。原料无毒,且环境友好,因此生产和使用过程对人体毒害小,且对环境污染低;本发明是对传统的沥青船底防锈漆进行改进、完善,主要表现在用氯醚树脂对沥青进行改性,与传统的沥青船底防锈漆相比,氯醚改性沥青船底防锈漆无毒、环保,比传统的沥青防锈漆性能更优秀。
Description
技术领域
本发明涉及一种防锈漆,尤其涉及一种船舶油性沥青防锈漆。
背景技术
海洋的腐蚀环境复杂,可以分为海洋大气区(常年不接触海水的部分)、海洋飞溅区(海水的飞溅能够喷洒到的部位)、海洋潮差区(海水涨潮时能够被海水浸没的部位)、海洋全浸区(常年被海水浸泡的区域)和海底泥土区(海水全浸区以下的部分);腐蚀类型又分为均匀腐蚀、点蚀、缝隙腐蚀、湍流腐蚀、空泡腐蚀、电偶腐蚀和腐蚀疲劳等。船舶,尤其是海洋船舶,所面临的环境十分复杂,船底的海洋全浸区,长年浸泡在高盐浓度的环境中,对防腐涂料的要求也较高。因此,如何开发一种针对船体,尤其是船底防锈的氯醚改性沥青防锈漆,是本领域一个技术问题。
发明内容
针对现有技术存在的不足,本发明所要解决的技术问题是,提供一种具有无毒、无污染、强附着力、漆膜致密、防锈性好等特点的船舶油性沥青防锈漆。
为解决上述技术问题,本发明所采取的技术方案是:一种船舶油性沥青防锈漆,由下列重量百分比的成分混合组成:
环氧树脂 10%~30%;
硫酸钡 10%~12%;
有机膨润土 5~7%;
硅石粉 5%~12%;
羟基乙酸 10%~20%;
桐油酸 5%~10%;
滑石粉 5%~8%;
去离子水 余量。
本发明船舶油性沥青防锈漆的优点是:原料无毒,且环境友好,因此生产和使用过程对人体毒害小,且对环境污染低;本发明是对传统的沥青船底防锈漆进行改进、完善,主要表现在用氯醚树脂对沥青进行改性,与传统的沥青船底防锈漆相比,氯醚改性沥青船底防锈漆无毒、环保,比传统的沥青防锈漆性能更优秀。
具体实施方式
下面结合具体实施例对本发明做进一步详细说明;
本发明船舶油性沥青防锈漆,由下列重量百分比的成分混合组成:
环氧树脂 10%~30%;
硫酸钡 10%~12%;
有机膨润土 5~7%;
硅石粉 5%~12%;
羟基乙酸 10%~20%;
桐油酸 5%~10%;
滑石粉 5%~8%;
去离子水 余量。
当然,上述说明并非是对本发明的限制,本发明也并不限于上述举例,本技术领域的普通技术人员,在本发明的实质范围内,作出的变化、改型、添加或替换,都应属于本发明的保护范围。
Claims (1)
1.一种船舶油性沥青防锈漆,其特征在于:由下列重量百分比的成分混合组成:
环氧树脂 10%~30%;
硫酸钡 10%~12%;
有机膨润土 5~7%;
硅石粉 5%~12%;
羟基乙酸 10%~20%;
桐油酸 5%~10%;
滑石粉 5%~8%;
去离子水 余量。